CN107383453A - A kind of wearability seal rubber - Google Patents
A kind of wearability seal rubber Download PDFInfo
- Publication number
- CN107383453A CN107383453A CN201710785925.5A CN201710785925A CN107383453A CN 107383453 A CN107383453 A CN 107383453A CN 201710785925 A CN201710785925 A CN 201710785925A CN 107383453 A CN107383453 A CN 107383453A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber
- seal
- wear
- vulcanization
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of wear-resisting type seal rubber, it is characterised in that its by following quality meter part be configured to packet into:400 500 parts of natural rubber, 40 60 parts of nitrile rubber, 20 30 parts of poly- allene siloxanes, 8 10 parts of zinc chloride, 57 parts of stearic acid, 79 parts of carbon black, 69 parts of paraffin, 35 parts of titanium oxide, 7 10 parts of aminodithioformic acid, 46 parts of vulcanization hexichol thiazole.
Description
Technical field
The invention belongs to rubber processing techniques field, and in particular to a kind of wearability seal rubber.
Background technology
The main function of seal is to prevent leakage, and it can play the gap for sealing faying face, and cut-out leakage channel reaches
Prevent the purpose of leakage.But automobile or machinery seal, it is desirable to sealing property of sealing component is good, safe and reliable, long lifespan, and
And have higher heat-resisting and anti-wear performance simultaneously, damage caused by reduce it in mechanical movement, confirm that it keeps for a long time
Function affect.And mainly based on natural rubber, used preparation raw material is processed into close seal rapidoprint at present
Sealing, it is usually poor in anti-wear performance, it is difficult to reach seal requirement.
The content of the invention
The problem of present invention is existing:For automobile or the seal of mechanical field, itself and Mechanical Contact have larger rub
Wipe, for a long time using sealing part abrasion can be caused, cause the reduction of its sealing effectiveness, its feature declines;And at present with natural rubber
Glue is the seal mainly to process raw material, and its anti-wear performance is poor, it is impossible to keeps the security performance of seal.To solve above-mentioned ask
Topic, the invention provides a kind of wearability seal rubber.
The present invention is achieved by the following technical solutions:
A kind of wear-resisting type seal rubber, it is respectively configured to sub-prime gauge part and is:
Natural rubber 400-500 parts, nitrile rubber 40-60 parts, poly- allene siloxanes 20-30 parts, zinc chloride 8-10 parts, tristearin
Sour 5-7 parts, carbon black 7-9 parts, paraffin 6-9 parts, titanium oxide 3-5 parts, aminodithioformic acid 7-10 parts, vulcanization hexichol thiazole 4-6
Part.
A kind of wear-resisting type seal rubber, comprises the following steps:
(1)Mixing:Natural rubber, nitrile rubber etc. are heated to 220-230 DEG C, constant temperature keeps 1-2h;(2)Plasticate, be kneaded:Will
Step(1)Gained colloid is through plasticating, mixed refining process;
(3)Shaping:By step(2)Seal is made in obtained rubber after extrusion forming;
(4)Vulcanization:By seal after vulcanizing treatment finished product seal.
Step(4)Described vulcanizing treatment, its temperature are 85-89 DEG C, and sulfur dioxide volumetric concentration is 53%-56%.
Further, it is made up of the composition of following quality meter part:
470 parts of natural rubber, 56 parts of nitrile rubber, 27 parts of poly- allene siloxanes, 9.6 parts of zinc chloride, 6.7 parts of stearic acid, charcoal
Black 8.3 parts, 7.8 parts of paraffin, 4.5 parts of titanium oxide, 9.4 parts of aminodithioformic acid, 5.8 parts of vulcanization hexichol thiazole.
The present invention has advantages below compared with prior art:Pass through the rubber seal that rubber formulation composition of the present invention is made
Glue, there is higher anti-wear performance, and it is high in resistance to elevated temperatures, and shrinkage factor is small.
