CN107314161A - A kind of construction drainage pipeline - Google Patents
A kind of construction drainage pipeline Download PDFInfo
- Publication number
- CN107314161A CN107314161A CN201710691524.3A CN201710691524A CN107314161A CN 107314161 A CN107314161 A CN 107314161A CN 201710691524 A CN201710691524 A CN 201710691524A CN 107314161 A CN107314161 A CN 107314161A
- Authority
- CN
- China
- Prior art keywords
- parts
- tube layer
- layer
- drainage pipeline
- construction drainage
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of construction drainage pipeline, including interior tube layer, polyurethane foam, quartz sand layer and external tube layer, said inner tube layer, polyurethane foam, quartz sand layer and external tube layer are set from the inside to the outside successively, described is that external tube layer is stainless steel layer, said inner tube layer outside is provided with support bar, the support bar is fixedly connected with interior tube layer and external tube layer respectively, the support bar is provided with three, fixed cover is provided with the outside of the external tube layer, the fixed cover side sets baffle plate, the baffle plate is integrally formed setting with fixed cover, the construction drainage pipeline has the function of fireproof heat insulating, structural stability is high, the interior tube layer used is easy for installation, anticorrosion effect is good.
Description
Technical field
The present invention relates to a kind of construction drainage pipeline.
Background technology
Building is people's soil, brick, watt, stone material, timber;(Modern age reinforced concrete, section bar)Constituted Deng construction material
Space that is a kind of for human habitation and using, such as house, bridge, factory building, gymnasium, cave dwelling, water tower, temple etc..Broadly come
Say, landscape, gardens are also wing.Say in a broad sense, the nest that animal is built consciously can also can be regarded as building.Western wise man
There is cloud:Building is the music of solidification, and building is a stone history records.The classical masterpiece of Roman architecture man's Vitruvius《Building
Ten books》Propose three standards of building:It is firm, practical, attractive in appearance, the architectural development of later age is affected always.Building composition
Three elements:Building function, Building technology and art of architecture image.
Pipeline be with pipe, pipe connector and valve etc. be connected into be used for convey gas, liquid or with solid particle
Fluid device.Feedwater, draining, heat supply, the oil transportation of the trunk pipeline given gas and long range in city, feed channel are most
Be laid in underground, and the process pipe in factory is laid on the ground more for ease of Operation and maintenance.The current of pipeline, supporting, slope
Degree and discharge opeing exhaust, compensation, insulation and heating, anti-corrosion and cleaning, identification and japanning and safety etc., no matter for over ground installation also
It is the problem of underground laying is all important.
Pipeline on ground, which should try one's best, to be avoided intersecting with road, railway and navigation channel.When not being avoided that intersection, infall across
Height more should be able to also make pedestrian and car and boat safety.The pipeline of underground is typically laid along road, is kept between various pipelines
Appropriately distance, to install and to repair;There is heat-insulation layer on the surface of heat supply pipeline, is laid in trench or protection pipe, should avoid
Gone bad by soil pressure and move pipe expansion.
Pipeline may bear the effect of many kinds of external force, including thrust of the weight, fluid matasomatism of in pipe end itself, wind and snow
Load, ground pressure, expand with heat and contract with cold caused thermal stress, oscillating load and earthquake disaster etc..In order to ensure pipeline intensity and
Rigidity, it is necessary to set various branch (to hang) frame, such as travel(l)ing rest, fixed support, guiding trestle and spring support.The setting of support
According to conditional decisions such as the diameter of pipeline, material, pipe wall thickness and load.The heat that fixed support is used for Discrete control pipeline is stretched
It is long, make expansion joint uniform operational;Guiding trestle makes pipe only move axially.
The current existing function without fireproof heat insulating, structural stability is not high, and the interior tube layer of use installs inconvenient,
Anticorrosion effect is bad.
