CN107354584A - A kind of Chloranthus glaber fibre spun-laced non-woven mask substrate and preparation method thereof - Google Patents
A kind of Chloranthus glaber fibre spun-laced non-woven mask substrate and preparation method thereof Download PDFInfo
- Publication number
- CN107354584A CN107354584A CN201710753597.0A CN201710753597A CN107354584A CN 107354584 A CN107354584 A CN 107354584A CN 201710753597 A CN201710753597 A CN 201710753597A CN 107354584 A CN107354584 A CN 107354584A
- Authority
- CN
- China
- Prior art keywords
- spun
- mask substrate
- speed
- chloranthus glaber
- laced
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to a kind of antibiotic health care spun laced fabric, more particularly to a kind of preparation method and application of Chloranthus glaber fibre spun-laced non-woven mask substrate, wherein, it is made of the raw material of following weight proportioning：The weight content of Chloranthus glaber fiber accounts for 10 ~ 100%, and the weight content of viscose rayon accounts for 0 ~ 90%, and the weight content of polyester fiber accounts for 0 ~ 80.Advantages of the present invention is shown：The healthcare functions such as not only there is the Chloranthus glaber fibre spun-laced non-woven mask substrate of exploitation antibacterial bacteriostatic, clean skin to be healthy and strong, skin-protecting face nursing, skin care; skin-friendly is good; wholesomeness is good, can be effectively facilitated metabolism, prevent skin senescence; there is good protective effect to human body; good hygroscopicity, wet guilding is good, good permeability; and mask substrate has the functions such as moisturizing, activating cell, oxygen supply, there is the effect such as nourishing, nutrition, health care to skin.
Description
Technical field
The present invention relates to a kind of health hydro-entangled non-woven fabric for medical textile, and grass is utilized especially with regard to one kind
The Chloranthus glaber fibre spun-laced non-woven mask substrate and its system that coral fiber, viscose rayon, polyester fiber mixing post-processing form
Preparation Method and application.
Background technology
Spun lacing concretion method is also known as jet net-spraying method, is a kind of new non-woven cloth process technology.Hydro-entangled non-woven fabric work
Skill is that fibre web is continuously sprayed by High-Pressure Water, make under hydraulic action fiber movement in fibre web, displacement and arrange again
Row and mutually entanglement, enable fibre web to reinforce and obtain certain physical and mechanical properties.Spun lacing method product hygroscopicity and gas permeability
Good, soft, intensity is higher, and drapability is good, not hair loss, and adhesive-free, free from environmental pollution, therefore " the green production that is otherwise known as
Product ".
The outward appearance of hydro-entangled non-woven fabric is than other non-woven materials closer to traditional textile.Hydro-entangled non-woven fabric belongs to soft
Property tangle, do not damage fiber, and needle stick injuries fiber.Hydro-entangled non-woven fabric has soft, gas permeability, drapability, moisture absorption
Property is good, intensity is high, flexibility is good, not hair loss, good hygroscopicity, low fuzz the features such as.In process typically without using viscous
Mixture, there is good wholesomeness, identical fibre with it is identical quantitative in the case of, its fracture strength can reach textile fabric
70%-80%, it is widely used in hygienic material, institute of family articles for use etc..
Spun-laced non-woven fabric mask base fabric not only has anti-moisture evaporation, promotes nutrient solution quickly to absorb, clean skin, protect
Functions such as sheath skin, the and the effect of elasticity of skin can be increased, prevent wrinkle generation, moistening skin-care, gloss moist, at present with
The continuous development of people's living standard and national economy, the health care consciousness of people steps up, and the market of facial mask needs
The amount of asking is very big, and various functions facial mask is loved by people, and people, which do not require nothing more than facial mask, has the function that U.S. face, but also requires
With performances such as health care, moisturizing, clean skin, antibacterial, cleanings, while there is security, convenience, validity, comfortableness, reliable
Property, feature, health, soft and moist smooth, high resilience, good luster, good hygroscopicity, hold that fluidity is good, it is high to hold liquid rate, using new
Type functional fiber, the facial mask of the hydro-entangled non-woven fabric exploitation of exploitation can separate skin and air contact, reduce evaporation of perspiration, promote
Enter the temperature rise of human skin, expand pore, promote sweat gland secretion, accelerate metabolism, penetrate into the nutrient solution in facial mask
To epidermis or deeper, accelerate the more moisture of percutaneous absorption, make skin-whitening, delay skin aging.At present, as a kind of high
Shelves feature cosmetics just obtain Rapid Popularization in this field, now have become a kind of fashionable, are widely used in medical treatment
Health field.
Chloranthus glaber fiber Chloranthus glaber is commonly called as spice all over the mountain, kwan-yin tea, nine joint flower, elder etc., is that Chloranthaceae is perennial often
Green undershrub, its form is beautiful, four seasons fragrance, has high medicinal, edible and ornamental value.China is the main of Chloranthus glaber
The place of production, the external place of production are distributed in Korea, Japan, Malaysia, Philippine, Vietnam, Cambodia, India, Sri Lanka.Chloranthus glaber
In six kinds of main components be astilbin, isoflavones, rhamnopyranosyl glucoside, tannin, the pyridine of piperazine skin, aesculetin, the Qin respectively
Pi Su.They commonly have the function that anti-inflammation, and to gold-coloured staphylococci, white, which reads ball bacterium and Escherichia coli, to be had well
Antibacterial and bacteriostasis.
Chloranthus glaber fiber uses natural plants --- -- Chloranthus glaber extract as raw material, is blended and spins with viscose rayon spinning solution
Silk forms.Chloranthus glaber fiber belongs to natural, green fiber, and Chloranthus glaber extract is from natural Chloranthus glaber leaf that its is effective
Composition extracts, and carries out ultra-fine grinding, the no added any chemical substance of extraction process.
Chloranthus glaber fiber remains the Chloranthus glaber plant given efficacy of itself, not only the pharmacological effect with Chloranthus glaber, such as
Anti-inflammation, dispelling wind and eliminating dampness, promoting blood circulation and stopping pain, there is alleviation, reduce lump, extend the life-span, improve sleep and other effects, it is often more important that
It has natural antibacterial functions, and to gold-coloured staphylococci, Escherichia coli, Candida albicans has good biocidal property, antibacterial
Rate reaches 99%, and repeatedly wear wash after keep antibiotic property.The antibiotic property of Chloranthus glaber fiber is good, to staphylococcus aureus and its
Antibody-resistant bacterium has different degrees of inhibitory action, 50 functions of remaining to keep antibacterial of washing.Chloranthus glaber fiber has excellent
Spinnability, it remains the basic mechanical property of cellulose fibre, can be with various other fiber blends.But wear no resistance, hygrometric state
Fracture strength is small.
