CN107268915A - A kind of compound profile wall board and preparation method thereof - Google Patents
A kind of compound profile wall board and preparation method thereof Download PDFInfo
- Publication number
- CN107268915A CN107268915A CN201710381867.XA CN201710381867A CN107268915A CN 107268915 A CN107268915 A CN 107268915A CN 201710381867 A CN201710381867 A CN 201710381867A CN 107268915 A CN107268915 A CN 107268915A
- Authority
- CN
- China
- Prior art keywords
- layer
- wall board
- profile wall
- planar design
- compound profile
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of compound profile wall board and preparation method thereof, including backplane level and moulding layer, fireproof wear-resisting layer is also covered with described moulding layer.Described moulding layer includes three-dimensional contouring layer and planar design layer, and the planar design layer is covered in the top of three-dimensional contouring layer.Planar design layer can envelope completely above backplane level with gusset.The compound profile wall board of the present invention is aesthetic in appearance, and the moulding of solid can have both been designed as needed or marble or the pattern of wood grain can be presented on overall sheet material；The sheet material used uses composite layered board intensity height, light weight due to material；Wear-resisting fireprotection layer on surface spraying makes compound profile wall board texture such as marble slab glossy, also increases the abrasion resistance and flame retardant effect of sheet material, increases its feature used.
Description
Technical field
The present invention relates to compound dalle field, a kind of compound profile wall board and its preparation side are related in particular to
Method.
Background technology
In Decoration Industry, as the improvement of people's living standards, people have higher and finer for home decoration
The wall product such as demand, particularly television background wall, sofa background, bedroom background, theme metope, entry, study can be carried
For the finishing of different occasion different parts, the aesthetic requirement of people is met.But current background decorative wall uses marble slab
Or tile panel decoration is formed, but such marble slab or tile panel are expensive, and heavier-weight is not easy to install, and
Without three-dimensional shape-designing；Or background decorative wall uses such as notification number for the compound of the A of CN 102535799 Chinese patent
Type background wallboard, can be designed that the strong moulding of third dimension, but its backplane level can not design pattern and not be durable,
Surface, which is easily made dirty, to be scratched, also not fireproof wear-resisting, it is therefore desirable to existing compound background decorative wall panels are improved, with reference to Dali
Slabstone and the advantage of compound background wallboard, produce compound profile wall board a kind of not only elegant in appearance but also wear-resisting.
The content of the invention
The invention aims to the defect for solving the compound background wallboard in background technology, there is provided one kind is compound
Profile wall board and preparation method thereof.
To achieve these goals, technical scheme is as follows：The invention discloses a kind of compound profile wall board
And preparation method thereof, including backplane level and moulding layer is also covered with fireproof wear-resisting layer on described moulding layer.
Further, described moulding layer includes three-dimensional contouring layer and planar design layer, and the planar design layer is covered in
The top of three-dimensional contouring layer.
Further, planar design layer can envelope completely above backplane level with gusset.
The second object of the present invention is to provide a kind of compound profile wall board and preparation method thereof, comprises the following steps：
Step one：Mould is produced according to the moulding of product；
Step 2：By 45-90% modified PVC, 2-9% accelerator triethanolamines, 2-10% curing agent vinyl triamines,
10%-50% stone flour, is coated under die surface, normal temperature and pressure after stirring and solidifies 5-8 minutes；
Step 3：The above-mentioned modified PVC lines three-dimensional contouring layer being cured is covered on machine with backplane level in suction, temperature setting
At 30 °, handled 2-5 minutes using adhesive bonding；
Step 4：The above-mentioned PVC lines three-dimensional contouring layer being combined with backplane level is covered on machine with planar design layer in suction, temperature
Degree is when being arranged on 180 °, utilizes adhesive treatment 2-5 minutes；
Step 5：Sheet material after above-mentioned backplane level and moulding layer are compound, is coated with the side UV of planar design layer and contains
The fireproof wear-resisting layer of disilicon trioxide, alundum (Al2O3).
Further, described planar design layer is polyvinyl chloride resin film or heat transfer film.
Further, described backplane level is glass magnesium fiberboard or calcium silicate board plate, and its thickness is 1.5-2.5cm.
Further, described modified PVC is calcium silicates or calcium carbonate modified PVC.