The content of the invention
The technical problem to be solved in the present invention is to provide a kind of function with fireproof heat insulating, structural stability is high, uses
Interior tube layer it is easy for installation, the good construction drainage pipeline of anticorrosion effect.
To solve the above problems, the present invention is adopted the following technical scheme that:
A kind of construction drainage pipeline, including interior tube layer, polyurethane foam, quartz sand layer and external tube layer, said inner tube
Layer, polyurethane foam, quartz sand layer and external tube layer are set from the inside to the outside successively, and described is that external tube layer is stainless steel layer, described
Support bar is provided with the outside of interior tube layer, the support bar is fixedly connected with interior tube layer and external tube layer respectively, and the support bar is provided with
Three, be provided with fixed cover on the outside of the external tube layer, the fixed cover side sets baffle plate, the baffle plate and fixed cover one into
Type is set.
Preferably, the polyurethane foam thickness is 8mm, heat insulation effect effect is kept.
Preferably, being provided with spring on the inside of the baffle plate so that baffle plate install compact.
Preferably, being provided with fixing bolt in the middle part of the baffle plate, good fixing effect can be kept, it is convenient to install.
Preferably, said inner tube thickness degree is 5mm, keep fluid conveying smooth reliable.
A kind of construction drainage pipeline, said inner tube layer is made up by mass fraction proportioning of following material:Styrene
- 23-28 parts of acrylonitrile copolymer, 5-8 parts of aluminium powder, 2-5 parts of silane coupler, 6-8 parts of castor bean wax, poly terephthalic acid fourth
7-10 parts of ester, 12-14 parts of mica powder, 6-8 parts of dimethicone, 7-10 parts of phthalic acid ester, 2-4 parts of phosphite, sulfydryl
5-10 parts of acid esters, 3-8 parts of triethoxysilane, 12-15 parts of rosin modified phenolic resin, 16-20 parts of polyvinyl acetate, carboxyl
2-5 parts of 7-8 parts of styrene-butadiene latex, 15-20 parts of styrene-acrylic emulsion, 3-9 parts of citric acid and activated carbon.
The preparation method of said inner tube layer comprises the following steps:
1)By styrene -23-28 parts of acrylonitrile copolymer, 5-8 parts of aluminium powder, 2-5 parts of silane coupler, 6-8 parts of castor bean wax,
7-10 parts of PA polybutyleneterephthalate, 12-14 parts of mica powder, 6-8 parts of dimethicone, 7-10 parts of phthalic acid ester, phosphorous
2-4 parts of hydrochlorate, 5-10 parts of sulfydryl acid esters, 3-8 parts of triethoxysilane, 12-15 parts of rosin modified phenolic resin, polyvinyl acetate
2-5 parts of 16-20 parts of ester, 7-8 parts of carboxylic styrene butadiene latex, 15-20 parts of styrene-acrylic emulsion, 3-9 parts of citric acid and activated carbon are put into and stirred
Mix in machine, regulation rotating speed is 3600-3800r/min, is reacted 6-11 minutes, standby;
2)By step 1)Gained raw material is put into autoclave, and regulation temperature is 78 DEG C, and regulation air pressure is 12 times of atmospheric pressure, reaction
It is 7-15 minutes, standby;
3)By step 2)Gained raw material is put into banbury, and regulation temperature is 220-245 DEG C, is in molten by raw material heating
State, it is standby;
4)By step 3)Gained raw material is put into injection machine, and injection machine is fed injection into mould, after natural cooling shaping
The interior tube layer of tubulose is obtained, it is standby.
5)By step 4)Tube layer is processed using lathe turning in gained so that spiral groove is formed on the outside of interior tube layer, i.e.,
Can.