The chemical composition of viscose rayon is close with cotton fiber, and performance is close to cotton fiber.The section of viscose rayon is band sawtooth
Circle, have a skin-core structure, longitudinal direction is straight groove.It is alkaline-resisting without acidproof, alkaline-resisting and acid resistance is poor compared with cotton fiber.Density
Approached with cotton fiber.Viscose rayon not only has the advantages that good hygroscopicity, breathes freely, be pleasant, and with soft, fine
Tie up that beautiful, dyeability is good, dyeing chromatogram is complete, the features such as bright.But wet break strength is small, pure viscose rayon system is utilized
The fabric shrinkage deformation obtained is big.Viscose fiber strength is less than cotton fiber, not water-fastness, and elongation at break is more than cotton fiber, wear-resisting
Property it is poor, Smaller load effect under be easily deformed, poor dimensional stability, rigidity is small, poor flexibility.
Polyester fiber has the advantages that intensity is high, recovery is good, heat setting is good, but polyester fiber mass specific resistance is big,
Electrostatic phenomenon protrudes, and it the difficulties such as networking effect difference in the combing net process of pure polyester fiber is present.
The content of the invention
The present invention proposes a kind of Chloranthus glaber fibre spun-laced non-woven mask substrate and preparation method thereof, the spun lacing prepared
Non-woven cloth mask substrate good hydrophilic property, small, soft, the excellent adsorption of rigidity, there is during use water to moisten slim and graceful skin sense
With efficient anti-aging, radioresistance, sterilization and oxidation resistant effect, cuticula that can be on softening skin forms one on skin
The very thin protective layer of layer, can not only prevent the moisture evaporation on skin or volatilization, accelerate to promote the infiltration and suction of nutriment
Receive, and the dust on skin surface, greasy dirt, dirt and greasy can be eliminated, careful pore, compact skin, plays well
Clean skin and skin care effect, while can prevent the wrinkle on skin from producing, promote skin to preserve moisture, improve the guarantor of skin
Outlet capacity, make skin more moist and moist, it is ensured that skin is ruddy, rich in gloss.By facial mask adsorb skin secretion and
Scurf etc., the dirt etc. on skin is can remove, make skin clean and tidy one new, reach the purpose of clean skin.
Realize the technical scheme is that：A kind of Chloranthus glaber fibre spun-laced non-woven mask substrate, spunlace non-woven face
Film base fabric is made up of the raw material of following percentage by weight：Chloranthus glaber fiber 10-100%, viscose rayon 0-90%, polyester fiber 0-
80%。
The performance indications of the spunlace non-woven mask substrate are：Actual quantification 38-72g/m2, average thickness 0.29-
0.48mm；Longitudinal strength 51.5-104.0N, horizontal strength 32.0-115.0N, vertically and horizontally strength ratio（0.48:1）-（1.81:1）；
Longitudinal elongation at break rate 14.21-48.32%, transverse breakage elongation 26.0-52.8%, vertically and horizontally elongation at break ratio（0.43:
1）-（0.96:1）；Longitudinal tear strength 5.3-15.38N, horizontal Tear strength 5.1-15.6N, vertically and horizontally Tear strength ratio
（0.55:1）-（1.18:1）.
The single fiber line density of the Chloranthus glaber fiber is 1.7 dtex, length 38.00mm.
The single fiber line density of the polyester fiber is 1.33-1.74 dtex, length 33.0-58.0mm.
The single fiber line density of the viscose rayon is 1.10-1.73 dtex, length 33.0-40.0mm.
A kind of preparation method of bacteriostasis and health-care Chloranthus glaber fibre spun-laced non-woven mask substrate, including following step
Suddenly, it is further illustrated below as follows：
The technological process of preparation：Selection raw material → determine mixed proportion and weigh weight → processing Chloranthus glaber fibre spun-laced non-woven
Mask substrate → performance test analysis.
1）The technological process of production is as follows：
Shredding → mixing → combing → lapping → drawing-off → spun lacing → is dried → batched
2）The key technology for processing Chloranthus glaber fibre spun-laced non-woven mask substrate is as follows：
→ multiple feeding machine → convoying curtain+mixing mill → opener → cotton storage tank → cotton feeding box → combing is mixed using automatic weighing
Machine → cross lapping machine → multi-roll drafting machine → spun-laced machine → dryer → up- coiler → cutting machine → into bag.
Weighing type opens series-parallel connection and closes process route category quantity-produced technological process, and production line is by without feed back conveyer, weighing
Device, opener, hopper and air-flow delivery system composition.Fiber after mixing, shredding conveys and is assigned to rear road by air-flow
In the feeding hopper of web-forming equipment.As a result of meausring apparatus, various composition is more accurate in batch mixing.
The preparation method of described Chloranthus glaber fibre spun-laced non-woven mask substrate, specific preparation process are as follows：
（1）Shredding mixes：Raw material is uniformly mixed, then feeds carding machine；Raw material is subjected to shredding, mixing, then by equal
Even mixing, then feeds carding machine.
