CN107325779A - A kind of solvent-free solid gum of furniture - Google Patents
A kind of solvent-free solid gum of furniture Download PDFInfo
- Publication number
- CN107325779A CN107325779A CN201710586202.2A CN201710586202A CN107325779A CN 107325779 A CN107325779 A CN 107325779A CN 201710586202 A CN201710586202 A CN 201710586202A CN 107325779 A CN107325779 A CN 107325779A
- Authority
- CN
- China
- Prior art keywords
- furniture
- acrylate
- solvent
- mercaptan
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to chemical field, specifically related to a kind of solvent-free solid gum of furniture, a kind of solvent-free solid gum of furniture, it includes aliphatic urethane acrylate 35%, acrylate monomer 25%~30%, mercaptan 15%~25%, tackifying resin 10%~15%, stearic acid 5%, borax 10%, ethylene glycol 8%, levelling agent 0.5%, defoamer 0.5%, preservative 0.2%, 4 8wt% other auxiliary agents, it is an advantage of the invention that：The adhesive property and water resistance of solid glue of the present invention are improved, and binding speed is fast, and cohesive force is strong, and ageing-resistant, good weatherability should not be hardened.
Description
Technical field
The present invention relates to chemical field, and in particular to a kind of solvent-free solid gum of furniture.
Background technology
The solid glue slow drying speed of prior art, mobility is bad, and standing time length, solid gum will be dried,
So as to fail, storage time is short.
The content of the invention
In order to solve the above problems, the present invention proposes a kind of solvent-free solid gum of furniture, with short production cycle, production
Product are stable.
A kind of solvent-free solid gum of furniture, it includes aliphatic urethane acrylate 35%, acrylate monomer 25%
~30%, mercaptan 15%~25%, tackifying resin 10%~15%, stearic acid 5%, borax 10%, ethylene glycol 8%, levelling agent 0.5%, froth breaking
Agent 0.5%, preservative 0.2%, 4-8wt% other auxiliary agents.
Described aliphatic urethane acrylate refers to the aliphatic urethane acrylate of 1~3 degree of functionality, aliphatic poly
Urethane acrylate refers to Sartomer CN704, CN965NS, CN8004, CN9002, CN966J75NS, CNUVE151NS, Changxing
6113rd, 615-100, at least one of 641.
Described acrylate monomer is at least one of acrylate or methacrylate, and mercaptan is knot containing ethers
The mercaptan of structure.
Described auxiliary agent is as follows：0.5wt% polyacrylamides, 2wt% essence hydrogen, 5wt% sodium oxide molybdenas.
It is an advantage of the invention that：The adhesive property and water resistance of solid glue of the present invention are improved, binding speed
It hurry up, cohesive force is strong, and ageing-resistant, good weatherability should not be hardened.
Specific embodiment
A kind of solvent-free solid gum of furniture, it includes aliphatic urethane acrylate 35%, acrylate monomer 25%
~30%, mercaptan 15%~25%, tackifying resin 10%~15%, stearic acid 5%, borax 10%, ethylene glycol 8%, levelling agent 0.5%, froth breaking
Agent 0.5%, preservative 0.2%, 4-8wt% other auxiliary agents.
First water, aliphatic urethane acrylate, acrylate monomer, mercaptan are entered with 60~80 revs/min of speed
Row stirring 6~10 minutes, then adding tackifying resin, stearic acid stirring makes it be uniformly dispersed in 15~30 minutes, sequentially adds
Defoamer, borax, ethylene glycol, levelling agent and other auxiliary agents are sequentially added, rotating speed is 40~50 revs/min of stirrings 30~40
Minute, preservative is eventually adding, is stirred 30~40 minutes.
Embodiment 1
A kind of solid glue, by weight, is prepared from by following raw material components：45 parts of aliphatic urethane acrylate,
35 parts of acrylate monomer, 1.8 parts of stearic acid, 7 parts of borax, 1 part of sodium hydroxide, 9 parts of catalyst, 4.5 parts of ethylene glycol, thickening tree
6 parts of fat, 0.3 part of essence, 0.2 part of polyacrylamide, 0.5 part of levelling agent, 0.5 part of defoamer, 110 parts of water.
Embodiment 2
A kind of solid glue, by weight, is prepared from by following raw material components：40 parts of aliphatic urethane acrylate,
30 parts of acrylate monomer, 0.2 part of stearic acid, 4 parts of borax, 0.5 part of sodium hydroxide, 6 parts of catalyst, 3 parts of ethylene glycol, thickening tree
4 parts of fat, 0.01 part of essence, 0.1 part of polyacrylamide, 0.3 part of levelling agent, 0.3 part of defoamer, 100 parts of water.
Embodiment 3
A kind of solid glue, by weight, is prepared from by following raw material components：50 parts of aliphatic urethane acrylate,
40 parts of acrylate monomer, 3 parts of stearic acid, 10 parts of borax, 1.5 parts of sodium hydroxide, 12 parts of catalyst, 6 parts of ethylene glycol, thickening tree
8 parts of fat, 0.5 part of essence, 0.3 part of polyacrylamide, 1 part of levelling agent, 1 part of defoamer, 120 parts of water.
Claims (4)
1. a kind of solvent-free solid gum of furniture, it include aliphatic urethane acrylate 35%, acrylate monomer 25%~
30%th, mercaptan 15%~25%, tackifying resin 10%~15%, stearic acid 5%, borax 10%, ethylene glycol 8%, levelling agent 0.5%, defoamer
0.5%th, preservative 0.2%, 4-8wt% other auxiliary agents.
2. a kind of furniture according to claim 1 is with without solution solids glue, it is characterised in that described aliphatic polyurethane
Acrylate refers to the aliphatic urethane acrylate of 1~3 degree of functionality, aliphatic urethane acrylate refer to Sartomer CN704,
CN965NS, CN8004, CN9002, CN966J75NS, CNUVE151NS, Changxing 6113,615-100, at least one of 641.
3. a kind of furniture according to claim 1 is with without solution solids glue, it is characterised in that described acrylate monomer
For at least one of acrylate or methacrylate, mercaptan is the mercaptan of the structure containing ethers.
4. a kind of furniture according to claim 1 is with without solution solids glue, it is characterised in that described auxiliary agent is as follows：0.
5wt% polyacrylamides, 2wt% essence hydrogen, 5wt% sodium oxide molybdenas.