CN107382114A - Waste and old concrete regeneration aggregate surface processing device and method - Google Patents
Waste and old concrete regeneration aggregate surface processing device and method Download PDFInfo
- Publication number
- CN107382114A CN107382114A CN201710651819.8A CN201710651819A CN107382114A CN 107382114 A CN107382114 A CN 107382114A CN 201710651819 A CN201710651819 A CN 201710651819A CN 107382114 A CN107382114 A CN 107382114A
- Authority
- CN
- China
- Prior art keywords
- regeneration aggregate
- liquid bed
- calcium silicate
- waste
- regeneration
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of waste and old concrete regeneration aggregate surface processing device and method of the present invention, is related to chemical building material technical field, the problem of poor is combined with cement slurry for existing waste and old concrete regeneration aggregate interface.The waste and old concrete regeneration aggregate surface processing device and method, the surface processing device being made up of first the belt feeder of interconnection, liquid bed and chain net type conveyer, regeneration aggregate is delivered to liquid bed via belt feeder, hydrated calcium silicate gel solution is placed in liquid bed;Chain net type conveyer drives regeneration aggregate to be moved in liquid bed;Last vibrating motor band hydrodynamic bed and hydrated calcium silicate gel solution and regeneration aggregate vibrations so that hydrated calcium silicate gel solution is equably wrapped in regeneration aggregate surface.The present invention effectively increases the intensity of regeneration aggregate and cement slurry linkage interface, so as to effectively increase the overall performance of regeneration concrete.
Description
Technical field
The present invention relates to chemical building material technical field, more particularly to a kind of waste and old concrete regeneration aggregate surface treatment
Device and method.
Background technology
During building waste cycling and reutilization produces regeneration concrete, by discarded concrete, fragment of brick through it is broken,
Regeneration concrete is prepared as regeneration aggregate after screening and occupy very important status, and realize that building waste is sharp again at present
Main path.Regeneration aggregate is that there are mortar attachment, Regenerated Bone in the surface of regeneration aggregate applied to concrete main bottleneck
Microcrack be present in the attachment of material micro mist, aggregate matrix.The old mortar strength of attachment is low, low with cement slurry bond strength.Again
Raw micro mist main component is stone flour, cement stone dust, soil, is non-sticky inorganic matter, equally also result in regeneration aggregate with it is new
Mix slurries faying face weakness.Microscopic checks in aggregate matrix causes regeneration aggregate water absorption big, aggregate low intensity.These are unfavorable
The regeneration concrete various aspects of performance that factor all makes to make substantially is inferior to natural aggregate concrete, it is impossible to prepares high-grade mix
Solidifying soil, limits recycling for building waste.
It is to improve the effective way of regeneration aggregate quality that intensive treatment is carried out to regeneration aggregate, and its main method is aggregate table
Face is modified.At present, conventional aggregate surface modification method has two kinds of Physical and chemical method.Physical strengthening method mainly passes through
Plant equipment is handled the aggregate after crushing, and by regeneration aggregate and itself or extraneous friction, is removed surface laitance, is reached
Strengthen the purpose of aggregate.This kind of method high energy consumption, and aggregate basal body structure can be damaged.Chemical method is mainly utilizationization
The peculiar property of slurries is learned, the processing such as is impregnated, eluted, dried to regeneration aggregate, reaches the purpose that aggregate is strengthened.Chemistry side
Method is divided to two kinds, and one kind uses inorganic slurry, and another kind uses organic slurry.Inorganic slurry mainly has cement mortar, cement mortar+fine
Mineral admixture, cement mortar+KIM powder are several.KIM powder is a kind of high effect leakage proof waterproof of Canadian Kaidunbaisen company production
Agent.Simple cement mortar or cement mortar+Separate Fine-grained Minerals admixture do not have invigoration effect to aggregate, and cement mortar+KIM has certain effect
Fruit, this can penetrate into aggregate mainly due to KIM powder and be internally formed crystal, also improve aggregate intensity.Organic procedures are mainly
Regeneration aggregate is impregnated using solution of silane and PVA (polyvinyl alcohol) solution.The regeneration aggregate impregnated via organic solution
Water absorption rate has a certain degree of decline.More than the method for chemical grout dipping complex process be present, cumbersome lack
Point.And simply improve aggregate matrix strength or reduce the water absorption rate of regeneration aggregate, do not solve regeneration aggregate circle
Face is combined the problem of poor with cement slurry.