(technological parameter and) key technology of shredding feeding process：The uniformity and physical and mechanical properties of Hydroentangled product all with
Feeding system has close relationship, if feeding fibre surface treatment is big, can directly affect the quality such as the quantitative of Hydroentangled product, thickness and refer to
Mark.（2）Opening：On the basis of abundant shredding is carried out to fiber, rational opening process and technological parameter are selected, is opened
Loose speed is appropriate, it is impossible to and it is excessive or too small, the purpose of shredding is not reached when too small, fiber is easily damaged when excessive, is produced short
Fiber, influence the quality of final products；
（2）The technological parameter and key technology of carding step：The height for combing work quality directly affects the quality of product, and it is
The fiber of shredding is further well mixed, makes to produce certain cohesive force and frictional force between fiber, and formed uniform
Web, the speed of reasonable selection carding element suitable, suitable control carding isolation distance size, reduce the damage to fiber, it is ensured that fiber
Net clearly, without clouding；
The technological parameter of carding machine：Feed end 0.25 ~ 0.63m/min of speed, 32.5 ~ 43.6m/min of linear velocity, hold-down roller 26.2
~ 35.9r/min, upper 28.6 ~ 35.4r/min of pallet, lower pallet 32.9 ~ 42.9r/min, upper 29.5 ~ 35.6r/min of outlet roller,
19.6 ~ 34.5r/min of lower outlet roller, 14.0 ~ 25.6r/min of upper back-off roller, 14.0 ~ 25.3r/min of lower back-off roller, upper doffer
32.8 ~ 40.7r/min, 34.1 ~ 42.8r/min of lower doffer, 1.06 ~ 2.35r/min of end, 179.1 ~ 206r/min of licker-in are fed for,
66.2 ~ 96.8r/min of working roll, 962 ~ 1010r/min of cylinder, output 18.3 ~ 27.3r/min of platen, card stripper 150.6 ~
182.8r/min, 45.0 ~ 45.8mm of gauge, 55 ~ 65m/min of carding machine fibre web output speed；
（3）Lapping：The technological parameter and key technology of lapping process：Using cross lapping machine, the product matter of spun laced fabric can be changed
Amount, want in production reasonable selection input curtain, compensation curtain, lapping curtain and export curtain speed, with improve the uniformity of product and by force
Power etc., from the suitable fibre web number of plies, it can ensure that quantifying for product reaches design requirement.
Raw material after combing is fed into cross lapping machine, the technological parameter of cross lapping machine：The m/ of linear velocity 33.4 ~ 41.8
Min, small 30.7 ~ 38.4m/min of vehicle speed, curtain 40.3 ~ 41.8/min of speed is inputted, export curtain 4.6 ~ 11.9m/min of speed, layer
4 ~ 6 layers of number, 2330 ~ 2780mm of width；
（4）Drawing-off：The technological parameter and key technology of drafting process：The size control of general drafting multiple is at 1 ~ 2 times, drafting machine
It is made up of 15 drawing-off card clothing rollers and gripping card clothing roller, forms 3 draw zones, by rationally designing the drafting multiple in each area,
Contribute to the arrangement of improvement behavior, increase tight ness rating, cohesive force and frictional force between fiber, improve the quality of Hydroentangled product；
Drafting machine is made up of 15 drawing-off card clothing rollers and gripping card clothing roller, forms 3 draw zones；The technological parameter of drafting machine：
1.1 ~ 1.8 times of total draft multiple, the first 7.0 ~ 11.0 times of roller drafting multiple, the second 12.0 ~ 16.2 times of roller drafting multiple, the 3rd roller
8.4 ~ 19.6 times of drafting multiple, 12.4 ~ 23.6 times of four-roller drafting multiple.The speed 10.18 of fibre web input drafting machine ~
10.84m/min, 15.0 ~ 16.8m/min of output speed of drafting machine；
（5）Spun lacing：Spun lacing uses spun-laced machine, and spun lacing road number uses 5 ~ 7 spun lacings, the technological parameter of spun-laced machine：Convoying curtain first
11.3 ~ 21.1m/min of speed, cylinder 15.5 ~ 29.8m/min of speed, the m/min of convoying curtain second speed 14.8 ~ 25, pressure
Power (bar) is respectively 23 ~ 65,40 ~ 105,60 ~ 115,30 ~ 105,58 ~ 110,70 ~ 110,67 ~ 110.Prewet 3.0 ~ 6.0bar,
Spray water bore dia 0.12mm, pitch-row 0.6mm, 12 ~ 18m/min of spun-laced machine output speed；
The technological parameter and key technology of spun lacing process：（1）Spun lacing prewets process using double lace curtaining clamping feedings, due to spun lacing
Pressure is small, therefore web is influenceed little.Fibre web must carry out pre-add wet process before spun lacing area is entered, and the purpose prewetted is fibre
Net can more fully absorb the energy using water-jet during spun lacing.The purpose prewetted：Fluffy fibre web is compacted, is excluded fine
Air in net, fibre web is set to effectively absorb the energy of water jet after entering spun lacing area, with reinforcing fibre entanglement effect.（2）
When spun lacing pressure increases, that is tangled between the fiber in web is more close, and fiber mutually interts often, between fiber
Frictional force and cohesive force it is larger, hole quantity is few, conversely, it is loose to be tangled between the fiber in web, number of pores quantitative change is more.
（3）Spun lacing distance it is bigger, when high pressure water flow strikes, current can with air produce frictional force, because current surface tension and rub
It is uneven to wipe resistance, causes the convergence of high-pressure water jet to reduce, the tiny water stream of high pressure is produced rupture and bifurcated, high pressure
The energy of water jet diminishes, and the central speed of high-pressure water jet reduces, and the fibre matting in web is not close, in loose fibre web
Hole it is big, quantity is more, is unfavorable for the reinforcing of Hydroentangled product；Conversely, spun lacing, apart from smaller, the fibre matting in web is tighter
Close, the hole in fibre web is small, and quantity is few, and Hydroentangled product strength is big.（4）Spun lacing road number typically uses 5 ~ 7 spun lacings, and spun lacing is prewetted
When, using double pin hole, pre- spun lacing aperture is 0.15mm, and the aperture of water needle plate is big, and pitch-row is big, can avoid in web
Fiber produce displacement, make the entanglement effect in web good.During second spun lacing, the aperture of water needle plate is small, contributes to pair
Fiber is punctured, and general aperture is 0.10 ~ 0.12mm.During three spun lacings, using the method for reverse side spun lacing, general aperture is
0.08~0.10mm.4th and during five spun lacings, using the method for reverse side spun lacing, it is ensured that spun laced fabric surface is fine and smooth, and feel is soft
With general aperture is 0.10 ~ 0.12mm.（5）It is required that liquid drugs injection plate surface is straight, the impact of high pressure liquid drugs injection can be born, use is high-strength
Degree, the water needle plate of highly dense material processing.Pin hole on water needle plate requires bright and clean, vertical, uniform, to ensure the collection of liquid drugs injection jet
Poly- property is good, the impact energy increase of water jet.Water needle plate surface will keep cleaning in production, maintained in time according to service life and
Cleaning, the appearance for the bad phenomenon such as avoid pin hole deformation and blockings in production, liquid drugs injection bifurcated, high-pressure water jet unstable, influence
The performance of Hydroentangled product.
