CN107283271A - A kind of abrasive finishing method of fast growing wood - Google Patents
A kind of abrasive finishing method of fast growing wood Download PDFInfo
- Publication number
- CN107283271A CN107283271A CN201710625852.3A CN201710625852A CN107283271A CN 107283271 A CN107283271 A CN 107283271A CN 201710625852 A CN201710625852 A CN 201710625852A CN 107283271 A CN107283271 A CN 107283271A
- Authority
- CN
- China
- Prior art keywords
- parts
- sanding
- fast growing
- growing wood
- abrasive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention discloses a kind of abrasive finishing method of fast growing wood, including following operating procedure:(1)The spot on fast growing wood surface is removed, then sanding auxiliary agent is uniformly sprayed on its surface;(2)Any one in sanding processing, model 100#, 120#, 150# of sanding material used is carried out to fast growing wood using Disc sander, wherein the ground of sanding material used is cloth abrasive band, abrasive material used is made up of the component of following parts by weight:29 36 parts of brown corundum abrasive, 13 parts of antifungin, 47 parts of behenyl acid amides, 12 parts of iodooctadecane, the abrasive material is using on adhesive gluing and ground.The abrasive finishing method for the fast growing wood that the present invention is provided, it is simple to operate, it is with low cost, safe operation process environmental protection, the fast growing wood after sanding, surface impulse- free robustness is present, it is smooth, it is that follow-up application operation brings and greatly facilitated, during sanding, be not in the phenomenon of fast growing wood fracture, high yield rate.
Description
Technical field
The invention belongs to the processing technique field of fast growing wood, and in particular to a kind of abrasive finishing method of fast growing wood.
Background technology
Fast-growing wood species refers to fast growth, morning of becoming a useful person, the period of felling in turn short trees kind, and China common are deep gloomy Chinese scholartree, poplar
Tree, eucalyptus, willow etc., the timber being made up of these quick growing species of trees is fast growing wood, and usual quality is softer, is typically used as papermaking, builds
Build, sheet material core raw material etc., also there is part to be used to manufacture furniture, but all have to make timber some processing, wherein at sanding
Reason is exactly an important processing method in fast growing wood manufacture field.The sanding of fast growing wood refers to specific sanding tool and material
Expect that the concavo-convex situation to product surface, fiber duct are swelled or abnormal conditions carry out necessary grinding, sand milling, to remove aging portion
Divide and the uneven place of protuberance, fast growing wood surface is reached the process of flat smooth, good sanding can lay heavily fortified point for application
Real basis.
But fast growing wood is during actual sanding operation, due to the soft characteristic of the quality of fast growing wood, cause sanding
Effect is not notable, and the wood surface burr after sanding is still more, and fast growing wood is during sanding, easily has crackle
Phenomenon, causes percent defective higher, it is seen that it is poor that existing process for sanding carries out effect during sanding processing to fast growing wood.
The content of the invention
In order to solve the above problems, the present invention provides a kind of abrasive finishing method of fast growing wood.
The present invention is achieved by the following technical solutions.
A kind of abrasive finishing method of fast growing wood, including following operating procedure:
(1)The spot on fast growing wood surface is removed, then sanding auxiliary agent is uniformly sprayed on its surface, wherein sanding auxiliary agent is by following
The component of parts by weight is made:14-18 parts of m-trifluoromethylbenzoic acid methyl esters, to 10-15 parts of bromo-acid methyl esters, N- octyl group diaminos
8-12 parts of ethyl glycine hydrochloride, 20-30 parts of ethanol, 40-45 parts of water;
(2)Sanding processing, model 100#, 120#, 150# of sanding material used are carried out to fast growing wood using Disc sander
In any one, wherein the ground of sanding material used is cloth abrasive band, abrasive material used is made up of the component of following parts by weight:
29-36 parts of brown corundum abrasive, 1-3 parts of antifungin, 4-7 parts of behenyl acid amides, 1-2 parts of iodooctadecane, the abrasive material is using gluing
In agent gluing and ground.
