CN107352867A - A kind of environment-friendly type building plate of material and its manufacture method - Google Patents
A kind of environment-friendly type building plate of material and its manufacture method Download PDFInfo
- Publication number
- CN107352867A CN107352867A CN201710541521.1A CN201710541521A CN107352867A CN 107352867 A CN107352867 A CN 107352867A CN 201710541521 A CN201710541521 A CN 201710541521A CN 107352867 A CN107352867 A CN 107352867A
- Authority
- CN
- China
- Prior art keywords
- parts
- waste material
- waste
- environment
- friendly type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of environment-friendly type building plate of material and its manufacture method, to reclaim waste material, foamed cement material, resin, fire proofing, concrete intensifier primary raw material, waste material is reclaimed in itself using raw materials such as concrete waste material, slabstone waste material, shraff, glass wastes, cost is than relatively low, and good practical effect, there is good plasticity and intensity, using resin, concrete intensifier etc., intensity is effectively raised, makes it overall more tough；Fire retardant is added in material, improve building construction thermal insulation, insulation, waterproof, fire-retardant performance, it is important that, main raw material(s) in the present invention is the waste material of recovery, polished, stir, batch mixing, drying, the process such as polishing, constructional material plate of the discarded raw material processing into environment-friendly type will be reclaimed；The manufacturing cost of building board is not only effectively reduced, and bulk strength can arrive the use demand of construction.
Description
Technical field
The present invention relates to a kind of environment-friendly type building plate of material and its manufacture method, belong to building board manufacturing technology field.
Background technology
Building board is one of very important raw material in building construction process, existing building board wide variety,
Also a great difference, user can select different building boards according to different purposes for price, material, processing method, but existing
Some building boards for waste and old resource utilization rate not enough, this also results in the increase of construction cost；The present invention provides one
Environmental-protecting performance constructional material plate of the kind using construction waste as raw material, can effectively improve resource utilization, and can reduce manufacture
Cost.
The content of the invention
The present invention provides a kind of environment-friendly type building plate of material and its manufacture method.
In order to solve the above-mentioned technical problem, the invention provides following technical scheme：
A kind of environment-friendly type building plate of material of the present invention, include the preparing raw material of following parts by weight：Recovery waste material 50-70 parts,
Foamed cement material 20-30 parts, resin 5-10 parts, fire proofing 5-10 parts, concrete intensifier 5-10 parts.
As a preferred technical solution of the present invention, include the preparing raw material of following parts by weight：Including following parts by weight
Preparing raw material：Reclaim 60 parts of waste material, 25 parts of foamed cement material, 5 parts of resin, 5 parts of fire proofing, 5 parts of concrete intensifier.
As a preferred technical solution of the present invention, recovery waste material includes the preparing raw material of following parts by weight：Concrete
Waste material 30-40 parts, slabstone waste material 30-40 parts, shraff 20-30 parts, glass waste 20-30 parts.
As a preferred technical solution of the present invention, recovery waste material includes the preparing raw material of following parts by weight：Concrete
30 parts of waste material, 30 parts of slabstone waste material, 20 parts of shraff, 20 parts of glass waste.
As a preferred technical solution of the present invention, the resin is thermoplastic resin.
As a preferred technical solution of the present invention, the fire proofing is polyurethane material.
Present invention also offers the preparation method of above-mentioned environment-friendly type building plate of material：
Step (1), concrete waste material, slabstone waste material, shraff, glass waste are weighed by weight ratio.
Step (2), concrete waste material, slabstone waste material, shraff, glass waste are put into disintegrating apparatus respectively
Row crushes, and powder is made, preferential from powder of the mesh number in 100 mesh once.
Step (3), manufactured powder in step 2 is added in mixing plant, adds suitable powder quality 1/3rd
Recovery waste material mixture is made after ten minutes in moisture, uniform stirring, stirring.
Step (4), foamed cement material, resin, fire proofing, mixed is added in obtained waste material mixture in step 3
Native reinforcing agent is coagulated, continues thereafter with stirring, liquid mixture is made.
Step (5), obtained liquid mixture in step 4 is poured into material board mold in proportion, mould is prevented from drying
In dry equipment, process is compressed in drying course, drying is taken out after 2 hours, carries out the polishing on surface.
