CN107285676A - A kind of environment-friendly type diatomite composition and its application - Google Patents
A kind of environment-friendly type diatomite composition and its application Download PDFInfo
- Publication number
- CN107285676A CN107285676A CN201710666748.9A CN201710666748A CN107285676A CN 107285676 A CN107285676 A CN 107285676A CN 201710666748 A CN201710666748 A CN 201710666748A CN 107285676 A CN107285676 A CN 107285676A
- Authority
- CN
- China
- Prior art keywords
- silica gel
- parts
- type
- weight
- diatom ooze
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of environment-friendly diatom ooze composition and its application, the diatomite composition includes 1 50 parts by weight diatomite, 1 60 parts by weight column chromatography silica gels;The column chromatography silica gel includes A types silica gel, Type B silica gel and c-type silica gel, wherein the weight ratio of the A types silica gel and Type B silica gel and c-type silica gel is 0.5 5:0.5‑5:0.5‑5.The invention also discloses the diatom ooze coating for including diatomite composition and auxiliary material.The diatom ooze composition and diatom ooze coating of the present invention, the controllable, the adsorbed hydroxyl content of micropore distribution is high, specific surface area is high, high adsorption capacity, damping ability is protruded, the depollution of environment effect of diatom ooze wall material can be significantly improved, temperature control effect and damping effect, have the advantages that cost is low, intensity is high, antistatic, absorption is strong.
Description
Technical field
The invention belongs to building material field, specifically, the present invention relates to a kind of environment-friendly type diatomite composition and its
Using.
Background technology
Interior decoration usually requires to use a variety of finishing materials, easily produces formaldehyde, benzene class and other indoor organic gas
Material TVOC overlying pollutions, improve indoor environment, and reduction finishing pollution is paid attention to by increasing people.
Diatom ooze is a kind of interior decoration wall material using diatomite as primary raw material, is made up of pure natural inorganic material, green
Colour circle is protected, and itself is without any pollution, free from extraneous odour.The nucleus of diatom ooze is diatomite.Diatomite is with SiO2Based on, light weight is dredged
Pine, density is 1.9~2.3g/mL, and specific surface area is 40~65m2/g.Diatomite is special porous construction, and rule is fitly
The micropore quantity being arranged in circular or aciculiform, its unit area is thousands of times of activated carbon.The molecular grating that diatomite is protruded
Its unique function of structures shape, makes it have extremely strong physical absorption and ion-exchange performance, extensively should after finishing
For fields such as functional coating, medicine filter aid, food additives, core radiation adsorbents.
In existing diatom ooze formula system, except conventional auxiliary additive, nano titanium oxide can be added toward contact
As photocatalyst catalyst, absorption is decomposed in diatom ooze surface or the organic molecule of endoporus;Or antibiotic bactericide, suppress
Bacterial growth.Diatomite is the nucleus of diatom ooze, but diatomite available diatomaceous earth products mistake from exploiting to being purified to
Often over high-temperature roasting in journey, on the one hand cause its specific surface area reduction (only 20-30m2/ g), under causing adsorption capacity significantly
Drop;On the other hand, high-temperature roasting causes the hydroxyl of diatomite microcosmic surface adjacent position to occur chemical dehydration, forms Si-O-
Si structures so that diatomite the adsorbed hydroxyl content is substantially reduced, thus also result in adsorption strength and adsorption capacity and and its
Corresponding reduction can also occur for the bond strength of its auxiliary material, and moisture absorption and damping ability are equally reduced.
In addition, diatomaceous pore size distribution range is mainly 50~3000nm, and the diameter of formaldehyde quasi-molecule is about
0.45nm, benzene quasi-molecule diameter is about 0.6nm.Therefore, most beneficial for the adsorbent of organic molecule in absorption finishing material
Pore size distribution range should be 1~2 nanometer, such material can the harmful substance such as PARA FORMALDEHYDE PRILLS(91,95), benzene class, TVOC accomplish to inhale with high selectivity
It is attached, and De contamination is less likely to occur.
In summary, this area diatomite material modified in the urgent need to developing, to improve the performances such as its absorption property.
The content of the invention
There is adjustable micropore distribution, high-ratio surface, high surface hydroxyl it is an object of the invention to provide a kind of environment-friendly type
The diatom ooze coating of the diatomite composition of content, high damping ability and high adsorption activity.
