CN107312634A - A kind of high-efficient aluminium alloy mold clean liquid - Google Patents
A kind of high-efficient aluminium alloy mold clean liquid Download PDFInfo
- Publication number
- CN107312634A CN107312634A CN201710330081.5A CN201710330081A CN107312634A CN 107312634 A CN107312634 A CN 107312634A CN 201710330081 A CN201710330081 A CN 201710330081A CN 107312634 A CN107312634 A CN 107312634A
- Authority
- CN
- China
- Prior art keywords
- liquid
- aluminium alloy
- camellia seed
- culture
- efficient aluminium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high-efficient aluminium alloy mold clean liquid, it is made up of following component:Cinnamic acid propylene glycol ester, glycerol caprylate, polyethylene glycol, sodium tripolyphosphate, ethoxylated dodecyl alcohol, regulation liquid, water;Aluminum alloy mould cleaning fluid prepared by the present invention has good cleaning action to dirts such as punching oil, drawing oil, cutting fluids, and using effect is good, and degreasing power is strong, and production cost is low, has no toxic side effect, with cleaning speed is fast, without phosphorus, asepsis environment-protecting the features such as.
Description
Technical field
The invention belongs to aluminum products processing technique field, and in particular to a kind of high-efficient aluminium alloy mold clean liquid.
Background technology
In household electrical appliances, automobile industry mould processing enterprise, most economical economical material is aluminium alloy, aluminium, aluminium alloy heat transfer
Good, light weight is the excellent base material of processing mold, due to the optimization and upgrading inside automobile industry in recent years, is constantly stimulated to mould
The growth of tool demand.Auto industry is for China, also in continuing to develop growth stage, the above-mentioned drive in above trend
Under, the advantage that China's Die Industry is developed be very it will be evident that still aluminum alloy mould in use, often
There are pollution, particularly greasy dirt caused by greasy dirt, debris easily to form oil film in aluminum alloy surface and be attached to surface formation colour film, when
Between it is long irreversible erosion can be formed to aluminum alloy surface, have a strong impact on product quality and die life, existing aluminium
The molten oil of alloy cleaning fluid is less efficient, and cost is high, and the feature of environmental protection is poor.
The content of the invention
The purpose of the present invention is that there is provided a kind of high-efficient aluminium alloy mold clean liquid the problem of being directed to existing.
The present invention is achieved by the following technical solutions:
A kind of high-efficient aluminium alloy mold clean liquid, is made up of following component by weight:Cinnamic acid propylene glycol ester 3-5, caprylic
Acid esters 5-8, polyethylene glycol 4-6, sodium tripolyphosphate 1.2-1.5, ethoxylated dodecyl alcohol 1.3-1.8, regulation liquid 2.5-3.4,
Water 90-100;
It is described regulation liquid and preparation method thereof be:
(1) cactus, the curvature of the spinal column leaf of bamboo, grape pip, arrowroot leaf are mixed, is crushed to the mesh of granularity 90, obtains mixed powder and mince, added
The water that 2 times of co-grinding amount of substance, heating boiling 40 minutes after natural cooling, is inoculated with test tube aspergillus oryzae, loads tub, culture
Interior is cultivated at 32 DEG C, and incubation time is 12 hours, obtains culture, carries out sterilization treatment;
(2) above-mentioned culture is added water, water: culture part by weight is=1: 2, under the conditions of 50 DEG C, with 850r/min rotating speeds
30min is stirred, the attapulgite of culture quality 2.5% and the camellia seed oil of culture quality 1.8% is then added, stirs
Afterwards, monascus specie is aseptically inoculated with, after 32 DEG C expand culture 12 hours, fermentation material is obtained;
(3)The water of 4 times of its quality is added into fermentation material, 50 DEG C are heated to, the ethanol of 2 times of fermentation material quality is then added, with
1200r/min rotating speeds are stirred 3.5 hours, and then insulation stands 2 hours, then carries out separation of solid and liquid under high speed centrifugation, is mixed
Liquid is closed, regulation liquid needed for being.
Further, the molecular weight of poly- second two is 8500-9000.
Further, the cactus, the curvature of the spinal column leaf of bamboo, grape pip, arrowroot leaf press 5:1:2:1 mass ratio is mixed.
Further, the aspergillus oryzae inoculum concentration is the 0.12-1.14% of co-grinding amount of substance.
Further, the monascus specie amount is attapulgite quality 5%.
Further, the attapulgite granularity is 600-750 mesh.