Beneficial effects of the present invention are:The polyurethane foam of setting has heat insulation effect, and the quartz sand layer of setting has
Good flameproof effect;The interior tube layer set keeps corrosion-resistant for polyethylene layer, and service life is long;The fixed cover of setting keeps peace
Dress is convenient;There are spring and fixing bolt holding structure compact on the baffle plate of setting, stability is high, possess on the outside of the interior tube layer of use
Spiral groove, so spreading glue can be arranged in pipeline on the outside of interior tube layer, and the material of use is corrosion-resistant, service life
It is long.
Brief description of the drawings
Fig. 1 is a kind of structure chart of construction drainage pipeline of the invention.
Embodiment
Embodiment 1
As shown in figure 1, a kind of construction drainage pipeline, including interior tube layer 1, polyurethane foam 2, quartz sand layer 3 and outer
Tube layer 4, said inner tube layer 1, polyurethane foam 2, quartz sand layer 3 and external tube layer 4 are set from the inside to the outside successively, and described is outer tube
Layer 4 is stainless steel layer, and the outside of said inner tube layer 1 is provided with support bar 5, the support bar 5 respectively with interior tube layer 1 and external tube layer 4
It is fixedly connected, the support bar 5 is provided with three, and the outside of external tube layer 4 is provided with fixed cover 6, and the side of fixed cover 6 is set
Baffle plate 7, the baffle plate 7 is integrally formed setting with fixed cover 6.
The thickness of polyurethane foam 2 is 8mm.
The inner side of baffle plate 7 is provided with spring 8.
The middle part of baffle plate 7 is provided with fixing bolt 9.
Said inner tube 1 thickness of layer is 5mm.
A kind of construction drainage pipeline, said inner tube layer is made up by mass fraction proportioning of following material:Styrene
- 23 parts of acrylonitrile copolymer, 5 parts of aluminium powder, 2-5 parts of silane coupler, 6 parts of castor bean wax, 7 parts of PA polybutyleneterephthalate, cloud
12 parts of female powder, 6 parts of dimethicone, 7 parts of phthalic acid ester, 2 parts of phosphite, 5 parts of sulfydryl acid esters, triethoxysilane 3
Part, 12 parts of rosin modified phenolic resin, 16 parts of polyvinyl acetate, 7 parts of carboxylic styrene butadiene latex, 15 parts of styrene-acrylic emulsion, citric acid 3
2 parts of part and activated carbon.
The preparation method of said inner tube layer comprises the following steps:
1)By styrene-it is 23 parts of acrylonitrile copolymer, 5 parts of aluminium powder, 2-5 parts of silane coupler, 6 parts of castor bean wax, poly- to benzene two
7 parts of butyl formate, 12 parts of mica powder, 6 parts of dimethicone, 7 parts of phthalic acid ester, 2 parts of phosphite, 5 parts of sulfydryl acid esters,
3 parts of triethoxysilane, 12 parts of rosin modified phenolic resin, 16 parts of polyvinyl acetate, 7 parts of carboxylic styrene butadiene latex, phenylpropyl alcohol breast
2 parts of 15 parts of liquid, 3 parts of citric acid and activated carbon are put into mixer, and regulation rotating speed is 3600-3800r/min, 6-11 points of reaction
Clock, it is standby;
2)By step 1)Gained raw material is put into autoclave, and regulation temperature is 78 DEG C, and regulation air pressure is 12 times of atmospheric pressure, reaction
It is 7-15 minutes, standby;
3)By step 2)Gained raw material is put into banbury, and regulation temperature is 220-245 DEG C, is in molten by raw material heating
State, it is standby;
4)By step 3)Gained raw material is put into injection machine, and injection machine is fed injection into mould, after natural cooling shaping
The interior tube layer of tubulose is obtained, it is standby.
5)By step 4)Tube layer is processed using lathe turning in gained so that spiral groove is formed on the outside of interior tube layer, i.e.,
Can.
