CN107286539A - A kind of Teflon plastics of high yield rate - Google Patents
A kind of Teflon plastics of high yield rate Download PDFInfo
- Publication number
- CN107286539A CN107286539A CN201710742210.1A CN201710742210A CN107286539A CN 107286539 A CN107286539 A CN 107286539A CN 201710742210 A CN201710742210 A CN 201710742210A CN 107286539 A CN107286539 A CN 107286539A
- Authority
- CN
- China
- Prior art keywords
- parts
- teflon
- high yield
- yield rate
- plastics
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of Teflon plastics of high yield rate, including component have：Teflon, alkyl hydrosulfide tin, calcium stearate, three basic aluminium sulphates, fatty acid amide, ox ester, the content of each component of the Teflon plastics of the high yield rate is：In parts by weight, 80 90 parts of Teflon, 5 11 parts of alkyl hydrosulfide tin, 9 14 parts of calcium stearate, 28 parts of three basic aluminium sulphate, 16 parts of fatty acid amide, 11 16 parts of ox ester, wherein the K values of the Teflon are 70 75.By the above-mentioned means, the Teflon plastics of the high yield rate of the present invention, can be made various products, the percent defective of generation is very low, effectively reduces production cost, with excellent performance, can meet the requirement of client, be widely used.
Description
Technical field
The present invention relates to Teflon plastic applications, the Teflon plastics of more particularly to a kind of high yield rate.
Background technology
Teflon, also known as polytetrafluoroethylene (PTFE), english abbreviation are PTFE.The product of Teflon material is typically referred to as " no
Adhesive coating layer ", is a kind of artificial synthesized high polymer material for having used fluorine to replace all hydrogen atoms in polyethylene.Teflon material has
The characteristics of having antiacid alkali resistant, resist various organic solvents, is practically insoluble in all solvents.Meanwhile, Teflon material has resistance to height
Warm the characteristics of, its coefficient of friction is extremely low, so can make lubrication way, also becomes the ideal of non-stick cooker and water pipe internal layer
Coating.Teflon material can be using pushing or being extruded and processed into type, can be with high-tension bus-bar or high frequency cable.Existing Teflon
Yield rate is low in imperial plastic applications, it is not easy to apply.
The content of the invention
The present invention solves the technical problem of a kind of Teflon plastics of high yield rate are provided, application effect is good.
In order to solve the above technical problems, one aspect of the present invention is：A kind of Teflon of high yield rate is provided
Imperial plastics, including component have：Teflon, alkyl hydrosulfide tin, calcium stearate, three basic aluminium sulphates, fatty acid amide, ox ester,
The content of each component of the Teflon plastics of the high yield rate is：In parts by weight, Teflon 80-90 parts, alkyl hydrosulfide tin
5-11 parts, 9-14 parts of calcium stearate, 2-8 parts of three basic aluminium sulphate, 1-6 parts of fatty acid amide, 11-16 parts of ox ester, wherein
The K values of the Teflon are 70-75.
In a preferred embodiment of the present invention, the content of each component of the Teflon plastics of the high yield rate is：With
Parts by weight meter, 80 parts of Teflon, 11 parts of alkyl hydrosulfide tin, 9 parts of calcium stearate, 8 parts of three basic aluminium sulphate, fatty acid amide
1 part, 16 parts of ox ester, wherein the K values of the Teflon are 70.
In a preferred embodiment of the present invention, the content of each component of the Teflon plastics of the high yield rate is：With
Parts by weight meter, 90 parts of Teflon, 5 parts of alkyl hydrosulfide tin, 14 parts of calcium stearate, 2 parts of three basic aluminium sulphate, fatty acid amide
6 parts, 11 parts of ox ester, wherein the K values of the Teflon are 75.
In a preferred embodiment of the present invention, the content of each component of the Teflon plastics of the high yield rate is：With
Parts by weight meter, 81 parts of Teflon, 10 parts of alkyl hydrosulfide tin, 10 parts of calcium stearate, 7 parts of three basic aluminium sulphate, fatty acid acyl
2 parts of amine, 15 parts of ox ester, wherein the K values of the Teflon are 71.
In a preferred embodiment of the present invention, the content of each component of the Teflon plastics of the high yield rate is：With
Parts by weight meter, 89 parts of Teflon, 6 parts of alkyl hydrosulfide tin, 13 parts of calcium stearate, 2-8 parts of three basic aluminium sulphate, fatty acid acyl
1-6 parts of amine, 11-16 parts of ox ester, wherein the K values of the Teflon are 74.
In a preferred embodiment of the present invention, the content of each component of the Teflon plastics of the high yield rate is：With
Parts by weight meter, 85 parts of Teflon, 8 parts of alkyl hydrosulfide tin, 11 parts of calcium stearate, 5 parts of three basic aluminium sulphate, fatty acid amide
4 parts, 14 parts of ox ester, wherein the K values of the Teflon are 73.
The beneficial effects of the invention are as follows：The Teflon plastics of the high yield rate of the present invention, can be made various products, produce
Percent defective it is very low, effectively reduce production cost, with excellent performance, the requirement of client can be met, using wide
It is general.
Embodiment
The technical scheme in the embodiment of the present invention will be clearly and completely described below, it is clear that described implementation
Example is only a part of embodiment of the present invention, rather than whole embodiments.Based on the embodiment in the present invention, this area is common
All other embodiment that technical staff is obtained under the premise of creative work is not made, belongs to the model that the present invention is protected
Enclose.
Embodiment one：
A kind of Teflon plastics of high yield rate are provided, including component have：Teflon, alkyl hydrosulfide tin, calcium stearate, three alkali
Formula aluminum sulfate, fatty acid amide, ox ester.The content of each component of the Teflon plastics of the high yield rate is：In parts by weight,
80 parts of Teflon, 11 parts of alkyl hydrosulfide tin, 9 parts of calcium stearate, 8 parts of three basic aluminium sulphate, 1 part of fatty acid amide, ox ester
16 parts, wherein the K values of the Teflon are 70.