Specifically, above-mentioned steps(1)The consumption of middle sanding auxiliary agent is that the usage amount of every square metre of timber is 300-400ml.
Specifically, above-mentioned adhesive is Arabic gum.
Technical scheme more than, the beneficial effects of the invention are as follows:
The abrasive finishing method for the fast growing wood that the present invention is provided, simple to operate, with low cost, safe operation process environmental protection, after sanding
Fast growing wood, surface impulse- free robustness is present, smooth, is that follow-up application operation brings and greatly facilitated, in the process of sanding
In, be not in the phenomenon of fast growing wood fracture, high yield rate.Wherein, the sanding auxiliary agent that the present invention is provided, can be carried in a short time
The hardness on the surface of raising speed greenwood so that fast growing wood is during sanding, and the wooden structures of fast growing wood will not be with sanding material
Bond, so as to occur the excessive phenomenon of burr;The abrasive material for the sanding material that the present invention is provided, both with higher hardness,
Sanding processing effectively can be carried out to fast growing wood, can guarantee that again during sanding, fast growing wood not caused to damage, will not made
The phenomenon that fast growing wood is broken, greatly improves yield rate.
Embodiment
Following examples are used to illustrate the present invention, but can not be used for limiting the scope of the present invention.The reality used in embodiment
The condition of applying can be for further adjustments according to the condition of producer, and unaccounted implementation condition is usually conventional laboratory conditions.
Embodiment 1
A kind of abrasive finishing method of fast growing wood, including following operating procedure:
(1)The spot on fast growing wood surface is removed, then sanding auxiliary agent is uniformly sprayed on its surface, wherein sanding auxiliary agent is by following
The component of parts by weight is made:It is 14 parts of m-trifluoromethylbenzoic acid methyl esters, sweet to 10 parts of bromo-acid methyl esters, N- octyl group diaminoethyls
8 parts of propylhomoserin hydrochloride, 20 parts of ethanol, 40 parts of water;
(2)Sanding processing, the model 100# of sanding material used, wherein sand used are carried out to fast growing wood using Disc sander
The ground of luminescent material is cloth abrasive band, and abrasive material used is made up of the component of following parts by weight:29 parts of brown corundum abrasive, antifungin 1
Part, 4 parts of behenyl acid amides, 1 part of iodooctadecane, the abrasive material is using on adhesive gluing and ground.
Specifically, above-mentioned steps(1)The consumption of middle sanding auxiliary agent is that the usage amount of every square metre of timber is 300ml.
Specifically, above-mentioned adhesive is Arabic gum.
Embodiment 2
A kind of abrasive finishing method of fast growing wood, including following operating procedure:
(1)The spot on fast growing wood surface is removed, then sanding auxiliary agent is uniformly sprayed on its surface, wherein sanding auxiliary agent is by following
The component of parts by weight is made:It is 16 parts of m-trifluoromethylbenzoic acid methyl esters, sweet to 13 parts of bromo-acid methyl esters, N- octyl group diaminoethyls
10 parts of propylhomoserin hydrochloride, 25 parts of ethanol, 43 parts of water;
(2)Sanding processing, the model 120# kinds of sanding material used, wherein used are carried out to fast growing wood using Disc sander
The ground of sanding material is cloth abrasive band, and abrasive material used is made up of the component of following parts by weight:33 parts of brown corundum abrasive, antifungin
2 parts, 6 parts of behenyl acid amides, 1 part of iodooctadecane, the abrasive material using adhesive it is glued with ground.
Specifically, above-mentioned steps(1)The consumption of middle sanding auxiliary agent is that the usage amount of every square metre of timber is 350ml.
Specifically, above-mentioned adhesive is Arabic gum.
