CN107307470B - A kind of top grade pajama fabric and preparation method thereof - Google Patents

A kind of top grade pajama fabric and preparation method thereof Download PDF

Info

Publication number
CN107307470B
CN107307470B CN201710633665.XA CN201710633665A CN107307470B CN 107307470 B CN107307470 B CN 107307470B CN 201710633665 A CN201710633665 A CN 201710633665A CN 107307470 B CN107307470 B CN 107307470B
Authority
CN
China
Prior art keywords
fiber
fabric
banana stem
soaping
degummed ramie
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201710633665.XA
Other languages
Chinese (zh)
Other versions
CN107307470A (en
Inventor
饶琼仙
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Three Yuan Yi you dress Limited by Share Ltd
Original Assignee
Three Yuan Yi You Dress Ltd By Share Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Three Yuan Yi You Dress Ltd By Share Ltd filed Critical Three Yuan Yi You Dress Ltd By Share Ltd
Priority to CN201710633665.XA priority Critical patent/CN107307470B/en
Publication of CN107307470A publication Critical patent/CN107307470A/en
Application granted granted Critical
Publication of CN107307470B publication Critical patent/CN107307470B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The present invention provides a kind of high-grade pajama fabrics and preparation method thereof, cotton fiber and banana stem fiber degummed ramie be first woven into covering yarn, blended with cocoon fiber progress again, which not only has the characteristics that the pro-skin of cocoon fiber, and its moisture permeability is also further enhanced；The banana stem fiber degummed ramie that the present invention uses is to recycle the banana stem of waste, meets the requirement of national recycling economy, reduces the cost of high-grade fabric；A small amount of pupa albumen is added in dyeing course can be enhanced the fragrance of nightwear, promote sleep quality；The present invention is using banana stem fiber degummed ramie as core, it is external to be wrapped up with natural high-quality cotton, it is woven into covering yarn, the shortcomings that not only overcoming banana stem fiber degummed ramie rough surface, but also the moisture permeability of blended yarn weaved fabric is improved, it is a kind of Optimum utilization technique of new type natural fiber.