Further, the camellia seed oil preparation method is:
(1)Raw material is selected, excellent camellia seed and linseed from free from insect pests, without lesion of going rotten;
(2)Pretreatment, 20min is soaked by camellia seed mass fraction for 0.12% Threonine solution at 55 DEG C, then, drip
Dried in solid carbon dioxide point, the hot-blast stove of 60 DEG C of feeding;
(3)Crush, the camellia seed of drying, linseed are respectively put into pulverizer, powder is ground into;
(4)Leaching, 5 are pressed by camellia seed powder, linseed meal:The mixing of 1 mass ratio is put into sealing container, and injection is preheated to 72
DEG C ethanol, soaked after being sufficiently stirred for;Its ethanol consumption, is 5 times of camellia seed powder weight, soaks 3.5 hours, filters out leaching
Liquid;
(5)It is concentrated in vacuo, the immersion liquid filtered is put into vacuum tank, carries out cryogenic vacuum concentration, you can obtain camellia seed oil.
Further, the cryogenic vacuum concentration, 35 DEG C of temperature control, vacuum is 61300Pa.
Further, the high-efficient aluminium alloy mold clean liquid temperature in use is 30-32 DEG C.
The present invention has advantages below compared with prior art:Aluminum alloy mould cleaning fluid prepared by the present invention to punching oil,
The dirts such as drawing oil, cutting fluid have good cleaning action, and using effect is good, and degreasing power is strong, and production cost is low, nontoxic secondary work
With, with cleaning speed is fast, without phosphorus, asepsis environment-protecting the features such as;The cleaning fluid that the present invention is prepared can destroy greasy dirt and aluminium alloy
Bonding force between die matrix, reduction greasy dirt and the surface tension on aluminum alloy mould interface, being capable of Rapid Cleaning aluminium alloy
The regulation liquid solubilization added in the greasy dirt of die surface, the present invention is strong, passes through the regulation liquid added in cleaning fluid and its
Its composition acts synergistically, and can clean up the greasy dirt being attached on aluminum alloy mould surface, have good matching, in 30-
In 32 DEG C of temperature ranges, can play maximum molten oily efficiency, with it is efficient, quick, time saving the characteristics of, do not corrode aluminium alloy mould
Have surface, no suspended substance, stability is high, is unlikely to deteriorate, usage cycles are long, to aluminum alloy mould surface non-hazardous, generation it is useless
Liquid is environmentally safe, does not destroy ecological environment.
Embodiment
Embodiment 1
A kind of high-efficient aluminium alloy mold clean liquid, is made up of following component by weight:Cinnamic acid propylene glycol ester 3, glycerine octanoic acid
Ester 5, polyethylene glycol 4, sodium tripolyphosphate 1.2, ethoxylated dodecyl alcohol 1.3, regulation liquid 2.5, water 90;
It is described regulation liquid and preparation method thereof be:
(1) cactus, the curvature of the spinal column leaf of bamboo, grape pip, arrowroot leaf are mixed, is crushed to the mesh of granularity 90, obtains mixed powder and mince, added
The water that 2 times of co-grinding amount of substance, heating boiling 40 minutes after natural cooling, is inoculated with test tube aspergillus oryzae, loads tub, culture
Interior is cultivated at 32 DEG C, and incubation time is 12 hours, obtains culture, carries out sterilization treatment;
(2) above-mentioned culture is added water, water: culture part by weight is=1: 2, under the conditions of 50 DEG C, with 850r/min rotating speeds
30min is stirred, the attapulgite of culture quality 2.5% and the camellia seed oil of culture quality 1.8% is then added, stirs
Afterwards, monascus specie is aseptically inoculated with, after 32 DEG C expand culture 12 hours, fermentation material is obtained;
(3)The water of 4 times of its quality is added into fermentation material, 50 DEG C are heated to, the ethanol of 2 times of fermentation material quality is then added, with
1200r/min rotating speeds are stirred 3.5 hours, and then insulation stands 2 hours, then carries out separation of solid and liquid under high speed centrifugation, is mixed
Liquid is closed, regulation liquid needed for being.
The molecular weight of poly- second two is 8500.
The cactus, the curvature of the spinal column leaf of bamboo, grape pip, arrowroot leaf press 5:1:2:1 mass ratio is mixed.
The aspergillus oryzae inoculum concentration is the 0.12% of co-grinding amount of substance.
The monascus specie amount is attapulgite quality 5%.
The attapulgite granularity is 600 mesh.
