CN107363483A - The production method of compound wear-resisting steel plates - Google Patents
The production method of compound wear-resisting steel plates Download PDFInfo
- Publication number
- CN107363483A CN107363483A CN201710619041.2A CN201710619041A CN107363483A CN 107363483 A CN107363483 A CN 107363483A CN 201710619041 A CN201710619041 A CN 201710619041A CN 107363483 A CN107363483 A CN 107363483A
- Authority
- CN
- China
- Prior art keywords
- parts
- wear
- steel material
- steel plates
- resisting steel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of production method of compound wear-resisting steel plates, including ordinary steel material to be composite and wear-resisting steel are pre-processed, and one layer of applicator is then coated with its surface；The applicator is made of following raw material：40 parts~50 parts of lube base oil, rosin ester are 5 parts~10 parts, 15 parts~20 parts of ox-hide cream, 5 parts~10 parts of boric acid, 5 parts~10 parts of 1 part~5 parts of gelatin and silica；Ordinary steel material and wear-resistant steel material consistency from top to bottom are stacked together, vacuumized, electron beam carries out soldering and sealing, is then first put into heating furnace and heats, then is rolled, heat-treated offline.The present invention on the basis of original production method mainly by being improved, specific applicator first is coated on the surface of ordinary steel material and wear-resistant steel material, the techniques such as soldering and sealing, heating, rolling, heat-treated offline are carried out again, so that it is guaranteed that cracking phenomena will not occur in process of production for compound wear-resisting steel plates.
Description
Technical field
The invention belongs to high-abrasive material technical field, more particularly to a kind of compound wear-resisting steel plates.
Background technology
Compound wear-resisting steel plates refer to specialize in the extraordinary plate product used under the conditions of large area abrasion industrial and mineral, are in plasticity and toughness
Preferable ordinary low-carbon steel or the compound certain thickness high rigidity of surface of low-alloy steel, the wear resistance alloyed layer of high-wearing feature, with
Adapt to requirement that is wear-resistant and reducing manufacturing cost.At present, easily ftractureed in the production process of compound wear-resisting steel plates
Phenomenon, this phenomenon how is overcome into the production technology of current compound wear-resisting steel plates technical problem urgently to be resolved hurrily.
The content of the invention
A kind of production method of compound wear-resisting steel plates provided by the present invention, this method solve existing compound wear-resisting steel plates
The problem of cracking phenomena easily occurs in production process.
In order to solve the above-mentioned technical problem, the technical solution adopted in the present invention is：
It comprises the following steps：
A. by ordinary steel material to be composite and wear-resistant steel material respectively by machining, the iron oxide on its respective surface is removed
Skin, dirt, and the two is processed into identical size；
B. it is coated with one layer of applicator in the ordinary steel material Jing Guo step A working process and the surface of wear-resistant steel material；Wherein,
The applicator is made of following raw material：40 parts~50 parts of lube base oil, rosin ester be 5 parts~10 parts,
5 parts~10 parts of 15 parts~20 parts of ox-hide cream, 5 parts~10 parts of boric acid, 1 part~5 parts of gelatin and silica；
C. the ordinary steel material after step B coating processing and wear-resistant steel material consistency from top to bottom are stacked together, Ran Hou
Vacuumized under vacuum condition, soldering and sealing is carried out using electron beam, obtains compound wear-resisting steel plates blank；
D. compound wear-resisting steel plates blank made from step C is put into heating furnace, carried out at being 1300 DEG C~1350 DEG C in temperature
Heat；
E. the compound wear-resisting steel plates blank heated by D steps is rolled, heat-treated offline.
Due to being had the advantages that using above-mentioned technical proposal, the present invention：
The present invention on the basis of original production method mainly by being improved, i.e., first by ordinary steel material and wear-resistant steel material
Surface coat specific applicator, then the techniques such as soldering and sealing, heating, rolling, heat-treated offline are carried out, so that it is guaranteed that compound
Cracking phenomena will not occur in process of production for wear-resisting steel plate.