Description

A kind of top grade pajama fabric and preparation method thereof
Technical field
The present invention relates to field of textile, particularly, are related to a kind of high-grade pajama fabric and preparation method thereof.
Background technique
Banana industry is one of the pillar industry of China's tropical agriculture, is that the Important Economic of China hot-zone increasing peasant income is made Object.The wastes such as the huge banana stem of yield are generated after banana picking.It is suitable to can extract quantity in banana stem Considerable banana fiber, every plant of Banana tree can produce 200-500g banana fiber, and the extractible banana stem fiber in China has 100,000 Ton or more.Banana stem fiber has many advantages, such as moisture absorption and fast moisture releasing, has in textile industry and has big application prospect.And its His natural plant cellulose fiber is the same, and banana fiber main component is cellulose, hemicellulose, lignin, adipocere matter and fruit Glue etc., but content of cellulose will be lower than flax, jute, and the content of hemicellulose and lignin is then higher.Due to banana fiber Research is started late, and extractive technique and degumming tech are immature.In the selection of banana stem fiber degumming tech, it can use for reference The Degumming method of the crudefiber crops process of fiber such as flax, jute, hemp, mainly there is chemical Degumming and biological degumming method.
It is complete due to having the characteristics that hemicellulose and content of lignin are high, cellulose crystallity is lower, fibre strength is lower The full degumming for using for reference traditional crudefiber crop degumming tech parameter progress banana stem fiber is difficult to reach promising result, and degummed ramie obtains Rate is low, and the energy consumption of production is high, alkali lye consumption amount is big, pollution is big.
Chinese invention patent CN105821487A discloses a kind of production method of banana stem fiber degummed ramie, improves essence The yield of fiber crops is done, the intensity of degummed ramie can also basically reach the requirement of weaving, but the fiber surface of the flaxen fiber is rougher, such as What is applied in fabric especially high-grade fabric, still requires study.
Summary of the invention
It is an object of that present invention to provide a kind of high-grade pajama fabrics and preparation method thereof, to solve technical problem.
To achieve the above object, the present invention provides a kind of high-grade pajama fabrics and preparation method thereof.
A kind of top grade pajama fabric, the ingredient including following weight percent:
Banana stem fiber degummed ramie 8-15%
Cotton fiber 25-35%
Cocoon fiber surplus.
Preferably, the long number of the keen-witted and capable harl of banana stem fiber is 200-220Nm, single fiber intensity >=3cN/ dtex。
Preferably, the cotton fiber and banana stem fiber degummed ramie are first woven into covering yarn and reuse, wherein banana Stalk fiber degummed ramie is core, external to be wrapped up with natural high-quality cotton.
A kind of preparation method of top grade pajama fabric, which comprises the following steps:
A, external to be wrapped up with natural high-quality cotton using banana stem fiber degummed ramie as core, using vortex spinning work Skill is woven into covering yarn；
B, covering yarn and cocoon fiber are carried out blended being made into fabric；
C, fabric is subjected to bleaching, actual conditions are as follows: by fabric in the bleaching liquid of 50-55 DEG C of temperature 20-25min is managed, the cold water treatment 8-15min of 25-30 DEG C of temperature is then used；Drying；
D, fabric is dyed using compregnate method, actual conditions are as follows: pads temperature control at 50-55 DEG C, pads rate 70-80% pads the pupa albumen of the natural plants coloring agent and 0.5-1% in treatment fluid containing 2-8%, bath raio 1:(15- 25), pH value 6.5-6.8；
E, stamp is carried out to fabric, then carries out clear water and pads, be put into pond of soaping with the 45-50 DEG C of liquid processing 15- that soaps 20min, bath raio 1:(50-60)；The liquid of soaping is reusable；
F, fabric is placed on stenter and carries out drying and shaping, stenter speed is 60-70m/min, temperature 130-140 DEG C, setting time is controlled in 25-30s.
Preferably, the bleaching liquid includes the ingredient of following weight percent: hydrogen peroxide 0.1-0.3%, water glass Glass 0.2-0.3%, scouring agent 0.5-1%, surplus are water.
Preferably, the liquid of soaping includes the ingredient of following weight percent: efficient neutral soaping agent dosage is 0.1- 0.2%, surplus is water.
Temperature is controlled at 60 DEG C hereinafter, and drying high-temperature shaping during bleaching, dye and soaping in the present invention Time be strict controlled within 30s, be conducive to the protection to banana stem fiber degummed ramie and pupa albumen, make the mixed of preparation Textile fabric has better moisture permeability and discharges the effect of fragrance.
The invention has the following advantages:
1, blend fibre of the invention not only has the characteristics that the pro-skin of cocoon fiber, and its moisture permeability also obtains Further enhancing；2, banana stem fiber degummed ramie used in the present invention is to recycle the banana stem of waste, symbol The requirement for closing national recycling economy, reduces the cost of high-grade fabric；3, a small amount of pupa albumen is added in dyeing course can be with Enhance the fragrance of nightwear, promotes sleep quality；4, the present invention is external with natural high quality cotton using banana stem fiber degummed ramie as core The shortcomings that yarn is wrapped up, and covering yarn is woven into, and not only overcomes banana stem fiber degummed ramie rough surface, but also mention The moisture permeability for having risen blended yarn weaved fabric is a kind of Optimum utilization technique of new type natural fiber.
Specific embodiment
The embodiment of the present invention is described in detail below, but the present invention can be limited and be covered according to claim Multitude of different ways implement.
Embodiment 1