The first aspect of the present invention there is provided a kind of diatomite composition, including:
1-50 parts by weight diatomite;With
1-60 parts by weight column chromatography silica gels,
Wherein, the column chromatography silica gel includes A types silica gel, Type B silica gel and c-type silica gel, wherein the A types silica gel and Type B
The weight ratio of silica gel and c-type silica gel is 0.5-5:0.5-5:0.5-5.
In another preference, the diatomite composition includes:
5-30 parts by weight diatomite;With
1-40 parts by weight column chromatography silica gels.
In another preference, the diatomite composition includes:
5-25 or 10-20 parts by weight diatomite;With
10-40 or 15-30 parts by weight column chromatography silica gels.
In another preference, the column chromatography silica gel includes A types silica gel, Type B silica gel and c-type silica gel, wherein the A types
The weight ratio of silica gel and Type B silica gel and c-type silica gel is 1-2:1-2:1-2.
In another preference, the column chromatography silica gel includes A types silica gel, Type B silica gel and c-type silica gel, wherein the A types
The weight ratio of silica gel and Type B silica gel and c-type silica gel is 1-2:1-2:1-1.5.
In another preference, the A types silica gel weight accounts for the 20 weight %-60 weights of the column chromatography silica gel weight
Measure %, preferably 25 weight %-50 weight %.
In another preference, the Type B silica gel weight accounts for the 20 weight %-60 weights of the column chromatography silica gel weight
Measure %, preferably 25 weight %-50 weight %.
In another preference, the c-type silica gel weight accounts for the 20 weight %-40 weights of the column chromatography silica gel weight
Measure %, preferably 25 weight %-35 weight %.
In another preference, the aperture size of the A types silica gel is 2-3nm.
In another preference, the aperture size of the Type B silica gel is 4-7nm.
In another preference, the aperture size of the c-type silica gel is 8-10nm
In another preference, the diatomite composition has following one or more features:
(1) aperture size of the A types silica gel is 2.2-2.8nm;
(2) aperture size of the Type B silica gel is 4.5-6.5nm;
(3) dioxide-containing silica >=99% in the A types silica gel, preferably >=99.5%, more preferably >=99.9%;
(4) dioxide-containing silica >=99% in the Type B silica gel, preferably >=99.5%, more preferably >=99.9%;
(5) the adsorbed hydroxyl content of the A types silica gel is 5~10 SiOH nm-2;
(6) the adsorbed hydroxyl content of the Type B silica gel is 5~10 SiOH nm-2;
(7) the diatomaceous particle size range is 400-800 mesh;
(8) diatomaceous whiteness >=70;
(9) the adsorbed hydroxyl content of the diatomite composition is 1~10 SiOH nm-2;
(10) specific surface area of the diatomite composition is 200~600;
(11) aperture size of the c-type silica gel is 8.5-9.5nm;
(12) dioxide-containing silica >=99% in the c-type silica gel;
(13) the adsorbed hydroxyl content of the c-type silica gel is 5~10 SiOH nm-2。
The second aspect of the present invention there is provided a kind of diatom ooze coating, comprising the diatomite composition described in first aspect and
Auxiliary material.
In another preference, the auxiliary material is dry powder, sierozem power, kaolin, lignocellulosic, titanium dioxide light are touched
Matchmaker, redispersible latex powder and cellulose ether.
In another preference, the diatom ooze coating includes:
The dry powder of 0-50 parts by weight, the sierozem power of 5-30 parts by weight, the kaolin of 1-30 parts by weight, 0.5-2 parts by weight
Lignocellulosic, the titanium dioxide photocatalyst of 2-10 parts by weight, the redispersible latex powder of 1-5 parts by weight, 0.5-5 parts by weight
Cellulose ether.
In another preference, the diatom ooze coating includes:
The dry powder of 0-35 parts by weight, the sierozem power of 5-25 parts by weight, the kaolin of 5-25 parts by weight, 0.5-2 parts by weight
Lignocellulosic, the titanium dioxide photocatalyst of 2-8 parts by weight, the redispersible latex powder of 1-5 parts by weight, 0.5-3 parts by weight
Cellulose ether.
