CN107384149A - A kind of ERW rust preventive paint technique and its spray painting used - Google Patents

A kind of ERW rust preventive paint technique and its spray painting used Download PDF

Info

Publication number
CN107384149A
CN107384149A CN201710648726.XA CN201710648726A CN107384149A CN 107384149 A CN107384149 A CN 107384149A CN 201710648726 A CN201710648726 A CN 201710648726A CN 107384149 A CN107384149 A CN 107384149A
Authority
CN
China
Prior art keywords
parts
powder
minutes
welded tube
revs
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710648726.XA
Other languages
Chinese (zh)
Inventor
王诗斌
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chaohu Pengyuan Metal Pipe Co Ltd
Original Assignee
Chaohu Pengyuan Metal Pipe Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Chaohu Pengyuan Metal Pipe Co Ltd filed Critical Chaohu Pengyuan Metal Pipe Co Ltd
Priority to CN201710648726.XA priority Critical patent/CN107384149A/en
Publication of CN107384149A publication Critical patent/CN107384149A/en
Pending legal-status Critical Current

Abstract

A kind of ERW rust preventive paint technique and its spray painting used, four layers of mixture are smeared on welded tube, will spray painting is uniform is sprayed on surface of welded pipe, during spray painting, keep welded tube normal temperature；Anti-corrosive powder paint is equably sprayed on the surface of welded tube by spray gun by the way of electrostatic spraying, forms one layer of anticorrosive coat；Welded tube is transferred in bakery after will be spray coated, solidified 10~20 minutes, then natural cooling is that can obtain finished product.Welded Pipe of the present invention uses special processing method, welded tube overall performance is improved, makes welded tube that there is corrosion-resistant, impact resistance and wear-resisting effect, by painting, priming paint is corrosion-resistant, impact resistance and wear-resisting, paint better, one layer of anti-corrosive powder paint is finally sprayed, when being impacted, anticorrosive coat can only deform will not peeling off phenomenon, etch-proof ability will not be lost, can effectively extend the service life of welded tube, overall corrosion-resistant, impact resistance and wear-resisting effect are significantly improved.

Description

A kind of ERW rust preventive paint technique and its spray painting used
Technical field：
The present invention relates to coating process technical field, and in particular to a kind of ERW rust preventive paint technique and its spray used Paint.
Background technology：
ERW, the steel pipe made of hot rolling or cold-rolled steel sheet or steel coil strip weldering carry out straight seam welding on welding equipment Obtained pipe is all ERW, (because the weld of steel pipe is in alignment so gain the name).It is different according to purposes, has Different rear road production processes, the standard of ERW is part B/T3091-2008.
Steel pipes with straight is mainly used in public waterworks, petrochemical industry, chemical industry, power industry, agricultural filling at home Irrigate, urban construction.It is used as liquid conveying：Feedwater, draining.It is used as gas conveying：Coal gas, steam, liquefied petroleum gas.Make structure With：Make pile driving pipe, make bridge；Harbour, road, building structure pipe etc..
ERW surface antirust art in the market is done bad, directly influences the service life of ERW.
The content of the invention：
The technical problems to be solved by the invention are to overcome prior art to provide a kind of ERW rust preventive paint technique And its spray painting used.
The technical problems to be solved by the invention are realized using following technical scheme.