Embodiment 2
As shown in figure 1, a kind of construction drainage pipeline, including interior tube layer 1, polyurethane foam 2, quartz sand layer 3 and outer
Tube layer 4, said inner tube layer 1, polyurethane foam 2, quartz sand layer 3 and external tube layer 4 are set from the inside to the outside successively, and described is outer tube
Layer 4 is stainless steel layer, and the outside of said inner tube layer 1 is provided with support bar 5, the support bar 5 respectively with interior tube layer 1 and external tube layer 4
It is fixedly connected, the support bar 5 is provided with three, and the outside of external tube layer 4 is provided with fixed cover 6, and the side of fixed cover 6 is set
Baffle plate 7, the baffle plate 7 is integrally formed setting with fixed cover 6.
The thickness of polyurethane foam 2 is 8mm.
The inner side of baffle plate 7 is provided with spring 8.
The middle part of baffle plate 7 is provided with fixing bolt 9.
Said inner tube 1 thickness of layer is 5mm.
A kind of construction drainage pipeline, said inner tube layer is made up by mass fraction proportioning of following material:Styrene
- 25.5 parts of acrylonitrile copolymer, 6.5 parts of aluminium powder, 3.5 parts of silane coupler, 7 parts of castor bean wax, PA polybutyleneterephthalate
8.5 parts, 13 parts of mica powder, 7 parts of dimethicone, 8.5 parts of phthalic acid ester, 3 parts of phosphite, 7.5 parts of sulfydryl acid esters, three
5.5 parts of Ethoxysilane, 13.5 parts of rosin modified phenolic resin, 18 parts of polyvinyl acetate, 7.5 parts of carboxylic styrene butadiene latex, benzene
2-5 parts of 17.5 parts of acrylic emulsion, 6 parts of citric acid and activated carbon.
The preparation method of said inner tube layer comprises the following steps:
1)By styrene -25.5 parts of acrylonitrile copolymer, 6.5 parts of aluminium powder, 3.5 parts of silane coupler, 7 parts of castor bean wax, poly- pair
8.5 parts of butyl phthalate, 13 parts of mica powder, 7 parts of dimethicone, 8.5 parts of phthalic acid ester, 3 parts of phosphite, sulfydryl
7.5 parts of acid esters, 5.5 parts of triethoxysilane, 13.5 parts of rosin modified phenolic resin, 18 parts of polyvinyl acetate, Carboxy
2-5 parts of 7.5 parts of latex, 17.5 parts of styrene-acrylic emulsion, 6 parts of citric acid and activated carbon are put into mixer, and regulation rotating speed is 3600-
3800r/min, reacts 6-11 minutes, standby;
2)By step 1)Gained raw material is put into autoclave, and regulation temperature is 78 DEG C, and regulation air pressure is 12 times of atmospheric pressure, reaction
It is 7-15 minutes, standby;
3)By step 2)Gained raw material is put into banbury, and regulation temperature is 220-245 DEG C, is in molten by raw material heating
State, it is standby;
4)By step 3)Gained raw material is put into injection machine, and injection machine is fed injection into mould, after natural cooling shaping
The interior tube layer of tubulose is obtained, it is standby.
5)By step 4)Tube layer is processed using lathe turning in gained so that spiral groove is formed on the outside of interior tube layer, i.e.,
Can.
Embodiment 3
As shown in figure 1, a kind of construction drainage pipeline, including interior tube layer 1, polyurethane foam 2, quartz sand layer 3 and outer
Tube layer 4, said inner tube layer 1, polyurethane foam 2, quartz sand layer 3 and external tube layer 4 are set from the inside to the outside successively, and described is outer tube
Layer 4 is stainless steel layer, and the outside of said inner tube layer 1 is provided with support bar 5, the support bar 5 respectively with interior tube layer 1 and external tube layer 4
It is fixedly connected, the support bar 5 is provided with three, and the outside of external tube layer 4 is provided with fixed cover 6, and the side of fixed cover 6 is set
Baffle plate 7, the baffle plate 7 is integrally formed setting with fixed cover 6.