The camellia seed oil preparation method is:
(1)Raw material is selected, excellent camellia seed and linseed from free from insect pests, without lesion of going rotten;
(2)Pretreatment, 20min is soaked by camellia seed mass fraction for 0.12% Threonine solution at 55 DEG C, then, drip
Dried in solid carbon dioxide point, the hot-blast stove of 60 DEG C of feeding;
(3)Crush, the camellia seed of drying, linseed are respectively put into pulverizer, powder is ground into;
(4)Leaching, 5 are pressed by camellia seed powder, linseed meal:The mixing of 1 mass ratio is put into sealing container, and injection is preheated to 72
DEG C ethanol, soaked after being sufficiently stirred for;Its ethanol consumption, is 5 times of camellia seed powder weight, soaks 3.5 hours, filters out leaching
Liquid;
(5)It is concentrated in vacuo, the immersion liquid filtered is put into vacuum tank, carries out cryogenic vacuum concentration, you can obtain camellia seed oil.
The cryogenic vacuum concentration, 35 DEG C of temperature control, vacuum is 61300Pa.
The high-efficient aluminium alloy mold clean liquid temperature in use is 30 DEG C.
Embodiment 2
A kind of high-efficient aluminium alloy mold clean liquid, is made up of following component by weight:Cinnamic acid propylene glycol ester 5, glycerine octanoic acid
Ester 8, polyethylene glycol 6, sodium tripolyphosphate 1.5, ethoxylated dodecyl alcohol 1.8, regulation liquid 3.4, water 100;
It is described regulation liquid and preparation method thereof be:
(1) cactus, the curvature of the spinal column leaf of bamboo, grape pip, arrowroot leaf are mixed, is crushed to the mesh of granularity 90, obtains mixed powder and mince, added
The water that 2 times of co-grinding amount of substance, heating boiling 40 minutes after natural cooling, is inoculated with test tube aspergillus oryzae, loads tub, culture
Interior is cultivated at 32 DEG C, and incubation time is 12 hours, obtains culture, carries out sterilization treatment;
(2) above-mentioned culture is added water, water: culture part by weight is=1: 2, under the conditions of 50 DEG C, with 850r/min rotating speeds
30min is stirred, the attapulgite of culture quality 2.5% and the camellia seed oil of culture quality 1.8% is then added, stirs
Afterwards, monascus specie is aseptically inoculated with, after 32 DEG C expand culture 12 hours, fermentation material is obtained;
(3)The water of 4 times of its quality is added into fermentation material, 50 DEG C are heated to, the ethanol of 2 times of fermentation material quality is then added, with
1200r/min rotating speeds are stirred 3.5 hours, and then insulation stands 2 hours, then carries out separation of solid and liquid under high speed centrifugation, is mixed
Liquid is closed, regulation liquid needed for being.
The molecular weight of poly- second two is 9000.
The cactus, the curvature of the spinal column leaf of bamboo, grape pip, arrowroot leaf press 5:1:2:1 mass ratio is mixed.
The aspergillus oryzae inoculum concentration is the 1.14% of co-grinding amount of substance.
The monascus specie amount is attapulgite quality 5%.
The attapulgite granularity is 750 mesh.
The camellia seed oil preparation method is:
(1)Raw material is selected, excellent camellia seed and linseed from free from insect pests, without lesion of going rotten;
(2)Pretreatment, 20min is soaked by camellia seed mass fraction for 0.12% Threonine solution at 55 DEG C, then, drip
Dried in solid carbon dioxide point, the hot-blast stove of 60 DEG C of feeding;
(3)Crush, the camellia seed of drying, linseed are respectively put into pulverizer, powder is ground into;
(4)Leaching, 5 are pressed by camellia seed powder, linseed meal:The mixing of 1 mass ratio is put into sealing container, and injection is preheated to 72
DEG C ethanol, soaked after being sufficiently stirred for;Its ethanol consumption, is 5 times of camellia seed powder weight, soaks 3.5 hours, filters out leaching
Liquid;
(5)It is concentrated in vacuo, the immersion liquid filtered is put into vacuum tank, carries out cryogenic vacuum concentration, you can obtain camellia seed oil.
The cryogenic vacuum concentration, 35 DEG C of temperature control, vacuum is 61300Pa.
The high-efficient aluminium alloy mold clean liquid temperature in use is 32 DEG C.
