CN107363488A - A kind of processing technology of high abrasion mould - Google Patents
A kind of processing technology of high abrasion mould Download PDFInfo
- Publication number
- CN107363488A CN107363488A CN201710595350.0A CN201710595350A CN107363488A CN 107363488 A CN107363488 A CN 107363488A CN 201710595350 A CN201710595350 A CN 201710595350A CN 107363488 A CN107363488 A CN 107363488A
- Authority
- CN
- China
- Prior art keywords
- mould
- heat treatment
- carried out
- salt bath
- high abrasion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of processing technology of high abrasion mould, comprise the following steps:(100)Refining:Choose alloy cold work die steel to refine as mold materials, and to it, go the removal of impurity;(200)Cold working:Cold working is carried out to the alloy cold work die steel after refining, by cold extrusion shaped;(300)Heat treatment:Salt bath heat treatment is carried out to the mould after shaping, is specially:Salt bath quenching is carried out at a temperature of 560 590 DEG C, the cool time is 30 40 minutes, quenches air cooling of being come out of the stove after terminating;(400)Surface treatment:Carry out surfaces nitrided processing to the mould after heat treatment, temperature during processing is 720 740 DEG C, and the time is 5.5 6 hours.By the above-mentioned means, the present invention can improve the wearability of mould, increase the service life, ensure permanence operation.
Description
Technical field
The present invention relates to mould manufacture field, more particularly to a kind of processing technology of high abrasion mould.
Background technology
Mould be in industrial production being molded, being blow molded, extruding, die casting or obtain the methods of forging forming, smelting, punching press
To the various moulds and instrument of required product.In brief, mould is the instrument for making formed article, this instrument by
Various parts are formed, and different moulds is made up of different parts.It mainly by the change of institute's moulding material physical state come
Realize the processing of article profile.It is known as the title of " mother of industry ".
Mould is blank is turned into the instrument for having given shape and the product of size under external force.It is widely used in punching
Sanction, die forging, cold-heading, extruding, metallic sintered products compacting, compression casting, and the compression moulding of the product such as engineering plastics, rubber, ceramics
Or in the forming of injection.
Mould has specific profile or cavity shape, can make blank by contour line using the contour shape with cutting edge
Separation (punching) occurs for shape.Using cavity shape blank can be made to obtain corresponding three-dimensional shape.Mould generally comprise dynamic model and
Cover half(Or punch-pin and cavity plate)Two parts, the two is partable.Product is taken out when separating, blank is injected mould type when closing up
Chamber shapes.Mould is precision instrument, complex-shaped, bears the expansive force of blank, thick to structural strength, rigidity, case hardness, surface
Rugosity and machining accuracy all have higher requirements.
Existing mould makes product keep dimensional accuracy and table due to produce friction strong many times with workpiece
Surface roughness is it is necessary to have high intensity, high rigidity and excellent wearability, generally by the addition wear-resistant component in material
Obtain, the mould that this mode obtains can not keep permanent abrasion resistant effect, can not meet the requirement of long-term use.
The content of the invention
The present invention solves the technical problem of provide a kind of processing technology of high abrasion mould, it is possible to increase mould
Wearability, increase the service life, ensure permanence operation.
In order to solve the above technical problems, one aspect of the present invention is:A kind of adding for high abrasion mould, is provided
Work technique, comprises the following steps:
(100)Refining:Choose alloy cold work die steel to refine as mold materials, and to it, go the removal of impurity;
(200)Cold working:Cold working is carried out to the alloy cold work die steel after refining, by cold extrusion shaped;
(300)Heat treatment:Salt bath heat treatment is carried out to the mould after shaping, is specially:Salt bath is carried out at a temperature of 560-590 DEG C
Quenching, the cool time is 30-40 minutes, quenches air cooling of being come out of the stove after terminating;
(400)Surface treatment:Carrying out surfaces nitrided processing to the mould after heat treatment, temperature during processing is 720-740 DEG C, when
Between be 5.5-6 hours.
In a preferred embodiment of the present invention, the alloy cold work die steel is Cr4W2MoV.
In a preferred embodiment of the present invention, chloride-based salt bath is used during the salt bath heat treatment.
