CN107345044A - A kind of high tenacity fire retardation PC/ABS - Google Patents
A kind of high tenacity fire retardation PC/ABS Download PDFInfo
- Publication number
- CN107345044A CN107345044A CN201710782547.5A CN201710782547A CN107345044A CN 107345044 A CN107345044 A CN 107345044A CN 201710782547 A CN201710782547 A CN 201710782547A CN 107345044 A CN107345044 A CN 107345044A
- Authority
- CN
- China
- Prior art keywords
- abs
- high tenacity
- fire retardation
- raw material
- tenacity fire
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
A kind of high tenacity fire retardation PC/ABS of the present invention, its raw material and raw material weight percentage composition are as follows:PC reclaimed materials 40 50%;Palmitin acid copolymer 0.1 1%;Boron nitride 0.1 3%;Lanthana 0.1 3%;Polytetrafluoroethylene (PTFE) 0.1 3%;ABS 40 60%.High tenacity fire retardation PC/ABS provided by the invention carries out blending and modifying using efficient alloy compatilizer to PC reclaimed materials and ABS, PC/ABS alloy materials are made, on the one hand PC melt viscosity can be reduced, improve its processing characteristics, on the other hand economic recycling is carried out to PC, extra burden will not be caused to environment.
Description
Technical field
The present invention relates to thermoplastic resin composition field in high polymer material technology, and in particular to a kind of PC
(Polycarbonate, makrolon) reclaimed materials is modified as the formula of high tenacity fire retardation PC (makrolon)/ABS alloys.
Background technology
PC is a kind of superior engineering plastics of combination property, have excellent impact flexibility, dimensional stability, electrically absolutely
The advantages that edge, creep resistant, weatherability, the transparency and nontoxicity, it is widely used in plant equipment, architectural engineering, traffic fortune
The field such as defeated, instrument and electric illumination.
PC also has the defects of some are obvious, such as:Processing fluidity is poor, easy stress cracking, to notch sensitive, easily abrasion,
Chemical proofing is poor, on the high side etc..PC consumption is larger, while caused defective material, regrinding-material in article manufacturing process
It is also more with the amount of reclaimed materials, therefore PC reclaimed materials is modified and can reused, it is significant.And ABS has
Preferable chemical resistance, good processability and higher cost performance.PC reclaimed materials and ABS are subjected to blending and modifying
PC/ABS alloy materials are made, on the one hand can reduce PC melt viscosity, improve its processing characteristics, while PC breach can be improved
Sensitiveness and chemical proofing, on the other hand PC can be recycled and reused again.
The content of the invention
To solve above-mentioned existing technical problem, the present invention uses following scheme:
A kind of high tenacity fire retardation PC/ABS, its raw material and raw material weight percentage composition are as follows:
PC reclaimed materials 40-50%;
Palmitin acid copolymer 0.1-1%;
Boron nitride 0.1-3%;
Lanthana 0.1-3%;
Polytetrafluoroethylene (PTFE) 0.1-3%;
ABS 40-60%.
High tenacity fire retardation PC/ABS provided by the invention is entered using efficient alloy compatilizer to PC reclaimed materials with ABS
Row blending and modifying, PC/ABS alloy materials are made, on the one hand can reduce PC melt viscosity, improve its processing characteristics, on the other hand
Economic recycling is carried out to PC, extra burden will not be caused to environment.
Embodiment
The present invention is described in detail below in conjunction with specific embodiment, herein illustrative examples and explanation of the invention
For explaining the present invention, but it is not as a limitation of the invention.
Embodiment
A kind of high tenacity fire retardation PC/ABS of the present invention, its raw material and raw material weight percentage composition are as follows:PC is returned
Rewinding 45%, palmitin acid copolymer 0.5%, boron nitride 0.5%, lanthana 1%, polytetrafluoroethylene (PTFE) 2%, ABS 51%.
The above-described embodiments merely illustrate the principles and effects of the present invention, not for the limitation present invention.It is any ripe
Know the personage of this technology all can carry out modifications and changes under the spirit and scope without prejudice to the present invention to above-described embodiment.Cause
This, those of ordinary skill in the art is complete without departing from disclosed spirit and institute under technological thought such as
Into all equivalent modifications or change, should by the present invention claim be covered.
Claims (1)
1. a kind of high tenacity fire retardation PC/ABS, it is characterised in that its raw material and raw material weight percentage composition are as follows:
PC reclaimed materials 40-50%;
Palmitin acid copolymer 0.1-1%;
Boron nitride 0.1-3%;
Lanthana 0.1-3%;
Polytetrafluoroethylene (PTFE) 0.1-3%;
ABS 40-60%.