CN107288281A - 一种防霉除菌壁纸及制备方法 - Google Patents
一种防霉除菌壁纸及制备方法 Download PDFInfo
- Publication number
- CN107288281A CN107288281A CN201710540748.4A CN201710540748A CN107288281A CN 107288281 A CN107288281 A CN 107288281A CN 201710540748 A CN201710540748 A CN 201710540748A CN 107288281 A CN107288281 A CN 107288281A
- Authority
- CN
- China
- Prior art keywords
- parts
- layer
- mould
- bacteria
- proof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开了一种防霉除菌壁纸及制备方法，所述壁纸包括基材层，基材层的上表面设置有防霉除菌层，防霉除菌层的上表面设有防水透气层，所述基材层的下表面设有自粘防水层，所述自粘防水层的下表面设有离型层。制备方法包括：先制备防霉除菌层，然后再按照顺序将各层粘合再一起即可。所述壁纸不仅具有较好的防止霉菌、细菌滋生，还能有效杀菌的作用，且对室内环境起到较好的净化作用，应用于室内装饰，为人们提供清洁、安全的生活环境，具有较好的应用价值。
Description
技术领域
本发明涉及壁纸技术领域，具体涉及一种防霉除菌壁纸及制备方法。
背景技术
壁纸，也称为墙纸，它是一种应用相当广泛的室内装饰材料。因为壁纸具有色彩多样、图案丰富、豪华气派、安全环保、施工方便、价格适宜等多种其它室内装饰材料所无法比拟的特点，故在欧美、东南亚、日本等发达国家和地区得到相当程度的普及。近年来，我国室内装饰装修持续升温，一度遭冷落的壁纸以其绚丽的新姿态重新走进了客厅、卧室、酒店、会议室等。随着人们生活水平的提高，人们需要要高品质的壁纸来装点自己的生活，人们对壁纸的其它功能性要求也越来越多。
随着人们物质文化生活的不断提高，人们对于健康和清洁问题的关心以及对优雅安乐等舒适性能的生活追求也在日益提高。但是，在日常生活当中，无法避免的厨房、卫生间、医院病房、卧室异味以及细菌滋生，往往会影响人们生活的舒适性。
因此，研究开发一种具有较好防霉除菌效果，又能对室内环境起到净化作用的室内用壁纸具有重要意义，也符合目前市场的需求，具有较好的应用前景。
发明内容
针对现有技术中的缺陷，本发明的目的是提供一种防霉除菌壁纸及制备方法，所述壁纸不仅具有较好的防止霉菌、细菌滋生，还能有效杀菌的作用，且对室内环境起到较好的净化作用，应用于室内装饰，为人们提供清洁、安全的生活环境，具有较好的应用价值。
本发明解决技术问题采用如下技术方案：
本发明涉及一种防霉除菌壁纸，包括基材层，基材层的上表面设置有防霉除菌层，防霉除菌层的上表面设有防水透气层，所述基材层的下表面设有自粘防水层，所述自粘防水层的下表面设有离型层；
所述防霉除菌层包括如下重量份的各原料：聚乙烯醇20~30份、水性聚氨酯10~20份、页岩硅藻泥5~12份、防霉除菌剂6~18份、纳米二氧化钛3~9份、凹凸棒石粘土7~15份、超细滑石粉5~10份、消泡剂2~6份。
优选地，所述防霉除菌层包括如下重量份的各原料：聚乙烯醇28份、水性聚氨酯17份、页岩硅藻泥10份、防霉除菌剂15份、纳米二氧化钛6份、凹凸棒石粘土12份、超细滑石粉8份、消泡剂4份。
优选地，所述防霉除菌剂包括如下重量份的各组分：迷迭香6~12份、薄荷10~15份、丁香种子5~9份、甘草10~20份、苦皮藤3~8份、马齿苋5~10份、昆布2~6份、肉桂3~7份、茵陈7~11份、紫苏9~13份。
优选地，所述防水透气层为石墨烯改性PP层。
优选地，所述自粘防水层为石墨烯改性环氧树脂层。
优选地，所述离型层为PP层或者PE层。
