CN107364205A - One kind is aluminized lampshade material and its manufacture craft - Google Patents
One kind is aluminized lampshade material and its manufacture craft Download PDFInfo
- Publication number
- CN107364205A CN107364205A CN201710566835.7A CN201710566835A CN107364205A CN 107364205 A CN107364205 A CN 107364205A CN 201710566835 A CN201710566835 A CN 201710566835A CN 107364205 A CN107364205 A CN 107364205A
- Authority
- CN
- China
- Prior art keywords
- parts
- material layer
- temperature
- area
- lampshade
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Aluminized lampshade material and its manufacture craft the invention discloses one kind, the lampshade material of aluminizing includes the material layer A and outer layer of nexine material layer B;The outer surface of the material layer B is provided with electrodeposited coating or/and protective layer;The material layer A is made of following raw material:PET resin, ABS resin, leakerna glue, butyl titanate, MDJ, carborundum, titanium nitride, chitosan oligosaccharide, dyestuff A;The material layer B is made of following raw material:Polyvinyl chloride resin, hydroxypropyl methyl cellulose, epoxy metering system vinegar resin, wood powder, Nafusaku, tricresyl phosphate (butoxyethyl group) ester, dyestuff B.The lampshade material of aluminizing has the advantages of mechanical performance is high, and anti-wear performance is good, and corrosion resistance is good;It is hardly damaged, service life is longer, and quality is small, and it is low to prepare cost.
Description
Technical field
The present invention relates to lampshade preparing technical field, specifically one kind is aluminized lampshade material and its manufacture craft.
Background technology
Lampshade is not only to cover on lamp in order that the effect that light flocks together, is also prevented from getting an electric shock, to protecting eye
Eyeball also has effect, so can all there is lampshade on most of lamps.Common lampshade material typically has fabrics, brown paper, metal material
Deng.The lampshade of cloth cover gives people the impression of succinct elegance, and the lampshade of paper can build dim and dreamlike atmosphere, but cloth material
The lampshade of matter and paper wood matter is easily damaged, and service life is shorter, and the lampshade of metal material has the makings and modern sense of kind of cool tone, but
It is the lampshade heavier mass of metal material, and cost is higher.In the market occur some composites preparation lampshade, but its
Generally existing bad mechanical property, anti-wear performance are poor, corrosion resistance is poor.Therefore, the present invention provide one kind aluminize lampshade material and
Its manufacture craft.
The content of the invention
Aluminized lampshade material and its manufacture craft it is an object of the invention to provide one kind, to solve in above-mentioned background technology
The problem of proposition.
To achieve the above object, the present invention provides following technical scheme:
One kind is aluminized lampshade material, and the lampshade material of aluminizing includes the material layer A and outer layer of nexine material layer B;Institute
The outer surface for stating material layer B is provided with electrodeposited coating or/and protective layer;
The material layer A is made of the raw material of following parts by weight:PET resin 38-50 parts, ABS resin 22-35 parts,
Leakerna glue 11-17 parts, butyl titanate 2-6 parts, MDJ 2-8 parts, carborundum 5-8 parts, titanium nitride 2-4
Part, chitosan oligosaccharide 4-7 parts, dyestuff A 0.1-1 parts;
The material layer B is made of the raw material of following parts by weight:Polyvinyl chloride resin 22-40 parts, hydroxypropyl methyl cellulose
15-20 parts, epoxy metering system vinegar resin 18-24 parts, wood powder 6-12 parts, Nafusaku 4-8 parts, tricresyl phosphate (butoxy second
Base) ester 2-8 parts, dyestuff B0.1-1 parts.
As the further scheme of the present invention:The material layer A is made of the raw material of following parts by weight:PET resin
42 parts, 31 parts of ABS resin, 12 parts of leakerna glue, 5 parts of butyl titanate, 5 parts of MDJ, 7 parts of carborundum, nitrogen
Change 3 parts of titanium, 5 parts of chitosan oligosaccharide, 0.3 part of dyestuff A.