A kind of ERW rust preventive paint technique, it is characterised in that：Comprise the following steps：
Unsaturated polyester resin 7-9 parts, dipropylene 2-3 parts, dipropylene glycol methyl ether 1-4 parts are added into mixer In, stir 20 minutes, then add the deionized water of styrene-acrylic emulsion 7-12 parts and 1/3rd parts by weight, stir 12 minutes, turn Speed is 680 revs/min~750 revs/min, stops stirring, obtains mixture one；
Welded tube feeding supersonic wave cleaning machine is cleaned by ultrasonic, in cleaning process, said mixture one added clearly In wash water, cleaned, after the completion of take out, dry inside and outside wall moisture, then cryogenic freezing, in the environment of less than subzero 23 DEG C Continuous freezing more than 8 hours；
Aqueous acrylic emulsion 46-50 parts, soap both sexes antistatic additive 9-10 parts, talcum powder 5-8 parts, aluminum oxide 2- 5 parts, calcium acetate 2-5 parts, acetic acid nanofiber 2-5 parts, flavouring agent 1-2 parts, coloring agent 1-2 parts, graphite powder 1-3 parts, stir 9 points Clock, rotating speed are 920 revs/min~960 revs/min, stop stirring, obtain mixture two；
Welded tube, which takes out, is sent into heating room, and the temperature heated in room is risen into 80-90 DEG C from 0 DEG C in 10-13 minutes, kept 10-15 minutes, 0-13 DEG C is cooled to, mixture two is applied to surface of welded pipe；
By meteorological white carbon 2-4 parts, silicone emulsion 2-5 parts and lavender concentrated oil 9-11 parts, stir 9 minutes, rotating speed For 920 revs/min~960 revs/min, stop stirring, obtain mixture three；
Welded tube, which takes out, is sent into heating room, and the temperature heated in room is risen into 130-160 DEG C from 0 DEG C in 10-13 minutes, kept 10-15 minutes, 0-10 DEG C is cooled to, mixture three is applied to surface of welded pipe；
By meteorological white carbon 1-3 parts, silicone emulsion 10-13 parts and lavender concentrated oil 1-2 parts, stir 9 minutes, rotating speed For 920 revs/min~960 revs/min, stop stirring, obtain mixture four；
Welded tube, which takes out, is sent into heating room, and the temperature heated in room is risen into 400-420 DEG C from 0 DEG C in 10-13 minutes, kept 10-15 minutes, mixture four is applied to surface of welded pipe；
Normal temperature is cooled to, using alcohol wipe, polishing, after surface is smooth, welded tube is sent into and takes out feeding heating room, will heat Temperature in room rises to 70-83 DEG C from 0 DEG C in 10-13 minutes, is kept for 3-5 minutes；
Welded tube is sent into temperature-lowering room again, cold wind is sent into from all directions immediately, welded tube is cooled to normal temperature rapidly；
Will spray painting is uniform is sprayed on surface of welded pipe, during spray painting, keep welded tube normal temperature；
Anti-corrosive powder paint is equably sprayed on the surface of welded tube by spray gun by the way of electrostatic spraying, shape Into one layer of anticorrosive coat；
Welded tube is transferred in bakery after will be spray coated, solidified 10~20 minutes, then natural cooling is that can obtain into Product.
The specific preparation method of spray painting used is, by unsaturated polyester resin 7-9 parts, dipropylene 2-3 parts, dipropyl two Alcohol methyl ether 1-4 parts are added in mixer, are stirred 20 minutes, are then added going for styrene-acrylic emulsion 7-12 parts and 1/3rd parts by weight Ionized water, stir 12 minutes, rotating speed is 680 revs/min~750 revs/min；
Carboxymethyl cellulose 5-7 parts are added, are stirred 5 minutes, rotating speed is 610 revs/min~700 revs/min；
95% ethanol 30-40 parts are added in acrylic acid crosslinked resin 11-13 parts and stirred, are added in mixer, Stirring 10 minutes, rotating speed are 400 revs/min~580 revs/min, then add remaining deionized water and stir, are sprayed Paint.