Step (6), the sheet material after being polished in step 5 is taken out, the lacquer painting on surface smear, after lacquer painting air-dries, be made
Constructional material plate.
A kind of environment-friendly type building plate of material of the present invention, including it is recovery waste material, foamed cement material, resin, fire proofing, mixed
Coagulate native reinforcing agent；Wherein main component is ceramic raw material, and recovery waste material is in itself using concrete waste material, slabstone waste material, waste ceramic
The raw materials such as material, glass waste, cost is than relatively low, and good practical effect, has good plasticity and intensity, using resin,
Concrete intensifier etc., effectively raises intensity, makes it overall more tough；Fire retardant is added in material, improves house
Building insulation, insulation, waterproof, fire-retardant performance, it is important that the main raw material(s) in the present invention is the waste material of recovery,
Polished, stirred, batch mixing, drying, the process such as polishing, constructional material plate of the discarded raw material processing into environment-friendly type will be reclaimed；No
The manufacturing cost of building board is only effectively reduced, and bulk strength can arrive the use demand of construction.
The beneficial effect that is reached of the present invention is：A kind of environment-friendly type building plate of material of the present invention and its manufacture method, material
It is upper using construction waste as primary raw material, by polishing, stirring, batch mixing, drying, the process such as polishing building board is made, this
Kind processing mode not only effectively raises resource utilization, and can reduce manufacturing cost, saves resource；This kind building simultaneously
Plate of material, intensity, hardness, fire-retardant, insulation, water resistance are satisfied by actual use demand.
Embodiment
The preferred embodiments of the present invention are illustrated below, it will be appreciated that preferred embodiment described herein is only used
In the description and interpretation present invention, it is not intended to limit the present invention.
Embodiment 1
A kind of environment-friendly type building plate of material of the present invention, include the preparing raw material of following parts by weight：Recovery waste material 50-70 parts,
Foamed cement material 20-30 parts, resin 5-10 parts, fire proofing 5-10 parts, concrete intensifier 5-10 parts.
Include the preparing raw material of following parts by weight：Include the preparing raw material of following parts by weight：Reclaim 60 parts of waste material, foaming water
25 parts of mud material, 5 parts of resin, 5 parts of fire proofing, 5 parts of concrete intensifier.
Recovery waste material includes the preparing raw material of following parts by weight：Concrete waste material 30-40 parts, slabstone waste material 30-40 parts, pottery
Porcelain waste material 20-30 parts, glass waste 20-30 parts.
Recovery waste material includes the preparing raw material of following parts by weight：30 parts of concrete waste material, 30 parts of slabstone waste material, shraff
20 parts, 20 parts of glass waste.
The resin is thermoplastic resin.The fire proofing is polyurethane material.
A kind of manufacture method of environment-friendly type building plate of material of the present invention, comprises the following steps：
Step (1), concrete waste material, slabstone waste material, shraff, glass waste are weighed by weight ratio.
Step (2), concrete waste material, slabstone waste material, shraff, glass waste are put into disintegrating apparatus respectively
Row crushes, and powder is made, preferential from powder of the mesh number in 100 mesh once.
Step (3), manufactured powder in step 2 is added in mixing plant, adds suitable powder quality 1/3rd
Recovery waste material mixture is made after ten minutes in moisture, uniform stirring, stirring.
Step (4), foamed cement material, resin, fire proofing, mixed is added in obtained waste material mixture in step 3
Native reinforcing agent is coagulated, continues thereafter with stirring, liquid mixture is made.
Step (5), obtained liquid mixture in step 4 is poured into material board mold in proportion, mould is prevented from drying
In dry equipment, process is compressed in drying course, drying is taken out after 2 hours, carries out the polishing on surface.
Step (6), the sheet material after being polished in step 5 is taken out, the lacquer painting on surface smear, after lacquer painting air-dries, be made
Constructional material plate.
