CN107337977A - A kind of water-based paint compositions with antibacterial environment protection function - Google Patents
A kind of water-based paint compositions with antibacterial environment protection function Download PDFInfo
- Publication number
- CN107337977A CN107337977A CN201710751099.2A CN201710751099A CN107337977A CN 107337977 A CN107337977 A CN 107337977A CN 201710751099 A CN201710751099 A CN 201710751099A CN 107337977 A CN107337977 A CN 107337977A
- Authority
- CN
- China
- Prior art keywords
- water
- based paint
- paint compositions
- protection function
- environment protection
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of water-based paint compositions with antibacterial environment protection function, the water-based paint compositions raw materials by weight portion meter includes:20~30 parts of aqueous resin dispersion, 0.5~3 part of antiseptic, 10~20 parts of conventional additives, 15~25 parts of filler, 40~50 parts of water, wherein conventional additives include coalescents, defoamer, levelling agent, wetting agent, dispersant, and antiseptic is one kind or its combination in nano silicon, nano titanium oxide, nano zine oxide.Water paint produced by the present invention has relatively low volatile organic content and good anti-microbial property, and preparation technology is simple, and cost is low.
Description
Technical field
The invention belongs to technical field of coatings, is a kind of aqueous coating composition with antibacterial environment protection function specifically
Thing.
Background technology
Water paint is to use water as decentralized medium and the coating of diluent, water-based compared with the coating of organic solvent type
Coating has saved substantial amounts of organic material resource, greatly reduces pollution of the volatilization of organic solvent in coating to air and constructed
Fire hazard in journey, water are resources extremely abundant on the earth, and it is taken conveniently, and cost is cheap, as the solvent in coating
Use, destruction or less will not be produced to water resource.Therefore water paint had both reduced the discharge of volatile organic solvent, again might be used
Save resource, the energy, while convenience in transport and storage.With the enhancing of people's environmental consciousness, the usage amount of water paint is year by year
Increase, the main flow direction of modern coatings industrial development will be increasingly becoming.
Coating must take into consideration its efficiency and toxicity problem with antiseptic, and security be consider use value it is important because
Element.At present, antiseptic mainly substituted aromatic hydrocarbons, heterocyclic compound, aminated compounds and the Organometallic compounds that coating uses
The organic antibacterial agents such as thing.A series of problems be present in security, slow release, durability, heat resistance etc. in organic antibacterial agent.
All there is advantage in inorganic antiseptic, therefore its application and research are got in security, persistence, broad-spectrum antiseptic type, heat resistance etc.
To be more valued by people.
The intrinsic high stability of inorganic antiseptic, excellent antibiotic property, it is safe, it has also become the master of antiseptic research
Stream.But because some metal ions with antibacterial ability are too high with toxicity or cost, at present widely used antibacterial from
Son is only limitted to silver, two kinds of zinc, and the antibacterial ability of wherein silver ion is most strong, and singly it is the optimal of inorganic antiseptic in terms of antibacterial ability
Select, silver-colored toxicity is also far smaller than zinc in addition, so being the optimal selection of inorganic antiseptic.There is also some for inorganic antiseptic
Problem:It is antibacterial stability problem first.Because inorganic antiseptic majority contains silver ion, be easily transformed into brown silver oxide or
Black elemental silver is reduced into through ultraviolet catalyzed, discoloration not only reduces its antibiotic property, but also restricted its is applied to white
Or in light-coloured coating.Secondly it is largely high using silver-colored cost, it is constrained in larger range of application.Two above-mentioned technology difficulties
The serious popularization and use for constraining inorganic antiseptic of topic, turns into the biggest problem in this industry.
The content of the invention
For problems of the prior art and deficiency, it is an object of the invention to provide one kind to have antibacterial environment protection work(
The water-based paint compositions of energy, there is the characteristics of relatively low volatile organic content and anti-microbial property are good.
Technical problem solved by the invention can be realized using following technical scheme:
A kind of water-based paint compositions with antibacterial environment protection function, its raw materials by weight portion meter include:Water-base resin disperses
20~30 parts of body, 0.5~3 part of antiseptic, 10~20 parts of conventional additives, 15~25 parts of filler, 40~50 parts of water, wherein, institute
Stating conventional additives includes coalescents, defoamer, levelling agent, wetting agent, dispersant.
Levelling agent is a kind of conventional coating additive, it can promote coating formed during drying and forming-film one it is smooth,
Smooth, uniform film, it can effectively reduce and cover with paint, lacquer, colour wash, etc. liquid surface tension, improve its levelability and a kind of material of uniformity, can change
The permeability of kind covering with paint liquid, can reduce the possibility that spot and spot are produced when brushing, increase spreadability, make film forming uniformly, certainly
So.