Embodiment
Embodiment 1:
A kind of wear-resisting type seal rubber, it is respectively configured to sub-prime gauge part and is:
410 parts of natural rubber, 44 parts of nitrile rubber, 23 parts of poly- allene siloxanes, 8.5 parts of zinc chloride, 5.6 parts of stearic acid, charcoal
Black 7.4 parts, 6.8 parts of paraffin, 3.7 parts of titanium oxide, 8 parts of aminodithioformic acid, 4.8 parts of vulcanization hexichol thiazole.
A kind of wear-resisting type seal rubber, comprises the following steps:
(1)Mixing:Natural rubber, nitrile rubber etc. are heated to 223 DEG C, constant temperature keeps 1.5h;
(2)Plasticate, be kneaded:By step(1)Gained colloid is through plasticating, mixed refining process;
(3)Shaping:By step(2)Seal is made in obtained rubber after extrusion forming;
(4)Vulcanization:By seal after vulcanizing treatment finished product seal.
Step(4)Described vulcanizing treatment, its temperature are 86 DEG C, and sulfur dioxide volumetric concentration is 54%.
Embodiment 2:
A kind of wear-resisting type seal rubber, it is respectively configured to sub-prime gauge part and is:
470 parts of natural rubber, 56 parts of nitrile rubber, 27 parts of poly- allene siloxanes, 9.6 parts of zinc chloride, 6.7 parts of stearic acid, charcoal
Black 8.3 parts, 7.8 parts of paraffin, 4.5 parts of titanium oxide, 9.4 parts of aminodithioformic acid, 5.8 parts of vulcanization hexichol thiazole.
A kind of wear-resisting type seal rubber, comprises the following steps:
(1)Mixing:Natural rubber, nitrile rubber etc. are heated to 227 DEG C, constant temperature keeps 2h;
(2)Plasticate, be kneaded:By step(1)Gained colloid is through plasticating, mixed refining process;
(3)Shaping:By step(2)Seal is made in obtained rubber after extrusion forming;
(4)Vulcanization:By seal after vulcanizing treatment finished product seal.
Step(4)Described vulcanizing treatment, its temperature are 88 DEG C, and sulfur dioxide volumetric concentration is 55%.
Experimental result:The seal made to embodiment 1, embodiment 2 carries out wearability test, relative to conventional formulation institute
The seal of processing, its anti-wear performance is improved more than 62%, and has strong resistance to elevated temperatures, in the larger feelings of difference variation
It, which shrinks, under condition declines 34%.
Claims (4)
1. a kind of wear-resisting type seal rubber, it is characterised in that it is respectively configured to sub-prime gauge part and is:
Natural rubber 400-500 parts, nitrile rubber 40-60 parts, poly- allene siloxanes 20-30 parts, zinc chloride 8-10 parts, tristearin
Sour 5-7 parts, carbon black 7-9 parts, paraffin 6-9 parts, titanium oxide 3-5 parts, aminodithioformic acid 7-10 parts, vulcanization hexichol thiazole 4-6
Part.
2. wear-resisting type seal rubber as claimed in claim 1, it is characterised in that comprise the following steps:
(1)Mixing:Natural rubber, nitrile rubber etc. are heated to 220-230 DEG C, constant temperature keeps 1-2h;(2)Plasticate, be kneaded:Will
Step(1)Gained colloid is through plasticating, mixed refining process;
(3)Shaping:By step(2)Seal is made in obtained rubber after extrusion forming;
(4)Vulcanization:By seal after vulcanizing treatment finished product seal.
3. wear-resisting type seal rubber as claimed in claim 2, it is characterised in that step(4)Described vulcanizing treatment, its temperature
For 85-89 DEG C, sulfur dioxide volumetric concentration is 53%-56%.
4. wear-resisting type seal rubber as claimed in claim 1, it is characterised in that be made up of the composition of following quality meter part:
470 parts of natural rubber, 56 parts of nitrile rubber, 27 parts of poly- allene siloxanes, 9.6 parts of zinc chloride, 6.7 parts of stearic acid, charcoal
Black 8.3 parts, 7.8 parts of paraffin, 4.5 parts of titanium oxide, 9.4 parts of aminodithioformic acid, 5.8 parts of vulcanization hexichol thiazole.