CN107337969A - A kind of power transmission tower surface antirust wear-resistant paint - Google Patents
A kind of power transmission tower surface antirust wear-resistant paint Download PDFInfo
- Publication number
- CN107337969A CN107337969A CN201710657637.1A CN201710657637A CN107337969A CN 107337969 A CN107337969 A CN 107337969A CN 201710657637 A CN201710657637 A CN 201710657637A CN 107337969 A CN107337969 A CN 107337969A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- power transmission
- transmission tower
- defoamer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of power transmission tower surface antirust wear-resistant paint, the power transmission tower surface antirust wear-resistant paint includes from inside to outside totally three layers, is subbing, middle coating intermediate and surface coating material successively.Wherein subbing quick-drying, penetration is strong, and adhesive force is splendid, and closure is fabulous, and film is fine and close in neat formation, do not ftracture, do not rise it is swollen;Wherein middle coating intermediate viscosity is high, good waterproof performance;Wherein surface coating material adhesive force is strong, extreme hardness, and scratch-resistant is wear-resisting.
Description
Technical field
The present invention relates to electrical equipment technical field, more particularly to a kind of power transmission tower surface antirust wear-resistant paint.
Background technology
Power transmission tower is trapezoidal or the building of the shape such as triangle, and height is usually 25-40 rice, is steel frame construction.It is defeated
Electric tower builds power plant in the wild, near power distribution station more, and it is the critical facility of power department, can trolley wire simultaneously play protection
With the effect of support.Design, manufacture, installation, maintenance and the quality testing of power transmission tower are modern power systems operation and development
Important leverage.
Power transmission tower is set up out of doors, and environment is more severe, throughout the year by the bad weathers such as sand and dust that drench with rain of exposing to the weather, therefore
The antirust Wear-resistant Treatment of power transmission tower, directly influence life-span and the security of power transmission tower.
The content of the invention
The technical problems to be solved by the invention are to provide a kind of power transmission tower surface antirust wear-resistant paint, and it can make defeated
Electric tower has the wear-resisting characteristic of antirust, ensure that the normal work of power transmission tower, increases the service life of power transmission tower.
The technical problems to be solved by the invention are realized using following technical scheme:
A kind of power transmission tower surface antirust wear-resistant paint, the power transmission tower surface antirust wear-resistant paint include from inside to outside totally three
Layer, is subbing, middle coating intermediate and surface coating material successively;
The subbing includes the constituent of following parts by weight:Organosilicon-modified styrene-acrylic olefin(e) acid emulsion 20-30 parts, go from
Sub- water 15-20 parts, rosin phenolic resin 15-18 parts, polyurethane-modified acrylic acid emulsion 10-18 parts, rutile titanium white powder 15-25
Part, organosilicon wetting agent 0.1-0.5 parts, polypropylene fibre 5-8 parts, polyurethane levelling agent 0.1-0.3 parts, bactericide 0.1-0.2
Part, defoamer 0.1-0.3 parts, thickener 0.3-0.6 parts;
The middle coating intermediate includes the constituent of following parts by weight:Styrene-acrylic emulsion 50-75 parts, aliphatic acid amine salt 10-15 parts,
Cocoanut fatty acid diethanolamide 5-10 parts, sodium molybdate 5-10 parts, cement 20-40 parts, 200 mesh silica flour 20-40 parts, ternary
Copolymer 1 2-15 parts, deionized water 20-30 parts, ethene rubber powder 10-15 parts, water reducer 0.1-0.5 parts, defoamer 0.2-0.6
Part, thickener 0.2-0.6 parts;
The surface coating material includes the constituent of following parts by weight:HCPE 50-65 parts, organic solvent
15-30 parts, carbon black 10-15 parts, aluminium triphosphate 8-10 parts, surfactant 1-3 parts, dimethylbenzene 1-3 parts, Ludox 3-8 parts,
Curing agent 3-5 parts, pitch 5-8 parts, sulphur 4-6 parts, chlorinated paraffin 5-10 parts, deionized water 10-15 parts, auxiliary agent 5-10 parts, oxygen
Change aluminium powder 5-10 parts, lead oxide powder 5-10 parts, aminopropyl triethoxysilane 5-8 parts, SiO 2 powder 2-5 parts, two
Titanium dioxide powder 2-5 parts, defoamer 0.5-1 parts.