In another preference, the diatom ooze coating includes:
The dry powder of 20-40 parts by weight, the sierozem power of 5-25 parts by weight, the kaolin of 5-25 parts by weight, 0.8-1.5 weight
The lignocellulosic of part, the titanium dioxide photocatalyst of 3-7 parts by weight, the redispersible latex powder of 1-4 parts by weight, 0.5-2 weight
The cellulose ether of part.
In another preference, the diatom ooze coating includes:
Dry powder, the sierozem power of 10-15 parts by weight, the kaolin of 5-15 parts by weight, the 0.8-1.2 weights of 25-35 parts by weight
Measure the lignocellulosic, the titanium dioxide photocatalyst of 4-6 parts by weight, the redispersible latex powder of 2-4 parts by weight, 0.8-1.5 of part
The cellulose ether of parts by weight.
In another preference, the diatom ooze coating also has following one or more features:
(1) particle size range of the dry powder is 400-800 mesh, preferably 400-600 mesh, is more preferably 400-500
Mesh;
(2) particle size range of the sierozem power is 400-800 mesh, preferably 400-600 mesh, is more preferably 400-500
Mesh;
(3) particle size range of the titanium dioxide photocatalyst is 800-1200 mesh, preferably 800-1000 mesh, more preferably for
900-1000 mesh;
(4) the kaolinic particle size range is 800-1200 mesh, preferably 800-1000 mesh, is more preferably 900-
1000 mesh;
(5) redispersible latex powder is selected from the group:The copolymerization rubber powder of vinylacetate and ethene, vinylacetate
With ethene and higher aliphatic vinyl acetate ternary polymerization rubber powder, vinylacetate and higher aliphatic vinyl acetate copolymerization rubber powder, third
Olefin(e) acid ester and styrene copolymerized rubber powder, vinylacetate and acrylate and higher aliphatic vinyl acetate ternary polymerization rubber powder, vinegar
Vinyl acetate homopolymerization rubber powder, styrene is combined with one or more kinds of in butadiene copolymer rubber powder;More excellent selection is
The copolymerization rubber powder of vinylacetate and ethene;
(6) cellulose ether is selected from the group:Hydroxymethyl cellulose ether, hydroxyalkyl vinyl cellulose ether, hydroxypropyl methyl fiber
Plain ether or its combination;
(7) the lignocellulosic length range is 1-3mm, preferably 2-3mm.
There is provided the diatomite composition described in first aspect or the diatom ooze described in second aspect for the third aspect of the present invention
Coating application, be used for indoor ornamentation material.
The diatom ooze composition and diatom ooze coating of the present invention, the controllable, the adsorbed hydroxyl content of micropore distribution is high, specific surface area
Height, high adsorption capacity, damping ability is protruded, and can significantly improve the depollution of environment effect of diatom ooze wall material, temperature control effect and damping
Effect, has the advantages that cost is low, intensity is high, antistatic, absorption is strong.
It should be understood that within the scope of the present invention, above-mentioned each technical characteristic of the invention and have in below (eg embodiment)
It can be combined with each other between each technical characteristic of body description, so as to constitute new or preferred technical scheme.As space is limited, exist
This no longer tires out one by one states.
Brief description of the drawings
Fig. 1 is than surface test result figure.
Fig. 2 is graph of pore diameter distribution.
Fig. 3 is infrared spectrum structure chart.
Embodiment
The present inventor's in-depth study by extensive, is surprised to find that to add the abundant column chromatography silicon of surface hydroxyl first
Glue is into diatom ooze, by increasing capacitance it is possible to increase to the absorption property of organic molecule, especially to containing polar functional group (such as aldehyde, alcohol,
Acid, ester, sulphur etc.), and also have good adjustment effect to the wetting balance in surrounding air.This hair is completed on this basis
It is bright.
Term explanation
Unless otherwise defined, otherwise whole technologies used herein are respectively provided with such as art of the present invention with scientific terminology
The identical meanings that are generally understood that of those of ordinary skill.
As used herein, in use, term " about " means that the value can be from enumerating in the numerical value specifically enumerated is mentioned
Value, which changes, is not more than 1%.For example, as used herein, statement " about 100 " include 99 and 101 and between whole values (for example,
99.1st, 99.2,99.3,99.4,100.5 etc.).
As used herein, term " containing " or " including (including) " can be open, semi-enclosed and enclosed.Change
Yan Zhi, the term also include " substantially by ... constitute " or " by ... constitute ".