The content of the invention
The problem of poor, mesh of the invention are combined with cement slurry for existing waste and old concrete regeneration aggregate interface
Be to provide a kind of waste and old concrete regeneration aggregate surface processing device that can effectively improve regeneration concrete overall performance and
Method.
The technical solution adopted for the present invention to solve the technical problems is:
Waste and old concrete regeneration aggregate surface processing device, including the belt feeder of interconnection, liquid bed and chain net type pass
Machine is sent, the regeneration aggregate is delivered to the liquid bed via the belt feeder, and the chain net type conveyer drives the Regenerated Bone
Material is moved in the liquid bed, and vibrating motor and damping spring are provided with below the liquid bed, is provided with below the damping spring
Bearing, the vibrating motor can drive the liquid bed to shake.
Further, the liquid bed is additionally provided with cover plate.
The invention also discloses a kind of waste and old concrete regeneration aggregate surface treatment method, using foregoing waste and old concrete again
Raw aggregate surface processing device, this method comprise the following steps:
First, regeneration aggregate is delivered to liquid bed via belt feeder, hydrated calcium silicate gel solution is placed in the liquid bed;
2nd, chain net type conveyer drives the regeneration aggregate to be moved in the liquid bed;
3rd, the vibrating motor drives the liquid bed and the hydrated calcium silicate gel solution and regeneration aggregate vibrations,
So that hydrated calcium silicate gel solution is equably wrapped in regeneration aggregate surface.Further, the hydrated calcium silicate gel is molten
Liquid, including:The weight ratio of calcareous material, siliceous material and water, wherein calcareous material and siliceous material is 0.3~3:1, the weight of water
Amount is 5~30 with the gross weight ratio of calcareous material and siliceous material:1.
Further, the preparation method of the hydrated calcium silicate gel solution is:Make calcium nitrate and silicic acid respectively first
Then both hybrid reactions are obtained gel mixed liquor by sodium water solution, then filtered to obtain powder, and finally plus water is stirred
Mix and can obtain hydrated calcium silicate gel solution.
Compared with prior art, the present invention is beneficial has technical effect that:
First, waste and old concrete regeneration aggregate surface processing device of the invention and method, pass through the skin of interconnection first
Surface processing device with machine, liquid bed and chain net type conveyer composition, liquid bed, liquid are delivered to by regeneration aggregate via belt feeder
Hydrated calcium silicate gel solution is placed in bed;Chain net type conveyer drives regeneration aggregate to be moved in liquid bed;Last vibrating motor
Band hydrodynamic bed and the vibrations of hydrated calcium silicate gel solution and regeneration aggregate so that hydrated calcium silicate gel solution equably wraps up
On regeneration aggregate surface.Regeneration aggregate by the vibrations of liquid bed processing after, can effectively remove originally be attached to it is inviscid on aggregate
Micro mist, to be clipped in the micro mist in gap it is also possible to shake.Hydrated calcium silicate gel solution can uniformly be wrapped in regeneration aggregate
The defects of surface is filled into aggregate surface simultaneously.The regeneration aggregate handled by liquid bed can directly be regenerated instead of natural aggregate
The stirring of concrete, need not move through and the step such as dry.After being contacted with cement slurry, hydrated calcium silicate gel solution can effectively promote
Enter the development of cement strength around regeneration aggregate, while gel solution can combine together with the Behavior of Hardened Cement Paste around aggregate.This
Sample, the intensity of regeneration aggregate and cement slurry linkage interface is just effectively increased, so as to effectively increase regeneration concrete
Overall performance.
2nd, waste and old concrete regeneration aggregate surface processing device and method of the invention provide a kind of new to regeneration
The method that aggregate carries out intensive treatment, i.e., regeneration concrete is carried out again after soaking regeneration aggregate with hydrated calcium silicate gel solution
Stirring.Regeneration aggregate is handled using this method, hydrated calcium silicate gel solution can fill microdefect and parcel on regeneration aggregate
On regeneration aggregate surface.Treated intensifying regenerating aggregate can be directly used for regeneration concrete production, enter again after can also drying
The production of row regeneration concrete.Party's forensic science is feasible, and the corollary equipment of mechanization processing can also be with existing concrete bone
Material induction system is integrated, and effectively increases the production efficiency of regeneration concrete.