The beneficial effects of the invention are as follows:Be used as mold materials by choosing alloy cold work die steel, by refining, it is cold plus
Work, heat treatment and surface treatment, the mould of high abrasion is obtained, by optimizing heat treatment and process of surface treatment, improve mould
It wearability, can increase the service life, ensure permanence operation.
Embodiment
Presently preferred embodiments of the present invention is described in detail below so that advantages and features of the invention can be easier to by
It will be appreciated by those skilled in the art that apparent clearly defined so as to be made to protection scope of the present invention.
The embodiment of the present invention includes:
Embodiment one
A kind of processing technology of high abrasion mould, comprises the following steps:
(100)Refining:Choose Cr4W2MoV to refine as mold materials, and to it, go the removal of impurity;
(200)Cold working:Cold working is carried out to the Cr4W2MoV after refining, by cold extrusion shaped;
(300)Heat treatment:Salt bath heat treatment is carried out to the mould after shaping, the salt bath uses chloride-based salt when being heat-treated
Bath;Specially:Salt bath quenching is carried out at a temperature of 560 DEG C, the cool time is 35 minutes, quenches air cooling of being come out of the stove after terminating;
(400)Surface treatment:Carry out surfaces nitrided processing to the mould after heat treatment, temperature during processing is 725 DEG C, and the time is
5.5 hour.
Embodiment two:
A kind of processing technology of high abrasion mould, comprises the following steps:
(100)Refining:Choose Cr4W2MoV to refine as mold materials, and to it, go the removal of impurity;
(200)Cold working:Cold working is carried out to the Cr4W2MoV after refining, by cold extrusion shaped;
(300)Heat treatment:Salt bath heat treatment is carried out to the mould after shaping, the salt bath uses chloride-based salt when being heat-treated
Bath;Specially:Salt bath quenching is carried out at a temperature of 590 DEG C, the cool time is 30 minutes, quenches air cooling of being come out of the stove after terminating;
(400)Surface treatment:Carry out surfaces nitrided processing to the mould after heat treatment, temperature during processing is 735 DEG C, and the time is
6 hours.
Embodiment three:
A kind of processing technology of high abrasion mould, comprises the following steps:
(100)Refining:Choose Cr4W2MoV to refine as mold materials, and to it, go the removal of impurity;
(200)Cold working:Cold working is carried out to the Cr4W2MoV after refining, by cold extrusion shaped;
(300)Heat treatment:Salt bath heat treatment is carried out to the mould after shaping, the salt bath uses chloride-based salt when being heat-treated
Bath;Specially:Salt bath quenching is carried out at a temperature of 575 DEG C, the cool time is 40 minutes, quenches air cooling of being come out of the stove after terminating;
(400)Surface treatment:Carry out surfaces nitrided processing to the mould after heat treatment, temperature during processing is 730 DEG C, and the time is
5.7 hour.
Present invention is disclosed a kind of processing technology of high abrasion mould, is used as mould material by choosing alloy cold work die steel
Material, by refining, cold working, heat treatment and surface treatment, obtains the mould of high abrasion, is heat-treated and is surface-treated by optimizing
Technique, the wearability of mould is improved, can increased the service life, ensure permanence operation.
Embodiments of the invention are the foregoing is only, are not intended to limit the scope of the invention, it is every to utilize this hair
The equivalent structure or equivalent flow conversion that bright description is made, or directly or indirectly it is used in other related technology necks
Domain, it is included within the scope of the present invention.
Claims (3)
1. a kind of processing technology of high abrasion mould, it is characterised in that comprise the following steps:
(100)Refining:Choose alloy cold work die steel to refine as mold materials, and to it, go the removal of impurity;
(200)Cold working:Cold working is carried out to the alloy cold work die steel after refining, by cold extrusion shaped;
(300)Heat treatment:Salt bath heat treatment is carried out to the mould after shaping, is specially:Salt bath is carried out at a temperature of 560-590 DEG C
Quenching, the cool time is 30-40 minutes, quenches air cooling of being come out of the stove after terminating;
(400)Surface treatment:Carrying out surfaces nitrided processing to the mould after heat treatment, temperature during processing is 720-740 DEG C, when
Between be 5.5-6 hours.
2. the processing technology of high abrasion mould according to claim 1, it is characterised in that the alloy cold work die steel is
Cr4W2MoV。
3. the processing technology of high abrasion mould according to claim 1, it is characterised in that used during the salt bath heat treatment
Chloride-based salt bath.