In order to preferably realize the present invention, further, the antiseptic be nano silicon, nano titanium oxide,
One kind or its combination in nano zine oxide.Nano-TiO2In H2O、O2Light-catalyzed reaction, caused hydroxyl free occur in system
With various bacteria and smelly precursor reactant so as to effectively sterilize and eliminate stink, thus nano-TiO can be made in base2Antiseptic.
Nano-TiO2Antiseptic has the ability that bacterium and its remains are killed to removing together, while can also be by the toxin of bacterial secretory
Decompose.And nano-TiO2Also there is following feature as bactericide:First, prompt effect is good, such as ag system antimicrobial agent
Effect about occurs in 24h or so, and nano-TiO2Only need 1h or so;Second, TiO2It is a kind of the anti-of semipermanent maintenance antibacterial effect
Microbial inoculum, unlike other antiseptics can with the dissolution of antiseptic and effect is gradually reduced;Third, there is good security, with skin
Contact has no adverse effects.
In order to preferably realize the present invention, further, the aqueous resin dispersion is acrylic resin, polyurethane tree
One kind in fat, aqueous polyester resin, epoxy water-base resin.
In order to preferably realize the present invention, further, the filler is in calcium carbonate, talcum powder, kaolin, diatomite
One kind or its combination.
In order to preferably realize the present invention, further, the diatomite is nano diatomite.
In order to preferably realize the present invention, further, the nano diatomite is obtained by calcining, grinding.
In order to preferably realize the present invention, further, the coalescents are that alcohol ethers hold solvent.Form emulsion or divide
The polymer of granular media generally has the glass transition temperature higher than room temperature, in order that emulsion particle merges as uniform paint well
Film, it is necessary to reduce MFT using coalescents.Popular says, general emulsion has film-forming temperature, works as environment temperature
Emulsion is not easy film forming during less than emulsion film forming temperature, and coalescents can improve emulsion film forming mechanism, help film forming.Film forming after film forming
Auxiliary agent volatilizees, and does not interfere with the characteristic of film.Coalescents are small molecule organic compounds, the film forming being present in paint film
Auxiliary agent is eventually gradually escaped and vapored away.
To better implement the present invention, further, it is diethyl alcohol ethers or propane diols ethers that the alcohol ethers, which hold solvent,.
To better implement the present invention, further, the defoamer includes at least one of foam inhibitor and foamicide.
Paint solution in process of production, pumping and it is filling when can produce bubble, in application because agitation can also produce bubble, be present in paint solution
In bubble as eliminated not in time, after paint film is dry, form unacceptable flaw.Defoaming is can not in formula design process
The factor ignored, the defaoming mechanisms of defoamer are to be penetrated into by wetting as caused by system on foam film and constantly will be thin
Spread on film, make the surface tension of foam film uneven and brokenly bubble.
To better implement the present invention, further, the defoamer is organic polyether ester or mineral oil.
The present invention compared with prior art, has advantages below and beneficial effect:
The present invention in aqueous coating system add nano silicon, nano titanium oxide, one kind in nano zine oxide or
It, which is combined, is used as antiseptic, and anti-microbial property is good;
The present invention adds filler-calcium carbonate, talcum powder, kaolin, diatomite, nano diatomite and tree in aqueous coating system
Resin system compatibility is more preferable, makes the reduction of water paint cost;
The present invention is applied to a variety of water-base resin matrixes, easy to spread.
Embodiment
The preparation method of nano diatomite is:Diatomite is firstly placed in Muffle furnace and calcined, it is 400~500 to set temperature
Calcined 2~3 hours at DEG C, be put into ball mill and grind after cooling, into the particle of 200 mesh, then in 15~20% carbon acid solution
Middle immersion is taken out for 3~4 hours, is washed with deionized to neutrality, is placed into Muffle furnace and is calcined, and temperature is at 800~900 DEG C
Calcining takes out grinding after 2~3 hours, and nano diatomite is made.
The preparation method of water paint is:
A prepares water-borne dispersions:By the percentage by weight of setting, by deionized water, bactericide, wetting agent, dispersant, defoamer
It is mixed evenly, adds nano material and filler, with 1000~3000rpm be uniformly dispersed at a high speed, obtain aqueous dispersion
Body;
The water-borne dispersions that B obtains step A are added in emulsion or the aqueous dispersion resin of stirring, add coalescents, stream
Flat agent, thickener, anti-settling agent, pH adjusting agent are dispersed with stirring uniformly;
C adds pigment or colouring agent;
D moisturizings simultaneously adjust viscosity, and environment friendly antibacterial waterborne paint is made.
Anti-microbial property is tested with reference to QB/T 2591-2003A, water paint volatile organic matter(VOC)According to《Room
Interior decoration ornament materials limits of harmful substances》GB 18582-2007 are tested.