Hold in the palm the effect of lace curtaining：Conveying and the effect of holding web are not only acted as, but also receives the percussion of spun lacing,
Also act as simultaneously and pass through the reflected-shock current after web to be tangled again to web reverse side using liquid drugs injection jet, hold in the palm net
Silk thread on curtain is thinner, and high pressure liquid drugs injection reflex power is bigger, and the entanglement effect of web is better, can significantly improve spun laced fabric
Total quality.Ask the percent opening on lace curtaining higher, high-pressure water jet more easily propagates through web and through support lace curtaining, the production of processing
Product mesh is more obvious, and the entanglement of web is close.
Influence of the web speed to spun laced fabric quality：When web speed is low, fibre web receives the time length of high-pressure water jet,
Impact energy quantitative change to web is big, and entanglement tightness degree becomes big between fiber, and Hydroentangled product strength increases.Defeated lace curtaining is being run
During, slack list, tension variation, deflector roll are not parallel etc. can all cause lace curtaining transverse shifting（It is travelling）, it is necessary to deviation correcting device come
Lace curtaining is kept to move between two parties in the horizontal.The speed of fibre web is：Speed of production is generally 40 ~ 100mm/min.
（6）Drying：The technological parameter and key technology of baking operation：Dryer is to be followed using deep fat inside dryer
Ring, by the heat distributed, the air of circumference, by means of the effect of circulating fan, negative pressure is produced in drying cylinder surrounding, is formed
Hot blast carries out convection type heat transfer drying, completes the purpose of drying.Rational hot blast temperature, flow are selected during drying, wind speed, is followed
Circular rector etc., drying effect is controlled, ensure product quality.Suitable control temperature and speed etc. are wanted during drying, temperature is too low then to be reached not
To the purpose of drying, the too low height of temperature, fiber embrittlement, spun laced fabric jaundice.Dried using dryer, the technique ginseng of dryer
Number：10.1 ~ 18.9m/min of linear velocity, set 110 ~ 180 DEG C of drying temperature；
（7）Winding：The technological parameter and key technology of rolling step：The effect of up- coiler is by the Hydroentangled product after drying, root
According to require, specification, standard etc., cut and coiling process, it is ensured that outward appearance, breadth and volume length meet the requirements, and meet in next step
Processing.It is wound using up- coiler, the technological parameter of up- coiler：300 ~ 1000m/ volumes of spooling length, winding diameter 450 ~
960mm, 11.0 ~ 28.8m/min of winding speed of up- coiler.
The step（5）Spun lacing road number uses 5 ~ 7 spun lacings, and spun lacing is prewetted using double pin hole, and pre- spun lacing aperture is
0.15mm, second spun lacing aperture are 0.10 ~ 0.12mm, and the 3rd spun lacing uses reverse side spun lacing, and aperture is 0.08 ~ 0.10mm；
4th and the 5th spun lacing aperture is 0.10 ~ 0.12mm.
The performance test of Chloranthus glaber fibre spun-laced non-woven cloth.
Performance indications and bacteriostasis rate of hydro-entangled non-woven fabric etc. are tested, the result of its performance test is as follows：Golden yellow grape
Coccus（ATCC6538）Bacteriostasis rate is more than 82.2%, Escherichia coli（8089）Bacteriostasis rate is more than 83.2%, Candida albicans
（ATCC10231）Bacteriostasis rate is more than 84.2%.
The making of facial mask：Cleaning shop will carry out sterilization and antibacterial processing in process of production, using suitable humiture,
Ensure that the environmental sanitation condition of cleaning shop meets national standard, bacteria containing amount is controlled in lowest range.Mainly include following several
Step：（1）Spunlace non-woven mask substrate is first processed, is ready work；（2）According to technical requirements and proportioning etc., appropriate
Preservative, anti-irritant composition, antiallergy thing, natural botanical extraction liquid, nutrient solution class additive, moistening liquid class additive, protect
Strong composition, moisturizing class additive, anti-aging additive, functional additive, Sodium Hyaluronate, surfactant, grease, perfume (or spice)
Essence, glycerine, water etc. uniformly mix, and under being stirred in high speed dispersion dish, form uniform and stable facial mask mixing liquid；（3）Then
According to technical requirements and size, spunlace non-woven base fabric is cut, then in cleaning shop, by facial mask mixing liquid
Carried out with spunlace non-woven mask substrate filling, it is ensured that steady quality, be enclosed in nutrition moistening liquid and other active ingredients
Skin is allowed to effectively absorb and enter in facial mask, during use；（4）According to National Technical condition, packaging, mark and check and accept regulation etc.
It is required that finally Face film towel is fitted into polybag in cleaning shop, is sealed with electronic sealing machine, then product packed,
As facial mask finished product.
The beneficial effects of the invention are as follows：Present invention is disclosed a kind of production of Chloranthus glaber fibre spun-laced non-woven mask substrate
Method and application, the preparation method procedure arrangement is reasonable, moderate cost, is adapted for producing in batches, all kinds of medical spinnings of preparation
The combination properties such as fabric are good, and stable effect is lasting.For ensure prepared by above-mentioned several functional fibers into spunlace non-woven
Mask substrate has the good characteristic of the above, it is necessary to possesses above-mentioned condition；Otherwise cannot give full play to comprehensive possessed by them
The premium properties of conjunction.Chloranthus glaber fibre spun-laced non-woven mask substrate does not only have skin-protecting face nursing, skin care, skin-friendly is good, defends
The features such as natural disposition is good, good hygroscopicity, wet guilding are good, good permeability, but also metabolism is effectively facilitated, prevent skin from declining
Always, there is good protective effect to human body, there is moisturizing, activating cell, oxygen supply with the spunlace non-woven mask substrate of its processing
Etc. function, there is the effect such as nourishing, nutrition, health care to skin, product purpose is extensive, is adapted to exploitation clean skin moisturizing, health and beauty
Facial mask.
The all raw material used in the present invention and the technique not described and equipment etc. are conventional use of, or can be with
Buy from the market.By common technical knowledge it is recognised that the present invention can not depart from the implementation of essential feature and essence by others
Scheme realized, so, in the scheme of following implementation, for each side, all simply citing is illustrated,
Be not it is only, it is all within the scope of the present invention or the change in equivalent the scope of the present invention included by the present invention.