Embodiment
Below in conjunction with instantiation, the invention will be further described：
Embodiment 1 --- compound wear-resisting steel plates
It comprises the following steps：
A. by ordinary steel material to be composite and wear-resistant steel material respectively by machining, the iron oxide on its respective surface is removed
Skin, dirt, and the two is processed into identical size；
B. it is coated with one layer of applicator in the ordinary steel material Jing Guo step A working process and the surface of wear-resistant steel material；Wherein,
The applicator is made of following raw material：40 parts of lube base oil, rosin ester are 5 parts, 15 parts of ox-hide cream, boron
5 parts of 5 parts of acid, 1 part of gelatin and silica；
C. the ordinary steel material after step B coating processing and wear-resistant steel material consistency from top to bottom are stacked together, Ran Hou
Vacuumized under vacuum condition, soldering and sealing is carried out using electron beam, obtains compound wear-resisting steel plates blank；
D. compound wear-resisting steel plates blank made from step C is put into heating furnace, heated at being 1300 DEG C in temperature；
E. the compound wear-resisting steel plates blank heated by D steps is rolled, heat-treated offline.
In the present embodiment, the probability that cracking phenomena occurs is 0.001%.
Embodiment 2 --- compound wear-resisting steel plates
It comprises the following steps：
A. by ordinary steel material to be composite and wear-resistant steel material respectively by machining, the iron oxide on its respective surface is removed
Skin, dirt, and the two is processed into identical size；
B. it is coated with one layer of applicator in the ordinary steel material Jing Guo step A working process and the surface of wear-resistant steel material；Wherein,
The applicator is made of following raw material：50 parts of lube base oil, rosin ester be 10 parts, 20 parts of ox-hide cream,
0 part of 10 parts of boric acid, 5 parts of gelatin and silica 1；
C. the ordinary steel material after step B coating processing and wear-resistant steel material consistency from top to bottom are stacked together, Ran Hou
Vacuumized under vacuum condition, soldering and sealing is carried out using electron beam, obtains compound wear-resisting steel plates blank；
D. compound wear-resisting steel plates blank made from step C is put into heating furnace, heated at being 1350 DEG C in temperature；
E. the compound wear-resisting steel plates blank heated by D steps is rolled, heat-treated offline.
In the present embodiment, the probability that cracking phenomena occurs is 0.0015%.
Embodiment 3 --- compound wear-resisting steel plates
It comprises the following steps：
A. by ordinary steel material to be composite and wear-resistant steel material respectively by machining, the iron oxide on its respective surface is removed
Skin, dirt, and the two is processed into identical size；
B. it is coated with one layer of applicator in the ordinary steel material Jing Guo step A working process and the surface of wear-resistant steel material；Wherein,
The applicator is made of following raw material：44 parts of lube base oil, rosin ester are 6 parts, 18 parts of ox-hide cream, boron
9 parts of 7 parts of acid, 2 parts of gelatin and silica；
C. the ordinary steel material after step B coating processing and wear-resistant steel material consistency from top to bottom are stacked together, Ran Hou
Vacuumized under vacuum condition, soldering and sealing is carried out using electron beam, obtains compound wear-resisting steel plates blank；
D. compound wear-resisting steel plates blank made from step C is put into heating furnace, heated at being 1305 DEG C in temperature；
E. the compound wear-resisting steel plates blank heated by D steps is rolled, heat-treated offline.
In the present embodiment, the probability that cracking phenomena occurs is 0.0015%.
Claims (1)
1. a kind of production method of compound wear-resisting steel plates, it is characterised in that comprise the following steps：
A. by ordinary steel material to be composite and wear-resistant steel material respectively by machining, the iron oxide on its respective surface is removed
Skin, dirt, and the two is processed into identical size；
B. it is coated with one layer of applicator in the ordinary steel material Jing Guo step A working process and the surface of wear-resistant steel material；Wherein,
The applicator is made of following raw material：40 parts~50 parts of lube base oil, rosin ester be 5 parts~10 parts,
5 parts~10 parts of 15 parts~20 parts of ox-hide cream, 5 parts~10 parts of boric acid, 1 part~5 parts of gelatin and silica；
C. the ordinary steel material after step B coating processing and wear-resistant steel material consistency from top to bottom are stacked together, Ran Hou
Vacuumized under vacuum condition, soldering and sealing is carried out using electron beam, obtains compound wear-resisting steel plates blank；
D. compound wear-resisting steel plates blank made from step C is put into heating furnace, carried out at being 1300 DEG C~1350 DEG C in temperature
Heat；
E. the compound wear-resisting steel plates blank heated by D steps is rolled, heat-treated offline.