A kind of top grade pajama fabric, the ingredient including following weight percent:
Banana stem fiber degummed ramie 10%
Cotton fiber 30%
Cocoon fiber surplus.
The long number of the keen-witted and capable harl of banana stem fiber is 200-220Nm, single fiber intensity >=3cN/dtex.
A kind of preparation method of top grade pajama fabric, which comprises the following steps:
A, external to be wrapped up with natural high-quality cotton using banana stem fiber degummed ramie as core, using vortex spinning work Skill is woven into covering yarn；
B, covering yarn and cocoon fiber are carried out blended being made into fabric；
C, fabric is subjected to bleaching, actual conditions are as follows: fabric is handled in the bleaching liquid of 52 DEG C of temperature 23min, then with the cold water treatment 12min of 28 DEG C of temperature；Drying；The bleaching liquid includes following weight percent The ingredient of ratio: hydrogen peroxide 0.2%, waterglass 0.25%, scouring agent 0.7%, surplus are water；
D, fabric is dyed using compregnate method, actual conditions are as follows: pads temperature control at 52 DEG C, pads rate 75%, Pad the pupa albumen of natural plants coloring agent in treatment fluid containing 2-8% and 0.8%, bath raio 1:20, pH value 6.5-6.8；
E, stamp is carried out to fabric, then carries out clear water and pads, be put into pond of soaping and handle 18min with 48 DEG C of liquid of soaping, Bath raio is 1:55；The liquid of soaping is reusable；The liquid of soaping includes the ingredient of following weight percent: in efficiently Property soaping agent dosage be 0.1-0.2%, surplus is water；
F, fabric is placed on stenter and carries out drying and shaping, stenter speed is 65m/min, and temperature is 135 DEG C, sizing Time controls in 25-30s.
Embodiment 2
A kind of top grade pajama fabric, the ingredient including following weight percent:
Banana stem fiber degummed ramie 15%
Cotton fiber 35%
Cocoon fiber surplus.
The long number of the keen-witted and capable harl of banana stem fiber is 200-220Nm, single fiber intensity >=3cN/dtex.
A kind of preparation method of top grade pajama fabric, which comprises the following steps:
A, external to be wrapped up with natural high-quality cotton using banana stem fiber degummed ramie as core, using vortex spinning work Skill is woven into covering yarn；
B, covering yarn and cocoon fiber are carried out blended being made into fabric；
C, fabric is subjected to bleaching, actual conditions are as follows: fabric is handled in the bleaching liquid of 55 DEG C of temperature 20min, then with the cold water treatment 8min of 30 DEG C of temperature；Drying；The bleaching liquid includes following weight percent The ingredient of ratio: hydrogen peroxide 0.3%, waterglass 0.2%, scouring agent 1%, surplus are water；
D, fabric is dyed using compregnate method, actual conditions are as follows: pads temperature control at 50 DEG C, pads rate 80%, It pads in treatment fluid containing 2% natural plants coloring agent and 0.5% pupa albumen, bath raio 1:25, pH value 6.5-6.8；
E, stamp is carried out to fabric, then carries out clear water and pads, be put into pond of soaping and handle 20min with 45 DEG C of liquid of soaping, Bath raio is 1:50；The liquid of soaping is reusable；The liquid of soaping includes the ingredient of following weight percent: in efficiently Property soaping agent dosage be 0.1-0.2%, surplus is water；
F, fabric is placed on stenter and carries out drying and shaping, stenter speed is 60m/min, and temperature is 140 DEG C, sizing Time controls in 25-30s.
Embodiment 3
A kind of top grade pajama fabric, the ingredient including following weight percent:
Banana stem fiber degummed ramie 8%
Cotton fiber 25%
Cocoon fiber surplus.
The long number of the keen-witted and capable harl of banana stem fiber is 200-220Nm, single fiber intensity >=3cN/dtex.
A kind of preparation method of top grade pajama fabric, which comprises the following steps:
A, external to be wrapped up with natural high-quality cotton using banana stem fiber degummed ramie as core, using vortex spinning work Skill is woven into covering yarn；
B, covering yarn and cocoon fiber are carried out blended being made into fabric；
C, fabric is subjected to bleaching, actual conditions are as follows: fabric is handled in the bleaching liquid of 50 DEG C of temperature 25min, then with the cold water treatment 15min of 25 DEG C of temperature；Drying；The bleaching liquid includes following weight percent The ingredient of ratio: hydrogen peroxide 0.1%, waterglass 0.3%, scouring agent 0.5%, surplus are water；
D, fabric is dyed using compregnate method, actual conditions are as follows: pads temperature control at 55 DEG C, pads rate 70%, It pads in treatment fluid containing 8% natural plants coloring agent and 1% pupa albumen, bath raio 1:15, pH value 6.5-6.8；
E, stamp is carried out to fabric, then carries out clear water and pads, be put into pond of soaping and handle 15min with 50 DEG C of liquid of soaping, Bath raio is 1:60；The liquid of soaping is reusable；The liquid of soaping includes the ingredient of following weight percent: in efficiently Property soaping agent dosage be 0.1-0.2%, surplus is water
F, fabric is placed on stenter and carries out drying and shaping, stenter speed is 70m/min, and temperature is 130 DEG C, sizing Time controls in 25-30s.
Comparative example 1
Covering yarn in embodiment 1 is replaced with into cotton fiber, remaining preparation condition is constant.
The fabric of embodiment 1-3 and comparative example 1 are tested below, obtain following data.
Embodiment 1 Embodiment 2 Embodiment 3 Comparative example 1
Dampness RET RET ㎡ K/W 7.3 7.3 7.3 8.0
Thermal resistance RCT RCT ㎡ K/W 0.07 0.07 0.07 0.09
By the above detection data it is found that top grade pajama fabric prepared by the present invention has compared to traditional staple blended yarn weaved fabric Standby better moisture permeability.
The foregoing is only a preferred embodiment of the present invention, is not intended to restrict the invention, for the skill of this field For art personnel, the invention may be variously modified and varied.All within the spirits and principles of the present invention, made any to repair Change, equivalent replacement, improvement etc., should all be included in the protection scope of the present invention.

