CN107382087A - A kind of electrically conductive coloured glaze - Google Patents

A kind of electrically conductive coloured glaze Download PDF

Info

Publication number
CN107382087A
CN107382087A CN201710604542.3A CN201710604542A CN107382087A CN 107382087 A CN107382087 A CN 107382087A CN 201710604542 A CN201710604542 A CN 201710604542A CN 107382087 A CN107382087 A CN 107382087A
Authority
CN
China
Prior art keywords
parts
coloured glaze
mass fraction
electrically conductive
graphite
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710604542.3A
Other languages
Chinese (zh)
Inventor
李建友
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Taicang City Shuangfeng Town Bocai Artwork Factory
Original Assignee
Taicang City Shuangfeng Town Bocai Artwork Factory
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Taicang City Shuangfeng Town Bocai Artwork Factory filed Critical Taicang City Shuangfeng Town Bocai Artwork Factory
Priority to CN201710604542.3A priority Critical patent/CN107382087A/en
Publication of CN107382087A publication Critical patent/CN107382087A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of electrically conductive coloured glaze, the coloured glaze is provided with conductive coating, and the conductive coating raw material composition is：Graphite：15 20 parts；Titanium dioxide：15 20 parts；Sodium metasilicate：40 50 parts；Antimony oxide：0.1 0.5 parts；Manganese dioxide：0.1 0.5 parts；Ferrous oxide：0.3 0.5 parts；Synthetic resin：30 40 parts；Au：0.5 0.8 parts；Alloy：12 parts；Nickel powder：38 parts；Above-mentioned number is mass fraction；It is preferred that the mass fraction of the graphite is 18 parts, the mass fraction of the titanium dioxide is 16 parts, and the mass fraction of the sodium metasilicate is 45 parts, and the mass fraction of the synthetic resin is 36 parts, and the mass fraction of the Au is 0.5 part.The present invention can realize the connection of circuit by coating conductive coating on coloured glaze surface, so not only simple, and not interfere with the attractive in appearance of coloured glaze, easy to operate, practical.

Description

A kind of electrically conductive coloured glaze
Technical field
The present invention relates to a kind of coloured glaze, especially a kind of coloured glaze coated with conductive layer.
Background technology
With the improvement of life, daily necessities and handicraft that coloured glaze makes are widely used in daily life, coloured glaze Product is also multimodal various, but existing coloured glaze is also generally all shape, pattern, the difference of color be present, has no big improvement, this Sample cannot possess that oneself is a little unique, also without the competitiveness got well, so as to influence sales volume, and some colored glaze products because Want that it is to accomplish to make its light by energization for some cause specifics, but so electric wire will expose, and influence attractive in appearance.
The content of the invention
The technical problems to be solved by the invention are the defects of overcoming prior art, there is provided a kind of electrically conductive coloured glaze.
In order to solve the above technical problems, the present invention provides a kind of electrically conductive coloured glaze, it is characterised in that the coloured glaze is provided with Conductive coating, the conductive coating raw material composition are：
Graphite：15-20 parts；
Titanium dioxide：15-20 parts；
Sodium metasilicate：40-50 parts；
Antimony oxide：0.1-0.5 parts；
Manganese dioxide：0.1-0.5 parts；
Ferrous oxide：0.3-0.5 parts；
Synthetic resin：30-40 parts；
Au：0.5-0.8 parts；
Alloy：1-2 parts；
Nickel powder：3-8 parts；
Above-mentioned number is mass fraction.
A kind of foregoing electrically conductive coloured glaze, it is characterised in that：The mass fraction of the graphite is 18 parts.
A kind of foregoing electrically conductive coloured glaze, it is characterised in that：The mass fraction of the titanium dioxide is 16 parts.
A kind of foregoing electrically conductive coloured glaze, it is characterised in that：The mass fraction of the sodium metasilicate is 45 parts.
A kind of foregoing electrically conductive coloured glaze, it is characterised in that：The mass fraction of the synthetic resin is 36 parts.
A kind of foregoing electrically conductive coloured glaze, it is characterised in that：The mass fraction of the Au is 0.5 part.
The beneficial effect that the present invention is reached：The present invention can realize electricity by coating conductive coating on coloured glaze surface The connection on road, it is so not only simple, and the attractive in appearance of coloured glaze is not interfered with, it is easy to operate, practical.
Embodiment
The invention will be further described below.Following examples are only used for the technical side for clearly illustrating the present invention Case, and can not be limited the scope of the invention with this.
A kind of electrically conductive coloured glaze, the coloured glaze are provided with conductive coating, and the conductive coating raw material composition is：
Graphite：15-20 parts；
Titanium dioxide：15-20 parts；
Sodium metasilicate：40-50 parts；
Antimony oxide：0.1-0.5 parts；
Manganese dioxide：0.1-0.5 parts；
Ferrous oxide：0.3-0.5 parts；
Synthetic resin：30-40 parts；
Au：0.5-0.8 parts；
Alloy：1-2 parts；
Nickel powder：3-8 parts；
Above-mentioned number is mass fraction.
It is preferred that the mass fraction of the graphite is 18 parts.
It is preferred that the mass fraction of the titanium dioxide is 16 parts.
It is preferred that the mass fraction of the sodium metasilicate is 45 parts.
It is preferred that the mass fraction of the synthetic resin is 36 parts.
It is preferred that the mass fraction of the Au is 0.5 part.
The present invention can realize the connection of circuit by coating conductive coating on coloured glaze surface, so not only simple, And the attractive in appearance of coloured glaze is not interfered with, it is easy to operate, practical.
Described above is only the preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art For member, without departing from the technical principles of the invention, some improvement and deformation can also be made, these are improved and deformation Also it should be regarded as protection scope of the present invention.

Claims (6)

1. a kind of electrically conductive coloured glaze, it is characterised in that the coloured glaze is provided with conductive coating, the conductive coating raw material composition For：
Graphite：15-20 parts；
Titanium dioxide：15-20 parts；
Sodium metasilicate：40-50 parts；
Antimony oxide：0.1-0.5 parts；
Manganese dioxide：0.1-0.5 parts；
Ferrous oxide：0.3-0.5 parts；
Synthetic resin：30-40 parts；
Au：0.5-0.8 parts；
Alloy：1-2 parts；
Nickel powder：3-8 parts；
Above-mentioned number is mass fraction.
A kind of 2. electrically conductive coloured glaze according to claim 1, it is characterised in that：The mass fraction of the graphite is 18 parts.
A kind of 3. electrically conductive coloured glaze according to claim 1, it is characterised in that：The mass fraction of the titanium dioxide is 16 Part.
A kind of 4. electrically conductive coloured glaze according to claim 1, it is characterised in that：The mass fraction of the sodium metasilicate is 45 Part.
A kind of 5. electrically conductive coloured glaze according to claim 1, it is characterised in that：The mass fraction of the synthetic resin is 36 Part.
A kind of 6. electrically conductive coloured glaze according to claim 1, it is characterised in that：The mass fraction of the Au is 0.5 part.
CN201710604542.3A 2017-07-24 2017-07-24 A kind of electrically conductive coloured glaze Pending CN107382087A (en)