Described anti-corrosive powder paint is formulated by the component of following weight：100 parts of polyester resin, mineral matter powder 5 Part, 0.1 part of graphene microchip, 1 part of sepiolite powder, 5 parts of pigment, 10 parts of nano titanium carbide, 0.5 part of selenium powder, rare earth oxide 1 Part, 0.5 part of curing agent, 15 parts of wax powder, 0.5 part of levelling agent, 0.5 part of brightener, 5 parts of zinc powder, 1 part of wollastonite in powder of calcining, denaturation 1 part of starch；
The preparation method of described anti-corrosive powder paint is as follows：
By polyester resin 3-5 parts, mineral matter powder 3-5 parts, sepiolite powder 3-5 parts, selenium powder 3-5 parts, rare earth oxide 3-5 Part, wax powder 3-5 parts, zinc powder 3-5 parts, calcining wollastonite in powder 3-5 parts and converted starch 3-5 parts are put into nylon ball grinder, continuously Ball milling 4-6 hours, 180-200 eye mesh screens are crossed, it is stand-by that collection obtains mixed powder；
By mixed powder in mixing tank with graphene microchip 3-5 parts, pigment 3-5 parts, nano titanium carbide 3-5 parts, solidification Agent 3-5 parts, levelling agent 3-5 parts and brightener 3-5 parts are fully pre-mixed, after the completion of be sent into extruder extrusion and tabletting, obtain piece Shape material；
Sheet feed powder is broken, it is sent into nylon ball grinder, continuous ball milling 4-6 hours, crosses 400-600 eye mesh screens, collection screen Lower thing obtains finished product anti-corrosive powder paint.
Described mineral matter powder from azurite, potassium feldspar, malachite green, malachite, natural marine stone, hauynite, tourmaline and One or both of muscovite or two or more combinations.
Described graphene microchip is the brilliant generation graphite carbon crystal of cellular fashion length with solid, the four of each carbon atom Individual valence electron all forms covalent bond and has been bound, it is impossible to the electron stream of displacement is formed, then cannot be conductive, and after generation Graphite carbon crystal utilizes the nano-milled mode of wet type, is formed with single direction grinding, and graphene microchip minimizing thickness is 5nm, Graphene microchip strengthens infrared radiation wavelength, and its wavelength peak-peak is at 7.5~9.5 μm.By adding graphite in coating Alkene microplate, surface of welded pipe resistivity can be reduced, while strengthen the degrees of fusion between each component.
The beneficial effects of the invention are as follows：Welded Pipe of the present invention uses special processing method, improves welded tube overall performance, makes Welded tube has corrosion-resistant, impact resistance and wear-resisting effect, and by painting, priming paint is corrosion-resistant, impact resistance and wear-resisting, effect of painting More preferably, finally spray one layer of anti-corrosive powder paint, when being impacted, anticorrosive coat can only deform will not peeling off phenomenon, Etch-proof ability will not be lost, can effectively extend the service life of welded tube, overall corrosion-resistant, impact resistance and wear-resisting effect obtain To being obviously improved.
Through experiment, the spray painting of this law technique Welded Pipe is contrasted with common method for paint spraying：
By experimental data, overall corrosion-resistant, impact resistance and wear-resisting effect are significantly improved.
Embodiment：
In order that the technical means, the inventive features, the objects and the advantages of the present invention are easy to understand, tie below Specific embodiment is closed, the present invention is expanded on further.