本发明还涉及一种制备防霉除菌壁纸的方法，包括如下步骤：
（1）防霉除菌剂的预处理：按照配比分别称取防霉除菌剂的各组分，粉碎并过150目筛，然后将粉碎后的各组分混合均匀，置于索氏提取器中，于75~80℃条件下在乙醇与水的混合溶剂中提取4~6h，得到提取液，然后将提取液浓缩，备用；
（2）防霉除菌层材料的制备：按照配比分别称取聚乙烯醇、水性聚氨酯及适量的水置于反应釜中，搅拌均匀后加入凹凸棒石粘土，搅拌并置于剪切机中剪切10~20min，然后向混合物中加入页岩硅藻泥和步骤（1）中得到的提取浓缩液，混合搅拌均匀并置于超声波中超声10~20min，再加入纳米二氧化钛、超细滑石粉和消泡剂，充分搅拌均匀，即得所述防霉除菌层材料；
（3）防霉除菌壁纸的制备：将基材层舒展开，在基材层的上表面涂覆防霉除菌材料，然后再在防霉除菌材料层的上表面粘附防水透气层，在基材层的下表面涂覆自粘防水层，然后再在自粘防水层的下表面粘附离型层，即可。
优选地，所述步骤（1）中混合溶剂的质量为防霉除菌剂粉料质量的10~16倍，其中乙醇与水的体积比为1:0.5~2。
优选地，所述步骤（2）中加入水的质量为聚合物质量的3~8倍。
与现有技术相比，本发明具有如下的有益效果：
（1）本发明所述的防霉除菌壁纸，不仅具有较好的防止霉菌、细菌滋生的效果，还能有效杀菌的作用，且对室内环境起到较好的净化作用，应用于室内装饰，为人们提供清洁、安全的生活环境，具有较好的应用价值。
（2）本发明所述的防霉除菌壁纸采用多层粘合而成，能够有效凸显每层的功能，实现了壁纸的多功能化需求，具有较好的应用前景。
（3）本发明所述的防霉除菌壁的防霉除菌层中采用纯中药组分作为防霉除菌剂，多种组分协同作用，能够有效杀除并防止墙体细菌、霉菌的滋生，且不会对室内环境造成污染，提高了产品的使用安全性。
（4）本发明所述的防霉除菌壁纸的防霉除菌层中添加有聚乙烯醇，能够有效增加防霉除菌材料的粘结性能，使得防霉除菌层能够与基材层和防水透气层紧密牢固结合，避免了在使用化学粘结剂进行粘结，不仅降低了使用成本，还减少了制备工艺，提高了操作便利性。
（5）本发明所述防霉除菌壁纸的制备工艺简单、条件温和、设备投资少，且生产过程安全、无污染，适合工业化推广生产，具有较好的应用前景。
具体实施方式
下面结合具体实施例，进一步阐述本发明。这些实施例仅用于说明本发明而不用于限制本发明的范围。下列实施例中未注明具体条件的实验方法，通常按照常规条件，例如Sambrook等分子克隆：实验室手册（New York:Cold Spring Harbor Laboratory Press,1989）中所述的条件，或按照制造厂商所建议的条件。
实施例1：
本发明优选实施例的一种防霉除菌壁纸及制备方法；
所述防霉除菌壁纸，包括基材层，基材层的上表面设置有防霉除菌层，防霉除菌层的上表面设有防水透气层，所述基材层的下表面设有自粘防水层，所述自粘防水层的下表面设有离型层；
所述防霉除菌层由如下重量份的各原料制备而成：
聚乙烯醇28份、水性聚氨酯17份、页岩硅藻泥10份、防霉除菌剂15份、纳米二氧化钛6份、凹凸棒石粘土12份、超细滑石粉8份、消泡剂4份。
其中，防霉除菌剂由如下重量份的各组分制备而成：
迷迭香8份、薄荷12份、丁香种子6份、甘草15份、苦皮藤5份、马齿苋7份、昆布4份、肉桂5份、茵陈10份、紫苏10份。
所述防水透气层为石墨烯改性PP层。
所述自粘防水层为石墨烯改性环氧树脂层。
所述离型层为PP层。
本发明制备防霉除菌壁纸的方法，包括如下步骤：
（1）防霉除菌剂的预处理：按照配比分别称取防霉除菌剂的各组分，粉碎并过150目筛，然后将粉碎后的各组分混合均匀，置于索氏提取器中，于78℃条件下在乙醇与水的混合溶剂中提取5h，得到提取液，然后将提取液浓缩，备用；
（2）防霉除菌层材料的制备：按照配比分别称取聚乙烯醇、水性聚氨酯及适量的水置于反应釜中，搅拌均匀后加入凹凸棒石粘土，搅拌并置于剪切机中剪切15min，然后向混合物中加入页岩硅藻泥和步骤（1）中得到的提取浓缩液，混合搅拌均匀并置于超声波中超声15min，再加入纳米二氧化钛、超细滑石粉和消泡剂，充分搅拌均匀，即得所述防霉除菌层材料；