As the further scheme of the present invention:The material layer B is made of the raw material of following parts by weight:Polyvinyl chloride resin
32 parts, 16 parts of hydroxypropyl methyl cellulose, 20 parts of epoxy metering system vinegar resin, 9 parts of wood powder, 6 parts of Nafusaku, tricresyl phosphate
5 parts of (butoxyethyl group) ester, dyestuff B0.2 parts.
As the further scheme of the present invention:The protective layer is PCT thinfilm protective coatings.
A kind of manufacture craft for lampshade material of aluminizing, comprises the following steps:
(1) material layer A is prepared, step is as follows:
A. PET resin, ABS resin, butyl titanate, MDJ, carborundum, titanium nitride are positioned over height
Mix 5-15min in mixed machine, then add chitosan oligosaccharide, continue use high-speed mixer and mixing 5-8min, then add leakerna glue with
Dyestuff A, continue to use high-speed mixer and mixing 15-25min;
B. by mixed material be sent into double screw extruder loading hopper in, through twin-screw high speed shear, extrusion, tie rod,
Cooling, it is granulated;
C. and then using upper step gains after mould molding, sizing, then cut off, produce material layer A;
(2) material layer B is prepared, step is as follows:
A. by polyvinyl chloride resin, hydroxypropyl methyl cellulose, epoxy metering system vinegar resin, wood powder and tricresyl phosphate (butoxy
Ethyl) ester high-speed mixer and mixing 25-30min, Nafusaku and dyestuff B are then added, continues to use high-speed mixer and mixing 15-
25min;
B. by mixed material be sent into double screw extruder loading hopper in, through twin-screw high speed shear, extrusion, tie rod,
Cooling, it is granulated;
C. and then using upper step gains after mould molding, sizing, then cut off, produce material layer B;
(3) material layer A and material layer B is combined with each other by roller heating;
(4) protective layer is aluminized or/and pasted on material layer B outer surface, produces lampshade material of aluminizing.
As the further scheme of the present invention:A. is by PET resin, ABS resin, butyl titanate, dihydro jasmine in step (1)
Jasmine ketone acid methyl esters, carborundum, titanium nitride are positioned over high-speed mixer and mixing 11min, then add chitosan oligosaccharide, continue to use in high mixer
7min is mixed, leakerna glue and dyestuff A is then added, continues to use high-speed mixer and mixing 22min.
As the further scheme of the present invention:Step (1) sets area's temperature of double screw extruder as 160-180 DEG C,
Two area's temperature are 180-195 DEG C, and three area's temperature are 190-200 DEG C, and four area's temperature are 195-215 DEG C, and five area's temperature are 215-220
DEG C, six area's temperature are 225-230 DEG C, and rate of feeding is 50-80 revs/min, and screw speed is 150-250 revs/min.
As the further scheme of the present invention:A. is by polyvinyl chloride resin, hydroxypropyl methyl cellulose, epoxy methyl in step (2)
Propylene vinegar resin, wood powder and tricresyl phosphate (butoxyethyl group) ester high-speed mixer and mixing 27min, then add Nafusaku and
Dyestuff B, continue to use high-speed mixer and mixing 20min.
As the further scheme of the present invention:Step (2) sets area's temperature of double screw extruder as 210-220 DEG C,
Two area's temperature are 210-220 DEG C, and three area's temperature are 225-235 DEG C, and four area's temperature are 240-255 DEG C, and five area's temperature are 250-260
DEG C, six area's temperature are 255-265 DEG C, and rate of feeding is 15-50 revs/min, and screw speed is 120-170 revs/min.
Compared with prior art, the beneficial effects of the invention are as follows:
The lampshade material of aluminizing has the advantages of mechanical performance is high, and anti-wear performance is good, and corrosion resistance is good;With traditional cloth
Skill, brown paper, the lampshade of metal material are compared, and are hardly damaged, and service life is longer, and quality is small, and it is low to prepare cost, can also be
Needle drawing case on material layer B, ensure good appearance, the use demand of people can be better met.
