CN107352836A - Superpower nucleus of ultra early-strength concrete admixture and preparation method thereof - Google Patents
Superpower nucleus of ultra early-strength concrete admixture and preparation method thereof Download PDFInfo
- Publication number
- CN107352836A CN107352836A CN201710659285.3A CN201710659285A CN107352836A CN 107352836 A CN107352836 A CN 107352836A CN 201710659285 A CN201710659285 A CN 201710659285A CN 107352836 A CN107352836 A CN 107352836A
- Authority
- CN
- China
- Prior art keywords
- nucleus
- superpower
- concrete admixture
- strength concrete
- calcium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Claims (10)
- A kind of 1. superpower nucleus of ultra early-strength concrete admixture, by stabilizer, dispersant, calcium silicates, triethanolamine, calcium nitrate Mixed with water compounding, its raw material composition is:Stabilizer 0.2~0.5%, dispersant 0.1~0.5%, calcium silicates 8~13%, three Monoethanolamine 5~8%, calcium nitrate 1~10%, surplus are water, total amount 100%;The percentage is mass percent.
- 2. the superpower nucleus of ultra early-strength concrete admixture according to claim 1, it is characterised in that:The stabilizer is One or several kinds of mixing in hydroxypropyl methyl cellulose, xanthans, sodium carboxymethylcellulose, hydroxyethyl cellulose.
- 3. the superpower nucleus of ultra early-strength concrete admixture according to claim 1, it is characterised in that:The dispersant is Phosphoric acid ester dispersant, polyethylene glycol, polyvinylpyrrolidone, wetting dispersing agent OT-75, AEO, nonyl One or several kinds of mixing in phenol polyethenoxy ether, anionic polycarboxylate's sodium salt.
- 4. the superpower nucleus of ultra early-strength concrete admixture according to claim 1, it is characterised in that:The calcium silicates is Powder calcium nitrate, particle diameter 5-20mm.
- 5. the superpower nucleus of ultra early-strength concrete admixture according to claim 1, it is characterised in that its raw material forms For:0.1% hydroxypropyl methyl cellulose, 0.1% xanthans, 0.1 phosphate ester, 0.1% polyethylene glycol, 10% calcium silicates, 6% triethanolamine, 6.56% calcium nitrate, surplus are water, total amount 100%;The percentage is mass percent.
- 6. the superpower nucleus of ultra early-strength concrete admixture according to claim 1, it is characterised in that its raw material forms For:0.1% hydroxyethyl cellulose, 0.1% carboxymethyl cellulose, 0.1 polyvinylpyrrolidone, 0.1% fatty alcohol polyoxy second Alkene ether, 10% calcium silicates, 6% triethanolamine, 6.56% calcium nitrate, surplus are water, total amount 100%;The percentage is Mass percent.
- 7. the superpower nucleus of ultra early-strength concrete admixture according to claim 1, it is characterised in that its raw material forms For:0.1% hydroxypropyl methyl cellulose, 0.1 wetting dispersing agent OT-75,0.1% NPE, 8% silicic acid Calcium, 7% triethanolamine, 5.66% calcium nitrate, surplus are water, total amount 100%;The percentage is mass percent.
- 8. the superpower nucleus of ultra early-strength concrete admixture according to claim 1, it is characterised in that its raw material forms For:0.1% hydroxypropyl methyl cellulose, 0.1% polyethylene glycol, 0.1% polycarboxylate sodium, 8% calcium silicates, 8% three ethanol Amine, 5.66% calcium nitrate, surplus are water, total amount 100%;The percentage is mass percent.
- 9. the superpower nucleus of ultra early-strength concrete admixture according to claim 1, it is characterised in that its raw material forms For:0.2% hydroxypropyl methyl cellulose, 0.1% polyethylene glycol, 0.1% polycarboxylate sodium, 11% calcium silicates, 8% three second Hydramine, 7.55% calcium nitrate, surplus are water, total amount 100%;The percentage is mass percent.
- 10. the preparation method of the superpower nucleus of ultra early-strength concrete admixture according to claim any one of 1-9, it is walked Suddenly it is:According to formula rate, at a temperature of 0 DEG C, stirred when being added dropwise, by stabilizer, dispersant, calcium silicates, triethanolamine, nitre Sour calcium is distributed in water, is well mixed, is produced.