Embodiment 1：A kind of ERW rust preventive paint technique, comprises the following steps：
By in 1 part of 7 parts of unsaturated polyester resin, 2 parts of dipropylene, dipropylene glycol methyl ether addition mixer, stir 20 minutes, then add the deionized water of 7 parts of styrene-acrylic emulsion and 1/3rd parts by weight, stir 12 minutes, rotating speed for 680 turns/ Minute~750 revs/min, stop stirring, obtain mixture one；
Welded tube feeding supersonic wave cleaning machine is cleaned by ultrasonic, in cleaning process, said mixture one added clearly In wash water, cleaned, after the completion of take out, dry inside and outside wall moisture, then cryogenic freezing, in the environment of less than subzero 23 DEG C Continuous freezing more than 8 hours；
46 parts of aqueous acrylic emulsion, 9 parts of soap both sexes antistatic additive, 5 parts of talcum powder, 2 parts of aluminum oxide, calcium acetate 2 parts, 2 parts of acetic acid nanofiber, 1 part of flavouring agent, 1 part of coloring agent, 1 part of graphite powder, stir 9 minutes, rotating speed be 920 revs/min ~960 revs/min, stop stirring, obtain mixture two；
Welded tube, which takes out, is sent into heating room, and the temperature heated in room is risen into 80-90 DEG C from 0 DEG C in 10-13 minutes, kept 10-15 minutes, 0-13 DEG C is cooled to, mixture two is applied to surface of welded pipe；
By 9 parts of meteorological 2 parts of white carbon, 2 parts of silicone emulsion and lavender concentrated oil, stirring 9 minutes, rotating speed is 920 turns/ Minute~960 revs/min, stop stirring, obtain mixture three；
Welded tube, which takes out, is sent into heating room, and the temperature heated in room is risen into 130-160 DEG C from 0 DEG C in 10-13 minutes, kept 10-15 minutes, 0-10 DEG C is cooled to, mixture three is applied to surface of welded pipe；
By 1 part of meteorological 1 part of white carbon, 10 parts of silicone emulsion and lavender concentrated oil, stir 9 minutes, rotating speed 920 Rev/min~960 revs/min, stop stirring, obtain mixture four；
Welded tube, which takes out, is sent into heating room, and the temperature heated in room is risen into 400-420 DEG C from 0 DEG C in 10-13 minutes, kept 10-15 minutes, mixture four is applied to surface of welded pipe；
Normal temperature is cooled to, using alcohol wipe, polishing, after surface is smooth, welded tube is sent into and takes out feeding heating room, will heat Temperature in room rises to 70-83 DEG C from 0 DEG C in 10-13 minutes, is kept for 3-5 minutes；
Welded tube is sent into temperature-lowering room again, cold wind is sent into from all directions immediately, welded tube is cooled to normal temperature rapidly；
Will spray painting is uniform is sprayed on surface of welded pipe, during spray painting, keep welded tube normal temperature；
Anti-corrosive powder paint is equably sprayed on the surface of welded tube by spray gun by the way of electrostatic spraying, shape Into one layer of anticorrosive coat；
Welded tube is transferred in bakery after will be spray coated, solidified 10~20 minutes, then natural cooling is that can obtain into Product.
The specific preparation method of spray painting used is, by 7 parts of unsaturated polyester resin, 2 parts of dipropylene, DPG first In 1 part of addition mixer of ether, stir 20 minutes, then add the deionized water of 7 parts of styrene-acrylic emulsion and 1/3rd parts by weight, stir Mix 12 minutes, rotating speed is 680 revs/min~750 revs/min；
5 parts of carboxymethyl cellulose is added, is stirred 5 minutes, rotating speed is 610 revs/min~700 revs/min；
It will stir, add in mixer, stirring 10 in 95% ethanol, 30 parts of 11 parts of addition acrylic acid crosslinked resins Minute, rotating speed is 400 revs/min~580 revs/min, then adds remaining deionized water and stirs, is painted.
Described anti-corrosive powder paint is formulated by the component of following weight：100 parts of polyester resin, mineral matter powder 5 Part, 0.1 part of graphene microchip, 1 part of sepiolite powder, 5 parts of pigment, 10 parts of nano titanium carbide, 0.5 part of selenium powder, rare earth oxide 1 Part, 0.5 part of curing agent, 15 parts of wax powder, 0.5 part of levelling agent, 0.5 part of brightener, 5 parts of zinc powder, 1 part of wollastonite in powder of calcining, denaturation 1 part of starch；
The preparation method of anti-corrosive powder paint is as follows：
By 3 parts of polyester resin, 3 parts of mineral matter powder, 3 parts of sepiolite powder, 3 parts of selenium powder, 3 parts of rare earth oxide, 3 parts of wax powder, 3 parts of 3 parts of zinc powder, 3 parts of wollastonite in powder of calcining and converted starch are put into nylon ball grinder, continuous ball milling 4-6 hours, cross 180- 200 eye mesh screens, it is stand-by that collection obtains mixed powder；
By mixed powder in mixing tank with 3 parts of graphene microchip, 3 parts of pigment, 3 parts of nano titanium carbide, 3 parts of curing agent, 3 parts of levelling agent and the fully premixing of 3 parts of brightener, after the completion of be sent into extruder extrusion and tabletting, obtain sheet material；
Sheet feed powder is broken, it is sent into nylon ball grinder, continuous ball milling 4-6 hours, crosses 400-600 eye mesh screens, collection screen Lower thing obtains finished product anti-corrosive powder paint.