Brief description of the drawings
Fig. 1 is the structural representation of waste and old concrete regeneration aggregate surface processing device in one embodiment of the invention.
In figure:
1- belt feeders;2- liquid beds;3- chain net type conveyers;4- vibrating motors;5- damping springs;6- bearings;7- cover plates.
Embodiment
A kind of waste and old concrete regeneration aggregate proposed by the present invention is surface-treated below in conjunction with the drawings and specific embodiments
Device and method is described in further detail.According to following explanation, advantages and features of the invention will become apparent from.Below will be by
Cited embodiment combination accompanying drawing, describe the technology contents and feature of the present invention in detail.It need to illustrate in addition, accompanying drawing is adopted
Non- accurately ratio is used with very simplified form and, only to convenience, lucidly aid in illustrating the embodiment of the present invention
Purpose.For sake of convenience, described below " on ", " under " the upper and lower direction with accompanying drawing is consistent, but this can not turn into this hair
The limitation of bright technical scheme.
Embodiment one
Describe the structure composition of the waste and old concrete regeneration aggregate surface processing device of the present invention in detail with reference to figure 1.
Waste and old concrete regeneration aggregate surface processing device, including the belt feeder 1 of interconnection, liquid bed 2 and chain net type
Conveyer 3, regeneration aggregate are delivered to liquid bed 2 via belt feeder 1, and chain net type conveyer 3 drives regeneration aggregate to be moved in liquid bed 2
Dynamic, the lower section of liquid bed 2 is provided with vibrating motor 4 and damping spring 5, and the lower section of damping spring 5 is provided with bearing 6, and vibrating motor 4 being capable of band
Hydrodynamic bed 2 shakes,.
Specifically, the process and principle that the device is strengthened to regeneration aggregate:Regeneration aggregate without intensive treatment
Liquid bed 2 is delivered to via belt feeder 1, hydrated calcium silicate gel solution is placed in liquid bed 2, chain net type conveyer 3 drives Regenerated Bone
Material moves in liquid bed 2, and the vibrating motor 4 of the lower section of liquid bed 2 can shake with hydrodynamic bed 2 and gel solution.Regeneration aggregate is in liquid bed 2
During middle motion, the upper uniform hydrated calcium silicate gel solution of surface energy attachment.Regeneration aggregate through covering liquid intensive treatment
It may be directly applied to the production of regeneration concrete.Regeneration aggregate can effectively be removed and be attached to originally after the vibrations of liquid bed 2 processing
Inviscid micro mist on aggregate, to be clipped in the micro mist in gap it is also possible to shake.Hydrated calcium silicate gel solution is viscosity
Material, the defects of being uniformly wrapped in regeneration aggregate surface while be filled into aggregate surface.The regeneration aggregate handled by liquid bed 2
Natural aggregate can be replaced directly to carry out the stirring of regeneration concrete, need not move through and the step such as dry.After being contacted with cement slurry,
Hydrated calcium silicate gel solution can effectively facilitate the development of cement strength around regeneration aggregate, while gel solution can be with bone
Behavior of Hardened Cement Paste around material combines together, so, effectively increases the intensity of regeneration aggregate and cement slurry linkage interface, so as to
Effectively increase the overall performance of regeneration concrete.
Certainly, mechanical system or the manpower modes such as agitator can be also used, only need to be uniform by hydrated calcium silicate gel solution
Ground is wrapped in regeneration aggregate surface.
It is preferred that in order to prevent hydrated calcium silicate gel solution in liquid bed 2 and regeneration aggregate from being sprayed in vibrations, liquid
Bed 2 is additionally provided with cover plate 7.
It is preferred that the lower section of damping spring 5 of the waste and old concrete regeneration aggregate surface processing device is provided with bearing 6, so as to
Liquid bed 2 is caused to produce the effect at the uniform velocity shaken in the presence of damping spring 5 and vibrating motor 4.