（3）防霉除菌壁纸的制备：将基材层舒展开，在基材层的上表面涂覆防霉除菌材料，然后再在防霉除菌材料层的上表面粘附防水透气层，在基材层的下表面涂覆自粘防水层，然后再在自粘防水层的下表面粘附离型层，即可。
步骤（1）中混合溶剂的质量为防霉除菌剂粉料质量的12倍，其中乙醇与水的体积比为1:1.5。
步骤（2）中加入水的质量为聚合物质量的6倍。
实施例2：
本发明优选实施例的一种防霉除菌壁纸及制备方法；
所述防霉除菌壁纸，包括基材层，基材层的上表面设置有防霉除菌层，防霉除菌层的上表面设有防水透气层，所述基材层的下表面设有自粘防水层，所述自粘防水层的下表面设有离型层；
所述防霉除菌层由如下重量份的各原料制备而成：
聚乙烯醇20份、水性聚氨酯10份、页岩硅藻泥5份、防霉除菌剂6份、纳米二氧化钛3份、凹凸棒石粘土7份、超细滑石粉5份、消泡剂2份。
其中，防霉除菌剂由如下重量份的各组分制备而成：
迷迭香6份、薄荷10份、丁香种子5份、甘草10份、苦皮藤3份、马齿苋5份、昆布2份、肉桂3份、茵陈7份、紫苏9份。
所述防水透气层为石墨烯改性PP层。
所述自粘防水层为石墨烯改性环氧树脂层。
所述离型层为PE层。
本发明制备防霉除菌壁纸的方法，包括如下步骤：
（1）防霉除菌剂的预处理：按照配比分别称取防霉除菌剂的各组分，粉碎并过150目筛，然后将粉碎后的各组分混合均匀，置于索氏提取器中，于75℃条件下在乙醇与水的混合溶剂中提取6h，得到提取液，然后将提取液浓缩，备用；
（2）防霉除菌层材料的制备：按照配比分别称取聚乙烯醇、水性聚氨酯及适量的水置于反应釜中，搅拌均匀后加入凹凸棒石粘土，搅拌并置于剪切机中剪切10min，然后向混合物中加入页岩硅藻泥和步骤（1）中得到的提取浓缩液，混合搅拌均匀并置于超声波中超声10min，再加入纳米二氧化钛、超细滑石粉和消泡剂，充分搅拌均匀，即得所述防霉除菌层材料；
（3）防霉除菌壁纸的制备：将基材层舒展开，在基材层的上表面涂覆防霉除菌材料，然后再在防霉除菌材料层的上表面粘附防水透气层，在基材层的下表面涂覆自粘防水层，然后再在自粘防水层的下表面粘附离型层，即可。
步骤（1）中混合溶剂的质量为防霉除菌剂粉料质量的10倍，其中乙醇与水的体积比为1:0.5。
步骤（2）中加入水的质量为聚合物质量的3倍。
实施例3：
本发明优选实施例的一种防霉除菌壁纸及制备方法；
所述防霉除菌壁纸，包括基材层，基材层的上表面设置有防霉除菌层，防霉除菌层的上表面设有防水透气层，所述基材层的下表面设有自粘防水层，所述自粘防水层的下表面设有离型层；
所述防霉除菌层由如下重量份的各原料制备而成：
聚乙烯醇30份、水性聚氨酯20份、页岩硅藻泥12份、防霉除菌剂18份、纳米二氧化钛9份、凹凸棒石粘土15份、超细滑石粉10份、消泡剂6份。
其中，防霉除菌剂由如下重量份的各组分制备而成：
迷迭香12份、薄荷15份、丁香种子9份、甘草20份、苦皮藤8份、马齿苋10份、昆布6份、肉桂7份、茵陈11份、紫苏13份。
所述防水透气层为石墨烯改性PP层。
所述自粘防水层为石墨烯改性环氧树脂层。
所述离型层为PE层。
本发明制备防霉除菌壁纸的方法，包括如下步骤：
（1）防霉除菌剂的预处理：按照配比分别称取防霉除菌剂的各组分，粉碎并过150目筛，然后将粉碎后的各组分混合均匀，置于索氏提取器中，于80℃条件下在乙醇与水的混合溶剂中提取4h，得到提取液，然后将提取液浓缩，备用；
（2）防霉除菌层材料的制备：按照配比分别称取聚乙烯醇、水性聚氨酯及适量的水置于反应釜中，搅拌均匀后加入凹凸棒石粘土，搅拌并置于剪切机中剪切20min，然后向混合物中加入页岩硅藻泥和步骤（1）中得到的提取浓缩液，混合搅拌均匀并置于超声波中超声20min，再加入纳米二氧化钛、超细滑石粉和消泡剂，充分搅拌均匀，即得所述防霉除菌层材料；
（3）防霉除菌壁纸的制备：将基材层舒展开，在基材层的上表面涂覆防霉除菌材料，然后再在防霉除菌材料层的上表面粘附防水透气层，在基材层的下表面涂覆自粘防水层，然后再在自粘防水层的下表面粘附离型层，即可。
