CN107384372A - A kind of LED fluorescent powder composition - Google Patents
A kind of LED fluorescent powder composition Download PDFInfo
- Publication number
- CN107384372A CN107384372A CN201710692038.3A CN201710692038A CN107384372A CN 107384372 A CN107384372 A CN 107384372A CN 201710692038 A CN201710692038 A CN 201710692038A CN 107384372 A CN107384372 A CN 107384372A
- Authority
- CN
- China
- Prior art keywords
- parts
- fluorescent powder
- powder composition
- led fluorescent
- nano
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of LED fluorescent powder composition, it is characterised in that includes the component of following parts by weight:Red fluorescence powder:20 ~ 35 parts;Yellow fluorescent powder:5 ~ 10 parts;Blue colour fluorescent powder:1 ~ 7 part;Nano silicon:1 ~ 6 part;Nano-calcium carbonate:3 ~ 8 parts;Organic adhesive:2 ~ 7 parts.A kind of LED fluorescent powder composition of the present invention, the white light being mixed into reach more than 92% close to preferable white-light spectrum, the full turgor of color, and fidelity is high.
Description
Technical field
The present invention relates to a kind of LED fluorescent powder composition.
Background technology
In recent years, with light emitting diode(LED)Gradually stepping up for luminous efficiency and being gradually reduced for cost, LED make
It is a kind of solid-state semiconductor material that can convert electrical energy into visible ray for a kind of new environmental type solid light source
Material, compared with other light sources, LED have energy-conservation, safety, long lifespan, energy consumption are low, generate heat less, brightness height, waterproof, shockproof, easy tune
The advantages that light, light beam are concentrated, are easy to maintenance, has become modern illumination development and the inexorable trend in future, white light LEDs are referred to as
" 21 century green light source ".
At present, gallium nitride based LED obtains white light main method and had:Blue-ray LED+yellow fluorescent powder, three-color LED synthesis are white
3 kinds of light, purple LED+three-color phosphor methods.Commercial white light LEDs are to utilize the GaN for launching 450-470 nano blue lights
Matrix LED chip and the blue light of surface coating excite the yttrium aluminate fluorescent material of the fluorescent material, mainly cerium dopping of yellow emission.This
Kind of commercial fluorescent material is there is also some shortcomings, the unstability of mainly poor color saturation and colour temperature.Color saturation compared with
Difference is due to lack red light portion in white light, and the unstability of colour temperature is due to that use for a long time moves back LED and fluorescent material performance
Caused by change.
Burst of ultraviolel white LED light source is to excite the fluorescent material of red, green, blue three primary colours assorted glimmering to produce by LED light
Light, remix what these fluorescence and LED light were realized.This white light LEDs refer to because three primary colours are various, thus with high colour developing
Number, high illumination effect, and adjustable color, and this fluorescence system is readily available, so that this mode turns into instantly
Research emphasis and focus, and be expected to turn into following white LED light source research dominant direction.
RGB fluorescent material is coordinated to prepare white light LEDs as excitaton source using ultraviolet LED, due to the fluorescent material of different substrates
Between there is radiation to reabsorb, can increase energy loss, reduce luminous efficiency, therefore the single-phase fluorescent material that ultraviolet LED excites
As mainstream development trend;Reported ultraviolet LED excites single-phase fluorescent material to have a lot, such as application number CN106929011A
The white emitting fluorescent powder that a kind of ultraviolet LED excites is provided in Chinese invention patent, its chemical general formula is M1-x-y-
ZSmxTbyTmzAlSiN3-2 (x+y+z)/2, wherein:M is at least one of Ca, Sr, Ba, 0.001≤x≤0.2,0.001
≤ y≤0.1,0.001≤z≤0.2, the white emitting fluorescent powder can launch white light under wavelength 250-390nm ultraviolet excitations, its
Excitation wavelength is shorter, and excitation spectrum scope is wide.
The content of the invention
To solve above-mentioned problem, it is an object of the invention to provide a kind of LED fluorescent powder composition and its preparation
Method.A kind of LED fluorescent powder composition, the white light being mixed into reach close to preferable white-light spectrum, the full turgor of color
To more than 92%, fidelity is high.
To reach above-mentioned purpose, the technical scheme is that:
A kind of LED fluorescent powder composition, include the component of following parts by weight:Red fluorescence powder:20 ~ 35 parts;Yellow fluorescent powder:
5 ~ 10 parts;Blue colour fluorescent powder:1 ~ 7 part;Nano silicon:1 ~ 6 part;Nano-calcium carbonate:3 ~ 8 parts;Organic adhesive:2 ~ 7 parts.
Further, the component of following parts by weight is included:Red fluorescence powder:25 ~ 30 parts;Yellow fluorescent powder:8 ~ 10 parts;
Blue colour fluorescent powder:1 ~ 5 part;Nano silicon:1 ~ 3 part;Nano-calcium carbonate:3 ~ 5 parts;Organic adhesive:2 ~ 4 parts.
Further, the component of following parts by weight is included:Red fluorescence powder:28 parts;Yellow fluorescent powder:9 parts;Blueness is glimmering
Light powder:2 parts;Nano silicon:2 parts;Nano-calcium carbonate:3.5 part;Organic adhesive:3 parts.