Embodiment
The technical scheme of this patent is described in more detail with reference to embodiment.
Embodiment 1
One kind is aluminized lampshade material, and the lampshade material of aluminizing includes the material layer A and outer layer of nexine material layer B;Institute
The outer surface for stating material layer B is provided with electrodeposited coating or/and protective layer;
The material layer A is made of the raw material of following parts by weight:38 parts of PET resin, 22 parts of ABS resin, lek are received
11 parts of glue, 2 parts of butyl titanate, 2 parts of MDJ, 5 parts of carborundum, 2 parts of titanium nitride, 4 parts of chitosan oligosaccharide, dyestuff A
0.1 part;
The material layer B is made of the raw material of following parts by weight:22 parts of polyvinyl chloride resin, hydroxypropyl methyl cellulose 15
Part, 18 parts of epoxy metering system vinegar resin, 6 parts of wood powder, 4 parts of Nafusaku, 2 parts of tricresyl phosphate (butoxyethyl group) ester, dyestuff
B0.1 parts.The protective layer is PCT thinfilm protective coatings.
A kind of manufacture craft for lampshade material of aluminizing, comprises the following steps:
(1) material layer A is prepared, step is as follows:
A. PET resin, ABS resin, butyl titanate, MDJ, carborundum, titanium nitride are positioned over height
5min is mixed in mixed machine, chitosan oligosaccharide is then added, continues to use high-speed mixer and mixing 5min, then adds leakerna glue and dyestuff A,
Continue to use high-speed mixer and mixing 15min;Area's temperature of double screw extruder is set as 160-180 DEG C, two area's temperature are 180-
195 DEG C, three area's temperature are 190-200 DEG C, and four area's temperature are 195-215 DEG C, and five area's temperature are 215-220 DEG C, and six area's temperature are
225-230 DEG C, rate of feeding is 50 revs/min, and screw speed is 150 revs/min;
B. by mixed material be sent into double screw extruder loading hopper in, through twin-screw high speed shear, extrusion, tie rod,
Cooling, it is granulated;
C. and then using upper step gains after mould molding, sizing, then cut off, produce material layer A;
(2) material layer B is prepared, step is as follows:
A. by polyvinyl chloride resin, hydroxypropyl methyl cellulose, epoxy metering system vinegar resin, wood powder and tricresyl phosphate (butoxy
Ethyl) ester high-speed mixer and mixing 25min, Nafusaku and dyestuff B are then added, continues to use high-speed mixer and mixing 15min;If
The area's temperature for determining double screw extruder is 210-220 DEG C, and two area's temperature are 210-220 DEG C, and three area's temperature are 225-235 DEG C,
Four area's temperature are 240-255 DEG C, and five area's temperature are 250-260 DEG C, and six area's temperature are 255-265 DEG C, and rate of feeding is 15 revs/min
Clock, screw speed are 120 revs/min;
B. by mixed material be sent into double screw extruder loading hopper in, through twin-screw high speed shear, extrusion, tie rod,
Cooling, it is granulated;
C. and then using upper step gains after mould molding, sizing, then cut off, produce material layer B;
(3) material layer A and material layer B is combined with each other by roller heating;
(4) protective layer is aluminized or/and pasted on material layer B outer surface, produces lampshade material of aluminizing.
Embodiment 2
One kind is aluminized lampshade material, and the lampshade material of aluminizing includes the material layer A and outer layer of nexine material layer B;Institute
The outer surface for stating material layer B is provided with electrodeposited coating or/and protective layer;
The material layer A is made of the raw material of following parts by weight:50 parts of PET resin, 35 parts of ABS resin, lek are received
17 parts of glue, 6 parts of butyl titanate, 8 parts of MDJ, 8 parts of carborundum, 4 parts of titanium nitride, 7 parts of chitosan oligosaccharide, dyestuff A
1 part;
The material layer B is made of the raw material of following parts by weight:40 parts of polyvinyl chloride resin, hydroxypropyl methyl cellulose 20
Part, 24 parts of epoxy metering system vinegar resin, 12 parts of wood powder, 8 parts of Nafusaku, 8 parts of tricresyl phosphate (butoxyethyl group) ester, dyestuff
1 part of B.The protective layer is PCT thinfilm protective coatings.