Mineral matter powder selects azurite, potassium feldspar, malachite green, malachite, natural marine stone, hauynite, tourmaline and muscovite One or both of or two or more combinations.
Graphene microchip is to generate graphite carbon crystal, four valency electricity of each carbon atom so that the cellular fashion length of solid is brilliant Son all forms covalent bond and has been bound, it is impossible to the electron stream of displacement is formed, then cannot be conductive, and graphitic carbon after generation Crystal utilizes the nano-milled mode of wet type, is formed with single direction grinding, graphene microchip minimizing thickness is 5nm, graphene Microplate strengthens infrared radiation wavelength, and its wavelength peak-peak is at 7.5~9.5 μm.By adding graphene microchip in coating, Surface of welded pipe resistivity can be reduced, while strengthens the degrees of fusion between each component.
Through experiment, the spray painting of this law technique Welded Pipe is contrasted with common method for paint spraying：
By experimental data, overall corrosion-resistant, impact resistance and wear-resisting effect are significantly improved.
Embodiment 2：A kind of ERW rust preventive paint technique, comprises the following steps：
By in 4 parts of 9 parts of unsaturated polyester resin, 3 parts of dipropylene, dipropylene glycol methyl ether addition mixers, stir 20 minutes, then add the deionized water of 12 parts of styrene-acrylic emulsion and 1/3rd parts by weight, stir 12 minutes, rotating speed for 680 turns/ Minute~750 revs/min, stop stirring, obtain mixture one；
Welded tube feeding supersonic wave cleaning machine is cleaned by ultrasonic, in cleaning process, said mixture one added clearly In wash water, cleaned, after the completion of take out, dry inside and outside wall moisture, then cryogenic freezing, in the environment of less than subzero 23 DEG C Continuous freezing more than 8 hours；
50 parts of aqueous acrylic emulsion, 10 parts of soap both sexes antistatic additive, 8 parts of talcum powder, 5 parts of aluminum oxide, acetic acid 5 parts of calcium, 5 parts of acetic acid nanofiber, 2 parts of flavouring agent, 2 parts of coloring agent, 3 parts of graphite powder, stir 9 minutes, rotating speed is 920 revs/min Clock~960 rev/min, stop stirring, obtain mixture two；
Welded tube, which takes out, is sent into heating room, and the temperature heated in room is risen into 80-90 DEG C from 0 DEG C in 10-13 minutes, kept 10-15 minutes, 0-13 DEG C is cooled to, mixture two is applied to surface of welded pipe；
By 11 parts of meteorological 4 parts of white carbon, 5 parts of silicone emulsion and lavender concentrated oil, stir 9 minutes, rotating speed 920 Rev/min~960 revs/min, stop stirring, obtain mixture three；
Welded tube, which takes out, is sent into heating room, and the temperature heated in room is risen into 130-160 DEG C from 0 DEG C in 10-13 minutes, kept 10-15 minutes, 0-10 DEG C is cooled to, mixture three is applied to surface of welded pipe；
By 2 parts of meteorological 3 parts of white carbon, 13 parts of silicone emulsion and lavender concentrated oil, stir 9 minutes, rotating speed 920 Rev/min~960 revs/min, stop stirring, obtain mixture four；
Welded tube, which takes out, is sent into heating room, and the temperature heated in room is risen into 400-420 DEG C from 0 DEG C in 10-13 minutes, kept 10-15 minutes, mixture four is applied to surface of welded pipe；
Normal temperature is cooled to, using alcohol wipe, polishing, after surface is smooth, welded tube is sent into and takes out feeding heating room, will heat Temperature in room rises to 70-83 DEG C from 0 DEG C in 10-13 minutes, is kept for 3-5 minutes；
Welded tube is sent into temperature-lowering room again, cold wind is sent into from all directions immediately, welded tube is cooled to normal temperature rapidly；
Will spray painting is uniform is sprayed on surface of welded pipe, during spray painting, keep welded tube normal temperature；
Anti-corrosive powder paint is equably sprayed on the surface of welded tube by spray gun by the way of electrostatic spraying, shape Into one layer of anticorrosive coat；
Welded tube is transferred in bakery after will be spray coated, solidified 10~20 minutes, then natural cooling is that can obtain into Product.