Claims (1)

1. a kind of top grade pajama fabric, it is characterised in that: the ingredient including following weight percent:
Banana stem fiber degummed ramie 15%
Cotton fiber 35%
Cocoon fiber surplus,
The long number of the keen-witted and capable harl of banana stem fiber be 200-220Nm, single fiber intensity >=3cN/dtex,
The preparation method of the top grade pajama fabric, comprising the following steps:
A, external to be wrapped up with natural high-quality cotton using banana stem fiber degummed ramie as core, it is spun using Technology of Air Vortex Spinning It is made into covering yarn；
B, covering yarn and cocoon fiber are carried out blended being made into fabric；
C, fabric is subjected to bleaching, actual conditions are as follows: fabric is handled in the bleaching liquid of 55 DEG C of temperature 20min, then with the cold water treatment 8min of 30 DEG C of temperature；Drying；The bleaching liquid includes following weight percent The ingredient of ratio: hydrogen peroxide 0.3%, waterglass 0.2%, scouring agent 1%, surplus are water；
D, fabric is dyed using compregnate method, actual conditions are as follows: pads temperature control at 50 DEG C, pads rate 80%, pad Contain 2% natural plants coloring agent and 0.5% pupa albumen, bath raio 1:25, pH value 6.5-6.8 in treatment fluid；
E, stamp is carried out to fabric, then carries out clear water and pads, be put into pond of soaping with 45 DEG C of liquid processing 20min that soap, bath raio For 1:50；The liquid of soaping is reusable；The liquid of soaping includes the ingredient of following weight percent: neutral soaping agent Dosage is 0.1-0.2%, and surplus is water；
F, fabric is placed on stenter and carries out drying and shaping, stenter speed is 60m/min, and temperature is 140 DEG C, setting time Control is in 25-30s.
CN201710633665.XA 2016-10-18 2016-10-18 A kind of top grade pajama fabric and preparation method thereof Active CN107307470B (en)