The thickness of polyurethane foam 2 is 8mm.
The inner side of baffle plate 7 is provided with spring 8.
The middle part of baffle plate 7 is provided with fixing bolt 9.
Said inner tube 1 thickness of layer is 5mm.
A kind of construction drainage pipeline, said inner tube layer is made up by mass fraction proportioning of following material:Styrene
- 28 parts of acrylonitrile copolymer, 8 parts of aluminium powder, silane coupled 5 parts, 8 parts of castor bean wax, 10 parts of PA polybutyleneterephthalate, mica
14 parts of powder, 8 parts of dimethicone, 10 parts of phthalic acid ester, 4 parts of phosphite, 10 parts of sulfydryl acid esters, triethoxysilane 8
Part, 15 parts of rosin modified phenolic resin, 20 parts of polyvinyl acetate, 8 parts of carboxylic styrene butadiene latex, 20 parts of styrene-acrylic emulsion, citric acid 9
5 parts of part and activated carbon.
The preparation method of said inner tube layer comprises the following steps:
1)By styrene -28 parts of acrylonitrile copolymer, 8 parts of aluminium powder, silane coupled 5 parts, 8 parts of castor bean wax, poly terephthalic acid
10 parts of butyl ester, 14 parts of mica powder, 8 parts of dimethicone, 10 parts of phthalic acid ester, 4 parts of phosphite, 10 parts of sulfydryl acid esters,
8 parts of triethoxysilane, 15 parts of rosin modified phenolic resin, 20 parts of polyvinyl acetate, 8 parts of carboxylic styrene butadiene latex, phenylpropyl alcohol breast
5 parts of 20 parts of liquid, 9 parts of citric acid and activated carbon are put into mixer, and regulation rotating speed is 3600-3800r/min, 6-11 points of reaction
Clock, it is standby;
2)By step 1)Gained raw material is put into autoclave, and regulation temperature is 78 DEG C, and regulation air pressure is 12 times of atmospheric pressure, reaction
It is 7-15 minutes, standby;
3)By step 2)Gained raw material is put into banbury, and regulation temperature is 220-245 DEG C, is in molten by raw material heating
State, it is standby;
4)By step 3)Gained raw material is put into injection machine, and injection machine is fed injection into mould, after natural cooling shaping
The interior tube layer of tubulose is obtained, it is standby.
5)By step 4)Tube layer is processed using lathe turning in gained so that spiral groove is formed on the outside of interior tube layer, i.e.,
Can.
Experimental example
Experimental subjects:The inner tube layer material for choosing common pipe material, special pipeline material and the present invention carries out test comparison.
Requirement of experiment:The inner tube layer material of common pipe material, special pipeline material and the present invention is used into identical faces
Product and thickness are detected.
Standard is detected;Tensile strength is detected using GBT228-2002 methods.Experimental method:To pipeline material
Anticorrosive detection is carried out, is detected by corrosion test chamber, and it is 120 DEG C to adjust test temperature temperature, and relative humidity is
85%, air pressure is 106kPa, and ozone concentration is 45%, and ultraviolet illumination intensity is 25uw/cm2, obtains etching time;Flame retardant effect
Pass through GB/T 31420-2015
Detect data such as following table:
With reference to upper table, the data of different pipeline materials gained under identical experimental method, interior tube layer material of the invention are contrasted
Expect that structural strength is higher, more preferably, anticorrosion effect is more preferable for flame retardant effect.
Beneficial effects of the present invention are:The polyurethane foam of setting has heat insulation effect, and the quartz sand layer of setting has
Good flameproof effect;The interior tube layer set keeps corrosion-resistant for polyethylene layer, and service life is long;The fixed cover of setting keeps peace
Dress is convenient;There are spring and fixing bolt holding structure compact on the baffle plate of setting, stability is high, possess on the outside of the interior tube layer of use
Spiral groove, so spreading glue can be arranged in pipeline on the outside of interior tube layer, and the material of use is corrosion-resistant, service life
It is long.