A kind of manufacture craft for lampshade material of aluminizing, comprises the following steps:
(1) material layer A is prepared, step is as follows:
A. PET resin, ABS resin, butyl titanate, MDJ, carborundum, titanium nitride are positioned over height
15min is mixed in mixed machine, chitosan oligosaccharide is then added, continues to use high-speed mixer and mixing 8min, then adds leakerna glue and dyestuff
A, continue to use high-speed mixer and mixing 25min;Area's temperature of double screw extruder is set as 160-180 DEG C, two area's temperature are
180-195 DEG C, three area's temperature are 190-200 DEG C, and four area's temperature are 195-215 DEG C, and five area's temperature are 215-220 DEG C, six area's temperature
Spend for 225-230 DEG C, rate of feeding is 80 revs/min, and screw speed is 250 revs/min;
B. by mixed material be sent into double screw extruder loading hopper in, through twin-screw high speed shear, extrusion, tie rod,
Cooling, it is granulated;
C. and then using upper step gains after mould molding, sizing, then cut off, produce material layer A;
(2) material layer B is prepared, step is as follows:
A. by polyvinyl chloride resin, hydroxypropyl methyl cellulose, epoxy metering system vinegar resin, wood powder and tricresyl phosphate (butoxy
Ethyl) ester high-speed mixer and mixing 30min, Nafusaku and dyestuff B are then added, continues to use high-speed mixer and mixing 25min;If
The area's temperature for determining double screw extruder is 210-220 DEG C, and two area's temperature are 210-220 DEG C, and three area's temperature are 225-235 DEG C,
Four area's temperature are 240-255 DEG C, and five area's temperature are 250-260 DEG C, and six area's temperature are 255-265 DEG C, and rate of feeding is 50 revs/min
Clock, screw speed are 170 revs/min;
B. by mixed material be sent into double screw extruder loading hopper in, through twin-screw high speed shear, extrusion, tie rod,
Cooling, it is granulated;
C. and then using upper step gains after mould molding, sizing, then cut off, produce material layer B;
(3) material layer A and material layer B is combined with each other by roller heating;
(4) protective layer is aluminized or/and pasted on material layer B outer surface, produces lampshade material of aluminizing.
Embodiment 3
One kind is aluminized lampshade material, and the lampshade material of aluminizing includes the material layer A and outer layer of nexine material layer B;Institute
The outer surface for stating material layer B is provided with electrodeposited coating or/and protective layer;The protective layer is PCT thinfilm protective coatings;
The material layer A is made of the raw material of following parts by weight:42 parts of PET resin, 31 parts of ABS resin, lek are received
12 parts of glue, 5 parts of butyl titanate, 5 parts of MDJ, 7 parts of carborundum, 3 parts of titanium nitride, 5 parts of chitosan oligosaccharide, dyestuff A
0.3 part.
The material layer B is made of the raw material of following parts by weight:32 parts of polyvinyl chloride resin, hydroxypropyl methyl cellulose 16
Part, 20 parts of epoxy metering system vinegar resin, 9 parts of wood powder, 6 parts of Nafusaku, 5 parts of tricresyl phosphate (butoxyethyl group) ester, dyestuff
B0.2 parts.