Preferably,
The subbing includes the constituent of following parts by weight:25 parts of organosilicon-modified styrene-acrylic olefin(e) acid emulsion, deionization
18 parts of water, 18 parts of rosin phenolic resin, 12 parts of polyurethane-modified acrylic acid emulsion, 18 parts of rutile titanium white powder, organosilicon wetting
0.4 part of agent, 6 parts of polypropylene fibre, 0.2 part of polyurethane levelling agent, 0.2 part of bactericide, 0.2 part of defoamer, 0.3 part of thickener;
The middle coating intermediate includes the constituent of following parts by weight:70 parts of styrene-acrylic emulsion, 12 parts of aliphatic acid amine salt, coconut oil
8 parts of fatty diglycollic amide, 8 parts of sodium molybdate, 25 parts of cement, 200 35 parts of mesh silica flours, 15 parts of terpolymer, deionization
28 parts of water, 12 parts of ethene rubber powder, 0.3 part of water reducer, 0.4 part of defoamer, 0.5 part of thickener;
The surface coating material includes the constituent of following parts by weight:60 parts of HCPE, 22 parts of organic solvent,
13 parts of carbon black, 10 parts of aluminium triphosphate, 2 parts of surfactant, 2 parts of dimethylbenzene, 5 parts of Ludox, 4 parts of curing agent, 6 parts of pitch,
4 parts of sulphur, 8 parts of chlorinated paraffin, 13 parts of deionized water, 8 parts of auxiliary agent, 6 parts of alumina powder, 8 parts of lead oxide powder, aminopropyl three
6 parts of Ethoxysilane, 3 parts of SiO 2 powder, 4 parts of titania powder, 0.8 part of defoamer.
Wherein, it is 2 in molar ratio by vinyl chloride, ethene, vinylacetate that terpolymer, which is, in the middle coating intermediate:1:
5 copolymerization form.
Beneficial effects of the present invention:The present invention sets three coatings altogether for power transmission tower, selects per coating and reasonably matches somebody with somebody
Side and ratio, wherein subbing quick-drying, penetration is strong, and adhesive force is splendid, and closure is fabulous, and film is fine and close in neat formation, do not ftracture,
Do not rise swollen;Wherein middle coating intermediate viscosity is high, good waterproof performance;Wherein surface coating material adhesive force is strong, extreme hardness, and scratch-resistant is wear-resisting.
Embodiment
In order that the technical means, the inventive features, the objects and the advantages of the present invention are easy to understand, tie below
Specific embodiment is closed, the present invention is expanded on further.
Embodiment 1
A kind of power transmission tower surface antirust wear-resistant paint, the power transmission tower surface antirust wear-resistant paint include from inside to outside totally three
Layer, is subbing, middle coating intermediate and surface coating material successively;
The subbing includes the constituent of following parts by weight:30 parts of organosilicon-modified styrene-acrylic olefin(e) acid emulsion, deionization
15 parts of water, 15 parts of rosin phenolic resin, 18 parts of polyurethane-modified acrylic acid emulsion, 25 parts of rutile titanium white powder, organosilicon wetting
0.5 part of agent, 8 parts of polypropylene fibre, 0.3 part of polyurethane levelling agent, 0.2 part of bactericide, 0.2 part of defoamer, 0.4 part of thickener;
The middle coating intermediate includes the constituent of following parts by weight:75 parts of styrene-acrylic emulsion, 15 parts of aliphatic acid amine salt, coconut oil
6 parts of fatty diglycollic amide, 6 parts of sodium molybdate, 22 parts of cement, 200 25 parts of mesh silica flours, 12 parts of terpolymer, deionization
28 parts of water, 11 parts of ethene rubber powder, 0.2 part of water reducer, 0.5 part of defoamer, 0.5 part of thickener;Wherein, the terpolymer is
It is 2 in molar ratio by vinyl chloride, ethene, vinylacetate:1:5 copolymerization form;
The surface coating material includes the constituent of following parts by weight:55 parts of HCPE, 18 parts of organic solvent,
12 parts of carbon black, 8 parts of aluminium triphosphate, 3 parts of surfactant, 2 parts of dimethylbenzene, 5 parts of Ludox, 4 parts of curing agent, 6 parts of pitch, sulphur
6 parts of sulphur, 10 parts of chlorinated paraffin, 15 parts of deionized water, 5 parts of auxiliary agent, 8 parts of alumina powder, 8 parts of lead oxide powder, aminopropyl three
8 parts of Ethoxysilane, 3 parts of SiO 2 powder, 3 parts of titania powder, 0.8 part of defoamer.