Embodiment
Below in conjunction with the embodiment of the present invention, technical scheme is clearly and completely described, it is clear that institute
The embodiment of description is only part of the embodiment of the present invention, rather than whole embodiments.Based on the embodiment in the present invention,
The every other embodiment that those of ordinary skill in the art are obtained under the premise of creative work is not paid, belongs to this hair
The scope of bright protection.
With reference to embodiment, the invention will be further described.
Embodiment 1
Using process above flow, equipment and technical measures etc., Chloranthus glaber fibre spun-laced non-woven mask substrate is developed, its
In, it is made of the raw material of following weight proportioning：The weight content of Chloranthus glaber fiber accounts for 70%, and the weight of viscose rayon contains
Amount accounts for 10%, and the weight content of polyester fiber accounts for 20%.The performance indications of spunlace non-woven mask substrate are：Actual quantification 50g/
m2, average thickness 0.30mm；Longitudinal strength 72.75N, horizontal strength 58.75N, vertically and horizontally strength ratio 1.24:1；Longitudinal fracture is stretched
Long rate 24.63%, transverse breakage elongation 43.13%, vertically and horizontally elongation at break is than 0.57:1；Longitudinal tear strength 9.75N, it is horizontal
To Tear strength 9.75N, vertically and horizontally Tear strength is than 1:1.Staphylococcus aureus（ATCC6538）Bacteriostasis rate 91.2%, large intestine
Bacillus（8089）Bacteriostasis rate 92.2%, Candida albicans（ATCC10231）Bacteriostasis rate 92.7%.
The Chloranthus glaber fibre spun-laced non-woven mask substrate of exploitation, there is skin-protecting face nursing, skin care, skin-friendly is good, defends
The healthcare functions such as natural disposition is good, the good, good permeability of good hygroscopicity, wet guilding, can be effectively facilitated metabolism, prevent skin from declining
Always, there is good protective effect to human body, there is moisturizing, activating cell, oxygen supply, suppression with the spunlace non-woven base fabric of its processing
The functions such as bacterium, antibacterial, there is the effect such as nourishing, nutrition, health care to skin, product purpose is extensive, is adapted to exploitation clean skin moisturizing, protects
The facial mask that fitness is held.
Embodiment 2
Using process above flow, equipment and technical measures etc., Chloranthus glaber fibre spun-laced non-woven mask substrate is developed, its
In, it is made of the raw material of following weight proportioning：The weight content of Chloranthus glaber fiber accounts for 60%, and the weight of viscose rayon contains
Amount accounts for 10%, and the weight content of polyester fiber accounts for 30%.The performance indications of spunlace non-woven mask substrate are：Actual quantification 50g/
m2, average thickness 0.32mm；Longitudinal strength 65.08N, horizontal strength 70.17N, vertically and horizontally strength ratio 0.93:1；Longitudinal fracture is stretched
Long rate 25.42%, transverse breakage elongation 35.75%, vertically and horizontally elongation at break is than 0.71:1；Longitudinal tear strength 10.17N,
Horizontal Tear strength 12.08N, vertically and horizontally Tear strength is than 0.84:1.Staphylococcus aureus（ATCC6538）Bacteriostasis rate
88.1%, Escherichia coli（8089）Bacteriostasis rate 88.2%, Candida albicans（ATCC10231）Bacteriostasis rate 88.3%.The Chloranthus glaber of exploitation
Fibre spun-laced non-woven mask substrate, have skin-protecting face nursing, skin care, skin-friendly is good, wholesomeness is good, good hygroscopicity, lead it is wet
The healthcare functions such as the good, good permeability of property, can be effectively facilitated metabolism, prevent skin senescence, there is good protection to human body
Effect, there is the function such as moisturizing, activating cell, oxygen supply, antibacterial, antibacterial with the spunlace non-woven base fabric of its processing, have to skin
There is the effect such as nourishing, nutrition, health care, product purpose is extensive, is adapted to exploitation clean skin moisturizing, the facial mask of health and beauty.
Embodiment 3
Using process above flow, equipment and technical measures etc., Chloranthus glaber fibre spun-laced non-woven mask substrate is developed, its
In, it is made of the raw material of following weight proportioning：The weight content of Chloranthus glaber fiber accounts for 80%, and the weight of viscose rayon contains
Amount accounts for 10%, and the weight content of polyester fiber accounts for 10%.
The performance indications of spunlace non-woven mask substrate are：Actual quantification 50g/m2, average thickness 0.35mm；Longitudinal direction strength
58.27N, horizontal strength 46.20N, vertically and horizontally strength ratio 1.26:1；Longitudinal elongation at break rate 20.6%, transverse breakage elongation
36.07%, vertically and horizontally elongation at break is than 0.57:1；Longitudinal tear strength 6.67N, horizontal Tear strength 6.93N, vertically and horizontally tears
Split strength ratio 0.96:1.Staphylococcus aureus（ATCC6538）Bacteriostasis rate 91.8%, Escherichia coli（8089）Bacteriostasis rate 92.9%,
Candida albicans（ATCC10231）Bacteriostasis rate 93.1%.The Chloranthus glaber fibre spun-laced non-woven mask substrate of exploitation, has skin care
The healthcare function such as beauty treatment, skin care, skin-friendly is good, wholesomeness is good, good hygroscopicity, the good, good permeability of wet guilding, can be effectively
Enhance metabolism, prevent skin senescence, there is good protective effect to human body, have with the spunlace non-woven base fabric of its processing
The function such as moisturizing, activating cell, oxygen supply, antibacterial, antibacterial, there is nourishing, nutrition, health care etc. to act on skin, product purpose is wide
It is general, it is adapted to exploitation clean skin moisturizing, the facial mask of health and beauty.