Embodiment 3
A kind of abrasive finishing method of fast growing wood, including following operating procedure:
(1)The spot on fast growing wood surface is removed, then sanding auxiliary agent is uniformly sprayed on its surface, wherein sanding auxiliary agent is by following
The component of parts by weight is made:It is 18 parts of m-trifluoromethylbenzoic acid methyl esters, sweet to 15 parts of bromo-acid methyl esters, N- octyl group diaminoethyls
12 parts of propylhomoserin hydrochloride, 30 parts of ethanol, 45 parts of water;
(2)Sanding processing, the model 150# of sanding material used, wherein sand used are carried out to fast growing wood using Disc sander
The ground of luminescent material is cloth abrasive band, and abrasive material used is made up of the component of following parts by weight:36 parts of brown corundum abrasive, antifungin 3
Part, 7 parts of behenyl acid amides, 2 parts of iodooctadecane, the abrasive material is using on adhesive gluing and ground.
Specifically, above-mentioned steps(1)The consumption of middle sanding auxiliary agent is that the usage amount of every square metre of timber is 400ml.
Specifically, above-mentioned adhesive is Arabic gum.
Comparative example 1
Sanding auxiliary agent is waits the second alcohol and water of weight to be formulated, without m-trifluoromethylbenzoic acid methyl esters, to bromo-acid first
Ester, N- octyl group diaminoethyl glycine hydrochloride salt components, remaining operating procedure are identical with embodiment 1.
Comparative example 2
Without antifungin, behenyl acid amides, iodooctadecane composition in abrasive material, only contain brown corundum abrasive, remaining operating procedure
It is identical with embodiment 2.
Sanding processing, sanding are carried out to the fast growing wood of same breed with the method provided in each embodiment and comparative example respectively
The result of processing is as shown in table 1:
The fast growing wood sanding treatment effect of table 1
Project | Sanding treatment effect |
Embodiment 1 | Impulse- free robustness, surface is smooth, and yield rate is 98.8% |
Comparative example 1 | Burr is more, and surface is more smooth, and yield rate is 94.2% |
Embodiment 2 | Impulse- free robustness, surface is smooth, and yield rate is 99.1% |
Comparative example 2 | Burr is more, surface irregularity, and yield rate is 88.2% |
Embodiment 3 | Impulse- free robustness, surface is smooth, and yield rate is 99.8% |
As shown in Table 1, the sanding processing method for the fast growing wood that the present invention is provided, obtained fast growing wood surface impulse- free robustness is smooth flat
It is whole and yield rate is higher.
Certainly, described above is not limitation of the present invention, and the present invention is also not limited to the example above, the art
Those of ordinary skill, in the essential scope of the present invention, the change made, changes, addition or replace, should all belong to of the invention
Protection domain.
Claims (3)
1. a kind of abrasive finishing method of fast growing wood, it is characterised in that including following operating procedure:
(1)The spot on fast growing wood surface is removed, then sanding auxiliary agent is uniformly sprayed on its surface, wherein sanding auxiliary agent is by following
The component of parts by weight is made:14-18 parts of m-trifluoromethylbenzoic acid methyl esters, to 10-15 parts of bromo-acid methyl esters, N- octyl group diaminos
8-12 parts of ethyl glycine hydrochloride, 20-30 parts of ethanol, 40-45 parts of water;
(2)Sanding processing, model 100#, 120#, 150# of sanding material used are carried out to fast growing wood using Disc sander
In any one, wherein the ground of sanding material used is cloth abrasive band, abrasive material used is made up of the component of following parts by weight:
29-36 parts of brown corundum abrasive, 1-3 parts of antifungin, 4-7 parts of behenyl acid amides, 1-2 parts of iodooctadecane, the abrasive material is using gluing
In agent gluing and ground.
2. a kind of abrasive finishing method of fast growing wood according to claim 1, it is characterised in that step(1)Middle sanding auxiliary agent
Consumption be that the usage amount of every square metre of timber is 300-400ml.
3. the abrasive finishing method of a kind of fast growing wood according to claim 1, it is characterised in that above-mentioned adhesive is Arab
Glue.