A kind of manufacture craft for lampshade material of aluminizing, comprises the following steps:
(1) material layer A is prepared, step is as follows:
A. PET resin, ABS resin, butyl titanate, MDJ, carborundum, titanium nitride are positioned over height
11min is mixed in mixed machine, chitosan oligosaccharide is then added, continues to use high-speed mixer and mixing 7min, then adds leakerna glue and dyestuff
A, continue to use high-speed mixer and mixing 22min;Area's temperature of double screw extruder is set as 160-180 DEG C, two area's temperature are
180-195 DEG C, three area's temperature are 190-200 DEG C, and four area's temperature are 195-215 DEG C, and five area's temperature are 215-220 DEG C, six area's temperature
Spend for 225-230 DEG C, rate of feeding is 70 revs/min, and screw speed is 210 revs/min;
B. by mixed material be sent into double screw extruder loading hopper in, through twin-screw high speed shear, extrusion, tie rod,
Cooling, it is granulated;
C. and then using upper step gains after mould molding, sizing, then cut off, produce material layer A;
(2) material layer B is prepared, step is as follows:
A. by polyvinyl chloride resin, hydroxypropyl methyl cellulose, epoxy metering system vinegar resin, wood powder and tricresyl phosphate (butoxy
Ethyl) ester high-speed mixer and mixing 27min, Nafusaku and dyestuff B are then added, continues to use high-speed mixer and mixing 20min;If
The area's temperature for determining double screw extruder is 210-220 DEG C, and two area's temperature are 210-220 DEG C, and three area's temperature are 225-235 DEG C,
Four area's temperature are 240-255 DEG C, and five area's temperature are 250-260 DEG C, and six area's temperature are 255-265 DEG C, and rate of feeding is 30 revs/min
Clock, screw speed are 150 revs/min;
B. by mixed material be sent into double screw extruder loading hopper in, through twin-screw high speed shear, extrusion, tie rod,
Cooling, it is granulated;
C. and then using upper step gains after mould molding, sizing, then cut off, produce material layer B;
(3) material layer A and material layer B is combined with each other by roller heating;
(4) protective layer is aluminized or/and pasted on material layer B outer surface, produces lampshade material of aluminizing.
The lampshade material of aluminizing has the advantages of mechanical performance is high, and anti-wear performance is good, and corrosion resistance is good;With traditional cloth
Skill, brown paper, the lampshade of metal material are compared, and are hardly damaged, and service life is longer, and quality is small, and it is low to prepare cost, can also be
Needle drawing case on material layer B, ensure good appearance, the use demand of people can be better met.
The better embodiment of this patent is explained in detail above, but this patent is not limited to above-mentioned embodiment party
Formula, can also be on the premise of this patent objective not be departed from one skilled in the relevant art's possessed knowledge
Make a variety of changes.
Claims (9)
- The lampshade material 1. one kind is aluminized, it is characterised in that the lampshade material of aluminizing includes the material layer A and outer layer of nexine material Bed of material B;The outer surface of the material layer B is provided with electrodeposited coating or/and protective layer;The material layer A is made of the raw material of following parts by weight:PET resin 38-50 parts, ABS resin 22-35 parts, lek Receive glue 11-17 parts, butyl titanate 2-6 parts, MDJ 2-8 parts, carborundum 5-8 parts, titanium nitride 2-4 parts, shell Oligosaccharides 4-7 parts, dyestuff A 0.1-1 parts;The material layer B is made of the raw material of following parts by weight:Polyvinyl chloride resin 22-40 parts, hydroxypropyl methyl cellulose 15- 20 parts, epoxy metering system vinegar resin 18-24 parts, wood powder 6-12 parts, Nafusaku 4-8 parts, tricresyl phosphate (butoxyethyl group) Ester 2-8 parts, dyestuff B0.1-1 parts.
- 2. lampshade material according to claim 1 of aluminizing, it is characterised in that the material layer A uses following parts by weight Raw material be made:42 parts of PET resin, 31 parts of ABS resin, 12 parts of leakerna glue, 5 parts of butyl titanate, dihydro jasmone acid first 5 parts of ester, 7 parts of carborundum, 3 parts of titanium nitride, 5 parts of chitosan oligosaccharide, 0.3 part of dyestuff A.