The specific preparation method of spray painting used is, by 9 parts of unsaturated polyester resin, 3 parts of dipropylene, DPG first In 4 parts of addition mixers of ether, stir 20 minutes, then add the deionized water of 12 parts of styrene-acrylic emulsion and 1/3rd parts by weight, Stirring 12 minutes, rotating speed are 680 revs/min~750 revs/min；
7 parts of carboxymethyl cellulose is added, is stirred 5 minutes, rotating speed is 610 revs/min~700 revs/min；
It will stir, add in mixer, stirring 10 in 95% ethanol, 40 parts of 13 parts of addition acrylic acid crosslinked resins Minute, rotating speed is 400 revs/min~580 revs/min, then adds remaining deionized water and stirs, is painted.
Described anti-corrosive powder paint is formulated by the component of following weight：100 parts of polyester resin, mineral matter powder 5 Part, 0.1 part of graphene microchip, 1 part of sepiolite powder, 5 parts of pigment, 10 parts of nano titanium carbide, 0.5 part of selenium powder, rare earth oxide 1 Part, 0.5 part of curing agent, 15 parts of wax powder, 0.5 part of levelling agent, 0.5 part of brightener, 5 parts of zinc powder, 1 part of wollastonite in powder of calcining, denaturation 1 part of starch；
The preparation method of anti-corrosive powder paint is as follows：
By 5 parts of polyester resin, 5 parts of mineral matter powder, 5 parts of sepiolite powder, 5 parts of selenium powder, 5 parts of rare earth oxide, 5 parts of wax powder, 5 parts of 5 parts of zinc powder, 5 parts of wollastonite in powder of calcining and converted starch are put into nylon ball grinder, continuous ball milling 4-6 hours, cross 180- 200 eye mesh screens, it is stand-by that collection obtains mixed powder；
By mixed powder in mixing tank with 5 parts of graphene microchip, 5 parts of pigment, 5 parts of nano titanium carbide, 5 parts of curing agent, 5 parts of levelling agent and the fully premixing of 5 parts of brightener, after the completion of be sent into extruder extrusion and tabletting, obtain sheet material；
Sheet feed powder is broken, it is sent into nylon ball grinder, continuous ball milling 4-6 hours, crosses 400-600 eye mesh screens, collection screen Lower thing obtains finished product anti-corrosive powder paint.
Mineral matter powder selects azurite, potassium feldspar, malachite green, malachite, natural marine stone, hauynite, tourmaline and muscovite One or both of or two or more combinations.
Graphene microchip is to generate graphite carbon crystal, four valency electricity of each carbon atom so that the cellular fashion length of solid is brilliant Son all forms covalent bond and has been bound, it is impossible to the electron stream of displacement is formed, then cannot be conductive, and graphitic carbon after generation Crystal utilizes the nano-milled mode of wet type, is formed with single direction grinding, graphene microchip minimizing thickness is 5nm, graphene Microplate strengthens infrared radiation wavelength, and its wavelength peak-peak is at 7.5~9.5 μm.By adding graphene microchip in coating, Surface of welded pipe resistivity can be reduced, while strengthens the degrees of fusion between each component.