Embodiment 3
A kind of high-efficient aluminium alloy mold clean liquid, is made up of following component by weight:Cinnamic acid propylene glycol ester 4, glycerine octanoic acid
Ester 6, polyethylene glycol 5, sodium tripolyphosphate 1.3, ethoxylated dodecyl alcohol 1.5, regulation liquid 2.8, water 95;
It is described regulation liquid and preparation method thereof be:
(1) cactus, the curvature of the spinal column leaf of bamboo, grape pip, arrowroot leaf are mixed, is crushed to the mesh of granularity 90, obtains mixed powder and mince, added
The water that 2 times of co-grinding amount of substance, heating boiling 40 minutes after natural cooling, is inoculated with test tube aspergillus oryzae, loads tub, culture
Interior is cultivated at 32 DEG C, and incubation time is 12 hours, obtains culture, carries out sterilization treatment;
(2) above-mentioned culture is added water, water: culture part by weight is=1: 2, under the conditions of 50 DEG C, with 850r/min rotating speeds
30min is stirred, the attapulgite of culture quality 2.5% and the camellia seed oil of culture quality 1.8% is then added, stirs
Afterwards, monascus specie is aseptically inoculated with, after 32 DEG C expand culture 12 hours, fermentation material is obtained;
(3)The water of 4 times of its quality is added into fermentation material, 50 DEG C are heated to, the ethanol of 2 times of fermentation material quality is then added, with
1200r/min rotating speeds are stirred 3.5 hours, and then insulation stands 2 hours, then carries out separation of solid and liquid under high speed centrifugation, is mixed
Liquid is closed, regulation liquid needed for being.
The molecular weight of poly- second two is 8800.
The cactus, the curvature of the spinal column leaf of bamboo, grape pip, arrowroot leaf press 5:1:2:1 mass ratio is mixed.
The aspergillus oryzae inoculum concentration is the 0.13% of co-grinding amount of substance.
The monascus specie amount is attapulgite quality 5%.
The attapulgite granularity is 700 mesh.
The camellia seed oil preparation method is:
(1)Raw material is selected, excellent camellia seed and linseed from free from insect pests, without lesion of going rotten;
(2)Pretreatment, 20min is soaked by camellia seed mass fraction for 0.12% Threonine solution at 55 DEG C, then, drip
Dried in solid carbon dioxide point, the hot-blast stove of 60 DEG C of feeding;
(3)Crush, the camellia seed of drying, linseed are respectively put into pulverizer, powder is ground into;
(4)Leaching, 5 are pressed by camellia seed powder, linseed meal:The mixing of 1 mass ratio is put into sealing container, and injection is preheated to 72
DEG C ethanol, soaked after being sufficiently stirred for;Its ethanol consumption, is 5 times of camellia seed powder weight, soaks 3.5 hours, filters out leaching
Liquid;
(5)It is concentrated in vacuo, the immersion liquid filtered is put into vacuum tank, carries out cryogenic vacuum concentration, you can obtain camellia seed oil.
The cryogenic vacuum concentration, 35 DEG C of temperature control, vacuum is 61300Pa.
The high-efficient aluminium alloy mold clean liquid temperature in use is 31 DEG C.
Comparative example 1:Differed only in embodiment 1 without regulation liquid.
Comparative example 2:Differed only in embodiment 1 in prepared by regulation liquid without camellia seed oil.
Comparative example 3:Differed only in embodiment 1 in prepared by regulation liquid without attapulgite.
Experiment:The aluminum alloy mould of same size is recorded into original quality, W1 is recorded as, it is then uniform to smear same etc.
The greasy dirt M of amount, is respectively adopted embodiment and comparative example cleaning fluid immersion treatment, is heated in 30 DEG C of waters bath with thermostatic control, same time
After take out, dry, record now quality is recorded as W2, molten oil mass Y=W 1+M-W2, tests W1=1000g, M=100g, the time is
30min, contrast:
Table 1
As can be seen from Table 1, the cleaning fluid that prepared by the present invention is approached with organic greasy dirt detergent scavenging effect, and production cost is obvious
Less than organic greasy dirt detergent, also, cleaning fluid prepared by the present invention is more environmentally-friendly;
Using above-mentioned identical test, the addition of different adjustment liquid in cleaning fluid, contrast same time is prepared in the method for embodiment 1
Influence to the molten oil mass of cleaning fluid:
Table 2
As can be seen from Table 2, the addition of regulation liquid in certain limit with the increase of regulation liquid addition, in same time
Molten oil mass can be with increase, and more than certain limit, with the increase of regulation liquid addition, molten oil mass can be reduced in same time,
Continuing to increase molten oil mass in the amount of regulation liquid, same time can keep constant, adjust the temperature in use of liquid to the molten of same time
Oil mass also has obvious influence, and the molten oil mass in same time can be reduced less than 30 DEG C or higher than 32 DEG C.