Column chromatography silica gel
Column chromatography silica gel is SiO2Content is up to more than 99% high-quality silica gel, and purity is high, safety and sanitation.It is main by shape
Colloidal particle into agglutinate structure is constituted.Colloidal particle is the condensation polymer of hydration status silica gel (multi-silicate), belongs to amorphous substance.
The micro hole structure that the gap of the aggregate of colloidal particle is formed inside reagent column chromatography silica gel particle.Therefore, column chromatography silica gel
Higher (the SiO of purity2Content is up to more than 99%), with more rich microcellular structure (average pore size 20-20000A ° can
In the range of control, the absorption of the material of heterogeneity, molecular weight and molecular structure is adapted to), specific surface area is high, about 300-
800m2The high-quality adsorption material of/g, the adsorbed hydroxyl content high (surface hydroxyl quantity is about diatomaceous 10 times) and high adsorption activity
Material.
In the present invention, column chromatography silica gel can be combined the core component as diatom ooze with diatomite, improve the suction of diatom ooze
Attached performance.
As used herein, diatomaceous particle size range is 400-800 mesh, preferably 400-600 mesh, is more preferably 400-
500 mesh.
As used herein, diatomaceous whiteness >=70, preferably >=80, more preferably >=90.
As used herein, " A types silica gel ", " pore column chromatography silica gel " have identical meanings, are used interchangeably, its titanium dioxide
Silicone content >=99%, preferably >=99.5%, more preferably >=99.9%, than surface 600-800m2/ g, aperture 2-3nm, mesh number
300-800 mesh, the adsorbed hydroxyl content:5~10 SiOH nm-2, 1.2 ten thousand/ton.
As used herein, " Type B silica gel ", " mesopore column chromatography silica gel " have identical meanings, are used interchangeably, its titanium dioxide
Silicone content >=99%, preferably >=99.5%, more preferably >=99.9%, than surface 400-600m2/ g, aperture 4-7nm, mesh number
300-800 mesh, the adsorbed hydroxyl content:5~10 SiOH nm-2, 1.2 ten thousand/ton.
As used herein, " c-type silica gel ", " macropore column chromatography silica gel " have identical meanings, are used interchangeably, its titanium dioxide
Silicone content >=99%, preferably >=99.5%, more preferably >=99.9%, than surface 300-400m2/ g, aperture 8-10nm, mesh number
300-800 mesh, the adsorbed hydroxyl content:5~10 SiOH nm-2, 1.2 ten thousand/ton.
Main advantages of the present invention are:
(1) diatomite composition and diatom ooze coating of the invention have high concentration of surface hydroxyl groups (column chromatography silica gel table
Face hydroxyl quantity is about 10 times of diatomite surface hydroxyl quantity), high-specific surface area, significantly improve absorption property, significantly carry
The adsorption capacity and damping ability of metope are risen, better clean-up effect, temperature control effect and damping effect can be obtained;
(2) diatomite composition and diatom ooze coating of the invention have pore, mesopore, the hole of macropore different stage, and
By controlling the proportionate relationship of diatomite and column chromatography silica gel to regulate and control the ratio in duct, varigrained powder accumulates shape
Into secondary duct at several to hundreds of nanometers, various various sizes of apertures can coexist, and be strengthened using different pore size size
To the absorption affinity of various sizes of organic molecule, suction-operated is played jointly;
(3) using the diatom ooze coating material coating metope of the present invention, cost is low, intensity is high, antistatic, adsorption capacity
It is high.
With reference to specific embodiment, the present invention is expanded on further.It should be understood that these embodiments are merely to illustrate the present invention
Rather than limitation the scope of the present invention.The experimental method of unreceipted actual conditions in the following example, generally according to conventional strip
Part, or according to the condition proposed by manufacturer.Unless otherwise indicated, otherwise percentage and number are percentage by weight and weight
Number.
Experiment material and reagent used can be obtained from commercially available channel unless otherwise instructed in following examples.
Universal method
In following examples and comparative example, purifying formaldehyde efficiency, purifying formaldehyde effect persistence, toluene purification efficiency, first
Benzene clean-up effect persistence is detected according to JC/T 1074-2008;
Hygroscopic capacity 24h and moisture releasing amount 24h are detected according to JC/T 2082-2011;
VOC VOC content, free formaldehyde, benzene toluene ethylbenzene dimethylbenzene summation, soluble heavy metal root
Detected according to GB 18582-2008.