Embodiment 2
A kind of power transmission tower surface antirust wear-resistant paint, the power transmission tower surface antirust wear-resistant paint include from inside to outside totally three
Layer, is subbing, middle coating intermediate and surface coating material successively;
The subbing includes the constituent of following parts by weight:25 parts of organosilicon-modified styrene-acrylic olefin(e) acid emulsion, deionization
18 parts of water, 18 parts of rosin phenolic resin, 12 parts of polyurethane-modified acrylic acid emulsion, 18 parts of rutile titanium white powder, organosilicon wetting
0.4 part of agent, 6 parts of polypropylene fibre, 0.2 part of polyurethane levelling agent, 0.2 part of bactericide, 0.2 part of defoamer, 0.3 part of thickener;
The middle coating intermediate includes the constituent of following parts by weight:70 parts of styrene-acrylic emulsion, 12 parts of aliphatic acid amine salt, coconut oil
8 parts of fatty diglycollic amide, 8 parts of sodium molybdate, 25 parts of cement, 200 35 parts of mesh silica flours, 15 parts of terpolymer, deionization
28 parts of water, 12 parts of ethene rubber powder, 0.3 part of water reducer, 0.4 part of defoamer, 0.5 part of thickener;Wherein, the terpolymer is
It is 2 in molar ratio by vinyl chloride, ethene, vinylacetate:1:5 copolymerization form;
The surface coating material includes the constituent of following parts by weight:60 parts of HCPE, 22 parts of organic solvent,
13 parts of carbon black, 10 parts of aluminium triphosphate, 2 parts of surfactant, 2 parts of dimethylbenzene, 5 parts of Ludox, 4 parts of curing agent, 6 parts of pitch,
4 parts of sulphur, 8 parts of chlorinated paraffin, 13 parts of deionized water, 8 parts of auxiliary agent, 6 parts of alumina powder, 8 parts of lead oxide powder, aminopropyl three
6 parts of Ethoxysilane, 3 parts of SiO 2 powder, 4 parts of titania powder, 0.8 part of defoamer.
Contrast test, difference such as following table are carried out using the coating of the present invention and common coating:
Hardness | Durability | Adhesive force | Closure | Wearability | |
Embodiment 1 | ★★★★ | ★★★★★ | ★★★★★ | ★★★★ | ★★★★ |
Embodiment 2 | ★★★★★ | ★★★★★ | ★★★★ | ★★★★★ | ★★★★★ |
Common coating | ★★ | ★★ | ★ | ★★★ | ★★ |
Three coatings of the present invention, per coating from rational formula and ratio, wherein subbing quick-drying, infiltration
Power is strong, and adhesive force is splendid, and closure is fabulous, and film is fine and close in neat formation, do not ftracture, do not rise it is swollen;Wherein middle coating intermediate viscosity is high, waterproof
Property is good;Wherein surface coating material adhesive force is strong, extreme hardness, and scratch-resistant is wear-resisting.
The general principle and principal character of the present invention has been shown and described above.It should be understood by those skilled in the art that
The present invention is not limited to the above embodiments, merely illustrating the principles of the invention described in above-described embodiment and specification,
Without departing from the spirit and scope, various changes and modifications of the present invention are possible, and these changes and improvements all fall
Enter in scope of the claimed invention.The scope of the present invention is defined by the appended claims and its equivalents.