The foregoing is only a specific embodiment of the invention, but protection scope of the present invention is not limited thereto, any
The change or replacement expected without creative work, should all be included within the scope of the present invention.
Claims (7)
1. a kind of construction drainage pipeline, it is characterised in that:Including interior tube layer, polyurethane foam, quartz sand layer and outer
Tube layer, said inner tube layer, polyurethane foam, quartz sand layer and external tube layer are set from the inside to the outside successively, and described is that external tube layer is
Stainless steel layer, said inner tube layer outside is provided with support bar, and the support bar is fixedly connected with interior tube layer and external tube layer respectively, institute
Support bar is stated provided with three, fixed cover is provided with the outside of the external tube layer, the fixed cover side sets baffle plate, the baffle plate with
Fixed cover is integrally formed setting.
2. construction drainage pipeline according to claim 1, it is characterised in that:The polyurethane foam thickness is
8mm。
3. construction drainage pipeline according to claim 1, it is characterised in that:Bullet is installed on the inside of the baffle plate
Spring.
4. construction drainage pipeline according to claim 1, it is characterised in that:Fixation is installed in the middle part of the baffle plate
Bolt.
5. construction drainage pipeline according to claim 1, it is characterised in that:Said inner tube thickness degree is 5mm.
6. a kind of construction drainage pipeline, it is characterised in that:Said inner tube layer is by mass fraction proportioning by following material system
Into:It is 23-28 parts of styrene-acrylonitrile copolymer, 5-8 parts of aluminium powder, 2-5 parts of silane coupler, 6-8 parts of castor bean wax, poly- to benzene
7-10 parts of diformazan acid butyl ester, 12-14 parts of mica powder, 6-8 parts of dimethicone, 7-10 parts of phthalic acid ester, phosphite 2-4
Part, 5-10 parts of sulfydryl acid esters, 3-8 parts of triethoxysilane, 12-15 parts of rosin modified phenolic resin, polyvinyl acetate 16-20
Part, 7-8 parts of carboxylic styrene butadiene latex, 15-20 parts of styrene-acrylic emulsion, 3-9 parts of citric acid and 2-5 parts of activated carbon.
7. construction drainage pipeline according to claim 6, it is characterised in that:The preparation method bag of said inner tube layer
Include following steps:
1)By styrene -23-28 parts of acrylonitrile copolymer, 5-8 parts of aluminium powder, 2-5 parts of silane coupler, 6-8 parts of castor bean wax,
7-10 parts of PA polybutyleneterephthalate, 12-14 parts of mica powder, 6-8 parts of dimethicone, 7-10 parts of phthalic acid ester, phosphorous
2-4 parts of hydrochlorate, 5-10 parts of sulfydryl acid esters, 3-8 parts of triethoxysilane, 12-15 parts of rosin modified phenolic resin, polyvinyl acetate
2-5 parts of 16-20 parts of ester, 7-8 parts of carboxylic styrene butadiene latex, 15-20 parts of styrene-acrylic emulsion, 3-9 parts of citric acid and activated carbon are put into and stirred
Mix in machine, regulation rotating speed is 3600-3800r/min, is reacted 6-11 minutes, standby;
2)By step 1)Gained raw material is put into autoclave, and regulation temperature is 78 DEG C, and regulation air pressure is 12 times of atmospheric pressure, reaction
It is 7-15 minutes, standby;
3)By step 2)Gained raw material is put into banbury, and regulation temperature is 220-245 DEG C, is in molten by raw material heating
State, it is standby;
4)By step 3)Gained raw material is put into injection machine, and injection machine is fed injection into mould, after natural cooling shaping
The interior tube layer of tubulose is obtained, it is standby;
5)By step 4)Tube layer is processed using lathe turning in gained so that spiral groove is formed on the outside of interior tube layer, you can.