Embodiment 4
Using process above flow, equipment and technical measures etc., Chloranthus glaber fibre spun-laced non-woven mask substrate is developed, its
In, it is made of the raw material of following weight proportioning：The weight content of Chloranthus glaber fiber accounts for 50%, and the weight of viscose rayon contains
Amount accounts for 10%, and the weight content of polyester fiber accounts for 40%.The performance indications of spunlace non-woven mask substrate are：Actual quantification 68g/
m2, average thickness 0.42mm；Longitudinal strength 80.25N, horizontal strength 40.25N, vertically and horizontally strength ratio 0.51:1；Longitudinal fracture is stretched
Long rate 17.25%, transverse breakage elongation 34.6%, vertically and horizontally elongation at break is than 0.46:1；Longitudinal tear strength 11.1N, it is horizontal
To Tear strength 11.2N, vertically and horizontally Tear strength is than 0.95:1.Staphylococcus aureus（ATCC6538）Bacteriostasis rate 85.7%, greatly
Enterobacteria（8089）Bacteriostasis rate 85.2%, Candida albicans（ATCC10231）Bacteriostasis rate 85.8%.The Chloranthus glaber of exploitation is fiber spun-laced
Non-woven mask substrate, there is skin-protecting face nursing, skin care, skin-friendly is good, wholesomeness is good, good hygroscopicity, wet guilding are good, ventilative
Property well wait healthcare function, metabolism can be effectively facilitated, prevent skin senescence, there is good protective effect to human body, use it
The spunlace non-woven base fabric of processing has the function such as moisturizing, activating cell, oxygen supply, antibacterial, antibacterial, has to skin and nourishes, seeks
The effect such as foster, health care, product purpose is extensive, is adapted to exploitation clean skin moisturizing, the facial mask of health and beauty.
Embodiment 5
Using process above flow, equipment and technical measures etc., Chloranthus glaber fibre spun-laced non-woven mask substrate is developed, its
In, it is made of the raw material of following weight proportioning：The weight content of Chloranthus glaber fiber accounts for 100%, and the weight of viscose rayon contains
Amount accounts for 0%, and the weight content of polyester fiber accounts for 0%.The performance indications of spunlace non-woven mask substrate are：Actual quantification 58g/m2,
Average thickness 0.32mm；Longitudinal strength 72.13N, horizontal strength 49.75N, vertically and horizontally strength ratio 1.45:1；Longitudinal elongation at break
Rate 19.25%, transverse breakage elongation 38.5%, vertically and horizontally elongation at break is than 0.50:1；Longitudinal tear strength 6.75N, laterally
Tear strength 6.88N, vertically and horizontally Tear strength is than 0.98:1.Staphylococcus aureus（ATCC6538）Bacteriostasis rate 93.7%, large intestine
Bacillus（8089）Bacteriostasis rate 93.1%, Candida albicans（ATCC10231）Bacteriostasis rate 93.0%.The Chloranthus glaber of exploitation is fiber spun-laced non-
Mask substrate is weaved, there is skin-protecting face nursing, skin care, skin-friendly is good, wholesomeness is good, good hygroscopicity, wet guilding are good, gas permeability
Well wait healthcare function, metabolism can be effectively facilitated, prevent skin senescence, there is good protective effect to human body, with itself plus
The spunlace non-woven base fabric of work has the function such as moisturizing, activating cell, oxygen supply, antibacterial, antibacterial, to skin have nourishing, nutrition,
Health care etc. acts on, and product purpose is extensive, is adapted to exploitation clean skin moisturizing, the facial mask of health and beauty.
Embodiment 6
Chloranthus glaber fibre spun-laced non-woven mask substrate is made of the raw material of following percentage by weight in the present embodiment：Chloranthus glaber
Fiber 10%, viscose rayon 90%.
Preparation method is as follows：
（1）Shredding mixes：Raw material is uniformly mixed, then feeds carding machine；
（2）The technological parameter of carding machine：End speed 0.25m/min, linear velocity 32.5m/min, hold-down roller 26.2r/min are fed,
Upper pallet 28.6r/min, lower pallet 32.9r/min, upper outlet roller 29.5r/min, lower outlet roller 19.6r/min, upper back-off roller
14.0r/min, lower back-off roller 14.0r/min, upper doffer 32.8r/min, lower doffer 34.1r/min, end 1.06r/min is fed for,
Licker-in 179.1r/min, working roll 66.2r/min, cylinder 962r/min, export platen 18.3r/min, card stripper 150.6r/
Min, gauge 45.0mm, carding machine fibre web output speed 55m/min；
（3）Lapping：Raw material after combing is fed into cross lapping machine, the technological parameter of cross lapping machine：The m/ of linear velocity 33.4
Min, small vehicle speed 30.7m/min, curtain speed 40.3/min is inputted, export curtain speed 4.6m/min, 4 layers of the number of plies, width
2330mm；
（4）Drawing-off：Drafting machine is made up of 15 drawing-off card clothing rollers and gripping card clothing roller, forms 3 draw zones；The work of drafting machine
Skill parameter：1.1 times of total draft multiple, the first 7.0 times of roller drafting multiple, the second 12.0 times of roller drafting multiple, the 3rd roller drawing-off times
8.4 times of number, 12.4 times of four-roller drafting multiple.Fibre web inputs the speed 10.18m/min of drafting machine, the output speed of drafting machine
15.0m/min；
（5）Spun lacing：Spun lacing road number uses 5 spun lacings, and spun lacing is prewetted using double pin hole, and pre- spun lacing aperture is 0.15mm, and second
Road spun lacing aperture is 0.10mm, and the 3rd spun lacing uses reverse side spun lacing, aperture 0.08mm；4th and the 5th spun lacing aperture
For 0.10mm.The technological parameter of spun-laced machine：Convoying curtain First Speed 11.3m/min, cylinder speed 15.5m/min, conveying
Curtain second speed 14.8m/min, pressure (bar) is respectively 23,40,60,30,58,70,67.Prewet 3.0bar, bore dia of spraying water
0.12mm, pitch-row 0.6mm, spun-laced machine output speed 12m/min；
（6）Drying：Dried using dryer, the technological parameter of dryer：Linear velocity 10.1m/min, set drying temperature
110℃；
（7）Winding：It is wound using up- coiler, the technological parameter of up- coiler：300m/ volumes of spooling length, winding diameter
450mm, the winding speed 11.0m/min of up- coiler.
The performance indications for the spunlace non-woven mask substrate prepared are：Actual quantification 38g/m2, average thickness 0.29mm；
Longitudinal strength 51.5N, horizontal strength 32.0N, vertically and horizontally strength ratio 0.48:1；Longitudinal elongation at break rate 14.21%, transverse breakage
Elongation 26.0%, vertically and horizontally elongation at break is than 0.43:1；Longitudinal tear strength 5.3N, horizontal Tear strength 5.1N, vertically and horizontally
Tear strength is than 0.55:1.
Embodiment 7
Chloranthus glaber fibre spun-laced non-woven mask substrate is made of the raw material of following percentage by weight in the present embodiment：Chloranthus glaber
Fiber 10%, viscose rayon 10%, polyester fiber 80%.