A kind of environment-friendly type building plate of material of the present invention, including it is recovery waste material, foamed cement material, resin, fire proofing, mixed
Coagulate native reinforcing agent；Wherein main component is ceramic raw material, and recovery waste material is in itself using concrete waste material, slabstone waste material, waste ceramic
The raw materials such as material, glass waste, cost is than relatively low, and good practical effect, has good plasticity and intensity, using resin,
Concrete intensifier etc., effectively raises intensity, makes it overall more tough；Fire retardant is added in material, improves house
Building insulation, insulation, waterproof, fire-retardant performance, it is important that the main raw material(s) in the present invention is the waste material of recovery,
Polished, stirred, batch mixing, drying, the process such as polishing, constructional material plate of the discarded raw material processing into environment-friendly type will be reclaimed；No
The manufacturing cost of building board is only effectively reduced, and bulk strength can arrive the use demand of construction.
A kind of environment-friendly type building plate of material of the present invention and its manufacture method, using construction waste as main former on material
Material, by polishing, stirring, batch mixing, drying, the process such as polishing building board is made, this processing mode not only effectively improves
Resource utilization, and can reduce manufacturing cost, save resource；This kind of constructional material plate simultaneously, intensity, hardness, fire-retardant, guarantor
Temperature, water resistance are satisfied by actual use demand.
Finally it should be noted that：The preferred embodiments of the present invention are the foregoing is only, are not intended to limit the invention,
Although the present invention is described in detail with reference to the foregoing embodiments, for those skilled in the art, it still may be used
To be modified to the technical scheme described in foregoing embodiments, or equivalent substitution is carried out to which part technical characteristic.
Within the spirit and principles of the invention, any modification, equivalent substitution and improvements made etc., it should be included in the present invention's
Within protection domain.
Claims (8)
1. a kind of environment-friendly type building plate of material, it is characterised in that include the preparing raw material of following parts by weight：Reclaim waste material 50-70
Part, foamed cement material 20-30 parts, resin 5-10 parts, fire proofing 5-10 parts, concrete intensifier 5-10 parts.
2. a kind of environment-friendly type building plate of material according to claim 1, it is characterised in that include the preparation of following parts by weight
Raw material：Reclaim 60 parts of waste material, 25 parts of foamed cement material, 5 parts of resin, 5 parts of fire proofing, 5 parts of concrete intensifier.
3. a kind of environment-friendly type building plate of material according to claim 2, it is characterised in that recovery waste material includes following weight
The preparing raw material of part：Concrete waste material 30-40 parts, slabstone waste material 30-40 parts, shraff 20-30 parts, glass waste 20-30
Part.
4. a kind of environment-friendly type building plate of material according to claim 3, it is characterised in that recovery waste material includes following weight
The preparing raw material of part：30 parts of concrete waste material, 30 parts of slabstone waste material, 20 parts of shraff, 20 parts of glass waste.
5. a kind of environment-friendly type building plate of material according to claim 1, it is characterised in that the resin is thermoplastic resin
Fat.
6. a kind of environment-friendly type building plate of material according to claim 1, it is characterised in that the fire proofing is polyurethane
Material.
7. the manufacture method of a kind of environment-friendly type building plate of material according to claim 1, it is characterised in that including following step
Suddenly,
S1 concrete waste material, slabstone waste material, shraff, glass waste) are weighed by weight ratio；
S2) concrete waste material, slabstone waste material, shraff, glass waste are put into disintegrating apparatus crushed respectively, is made
It is preferential from powder of the mesh number in 100 mesh once into powder；
S3) manufactured powder in step 2 is added in mixing plant, adds the moisture of suitable powder quality 1/3rd, uniformly
Recovery waste material mixture is made after ten minutes in stirring, stirring；
S4 foamed cement material, resin, fire proofing, concrete enhancing) are added in obtained waste material mixture in step 3
Agent, stirring is continued thereafter with, liquid mixture is made；
S5) obtained liquid mixture in step 4 is poured into material board mold in proportion, mould is prevented in drying plant,
Process is compressed in drying course, drying is taken out after 2 hours, carries out the polishing on surface；
S6) sheet material after being polished in step 5 is taken out, the lacquer painting on surface smear, after lacquer painting air-dries, construction material is made
Plate.
8. the manufacture method of a kind of environment-friendly type building plate of material according to claim 7, it is characterised in that the lacquer painting is
One or more in metal lacquer painting, F-C paint face, latex lacquer painting, facing mortar.