步骤（1）中混合溶剂的质量为防霉除菌剂粉料质量的16倍，其中乙醇与水的体积比为1: 2。
步骤（2）中加入水的质量为聚合物质量的8倍。
分别将实施例1~3制备得到的壁纸分别进行性能测试，按照GB/T 21866-2008《 抗菌涂料(漆膜)抗菌性测定法和抗菌效果》分别对其进行抗菌性能和效果进行测试，具体除菌率结果见下表：
| 抗菌性能/% | 抗菌耐久性能/% | |
| 实施例1 | 99.7 | 97.2 |
| 实施例2 | 99.6 | 96.9 |
| 实施例3 | 99.6 | 97.1 |
由上表所示，本发明所制备得到的壁纸的具有较好的抗菌效果和抗菌持久性。
综上所述，本发明所述的防霉除菌壁纸，不仅具有较好的防止霉菌、细菌滋生的效果，还能有效杀菌的作用，且对室内环境起到较好的净化作用，应用于室内装饰，为人们提供清洁、安全的生活环境，具有较好的应用价值。
本发明所述防霉除菌壁纸的制备工艺简单、条件温和、设备投资少，且生产过程安全、无污染，适合工业化推广生产，具有较好的应用前景。
以上对本发明的具体实施例进行了描述。需要理解的是，本发明并不局限于上述特定实施方式，本领域技术人员可以在权利要求的范围内做出各种变形或修改，这并不影响本发明的实质内容。
Claims (9)
1.一种防霉除菌壁纸，其特征在于：包括基材层，基材层的上表面设置有防霉除菌层，防霉除菌层的上表面设有防水透气层，所述基材层的下表面设有自粘防水层，所述自粘防水层的下表面设有离型层；
所述防霉除菌层包括如下重量份的各原料：聚乙烯醇20~30份、水性聚氨酯10~20份、页岩硅藻泥5~12份、防霉除菌剂6~18份、纳米二氧化钛3~9份、凹凸棒石粘土7~15份、超细滑石粉5~10份、消泡剂2~6份。
2.根据权利要求1所述的防霉除菌壁纸，其特征在于：所述防霉除菌层包括如下重量份的各原料：聚乙烯醇28份、水性聚氨酯17份、页岩硅藻泥10份、防霉除菌剂15份、纳米二氧化钛6份、凹凸棒石粘土12份、超细滑石粉8份、消泡剂4份。
3.根据权利要求1或2中所述的防霉除菌壁纸，其特征在于：所述防霉除菌剂包括如下重量份的各组分：迷迭香6~12份、薄荷10~15份、丁香种子5~9份、甘草10~20份、苦皮藤3~8份、马齿苋5~10份、昆布2~6份、肉桂3~7份、茵陈7~11份、紫苏9~13份。
4.根据权利要求1所述的防霉除菌壁纸，其特征在于：所述防水透气层为石墨烯改性PP层。
5.根据权利要求1所述的防霉除菌壁纸，其特征在于：所述自粘防水层为石墨烯改性环氧树脂层。
6.根据权利要求1所述的防霉除菌壁纸，其特征在于：所述离型层为PP层或者PE层。
7.一种制备如权利要求1~6任一项所述的防霉除菌壁纸的方法，其特征在于：包括如下步骤：
（1）防霉除菌剂的预处理：按照配比分别称取防霉除菌剂的各组分，粉碎并过150目筛，然后将粉碎后的各组分混合均匀，置于索氏提取器中，于75~80℃条件下在乙醇与水的混合溶剂中提取4~6h，得到提取液，然后将提取液浓缩，备用；
（2）防霉除菌层材料的制备：按照配比分别称取聚乙烯醇、水性聚氨酯及适量的水置于反应釜中，搅拌均匀后加入凹凸棒石粘土，搅拌并置于剪切机中剪切10~20min，然后向混合物中加入页岩硅藻泥和步骤（1）中得到的提取浓缩液，混合搅拌均匀并置于超声波中超声10~20min，再加入纳米二氧化钛、超细滑石粉和消泡剂，充分搅拌均匀，即得所述防霉除菌层材料；
（3）防霉除菌壁纸的制备：将基材层舒展开，在基材层的上表面涂覆防霉除菌材料，然后再在防霉除菌材料层的上表面粘附防水透气层，在基材层的下表面涂覆自粘防水层，然后再在自粘防水层的下表面粘附离型层，即可。
8.根据权利要求7所述的防霉除菌壁纸的制备方法，其特征在于：所述步骤（1）中混合溶剂的质量为防霉除菌剂粉料质量的10~16倍，其中乙醇与水的体积比为1:0.5~2。
9.根据权利要求7所述的防霉除菌壁纸的制备方法，其特征在于：所述步骤（2）中加入水的质量为聚合物质量的3~8倍。