CN107337448A - A kind of production method of permanent-magnet ferrite - Google Patents
A kind of production method of permanent-magnet ferrite Download PDFInfo
- Publication number
- CN107337448A CN107337448A CN201710573544.0A CN201710573544A CN107337448A CN 107337448 A CN107337448 A CN 107337448A CN 201710573544 A CN201710573544 A CN 201710573544A CN 107337448 A CN107337448 A CN 107337448A
- Authority
- CN
- China
- Prior art keywords
- permanent
- magnet ferrite
- ferrite
- production method
- magnet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a kind of preparation method of permanent-magnet ferrite, comprise the following steps:1)Prepare it is ferritic match somebody with somebody square iron phosphorus, zirconium dioxide, strontium carbonate and calcium carbonate, the uniform mixed slurry of wet method, 1300 DEG C of high temperature place a period of time, preheating, obtain the permanent ferrite prefiring materials of Y33H 2;2)Preburning material is subjected to coarse crushing;3)Fine crushing is carried out in ball mill;4)It is molded under 11000Oe 13000oe magnetic fields, obtains permanent-magnet ferrite green compact;5)By permanent-magnet ferrite green sintering, permanent-magnet ferrite is obtained.Using permanent-magnet ferrite made of the method for the present invention, there is very high magnetic property, can be used in manufacturing the higher pump housings of requirement such as permagnetic synchronous motor.
Description
Technical field
The present invention relates to a kind of preparation method of permanent-magnet ferrite.
Background technology
The moulding process of permanent-magnet ferrite mainly has two kinds of dry-pressing and wet pressing, and the properties of product of wherein Wet-pressing molding are generally high
In dry-pressing formed product, but the shaping speed of product is slow, qualification rate is low, the dry-pressing formed production advantage be higher than wet pressing into
Type, shaping speed is fast, qualification rate is high, is easy to produce small size and complex-shaped product.
At present, the magnetic property of dry-pressing product is not universal high, and general preferable dry-pressing material remanent magnetism is intrinsic in 360-370mT
Coercivity is in 220KA/m-240KA/m.Dry-pressing product is mainly used in toy motor, and added value of product is not high, is not suitable for requirement
Higher pump housing class permanent-magnet synchronous small machine.
The content of the invention
The purpose of the present invention is overcome the deficiencies in the prior art part, there is provided a kind of production method of permanent-magnet ferrite.
The production method of the permanent-magnet ferrite of the present invention, comprises the following steps:
1)Prepare ferritic to match somebody with somebody square iron phosphorus, zirconium dioxide, strontium carbonate and calcium carbonate, the uniform mixed slurry of wet method, 1300 DEG C of height
Temperature places a period of time, preheating, obtains Y33H-2 permanent ferrite prefiring materials;
2)Preburning material is subjected to coarse crushing;
3)Fine crushing is carried out in ball mill;
4)It is molded under 11000Oe-13000oe magnetic fields, obtains permanent-magnet ferrite green compact;
5)By permanent-magnet ferrite green sintering, permanent-magnet ferrite is obtained.
Preferably,
Described step 2)In, coarse crushing to particle diameter 2-5 microns.
Described step 3)In, thin broken is broken to particle diameter 0.5-1 microns, before finely divided, adds calcium carbonate, silica,
It is additionally added dispersant sorbierite.
Using permanent-magnet ferrite made of the method for the present invention, there is very high magnetic property, it is same to can be used in manufacture permanent magnetism
Walk the higher pump housings of requirement such as motor.
Embodiment
With reference to embodiment, the present invention is described in further detail.
Embodiment 1
The production method of the permanent-magnet ferrite of the present invention, comprises the following steps:
1)Prepare ferritic to match somebody with somebody square iron phosphorus, zirconium dioxide, strontium carbonate and calcium carbonate, the uniform mixed slurry of wet method, 1300 DEG C of height
Temperature places a period of time, preheating, obtains Y33H-2 permanent ferrite prefiring materials;
2)Preburning material is subjected to coarse crushing;
3)Fine crushing is carried out in ball mill;
4)It is molded under 13000Oe magnetic fields, obtains permanent-magnet ferrite green compact;
5)By permanent-magnet ferrite green sintering, permanent-magnet ferrite is obtained.
Described step 2)In, coarse crushing to 2 microns of particle diameter.
Described step 3)In, thin broken is broken to 0.5 micron of particle diameter, before finely divided, adds calcium carbonate, silica, also
Add dispersant sorbierite.
Embodiment 2
The production method of the permanent-magnet ferrite of the present invention, comprises the following steps:
1)Prepare ferritic to match somebody with somebody square iron phosphorus, zirconium dioxide, strontium carbonate and calcium carbonate, the uniform mixed slurry of wet method, 1300 DEG C of height
Temperature places a period of time, preheating, obtains Y33H-2 permanent ferrite prefiring materials;
2)Preburning material is subjected to coarse crushing;
3)Fine crushing is carried out in ball mill;
4)It is molded under 12000Oe magnetic fields, obtains permanent-magnet ferrite green compact;
5)By permanent-magnet ferrite green sintering, permanent-magnet ferrite is obtained.
Described step 2)In, coarse crushing to 5 microns of particle diameter.
Described step 3)In, thin broken is broken to 1 micron of particle diameter, before finely divided, adds calcium carbonate, silica, also adds
Enter dispersant sorbierite.
Embodiment 3
The production method of the permanent-magnet ferrite of the present invention, comprises the following steps:
1)Prepare ferritic to match somebody with somebody square iron phosphorus, zirconium dioxide, strontium carbonate and calcium carbonate, the uniform mixed slurry of wet method, 1300 DEG C of height
Temperature places a period of time, preheating, obtains Y33H-2 permanent ferrite prefiring materials;
2)Preburning material is subjected to coarse crushing;
3)Fine crushing is carried out in ball mill;
4)It is molded under 11000Oe magnetic fields, obtains permanent-magnet ferrite green compact;
5)By permanent-magnet ferrite green sintering, permanent-magnet ferrite is obtained.
Described step 2)In, coarse crushing to 3 microns of particle diameter.
Described step 3)In, thin broken is broken to 0.8 micron of particle diameter, before finely divided, adds calcium carbonate, silica, also
Add dispersant sorbierite.
Claims (3)
1. a kind of production method of permanent-magnet ferrite, it is characterised in that comprise the following steps:
1)Prepare ferritic to match somebody with somebody square iron phosphorus, zirconium dioxide, strontium carbonate and calcium carbonate, the uniform mixed slurry of wet method, 1300 DEG C of height
Temperature places a period of time, preheating, obtains Y33H-2 permanent ferrite prefiring materials;
2)Preburning material is subjected to coarse crushing;
3)Fine crushing is carried out in ball mill;
4)It is molded under 11000Oe-13000oe magnetic fields, obtains permanent-magnet ferrite green compact;
5)By permanent-magnet ferrite green sintering, permanent-magnet ferrite is obtained.
2. the production method of permanent-magnet ferrite according to claim 1, it is characterised in that described step 2)In, it is thick broken
It is broken to particle diameter 2-5 microns.
3. the production method of permanent-magnet ferrite according to claim 1, it is characterised in that described step 3)In, thin broken
Particle diameter 0.5-1 microns are broken to, before finely divided, calcium carbonate, silica added, is additionally added dispersant sorbierite.