Claims (9)
1. a kind of high-efficient aluminium alloy mold clean liquid, it is characterised in that be made up by weight of following component:Cinnamic acid propane diols
Ester 3-5, glycerol caprylate 5-8, polyethylene glycol 4-6, sodium tripolyphosphate 1.2-1.5, ethoxylated dodecyl alcohol 1.3-1.8, tune
Save liquid 2.5-3.4, water 90-100;
It is described regulation liquid and preparation method thereof be:
(1) cactus, the curvature of the spinal column leaf of bamboo, grape pip, arrowroot leaf are mixed, is crushed to the mesh of granularity 90, obtains mixed powder and mince, added
The water that 2 times of co-grinding amount of substance, heating boiling 40 minutes after natural cooling, is inoculated with test tube aspergillus oryzae, loads tub, culture
Interior is cultivated at 32 DEG C, and incubation time is 12 hours, obtains culture, carries out sterilization treatment;
(2) above-mentioned culture is added water, water: culture part by weight is=1: 2, under the conditions of 50 DEG C, with 850r/min rotating speeds
30min is stirred, the attapulgite of culture quality 2.5% and the camellia seed oil of culture quality 1.8% is then added, stirs
Afterwards, monascus specie is aseptically inoculated with, after 32 DEG C expand culture 12 hours, fermentation material is obtained;
(3)The water of 4 times of its quality is added into fermentation material, 50 DEG C are heated to, the ethanol of 2 times of fermentation material quality is then added, with
1200r/min rotating speeds are stirred 3.5 hours, and then insulation stands 2 hours, then carries out separation of solid and liquid under high speed centrifugation, is mixed
Liquid is closed, regulation liquid needed for being.
2. a kind of high-efficient aluminium alloy mold clean liquid as claimed in claim 1, it is characterised in that the poly- molecular weight of second two is
8500-9000。
3. a kind of high-efficient aluminium alloy mold clean liquid as claimed in claim 1, it is characterised in that the cactus, Monstera deliciosa
Leaf, grape pip, arrowroot leaf press 5:1:2:1 mass ratio is mixed.
4. a kind of high-efficient aluminium alloy mold clean liquid as claimed in claim 1, it is characterised in that the aspergillus oryzae inoculum concentration is
The 0.12-1.14% of co-grinding amount of substance.
5. a kind of high-efficient aluminium alloy mold clean liquid as claimed in claim 1, it is characterised in that the monascus specie amount is
Attapulgite quality 5%.
6. a kind of high-efficient aluminium alloy mold clean liquid as claimed in claim 1, it is characterised in that the attapulgite granularity is
600-750 mesh.
7. a kind of high-efficient aluminium alloy mold clean liquid as claimed in claim 1, it is characterised in that the camellia seed oil preparation side
Method is:
(1)Raw material is selected, excellent camellia seed and linseed from free from insect pests, without lesion of going rotten;
(2)Pretreatment, 20min is soaked by camellia seed mass fraction for 0.12% Threonine solution at 55 DEG C, then, drip
Dried in solid carbon dioxide point, the hot-blast stove of 60 DEG C of feeding;
(3)Crush, the camellia seed of drying, linseed are respectively put into pulverizer, powder is ground into;
(4)Leaching, 5 are pressed by camellia seed powder, linseed meal:The mixing of 1 mass ratio is put into sealing container, and injection is preheated to 72
DEG C ethanol, soaked after being sufficiently stirred for;Its ethanol consumption, is 5 times of camellia seed powder weight, soaks 3.5 hours, filters out leaching
Liquid;
(5)It is concentrated in vacuo, the immersion liquid filtered is put into vacuum tank, carries out cryogenic vacuum concentration, you can obtain camellia seed oil.
8. a kind of high-efficient aluminium alloy mold clean liquid as claimed in claim 7, it is characterised in that the cryogenic vacuum concentration,
35 DEG C of temperature control, vacuum is 61300Pa.
9. a kind of high-efficient aluminium alloy mold clean liquid as claimed in claim 7, it is characterised in that the high-efficient aluminium alloy mould
Cleaning fluid temperature in use is 30-32 DEG C.