- 3. lampshade material according to claim 1 of aluminizing, it is characterised in that the material layer B uses following parts by weight Raw material be made:32 parts of polyvinyl chloride resin, 16 parts of hydroxypropyl methyl cellulose, 20 parts of epoxy metering system vinegar resin, 9 parts of wood powder, 6 parts of Nafusaku, 5 parts of tricresyl phosphate (butoxyethyl group) ester, dyestuff B0.2 parts.
- 4. lampshade material according to claim 1 of aluminizing, it is characterised in that the protective layer is PCT thinfilm protective coatings.
- 5. the manufacture craft of a kind of lampshade material of aluminizing as described in claim 1-4 is any, it is characterised in that including following step Suddenly:(1) material layer A is prepared, step is as follows:A. PET resin, ABS resin, butyl titanate, MDJ, carborundum, titanium nitride are positioned over high mixer Middle mixing 5-15min, then adds chitosan oligosaccharide, continues to use high-speed mixer and mixing 5-8min, then adds leakerna glue and dyestuff A, continue to use high-speed mixer and mixing 15-25min;B. by mixed material be sent into double screw extruder loading hopper in, through twin-screw high speed shear, extrusion, tie rod, cooling, It is granulated;C. and then using upper step gains after mould molding, sizing, then cut off, produce material layer A;(2) material layer B is prepared, step is as follows:A. by polyvinyl chloride resin, hydroxypropyl methyl cellulose, epoxy metering system vinegar resin, wood powder and tricresyl phosphate (butoxy second Base) ester high-speed mixer and mixing 25-30min, Nafusaku and dyestuff B are then added, continues to use high-speed mixer and mixing 15- 25min;B. by mixed material be sent into double screw extruder loading hopper in, through twin-screw high speed shear, extrusion, tie rod, cooling, It is granulated;C. and then using upper step gains after mould molding, sizing, then cut off, produce material layer B;(3) material layer A and material layer B is combined with each other by roller heating;(4) protective layer is aluminized or/and pasted on material layer B outer surface, produces lampshade material of aluminizing.
- 6. the manufacture craft of lampshade material according to claim 5 of aluminizing, it is characterised in that A. is by PET trees in step (1) Fat, ABS resin, butyl titanate, MDJ, carborundum, titanium nitride are positioned over high-speed mixer and mixing 11min, Then chitosan oligosaccharide is added, continues to use high-speed mixer and mixing 7min, then adds leakerna glue and dyestuff A, continues to use in high mixer Mix 22min.
- 7. the manufacture craft of lampshade material according to claim 5 of aluminizing, it is characterised in that step (1) sets twin-screw One area's temperature of extruder is 160-180 DEG C, and two area's temperature are 180-195 DEG C, and three area's temperature are 190-200 DEG C, four area's temperature For 195-215 DEG C, five area's temperature are 215-220 DEG C, and six area's temperature are 225-230 DEG C, and rate of feeding is 50-80 revs/min, spiral shell Bar rotating speed is 150-250 revs/min.
- 8. the manufacture craft of lampshade material according to claim 5 of aluminizing, it is characterised in that a. is by PVC trees in step (2) In fat, hydroxypropyl methyl cellulose, epoxy metering system vinegar resin, wood powder and tricresyl phosphate (butoxyethyl group) ester high mixer 27min is mixed, Nafusaku and dyestuff B is then added, continues to use high-speed mixer and mixing 20min.
- 9. the manufacture craft of lampshade material according to claim 5 of aluminizing, it is characterised in that step (2) sets twin-screw One area's temperature of extruder is 210-220 DEG C, and two area's temperature are 210-220 DEG C, and three area's temperature are 225-235 DEG C, four area's temperature For 240-255 DEG C, five area's temperature are 250-260 DEG C, and six area's temperature are 255-265 DEG C, and rate of feeding is 15-50 revs/min, spiral shell Bar rotating speed is 120-170 revs/min.