Embodiment 1
Take 10 parts of diatomite, 10 parts of A types silica gel, 5 parts of Type B silica gel, 5 parts of c-type silica gel, 5 parts of kaolin, redispersible breast
3 parts of rubber powder, 1 part of lignocellulosic, 5 parts of titanium dioxide photocatalyst, 15 parts of sierozem power, 1 part of cellulose ether, 30 parts of dry powder, mixing
Add in powder stirring machine, be sufficiently stirred for 30-40 minutes after uniform, form pre-composition.
Above-mentioned pre-composition is mixed with water, until it is uniform, ash pulpous state diatom ooze coating is made.
Embodiment 2
Take 15 parts of diatomite, 10 parts of A types silica gel, 10 parts of Type B silica gel, 10 parts of c-type silica gel, 10 parts of kaolin, latex powder 3
Part, 1 part of wood-fibred, 5 parts of titanium dioxide photocatalyst, 15 parts of sierozem power, 1 part of cellulose ether, 25 parts of dry powder is added after being well mixed
In powder stirring machine, it is sufficiently stirred for 30-40 minutes, forms pre-composition.
Above-mentioned pre-composition is mixed with water, until it is uniform, ash pulpous state diatom ooze coating is made.
Than surface test result and graph of pore diameter distribution as depicted in figs. 1 and 2.The results of FT-IR is as shown in Figure 3.
The diatom ooze coating that can be seen that gained from Fig. 1, Fig. 2 is higher than surface, and pore size distribution range is in 2-8nm;From figure
3 as can be seen that 3402cm-1 wave numbers are mainly the water absworption peak of diatom ooze coating surface combination, 1091cm-1 ripples on infrared spectrum
Number is mainly the absworption peak of Si-OH in diatom ooze coating structure, and from above-mentioned figure, the diatom ooze coating is higher than surface, aperture
Distribution is moderate, can absorb many organic molecules;And substantial amounts of Si-OH is contained on surface, can fully damping, can strongly inhale again
Receive polarity organic molecule.
Embodiment 3
Take 20 parts of diatomite, 5 parts of A types silica gel, 5 parts of Type B silica gel, 5 parts of c-type silica gel, 15 parts of kaolin, 3 parts of latex powder, wood
1 part of fiber, 5 parts of titanium dioxide photocatalyst, 10 parts of sierozem power, 1 part of cellulose ether adds powder after 30 parts of dry powder is well mixed and stirred
Mix in machine, be sufficiently stirred for 30-40 minutes, form pre-composition.
Above-mentioned pre-composition is mixed with water, until it is uniform, ash pulpous state diatomite material is made.
Embodiment 4
Take 20 parts of diatomite, 5 parts of A types silica gel, 10 parts of Type B silica gel, 5 parts of c-type silica gel, 10 parts of kaolin, 3 parts of latex powder,
1 part of wood-fibred, 5 parts of titanium dioxide photocatalyst, 10 parts of sierozem power, 1 part of cellulose ether, 30 parts of dry powder adds powder after being well mixed
In body mixer, it is sufficiently stirred for 30-40 minutes, forms pre-composition.
Above-mentioned pre-composition is mixed with water, until it is uniform, ash pulpous state diatomite material is made.
The embodiment testing result of table 1
Comparative example 1-4:
Basic be the same as Example 1-4 is formulated, difference is, A+B+C column chromatography silica gels are substituted for the MCM-41 of equivalent
Mesopore molecular sieve.
The comparative example testing result of table 2
It can be seen that from the experimental result of Tables 1 and 2 (contrast experiment 1-4), although MCM-41 molecular sieves (>=42 ten thousand/ton)
In terms of toluene purifying rate and toluene purification persistence and the present invention diatom ooze almost indifference, but have benefited from the present invention
The abundant surface hydroxyl of the diatomite composition of addition, diatom ooze of the invention is to the purification efficiency of polar micromolecules formaldehyde and holds
Long property is significantly larger than contrast and experiment, and in terms of moisture absorption and humidity conditioning function, result of the invention is also significantly larger than contrasted
Experimental result.