In order to make the purpose , technical scheme and advantage of the present invention be clearer, with reference to embodiments, to the present invention
It is further elaborated.
Embodiment 1:
A kind of water-based paint compositions with antibacterial environment protection function of the present embodiment, the water-based paint compositions raw material is by weight
Number meter includes:20 parts of aqueous resin dispersion acrylic resin, 0.5 part of antiseptic nano silicon, conventional additives 10
Part, 15 parts of filler-calcium carbonate, 40 parts of water, wherein, the conventional additives include coalescents propandiol butyl ether, defoamer mineral
Oil, levelling agent carboxymethyl cellulose, wetting agent, dispersant.
The obtained water paint with antibacterial environment protection function of the present embodiment is through industry internal standard testing inspection, as a result such as
Under:86.7% is reached to 24 hours sterilizing rates of Escherichia coli, 94.8% is reached to 24 hours sterilizing rates of Escherichia coli, VOC content
75.8g/L。
Embodiment 2:
A kind of water-based paint compositions with antibacterial environment protection function of the present embodiment, the water-based paint compositions raw material is by weight
Number meter includes:25 parts of aqueous resin dispersion polyurethane resin, 1 part of antiseptic nano titanium oxide, 15 parts of conventional additives,
20 parts of filler talcum powder, 45 parts of water, wherein, the conventional additives include coalescents propylene glycol methyl ether acetate, defoamer
Organic polyether ester, levelling agent carboxymethyl cellulose, wetting agent, dispersant.
The obtained water paint with antibacterial environment protection function of the present embodiment is through industry internal standard testing inspection, as a result such as
Under:85.9% is reached to 24 hours sterilizing rates of Escherichia coli, 93.2% is reached to 24 hours sterilizing rates of Escherichia coli, VOC content
82.8g/L。
Embodiment 3:
A kind of water-based paint compositions with antibacterial environment protection function of the present embodiment, the water-based paint compositions raw material is by weight
Number meter includes:20 parts of aqueous resin dispersion aqueous polyester resin, 2 parts of antiseptic nano zine oxide, 20 parts of conventional additives,
25 parts of filler kaolin, 50 parts of water, wherein, the conventional additives include coalescents propandiol butyl ether, defoamer mineral oil,
Levelling agent carboxymethyl cellulose, wetting agent, dispersant.
The obtained water paint with antibacterial environment protection function of the present embodiment is through industry internal standard testing inspection, as a result such as
Under:87.9% is reached to 24 hours sterilizing rates of Escherichia coli, 92.2% is reached to 24 hours sterilizing rates of Escherichia coli, VOC content
72.9g/L。
Embodiment 4:
A kind of water-based paint compositions with antibacterial environment protection function of the present embodiment, the water-based paint compositions raw material is by weight
Number meter includes:20 parts of aqueous resin dispersion epoxy water-base resin, 3 parts of antiseptic nano titanium oxide, conventional additives 10
Part, 15 parts of filler diatomite, 40 parts of water, wherein, the conventional additives include coalescents propylene glycol methyl ether acetate, defoaming
The organic polyether ester of agent, levelling agent carboxymethyl cellulose, wetting agent, dispersant.
The obtained water paint with antibacterial environment protection function of the present embodiment is through industry internal standard testing inspection, as a result such as
Under:87.5% is reached to 24 hours sterilizing rates of Escherichia coli, 91.2% is reached to 24 hours sterilizing rates of Escherichia coli, VOC content
77.9g/L。
Embodiment 5:
A kind of water-based paint compositions with antibacterial environment protection function of the present embodiment, the water-based paint compositions raw material is by weight
Number meter includes:20 parts of aqueous resin dispersion aqueous polyester resin, 2 parts of antiseptic nano zine oxide, 20 parts of conventional additives,
25 parts of filler nanometer diatomite, 50 parts of water, wherein, the conventional additives include coalescents propandiol butyl ether, defoamer ore deposit
Thing oil, levelling agent carboxymethyl cellulose, wetting agent, dispersant.
The obtained water paint with antibacterial environment protection function of the present embodiment is through industry internal standard testing inspection, as a result such as
Under:91.0% is reached to 24 hours sterilizing rates of Escherichia coli, 90.5% is reached to 24 hours sterilizing rates of Escherichia coli, VOC content
85.7g/L。
Embodiment 6:
A kind of water-based paint compositions with antibacterial environment protection function of the present embodiment, the water-based paint compositions raw material is by weight
Number meter includes:20 parts of aqueous resin dispersion acrylic resin, 1.7 parts of antiseptic nano zine oxide, 20 parts of conventional additives,
25 parts of filler-calcium carbonate, talcum powder, 50 parts of water, wherein, the conventional additives include coalescents propylene glycol methyl ether acetate,
The organic polyether ester of defoamer, levelling agent carboxymethyl cellulose, wetting agent, dispersant.