Through experiment, the spray painting of this law technique Welded Pipe is contrasted with common method for paint spraying：
By experimental data, overall corrosion-resistant, impact resistance and wear-resisting effect are significantly improved.
General principle, principal character and the advantages of the present invention of the present invention has been shown and described above.The technology of the industry Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the simply explanation described in above-described embodiment and specification is originally The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its Equivalent thereof.

Claims (6)

  1. A kind of 1. ERW rust preventive paint technique, it is characterised in that：Comprise the following steps：
    Unsaturated polyester resin 7-9 parts, dipropylene 2-3 parts, dipropylene glycol methyl ether 1-4 parts are added in mixer, stirred Mix 20 minutes, then add the deionized water of styrene-acrylic emulsion 7-12 parts and 1/3rd parts by weight, stir 12 minutes, rotating speed is 680 revs/min~750 revs/min, stop stirring, obtain mixture one；
    Welded tube feeding supersonic wave cleaning machine is cleaned by ultrasonic, in cleaning process, said mixture one is added into rinse water In, cleaned, after the completion of take out, dry inside and outside wall moisture, then cryogenic freezing is continuous in the environment of less than subzero 23 DEG C Freezing more than 8 hours；
    Aqueous acrylic emulsion 46-50 parts, soap both sexes antistatic additive 9-10 parts, talcum powder 5-8 parts, aluminum oxide 2-5 parts, Calcium acetate 2-5 parts, acetic acid nanofiber 2-5 parts, flavouring agent 1-2 parts, coloring agent 1-2 parts, graphite powder 1-3 parts, stir 9 minutes, Rotating speed is 920 revs/min~960 revs/min, stops stirring, obtains mixture two；
    Welded tube, which takes out, is sent into heating room, and the temperature heated in room is risen into 80-90 DEG C from 0 DEG C in 10-13 minutes, keeps 10-15 Minute, 0-13 DEG C is cooled to, mixture two is applied to surface of welded pipe；
    By meteorological white carbon 2-4 parts, silicone emulsion 2-5 parts and lavender concentrated oil 9-11 parts, stir 9 minutes, rotating speed 920 Rev/min~960 revs/min, stop stirring, obtain mixture three；
    Welded tube, which takes out, is sent into heating room, and the temperature heated in room is risen into 130-160 DEG C from 0 DEG C in 10-13 minutes, keeps 10- 15 minutes, 0-10 DEG C is cooled to, mixture three is applied to surface of welded pipe；
    By meteorological white carbon 1-3 parts, silicone emulsion 10-13 parts and lavender concentrated oil 1-2 parts, stir 9 minutes, rotating speed is 920 revs/min~960 revs/min, stop stirring, obtain mixture four；
    Welded tube, which takes out, is sent into heating room, and the temperature heated in room is risen into 400-420 DEG C from 0 DEG C in 10-13 minutes, keeps 10- 15 minutes, mixture four is applied to surface of welded pipe；
    Normal temperature is cooled to, using alcohol wipe, polishing, after surface is smooth, welded tube is sent into and takes out feeding heating room, by heating room Temperature rise to 70-83 DEG C in 10-13 minutes from 0 DEG C, kept for 3-5 minutes；
    Welded tube is sent into temperature-lowering room again, cold wind is sent into from all directions immediately, welded tube is cooled to normal temperature rapidly；
    Will spray painting is uniform is sprayed on surface of welded pipe, during spray painting, keep welded tube normal temperature；
    Anti-corrosive powder paint is equably sprayed on the surface of welded tube by spray gun by the way of electrostatic spraying, forms one Layer anticorrosive coat；
    Welded tube is transferred in bakery after will be spray coated, solidified 10~20 minutes, then natural cooling is that can obtain finished product.