All documents referred in the present invention are all incorporated as reference in this application, independent just as each document
It is incorporated as with reference to such.In addition, it is to be understood that after the above-mentioned instruction content of the present invention has been read, those skilled in the art can
To be made various changes or modifications to the present invention, these equivalent form of values equally fall within the model that the application appended claims are limited
Enclose.
Claims (10)
1. a kind of diatomite composition, it is characterised in that the diatomite composition includes:
1-50 parts by weight diatomite;With
1-60 parts by weight column chromatography silica gels,
Wherein, the column chromatography silica gel includes A types silica gel, Type B silica gel and c-type silica gel, wherein the A types silica gel and Type B silica gel
Weight ratio with c-type silica gel is 0.5-5:0.5-5:0.5-5.
2. diatomite composition as claimed in claim 1, it is characterised in that the aperture size of the c-type silica gel is 8-10nm.
3. diatomite composition as claimed in claim 1, it is characterised in that the aperture size of the A types silica gel is 2-3nm.
4. diatomite composition as claimed in claim 1, it is characterised in that the aperture size of the Type B silica gel is 4-7nm.
5. diatomite composition as claimed in claim 1, it is characterised in that the diatomite composition have with next or
Multiple features:
(1) aperture size of the A types silica gel is 2.2-2.8nm;
(2) aperture size of the Type B silica gel is 4.5-6.5nm;
(3) dioxide-containing silica >=99% in the A types silica gel;
(4) dioxide-containing silica >=99% in the Type B silica gel;
(5) the adsorbed hydroxyl content of the A types silica gel is 5~10 SiOH nm-2;
(6) the adsorbed hydroxyl content of the Type B silica gel is 5~10 SiOH nm-2;
(7) the diatomaceous particle size range is 400-800 mesh;
(8) diatomaceous whiteness >=70;
(9) the adsorbed hydroxyl content of the diatomite composition is 1~10 SiOH nm-2;
(10) specific surface area of the diatomite composition is 200~600;
(11) aperture size of the c-type silica gel is 8.5-9.5nm;
(12) dioxide-containing silica >=99% in the c-type silica gel;
(13) the adsorbed hydroxyl content of the c-type silica gel is 5~10 SiOH nm-2。
6. a kind of diatom ooze coating, it is characterised in that the diatom ooze coating includes the diatom described in claim any one of 1-5
Local soil type's compound and auxiliary material.
7. diatom ooze coating as claimed in claim 6, it is characterised in that the auxiliary material be dry powder, sierozem power, kaolin,
Lignocellulosic, titanium dioxide photocatalyst, redispersible latex powder and cellulose ether.
8. diatom ooze coating as claimed in claim 7, it is characterised in that the diatom ooze coating includes:
Dry powder, the sierozem power of 5-30 parts by weight, the kaolin of 1-30 parts by weight, the wood of 0.5-2 parts by weight of 0-50 parts by weight
Matter cellulose, the titanium dioxide photocatalyst of 2-10 parts by weight, the redispersible latex powder of 1-5 parts by weight, the fibre of 0.5-5 parts by weight
The plain ether of dimension.
9. diatom ooze coating as claimed in claim 7 or 8, it is characterised in that the diatom ooze coating also has with next
Or multiple features:
(1) particle size range of the dry powder is 400-800 mesh;
(2) particle size range of the sierozem power is 400-800 mesh;
(3) particle size range of the titanium dioxide photocatalyst is 800-1200 mesh;
(4) the kaolinic particle size range is 800-1200 mesh;
(5) redispersible latex powder is selected from the group:The copolymerization rubber powder of vinylacetate and ethene, vinylacetate and second
Alkene and higher aliphatic vinyl acetate ternary polymerization rubber powder, vinylacetate and higher aliphatic vinyl acetate copolymerization rubber powder, acrylic acid
Ester and styrene copolymerized rubber powder, vinylacetate and acrylate and higher aliphatic vinyl acetate ternary polymerization rubber powder, acetic acid second
Composition more than one or both of alkene ester homopolymerization rubber powder, styrene and butadiene copolymer rubber powder;
(6) cellulose ether is selected from the group:Hydroxymethyl cellulose ether, hydroxyalkyl vinyl cellulose ether, hydroxypropyl methyl cellulose ether,
Or its combination;
(7) the lignocellulosic length range is 1-3mm.
10. the diatom ooze coating application described in diatomite composition as claimed in claim 1 or claim 6, its feature exists
In be used for indoor ornamentation material.