Claims (3)
- A kind of 1. power transmission tower surface antirust wear-resistant paint, it is characterised in that:The power transmission tower surface antirust wear-resistant paint include by It is interior and outer totally three layers, it is subbing, middle coating intermediate and surface coating material successively;The subbing includes the constituent of following parts by weight:Organosilicon-modified styrene-acrylic olefin(e) acid emulsion 20-30 parts, deionized water 15-20 parts, rosin phenolic resin 15-18 parts, polyurethane-modified acrylic acid emulsion 10-18 parts, rutile titanium white powder 15-25 parts, Organosilicon wetting agent 0.1-0.5 parts, polypropylene fibre 5-8 parts, polyurethane levelling agent 0.1-0.3 parts, bactericide 0.1-0.2 parts, Defoamer 0.1-0.3 parts, thickener 0.3-0.6 parts;The middle coating intermediate includes the constituent of following parts by weight:Styrene-acrylic emulsion 50-75 parts, aliphatic acid amine salt 10-15 parts, coconut Fatty acid oil diglycollic amide 5-10 parts, sodium molybdate 5-10 parts, cement 20-40 parts, 200 mesh silica flour 20-40 parts, ternary polymerization Thing 12-15 parts, deionized water 20-30 parts, ethene rubber powder 10-15 parts, water reducer 0.1-0.5 parts, defoamer 0.2-0.6 parts, increase Thick dose of 0.2-0.6 part;The surface coating material includes the constituent of following parts by weight:HCPE 50-65 parts, organic solvent 15-30 Part, carbon black 10-15 parts, aluminium triphosphate 8-10 parts, surfactant 1-3 parts, dimethylbenzene 1-3 parts, Ludox 3-8 parts, solidification Agent 3-5 parts, pitch 5-8 parts, sulphur 4-6 parts, chlorinated paraffin 5-10 parts, deionized water 10-15 parts, auxiliary agent 5-10 parts, aluminum oxide Powder 5-10 parts, lead oxide powder 5-10 parts, aminopropyl triethoxysilane 5-8 parts, SiO 2 powder 2-5 parts, titanium dioxide Titanium powder 2-5 parts, defoamer 0.5-1 parts.
- A kind of 2. power transmission tower surface antirust wear-resistant paint according to claim 1, it is characterised in that:The subbing includes the constituent of following parts by weight:25 parts of organosilicon-modified styrene-acrylic olefin(e) acid emulsion, deionized water 18 Part, 18 parts of rosin phenolic resin, 12 parts of polyurethane-modified acrylic acid emulsion, 18 parts of rutile titanium white powder, organosilicon wetting agent 0.4 Part, 6 parts of polypropylene fibre, 0.2 part of polyurethane levelling agent, 0.2 part of bactericide, 0.2 part of defoamer, 0.3 part of thickener;The middle coating intermediate includes the constituent of following parts by weight:70 parts of styrene-acrylic emulsion, 12 parts of aliphatic acid amine salt, coconut oil fat Sour 8 parts of diglycollic amide, 8 parts of sodium molybdate, 25 parts of cement, 200 35 parts of mesh silica flours, 15 parts of terpolymer, deionized water 28 Part, 12 parts of ethene rubber powder, 0.3 part of water reducer, 0.4 part of defoamer, 0.5 part of thickener;The surface coating material includes the constituent of following parts by weight:60 parts of HCPE, 22 parts of organic solvent, carbon black 13 parts, 10 parts of aluminium triphosphate, 2 parts of surfactant, 2 parts of dimethylbenzene, 5 parts of Ludox, 4 parts of curing agent, 6 parts of pitch, sulphur 4 Part, 8 parts of chlorinated paraffin, 13 parts of deionized water, 8 parts of auxiliary agent, 6 parts of alumina powder, 8 parts of lead oxide powder, the ethoxy of aminopropyl three 6 parts of base silane, 3 parts of SiO 2 powder, 4 parts of titania powder, 0.8 part of defoamer.
- A kind of 3. power transmission tower surface antirust wear-resistant paint according to claim 1 or 2, it is characterised in that:The middle level applies It is 2 in molar ratio by vinyl chloride, ethene, vinylacetate that terpolymer, which is, in material:1:5 copolymerization form.