The obtained water paint with antibacterial environment protection function of the present embodiment is through industry internal standard testing inspection, as a result such as
Under:85.4% is reached to 24 hours sterilizing rates of Escherichia coli, 94.4% is reached to 24 hours sterilizing rates of Escherichia coli, VOC content
79.8g/L。
Embodiment 7:
A kind of water-based paint compositions with antibacterial environment protection function of the present embodiment, the water-based paint compositions raw material is by weight
Number meter includes:20 parts of aqueous resin dispersion aqueous polyester resin, antiseptic nano silicon, nano titanium oxide 2.5
Part, 20 parts of conventional additives, 19 parts of filler-calcium carbonate, diatomite, 50 parts of water, wherein, the conventional additives help including film forming
Agent propandiol butyl ether, defoamer mineral oil, levelling agent carboxymethyl cellulose, wetting agent, dispersant.
The obtained water paint with antibacterial environment protection function of the present embodiment is through industry internal standard testing inspection, as a result such as
Under:92.3% is reached to 24 hours sterilizing rates of Escherichia coli, 94.1% is reached to 24 hours sterilizing rates of Escherichia coli, VOC content
81.8g/L。
Embodiment 8:
A kind of water-based paint compositions with antibacterial environment protection function of the present embodiment, the water-based paint compositions raw material is by weight
Number meter includes:20 parts of aqueous resin dispersion epoxy water-base resin, 3 parts of antiseptic nano silicon, nano zine oxide, often
20 parts of additive of rule, 23 parts of filler kaolin, nano diatomite, 49 parts of water, wherein, the conventional additives include coalescents
The organic polyether ester of propylene glycol methyl ether acetate, defoamer, levelling agent carboxymethyl cellulose, wetting agent, dispersant.
The obtained water paint with antibacterial environment protection function of the present embodiment is through industry internal standard testing inspection, as a result such as
Under:85.6% is reached to 24 hours sterilizing rates of Escherichia coli, 91.6% is reached to 24 hours sterilizing rates of Escherichia coli, VOC content
82.5g/L。
Finally illustrate, have been shown and described above the present invention general principle and principal character and the present invention it is excellent
Point.It will be understood by a person skilled in the art that the present invention is not limited to the above embodiments, described in above-described embodiment and specification
The simply present invention principle, without departing from the spirit and scope of the present invention, the present invention, which also has, various change and to be changed
Enter, these changes and improvements all fall within the protetion scope of the claimed invention.
Claims (10)
1. a kind of water-based paint compositions with antibacterial environment protection function, it is characterised in that the water-based paint compositions raw material is pressed
Parts by weight meter includes:20~30 parts of aqueous resin dispersion, 0.5~3 part of antiseptic, 10~20 parts of conventional additives, filler
15~25 parts, 40~50 parts of water, wherein, the conventional additives include coalescents, defoamer, levelling agent, wetting agent, scattered
Agent.
A kind of 2. water-based paint compositions with antibacterial environment protection function according to claim 1, it is characterised in that:It is described
Antiseptic is one kind or its combination in nano silicon, nano titanium oxide, nano zine oxide.
A kind of 3. water-based paint compositions with antibacterial environment protection function according to claim 1, it is characterised in that:It is described
Aqueous resin dispersion is one kind in acrylic resin, polyurethane resin, aqueous polyester resin, epoxy water-base resin.
A kind of 4. water-based paint compositions with antibacterial environment protection function according to claim 1, it is characterised in that:It is described
Filler is one kind or its combination in calcium carbonate, talcum powder, kaolin, diatomite.
A kind of 5. water-based paint compositions with antibacterial environment protection function according to claim 4, it is characterised in that:It is described
Diatomite is nano diatomite.
A kind of 6. water-based paint compositions with antibacterial environment protection function according to claim 5, it is characterised in that:It is described
Nano diatomite calcined by diatomite, is ground and is made.
A kind of 7. water-based paint compositions with antibacterial environment protection function according to claim 1, it is characterised in that:It is described
Coalescents are that alcohol ethers hold solvent.
A kind of 8. water-based paint compositions with antibacterial environment protection function according to claim 7, it is characterised in that:It is described
It is diethyl alcohol ethers or propane diols ethers that alcohol ethers, which hold solvent,.
A kind of 9. water-based paint compositions with antibacterial environment protection function according to claim 1, it is characterised in that:It is described
Defoamer includes at least one of foam inhibitor and foamicide.
A kind of 10. water-based paint compositions with antibacterial environment protection function according to claim 1, it is characterised in that:Institute
It is organic polyether ester or mineral oil to state defoamer.