Embodiment two：
A kind of Teflon plastics of high yield rate are provided, including component have：Teflon, alkyl hydrosulfide tin, calcium stearate, three alkali
Formula aluminum sulfate, fatty acid amide, ox ester.The content of each component of the Teflon plastics of the high yield rate is：In parts by weight,
90 parts of Teflon, 5 parts of alkyl hydrosulfide tin, 14 parts of calcium stearate, 2 parts of three basic aluminium sulphate, 6 parts of fatty acid amide, ox ester
11 parts, wherein the K values of the Teflon are 75.
Embodiment three：
A kind of Teflon plastics of high yield rate are provided, including component have：Teflon, alkyl hydrosulfide tin, calcium stearate, three alkali
Formula aluminum sulfate, fatty acid amide, ox ester.The content of each component of the Teflon plastics of the high yield rate is：In parts by weight,
81 parts of Teflon, 10 parts of alkyl hydrosulfide tin, 10 parts of calcium stearate, 7 parts of three basic aluminium sulphate, 2 parts of fatty acid amide, ox
15 parts of ester, wherein the K values of the Teflon are 71.
Example IV：
A kind of Teflon plastics of high yield rate are provided, including component have：Teflon, alkyl hydrosulfide tin, calcium stearate, three alkali
Formula aluminum sulfate, fatty acid amide, ox ester.The content of each component of the Teflon plastics of the high yield rate is：In parts by weight,
89 parts of Teflon, 6 parts of alkyl hydrosulfide tin, 13 parts of calcium stearate, 2-8 parts of three basic aluminium sulphate, 1-6 parts of fatty acid amide,
11-16 parts of ox ester, wherein the K values of the Teflon are 74.
Embodiment five：
A kind of Teflon plastics of high yield rate are provided, including component have：Teflon, alkyl hydrosulfide tin, calcium stearate, three alkali
Formula aluminum sulfate, fatty acid amide, ox ester.The content of each component of the Teflon plastics of the high yield rate is：In parts by weight,
85 parts of Teflon, 8 parts of alkyl hydrosulfide tin, 11 parts of calcium stearate, 5 parts of three basic aluminium sulphate, 4 parts of fatty acid amide, ox ester
14 parts, wherein the K values of the Teflon are 73.
The beneficial effects of the invention are as follows：
First, various products can be made in the Teflon plastics of the high yield rate, and the percent defective of generation is very low, effectively reduces
Production cost；
2nd, the Teflon plastics of the high yield rate have excellent performance, can meet the requirement of client, be widely used.
Embodiments of the invention are the foregoing is only, are not intended to limit the scope of the invention, it is every to utilize this hair
Equivalent structure or equivalent flow conversion that bright description is made, or directly or indirectly it is used in other related technology necks
Domain, is included within the scope of the present invention.
Claims (6)
1. a kind of Teflon plastics of high yield rate, it is characterised in that including component have：Teflon, alkyl hydrosulfide tin, tristearin
Sour calcium, three basic aluminium sulphates, fatty acid amide, ox ester, the content of each component of the Teflon plastics of the high yield rate is：With
Parts by weight meter, 80-90 parts of Teflon, 5-11 parts of alkyl hydrosulfide tin, 9-14 parts of calcium stearate, 2-8 parts of three basic aluminium sulphate,
1-6 parts of fatty acid amide, 11-16 parts of ox ester, wherein the K values of the Teflon are 70-75.
2. the Teflon plastics of high yield rate according to claim 1, it is characterised in that the Teflon of the high yield rate
The content of each component of plastics is：In parts by weight, 80 parts of Teflon, 11 parts of alkyl hydrosulfide tin, 9 parts of calcium stearate, three alkali
8 parts of formula aluminum sulfate, 1 part of fatty acid amide, 16 parts of ox ester, wherein the K values of the Teflon are 70.
3. the Teflon plastics of high yield rate according to claim 1, it is characterised in that the Teflon of the high yield rate
The content of each component of plastics is：In parts by weight, 90 parts of Teflon, 5 parts of alkyl hydrosulfide tin, 14 parts of calcium stearate, three alkali
2 parts of formula aluminum sulfate, 6 parts of fatty acid amide, 11 parts of ox ester, wherein the K values of the Teflon are 75.
4. the Teflon plastics of high yield rate according to claim 1, it is characterised in that the Teflon of the high yield rate
The content of each component of plastics is：In parts by weight, 81 parts of Teflon, 10 parts of alkyl hydrosulfide tin, 10 parts of calcium stearate, three
7 parts of basic aluminium sulphate, 2 parts of fatty acid amide, 15 parts of ox ester, wherein the K values of the Teflon are 71.
5. the Teflon plastics of high yield rate according to claim 1, it is characterised in that the Teflon of the high yield rate
The content of each component of plastics is：In parts by weight, 89 parts of Teflon, 6 parts of alkyl hydrosulfide tin, 13 parts of calcium stearate, three alkali
2-8 parts of formula aluminum sulfate, 1-6 parts of fatty acid amide, 11-16 parts of ox ester, wherein the K values of the Teflon are 74.
6. the Teflon plastics of high yield rate according to claim 1, it is characterised in that the Teflon of the high yield rate
The content of each component of plastics is：In parts by weight, 85 parts of Teflon, 8 parts of alkyl hydrosulfide tin, 11 parts of calcium stearate, three alkali
5 parts of formula aluminum sulfate, 4 parts of fatty acid amide, 14 parts of ox ester, wherein the K values of the Teflon are 73.