Embodiment two
Please continue to refer to Fig. 1, the invention also discloses a kind of processing method on waste and old concrete regeneration aggregate surface.The party
Method uses foregoing waste and old concrete regeneration aggregate surface processing device, comprises the following steps that:
First, regeneration aggregate is delivered to liquid bed 2 via belt feeder 1, hydrated calcium silicate gel solution is placed in liquid bed 2;
2nd, chain net type conveyer 3 drives regeneration aggregate to be moved in liquid bed 2;
3rd, vibrating motor 4 shakes with hydrodynamic bed 2 and hydrated calcium silicate gel solution and regeneration aggregate so that aquation silicon
Sour calcium gel solution is equably wrapped in regeneration aggregate surface.
In summary, waste and old concrete regeneration aggregate surface processing device of the invention and method, first by mutually interconnecting
The surface processing device of the belt feeder, liquid bed and the chain net type conveyer composition that connect, regeneration aggregate is delivered to via belt feeder
Liquid bed, hydrated calcium silicate gel solution is placed in liquid bed;Chain net type conveyer drives regeneration aggregate to be moved in liquid bed;Finally shake
Dynamic motor belt motor hydrodynamic bed and hydrated calcium silicate gel solution and regeneration aggregate vibrations so that hydrated calcium silicate gel solution is uniform
Ground is wrapped in regeneration aggregate surface.
The invention provides a kind of new method that intensive treatment is carried out to regeneration aggregate, that is, use hydrated calcium silicate gel
The stirring of regeneration concrete is carried out after solution immersion regeneration aggregate again.Regeneration aggregate is handled using this method, hydrated calcium silicate coagulates
Sol solution can fill the microdefect on regeneration aggregate and be wrapped in regeneration aggregate surface.Treated intensifying regenerating aggregate can be direct
Produced for regeneration concrete, carry out the production of regeneration concrete after can also drying again.Hydrated calcium silicate gel solution can have
Effect improves the surface defect of regeneration aggregate, improves the boundary strength of regeneration aggregate and cement slurry, mixed so as to improve regeneration
Coagulate the overall performance of soil.The regeneration aggregate surface reinforcing method science that this patent proposes is feasible, the corollary equipment of mechanization processing
It can also be integrated with existing aggregate induction system, effectively increase the production efficiency of regeneration concrete.
Foregoing description is only the description to present pre-ferred embodiments, not to any restriction of the scope of the invention, this hair
Any change, the modification that the those of ordinary skill in bright field does according to the disclosure above content, belong to the protection of claims
Scope.
Claims (5)
1. waste and old concrete regeneration aggregate surface processing device, it is characterised in that the belt feeder including interconnection, liquid bed and
Chain net type conveyer, the regeneration aggregate are delivered to the liquid bed via the belt feeder, and the chain net type conveyer drives institute
State regeneration aggregate to move in the liquid bed, vibrating motor and damping spring, the damping spring are installed below the liquid bed
Lower section is provided with bearing, and the vibrating motor can drive the liquid bed to shake.
2. waste and old concrete regeneration aggregate surface processing device according to claim 1, it is characterised in that the liquid bed is also
Provided with cover plate.
3. a kind of waste and old concrete regeneration aggregate surface treatment method, it is characterised in that using as claimed in claim 1 or 2
Waste and old concrete regeneration aggregate surface processing device, this method comprise the following steps:
First, regeneration aggregate is delivered to liquid bed via belt feeder, hydrated calcium silicate gel solution is placed in the liquid bed;
2nd, chain net type conveyer drives the regeneration aggregate to be moved in the liquid bed;
3rd, the vibrating motor drives the liquid bed and the hydrated calcium silicate gel solution and regeneration aggregate vibrations so that
Hydrated calcium silicate gel solution is equably wrapped in regeneration aggregate surface.
4. according to the method for claim 3, it is characterised in that the hydrated calcium silicate gel solution, including:Calcareous material
Material, siliceous material and water, wherein the weight ratio of calcareous material and siliceous material are 0.3~3:1, the weight of water and calcareous material and
The gross weight ratio of siliceous material is 5~30:1.
5. according to the method for claim 4, it is characterised in that the preparation method of the hydrated calcium silicate gel solution is:
Make calcium nitrate and sodium silicate aqueous solution respectively first, both hybrid reactions are then obtained into gel mixed liquor, then taken out
Filter obtains powder, and finally plus water is stirred and can obtain hydrated calcium silicate gel solution.