Further, the red fluorescence powder is fluogermanic acid potassium, and particle diameter is 10 ~ 30 μm.
Further, the yellow fluorescent powder is silicate, 5 μm of particle diameter <.
Further, the blue colour fluorescent powder is the graphite phase carbon nitride after nitric acid treatment, and particle diameter is 2 ~ 12 μm.
Further, the particle diameter of the nano silicon is 10 ~ 30nm.
Further, the particle diameter of the nano-calcium carbonate is 20 ~ 50nm.
Further, organic adhesive is waterglass or any of phenolic resin or Lauxite.
The beneficial effects of the present invention are:
A kind of LED fluorescent powder composition of the present invention, the white light being mixed into are full close to preferable white-light spectrum, color
Degree reaches more than 92%, and fidelity is high.
Embodiment
In order to make the purpose , technical scheme and advantage of the present invention be clearer, it is further detailed with reference to embodiments
Describe in detail bright.
Embodiment 1
A kind of LED fluorescent powder composition, include the component of following parts by weight:Red fluorescence powder:23 parts;Yellow fluorescent powder:6
Part;Blue colour fluorescent powder:5 parts;Nano silicon:1 part;Nano-calcium carbonate:7 parts;Organic adhesive:4 parts.
Embodiment 2
A kind of LED fluorescent powder composition, include the component of following parts by weight:Red fluorescence powder:20 parts;Yellow fluorescent powder:5
Part;Blue colour fluorescent powder:7 parts;Nano silicon:3 parts;Nano-calcium carbonate:8 parts;Organic adhesive:2 parts.
Embodiment 3
A kind of LED fluorescent powder composition, include the component of following parts by weight:Red fluorescence powder:28 parts;Yellow fluorescent powder:9
Part;Blue colour fluorescent powder:2 parts;Nano silicon:2 parts;Nano-calcium carbonate:3.5 part;Organic adhesive:3 parts.
Embodiment 4
A kind of LED fluorescent powder composition, include the component of following parts by weight:Red fluorescence powder:30 parts;Yellow fluorescent powder:8
Part;Blue colour fluorescent powder:1 part;Nano silicon:5 parts;Nano-calcium carbonate:5 parts;Organic adhesive:7 parts.
Embodiment 5
A kind of LED fluorescent powder composition, include the component of following parts by weight:Red fluorescence powder:35 parts;Yellow fluorescent powder:10
Part;Blue colour fluorescent powder:3 parts;Nano silicon:6 parts;Nano-calcium carbonate:3 parts;Organic adhesive:5 parts.
A kind of LED fluorescent powder composition of the present invention, the white light being mixed into are satisfied close to preferable white-light spectrum, color
Turgor reaches more than 92%, and fidelity is high.
It should be noted that the above embodiments are merely illustrative of the technical solutions of the present invention and it is unrestricted.Although with reference to compared with
The present invention is described in detail good embodiment, it will be understood by those within the art that, can be to the technology of invention
Scheme is modified or equivalent substitution, and without departing from the scope of technical solution of the present invention, it all should cover the power in the present invention
In sharp claimed range.
Claims (9)
1. a kind of LED fluorescent powder composition, it is characterised in that include the component of following parts by weight:Red fluorescence powder:20~35
Part;Yellow fluorescent powder:5 ~ 10 parts;Blue colour fluorescent powder:1 ~ 7 part;Nano silicon:1 ~ 6 part;Nano-calcium carbonate:3 ~ 8 parts;Have
Machine adhesive:2 ~ 7 parts.
2. a kind of LED fluorescent powder composition according to claim 1, it is characterised in that include the group of following parts by weight
Point:Red fluorescence powder:25 ~ 30 parts;Yellow fluorescent powder:8 ~ 10 parts;Blue colour fluorescent powder:1 ~ 5 part;Nano silicon:1 ~ 3 part;
Nano-calcium carbonate:3 ~ 5 parts;Organic adhesive:2 ~ 4 parts.
3. a kind of LED fluorescent powder composition according to claim 1, it is characterised in that include the group of following parts by weight
Point:Red fluorescence powder:28 parts;Yellow fluorescent powder:9 parts;Blue colour fluorescent powder:2 parts;Nano silicon:2 parts;Nano-calcium carbonate:
3.5 part;Organic adhesive:3 parts.
4. a kind of LED fluorescent powder composition according to claim 1, it is characterised in that the red fluorescence powder is fluorine germanium
Sour potassium, particle diameter are 10 ~ 30 μm.
5. a kind of LED fluorescent powder composition according to claim 1, it is characterised in that the yellow fluorescent powder is silicic acid
Salt, 5 μm of particle diameter <.
6. a kind of LED fluorescent powder composition according to claim 1, it is characterised in that the blue colour fluorescent powder is process
Graphite phase carbon nitride after nitric acid treatment, particle diameter are 2 ~ 12 μm.
A kind of 7. LED fluorescent powder composition according to claim 1, it is characterised in that the grain of the nano silicon
Footpath is 10 ~ 30nm.
A kind of 8. LED fluorescent powder composition according to claim 1, it is characterised in that the particle diameter of the nano-calcium carbonate
For 20 ~ 50nm.
9. a kind of LED fluorescent powder composition according to claim 1, it is characterised in that organic adhesive is water glass
Glass or any of phenolic resin or Lauxite.