CN107936352A - A kind of low-temperature impact resistance clear PE composite material - Google Patents
A kind of low-temperature impact resistance clear PE composite material Download PDFInfo
- Publication number
- CN107936352A CN107936352A CN201711113431.9A CN201711113431A CN107936352A CN 107936352 A CN107936352 A CN 107936352A CN 201711113431 A CN201711113431 A CN 201711113431A CN 107936352 A CN107936352 A CN 107936352A
- Authority
- CN
- China
- Prior art keywords
- parts
- low
- composite material
- impact resistance
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of low-temperature impact resistance clear PE composite material, it is made of the component of following parts by weight:PE is 60 parts 80 parts;AES is 5 parts 10 parts;Hydrogenated styrene butadiene block copolymer is 6 parts 12 parts;Antioxidant is 0.1 part 0.5 part;Lubricant is 0.1 part 0.3 part.SBES is evenly distributed on as dispersed phase in the continuous phase of PE formation, when being subject to external impacts, the SEBS elastomer particles being dispersed in PE resins can absorb substantial amounts of impact energy, so that the low-temperature flexibility increase of PE composite materials by triggering crazing and inducing shear band;In addition the presence of chemical bond limits the Entropy Changes of each block between SBES differences block, and block copolymer can produce microcosmic phase separation, and form the domain structure of very little, and this domain structure is less than the wavelength of light.When crystalline size is less than visible wavelength, light is not reflected and reflected, this can improve the transparency of material.
Description
Technical field
The invention belongs to technical field of polymer materials, particularly relates to a kind of low-temperature impact resistance clear PE composite material.
Background technology
Polyethylene (PE) have it is light, nontoxic, odorless, chemical stability is good, and electrical insulation capability is good, and insoluble at normal temperatures
In common solvent, the advantages that water imbibition is small.In recent years become the kind that growth rate is most fast in five big resins for universal use, extensively should
For fields such as chemical industry, building materials, household electrical appliances, automobiles, become the resins for universal use of yield first, but polyethylene also there are many deficiencies in itself
Impact resistance is poor under part, mainly cryogenic conditions, and the transparency is poor, and appearance lacks aesthetic feeling so that PE is in packaging, Medical treatment device
The application in the fields such as tool, household supplies is restricted.
The content of the invention
The object of the present invention is to provide a kind of low-temperature impact resistance clear PE composite material and preparation method thereof, answered with improving PE
The low-temperature impact property and the transparency of condensation material.
The present invention is achieved by the following technical solutions:
A kind of low-temperature impact resistance clear PE composite material, is made of the component of following parts by weight:
The PE is linear low density polyethylene.
The PE is LLDPE 7042.
The antioxidant is three (2,4- di-t-butyl) phenyl-phosphites, four [β-(3,5- di-tert-butyl-hydroxy phenyls)
Propionic acid] pentaerythritol ester or 1,3,5- trimethyls -2,4, one kind or more in 6- (3,5- di-t-butyl -4- hydroxyphenylmethyls) benzene
Kind.
The lubricant is the one or more in zinc stearate, calcium stearate or potassium stearate.
The beneficial effects of the invention are as follows:
SBES is evenly distributed on as dispersed phase in the continuous phase of PE formation, when being subject to external impacts, is dispersed in PE trees
SEBS elastomer particles in fat can absorb substantial amounts of impact energy, so that PE by triggering crazing and inducing shear band
The low-temperature flexibility increase of composite material.
Embodiment
Carry out the technical solution that the present invention will be described in detail by the following examples, following embodiment is only exemplary, only
It can be used for explanation and illustration technical scheme, and be not to be construed as the limitation to technical solution of the present invention.
Embodiment 1
(1) 60 parts of PE, 5 parts of AES, 6 parts of SEBS, 0.1 part of Irganox168,0.1 part of calcium stearate is weighed to be mixed and stirred for
Uniformly, mixture is obtained;
(2) the mixture extruding pelletization that will be obtained in step (1), that is, obtain PE composite materials P1.
Wherein, double screw extruder includes six humidity provinces sequentially arranged, and the temperature of the first humidity province is 140 DEG C, the
The temperature of two humidity provinces is 170 DEG C, and the temperature of the 3rd humidity province is 170 DEG C, and the temperature of the 4th humidity province is 170 DEG C, the 5th temperature
The temperature for spending area is 170 DEG C, and the temperature of the 6th humidity province is 170 DEG C, and the head temperature of double screw extruder is 170 DEG C, screw rod
Rotating speed is 200r/min.
Embodiment 2
(1) 80 parts of PE, 10 parts of AES, 12 parts of SEBS, 0.1 part of Irganox1010,0.2 part of Irganox1330,0.2 are weighed
Part Irganox168,0.3 part of odium stearate are mixed and stirred for uniformly, obtaining mixture;
(2) the mixture extruding pelletization that will be obtained in step (1), that is, obtain PE composite materials P2.
Wherein, double screw extruder includes six humidity provinces sequentially arranged, and the temperature of the first humidity province is 160 DEG C, the
The temperature of two humidity provinces is 200 DEG C, and the temperature of the 3rd humidity province is 200 DEG C, and the temperature of the 4th humidity province is 200 DEG C, the 5th temperature
The temperature for spending area is 200 DEG C, and the temperature of the 6th humidity province is 200 DEG C, and the head temperature of double screw extruder is 200 DEG C, screw rod
Rotating speed is 260r/min.
Embodiment 3
(1) 70 parts of PE, 8 parts of AES, 9 parts of SEBS, 0.3 part of Irganox1330,0.2 part of potassium stearate is weighed to be mixed and stirred for
Uniformly, mixture is obtained;
(2) the mixture extruding pelletization that will be obtained in step (1), that is, obtain PE composite materials P3.
Wherein, double screw extruder includes six humidity provinces sequentially arranged, and the temperature of the first humidity province is 150 DEG C, the
The temperature of two humidity provinces is 185 DEG C, and the temperature of the 3rd humidity province is 185 DEG C, and the temperature of the 4th humidity province is 185 DEG C, the 5th temperature
The temperature for spending area is 185 DEG C, and the temperature of the 6th humidity province is 185 DEG C, and the head temperature of double screw extruder is 185 DEG C, screw rod
Rotating speed is 230r/min.
It the above is only the description of the preferred embodiment of the present invention, it is noted that due to the finiteness of literal expression, and
Objectively there are unlimited concrete structure, for those skilled in the art, the principle of the invention is not being departed from
On the premise of, some improvements and modifications can also be made, these improvements and modifications also should be regarded as protection scope of the present invention.
Claims (5)
1. a kind of low-temperature impact resistance clear PE composite material, it is characterised in that be made of the component of following parts by weight:
2. low-temperature impact resistance clear PE composite material according to claim 1, it is characterised in that the PE is linear low close
Spend polyethylene.
3. low-temperature impact resistance clear PE composite material according to claim 2, it is characterised in that the PE is LLDPE
7042。
4. low-temperature impact resistance clear PE composite material according to claim 1, it is characterised in that the antioxidant is three
(2,4- di-t-butyl) phenyl-phosphite, four [β-(3,5- di-tert-butyl-hydroxy phenyl) propionic acid] pentaerythritol esters or 1,3,
5- trimethyls -2,4, the one or more in 6- (3,5- di-t-butyl -4- hydroxyphenylmethyls) benzene.
5. low-temperature impact resistance clear PE composite material according to claim 1, it is characterised in that the lubricant is tristearin
One or more in sour zinc, calcium stearate or potassium stearate.