Preparation method is as follows：
（1）Shredding mixes：Raw material is uniformly mixed, then feeds carding machine；
（2）The technological parameter of carding machine：End speed 0.45m/min, linear velocity 38.5m/min, hold-down roller 31.5r/min are fed,
Upper pallet 30.6r/min, lower pallet 38.4r/min, upper outlet roller 32.8r/min, lower outlet roller 32.7r/min, upper back-off roller
21.5r/min, lower back-off roller 20.9r/min, upper doffer 36.9r/min, lower doffer 39.8r/min, end 2.15r/min is fed for,
Licker-in 195.6r/min, working roll 88.5r/min, cylinder 1000r/min, export platen 23.6r/min, card stripper 176.4r/
Min, gauge 45.6mm, carding machine fibre web output speed 60m/min；
（3）Lapping：Raw material after combing is fed into cross lapping machine, the technological parameter of cross lapping machine：The m/ of linear velocity 36.8
Min, small vehicle speed 35.4m/min, curtain speed 41.2/min is inputted, export curtain speed 8.9m/min, 5 layers of the number of plies, width
2520mm；
（4）Drawing-off：Drafting machine is made up of 15 drawing-off card clothing rollers and gripping card clothing roller, forms 3 draw zones；The work of drafting machine
Skill parameter：1.5 times of total draft multiple, the first 9.8 times of roller drafting multiple, the second 14.6 times of roller drafting multiple, the 3rd roller drawing-off times
15.7 times of number, 19.6 times of four-roller drafting multiple.Fibre web inputs the speed 10.65m/min of drafting machine, the output speed of drafting machine
16.2m/min；
（5）Spun lacing：Spun lacing road number uses 6 spun lacings, and spun lacing is prewetted using double pin hole, and pre- spun lacing aperture is 0.15mm, and second
Road spun lacing aperture is 0.11mm, and the 3rd spun lacing uses reverse side spun lacing, aperture 0.09mm；4th and the 5th spun lacing aperture
For 0.11mm.The technological parameter of spun-laced machine：Convoying curtain First Speed 18.5m/min, cylinder speed 23.2m/min, conveying
The m/min of curtain second speed 20, pressure (bar) is respectively 50,65,85,85,95,100,85.Prewet 5.0bar, bore dia of spraying water
0.12mm, pitch-row 0.6mm, spun-laced machine output speed 15m/min；
（6）Drying：Dried using dryer, the technological parameter of dryer：Linear velocity 15.3m/min, set drying temperature
150℃；
（7）Winding：It is wound using up- coiler, the technological parameter of up- coiler：800m/ volumes of spooling length, winding diameter
760mm, the winding speed 20.3m/min of up- coiler.
The performance indications for the spunlace non-woven mask substrate prepared are：Actual quantification 56g/m2, average thickness 0.36mm；
Longitudinal strength 95.2N, horizontal strength 86.4N, vertically and horizontally strength ratio 1.32:1；Longitudinal elongation at break rate 35.2%, transverse breakage is stretched
Long rate 36.5%, vertically and horizontally elongation at break is than 0.65:1；Longitudinal tear strength 10.3N, horizontal Tear strength 8.6N, vertically and horizontally
Tear strength is than 0.85:1.
Embodiment 8
Chloranthus glaber fibre spun-laced non-woven mask substrate is made of the raw material of following percentage by weight in the present embodiment：Chloranthus glaber
Fiber 50%, viscose rayon 20%, polyester fiber 30.
Preparation method is as follows：
（1）Shredding mixes：Raw material is uniformly mixed, then feeds carding machine；
（2）The technological parameter of carding machine：End speed 0.63m/min, linear velocity 43.6m/min, hold-down roller 35.9r/min are fed,
Upper pallet 35.4r/min, lower pallet 42.9r/min, upper outlet roller 35.6r/min, lower outlet roller 34.5r/min, upper back-off roller
25.6r/min, lower back-off roller 25.3r/min, upper doffer 40.7r/min, lower doffer 42.8r/min, end 2.35r/min is fed for,
Licker-in 206r/min, working roll 96.8r/min, cylinder 1010r/min, export platen 27.3r/min, card stripper 182.8r/
Min, gauge 45.8mm, carding machine fibre web output speed 65m/min；
（3）Lapping：Raw material after combing is fed into cross lapping machine, the technological parameter of cross lapping machine：The m/ of linear velocity 41.8
Min, small vehicle speed 38.4m/min, curtain speed 41.8/min is inputted, export curtain speed 11.9m/min, 6 layers of the number of plies, width
2780mm；
（4）Drawing-off：Drafting machine is made up of 15 drawing-off card clothing rollers and gripping card clothing roller, forms 3 draw zones；The work of drafting machine
Skill parameter：1.8 times of total draft multiple, the first 11.0 times of roller drafting multiple, the second 16.2 times of roller drafting multiple, the 3rd roller drawing-off times
19.6 times of number, 23.6 times of four-roller drafting multiple.Fibre web inputs the speed 10.84m/min of drafting machine, the output speed of drafting machine
16.8m/min；
（5）Spun lacing：Spun lacing road number uses 7 spun lacings, and spun lacing is prewetted using double pin hole, and pre- spun lacing aperture is 0.15mm, and second
Road spun lacing aperture is 0.12mm, and the 3rd spun lacing uses reverse side spun lacing, aperture 0.10mm；4th and the 5th spun lacing aperture
For 0.12mm.The technological parameter of spun-laced machine：Convoying curtain First Speed 21.1m/min, cylinder speed 29.8m/min, conveying
The m/min of curtain second speed 25, pressure (bar) is respectively 65,105,115,105,110,110,110.Prewet 6.0bar, water spray
Bore dia 0.12mm, pitch-row 0.6mm, spun-laced machine output speed 18m/min；
（6）Drying：Dried using dryer, the technological parameter of dryer：Linear velocity 18.9m/min, set drying temperature
180℃；
（7）Winding：It is wound using up- coiler, the technological parameter of up- coiler：1000m/ volumes of spooling length, winding diameter
960mm, the winding speed 28.8m/min of up- coiler.