  2. 2. according to a kind of ERW rust preventive paint technique described in claim 1, it is characterised in that：The specific system of spray painting used Preparation Method is that unsaturated polyester resin 7-9 parts, dipropylene 2-3 parts, dipropylene glycol methyl ether 1-4 parts are added into mixer In, stir 20 minutes, then add the deionized water of styrene-acrylic emulsion 7-12 parts and 1/3rd parts by weight, stir 12 minutes, turn Speed is 680 revs/min~750 revs/min；
    Carboxymethyl cellulose 5-7 parts are added, are stirred 5 minutes, rotating speed is 610 revs/min~700 revs/min；
    95% ethanol 30-40 parts are added in acrylic acid crosslinked resin 11-13 parts and stirred, are added in mixer, are stirred 10 minutes, rotating speed was 400 revs/min~580 revs/min, then adds remaining deionized water and stirs, is painted.
  3. 3. according to a kind of ERW rust preventive paint technique described in claim 1, it is characterised in that：Described anticorrosive powder Coating is formulated by the component of following weight：100 parts of polyester resin, 5 parts of mineral matter powder, 0.1 part of graphene microchip, Hai Pao 1 part of stone flour, 5 parts of pigment, 10 parts of nano titanium carbide, 0.5 part of selenium powder, 1 part of rare earth oxide, 0.5 part of curing agent, 15 parts of wax powder, 0.5 part of levelling agent, 0.5 part of brightener, 5 parts of zinc powder, 1 part of wollastonite in powder of calcining, 1 part of converted starch.
  4. 4. according to a kind of ERW rust preventive paint technique described in claim 1, it is characterised in that：Described anticorrosive powder The preparation method of coating is as follows：
    By polyester resin 3-5 parts, mineral matter powder 3-5 parts, sepiolite powder 3-5 parts, selenium powder 3-5 parts, rare earth oxide 3-5 parts, wax Powder 3-5 parts, zinc powder 3-5 parts, calcining wollastonite in powder 3-5 parts and converted starch 3-5 parts are put into nylon ball grinder, continuous ball milling 4- 6 hours, 180-200 eye mesh screens are crossed, it is stand-by that collection obtains mixed powder；
    By mixed powder in mixing tank with graphene microchip 3-5 parts, pigment 3-5 parts, nano titanium carbide 3-5 parts, curing agent 3-5 Part, levelling agent 3-5 parts and brightener 3-5 parts be fully pre-mixed, after the completion of be sent into extruder extrusion and tabletting, obtain sheet material；
    Sheet feed powder is broken, it is sent into nylon ball grinder, continuous ball milling 4-6 hours, crosses 400-600 eye mesh screens, collects screenings Obtain finished product anti-corrosive powder paint.
  5. 5. according to a kind of ERW rust preventive paint technique described in claim 1, it is characterised in that：Described mineral matter powder From one or both of azurite, potassium feldspar, malachite green, malachite, natural marine stone, hauynite, tourmaline and muscovite or Two or more combinations.
  6. 6. according to a kind of ERW rust preventive paint technique described in claim 1, it is characterised in that：Described graphene is micro- Piece is the brilliant generation graphite carbon crystal of cellular fashion length with solid, and four valence electrons of each carbon atom form covalent bond quilt Hold onto, it is impossible to the electron stream of displacement is formed, then cannot be conductive, graphite carbon crystal utilizes wet type nanometer after generation Lapping mode, formed with single direction grinding, graphene microchip minimizing thickness is 5nm, and graphene microchip strengthens infrared ray spoke Ejected wave is grown, and its wavelength peak-peak is at 7.5~9.5 μm.By adding graphene microchip in coating, surface of welded pipe can be reduced Resistivity, while strengthen the degrees of fusion between each component.
CN201710648726.XA 2017-08-01 2017-08-01 A kind of ERW rust preventive paint technique and its spray painting used Pending CN107384149A (en)