The performance indications for the spunlace non-woven mask substrate prepared are：Actual quantification 72g/m2, average thickness 0.48mm；
Longitudinal strength 104.0N, horizontal strength 115.0N, vertically and horizontally strength ratio 1.81:1；Longitudinal elongation at break rate 48.32%, it is laterally disconnected
Elongation 52.8% is split, vertically and horizontally elongation at break is than 0.96:1；Longitudinal tear strength 15.38N, horizontal Tear strength 15.6N,
Vertically and horizontally Tear strength is than 1.18:1.
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all essences in the present invention
God any modification, equivalent substitution and improvements made etc., should be included in the scope of the protection with principle.
Claims (9)
1. a kind of Chloranthus glaber fibre spun-laced non-woven mask substrate, it is characterised in that spunlace non-woven mask substrate is by following heavy
The raw material of amount percentage is made：Chloranthus glaber fiber 10-100%, viscose rayon 0-90%, polyester fiber 0-80%.
2. Chloranthus glaber fibre spun-laced non-woven mask substrate according to claim 1, it is characterised in that：The spun lacing is non-to knit
The performance indications for making mask substrate are：Actual quantification 38-72g/m2, average thickness 0.29-0.48mm；Longitudinal strength 51.5-
104.0N, horizontal strength 32.0-115.0N, vertically and horizontally strength ratio（0.48:1）-（1.81:1）；Longitudinal elongation at break rate 14.21-
48.32%, transverse breakage elongation 26.0-52.8%, vertically and horizontally elongation at break ratio（0.43:1）-（0.96:1）；Longitudinal tear
Strength 5.3-15.38N, horizontal Tear strength 5.1-15.6N, vertically and horizontally Tear strength ratio（0.55:1）-（1.18:1）.
3. Chloranthus glaber fibre spun-laced non-woven mask substrate according to claim 1 or 2, it is characterised in that the careless coral
The single fiber line density of coral fiber is 1.7 dtex, length 38.00mm.
4. Chloranthus glaber fibre spun-laced non-woven mask substrate according to claim 1 or 2, it is characterised in that the terylene
The single fiber line density of fiber is 1.33-1.74 dtex, length 33.0-58.0mm.
5. Chloranthus glaber fibre spun-laced non-woven mask substrate according to claim 1 or 2, it is characterised in that the viscose glue
The single fiber line density of fiber is 1.10-1.73 dtex, length 33.0-40.0mm.
6. the preparation method of the Chloranthus glaber fibre spun-laced non-woven mask substrate described in claim 1, it is characterised in that specific system
Standby step is as follows：
（1）Shredding mixes：Mix raw material shredding and uniformly；
（2）Comb, by step（1）Well mixed raw material feeding carding machine, the technological parameter of carding machine：Feed end speed 0.25
~ 0.63m/min, 32.5 ~ 43.6m/min of linear velocity, hold-down roller 26.2 ~ 35.9r/min, upper 28.6 ~ 35.4r/min of pallet, under
Pallet 32.9 ~ 42.9r/min, upper 29.5 ~ 35.6r/min of outlet roller, 19.6 ~ 34.5r/min of lower outlet roller, upper back-off roller 14.0
~ 25.6r/min, lower back-off roller 14.0 ~ 25.3r/min, upper 32.8 ~ 40.7r/min of doffer, 34.1 ~ 42.8r/min of lower doffer,
It is fed for 1.06 ~ 2.35r/min of end, 179.1 ~ 206r/min of licker-in, 66.2 ~ 96.8r/min of working roll, 962 ~ 1010r/ of cylinder
Min, export 18.3 ~ 27.3r/min of platen, 150.6 ~ 182.8r/min of card stripper, 45.0 ~ 45.8mm of gauge, carding machine fibre web
55 ~ 65m/min of output speed；
（3）Lapping：By step（2）Raw material feeding cross lapping machine after combing, the technological parameter of cross lapping machine：Linear velocity
33.4 ~ 41.8 m/min, small 30.7 ~ 38.4m/min of vehicle speed, input curtain 40.3 ~ 41.8/min of speed, output curtain speed 4.6 ~
11.9m/min, 4 ~ 6 layers of the number of plies, 2330 ~ 2780mm of width；
（4）Drawing-off：Step（3）Raw material after lapping enters drafting machine, and drafting machine is by 15 drawing-off card clothing rollers and grips pin cloth
Roller group into, formed 3 draw zones；The technological parameter of drafting machine：1.1 ~ 1.8 times of total draft multiple, the first roller drafting multiple 7.0 ~
11.0 times, the second 12.0 ~ 16.2 times of roller drafting multiple, the 3rd 8.4 ~ 19.6 times of roller drafting multiple, four-roller drafting multiple 12.4 ~
23.6 times.
7. fibre web inputs the 10.18 ~ 10.84m/min of speed, 15.0 ~ 16.8m/min of output speed of drafting machine of drafting machine；
（5）Spun lacing：Step（4）Raw material after middle drawing-off enters spun-laced machine, and spun lacing road number uses 5 ~ 7 spun lacings, the work of spun-laced machine
Skill parameter：Convoying curtain 11.3 ~ 21.1m/min of First Speed, cylinder 15.5 ~ 29.8m/min of speed, convoying curtain second speed
14.8 ~ 25 m/min, pressure (bar) are respectively 23 ~ 65,40 ~ 105,60 ~ 115,30 ~ 105,58 ~ 110,70 ~ 110,67 ~ 110.
8. prewet 3.0 ~ 6.0bar, spray water bore dia 0.12mm, pitch-row 0.6mm, 12 ~ 18m/min of spun-laced machine output speed；
（6）Drying：Dried using dryer, the technological parameter of dryer：10.1 ~ 18.9m/min of linear velocity, setting drying
110 ~ 180 DEG C of temperature；
（7）Winding：It is wound using up- coiler, the technological parameter of up- coiler：300 ~ 1000m/ volumes of spooling length, winding diameter
450 ~ 960mm, 11.0 ~ 28.8m/min of winding speed of up- coiler.
9. the preparation method of the Chloranthus glaber fibre spun-laced non-woven mask substrate described in claim 6, it is characterised in that：The step
Suddenly（5）Spun lacing road number uses 5 ~ 7 spun lacings, and spun lacing is prewetted using double pin hole, and pre- spun lacing aperture is 0.15mm, second spun lacing
Aperture is 0.10 ~ 0.12mm, and the 3rd spun lacing uses reverse side spun lacing, and aperture is 0.08 ~ 0.10mm；4th and the 5th spun lacing
Aperture is 0.10 ~ 0.12mm.