Further, described adhesive is resins synthesis glue.
Further, in step 2：By 90% modified PVC, 3% accelerator, 3% curing agent, 4% stone flour is stirred
It is coated under die surface, normal temperature and pressure and solidifies 6 minutes after mixing uniformly.
The present invention has advantages below compared to background technology：The compound profile wall board of the present invention is aesthetic in appearance, both can be with
Marble or the pattern of wood grain can be also presented on overall sheet material by designing the moulding of solid as needed；The sheet material used by
In use composite layered board intensity height, the light weight of material；Wear-resisting fireprotection layer on surface spraying makes compound profile wall board
Texture is glossy such as marble slab, also increases the abrasion resistance and flame retardant effect of sheet material, increases its feature used.
Brief description of the drawings
Fig. 1 is the structural representation of compound profile wall board of the invention；
Wherein：1- backplane levels；2- three-dimensional contourings layer；3- planar designs layer；4- wearing layers.
Embodiment
Below in conjunction with drawings and examples, the technical scheme in the present invention is clearly and completely described.Based on this hair
Embodiment in bright, the every other implementation that those of ordinary skill in the art are obtained under the premise of creative work is not made
Example, belongs to the scope of protection of the invention.
Embodiment 1：
Also covered on a kind of compound profile wall board and preparation method thereof, including backplane level 1 and moulding layer, described moulding layer
Wear-resisting fireprotection layer 4 is stamped, described moulding layer includes three-dimensional contouring layer 2 and planar design layer 3, and the planar design layer 3 is covered
On the top of three-dimensional contouring layer 2, planar design layer 3 can envelope completely above backplane level 1 with gusset.
The compound profile wall board and preparation technology it is as follows：
(1) mould is produced according to the moulding of product；
(2) by 90% modified PVC, 3% accelerator triethanolamine, 3% curing agent vinyl triamine, 4% stone flour is stirred
It is coated under die surface, normal temperature and pressure and solidifies 6 minutes after mixing uniformly, modified PVC is calcium silicates modified PVC.
(3) the above-mentioned modified PVC lines three-dimensional contouring layer being cured is covered on machine with backplane level in suction, temperature setting exists
At 30 °, handled 4 minutes using adhesive bonding, described adhesive is resins synthesis glue, described backplane level is fine for calcium silicates
Plate is tieed up, thickness is 2cm.
(4) the above-mentioned PVC lines three-dimensional contouring layer being combined with backplane level is covered on machine with planar design layer in suction, temperature is set
Put at 180 °, using adhesive treatment 4 minutes, described adhesive was resins synthesis glue.
(5) sheet material after above-mentioned backplane level and moulding layer are compound, is coated with the side abnormity UV of planar design layer and contains
The fireproof wear-resisting layer of disilicon trioxide, alundum (Al2O3).
Embodiment 2：
On a kind of structure and its manufacture method of compound mould board, including backplane level 1 and moulding layer, described moulding layer
Fireproof wear-resisting layer 4 is also covered with, described moulding layer includes three-dimensional contouring layer 2 and planar design layer 3, the planar design layer 3
Be covered in the top of three-dimensional contouring layer 2, planar design layer 3 can envelope completely above backplane level 1 with gusset.
The preparation technology of the compound mould board is as follows：
(1) mould is produced according to the moulding of product；
(2) by 90% modified PVC, 3% accelerator triethanolamine, 3% curing agent vinyl triamine, 4% stone flour is stirred
It is coated under die surface, normal temperature and pressure and solidifies 6 minutes after mixing uniformly, modified PVC is calcium carbonate modified PVC.
(3) the above-mentioned modified PVC lines three-dimensional contouring layer being cured is covered on machine with backplane level in suction, temperature setting exists
At 30 °, handled 4 minutes using adhesive bonding, described adhesive is resins synthesis glue, described backplane level is glass magnesium fiber
Plate, thickness is 2cm.
(4) the above-mentioned PVC lines three-dimensional contouring layer being combined with backplane level is covered on machine with planar design layer in suction, temperature is set
Put at 180 °, using adhesive treatment 4 minutes, described adhesive was resins synthesis glue.
(5) sheet material after above-mentioned backplane level and moulding layer are compound, is coated with containing three oxygen in the special-shaped UV of planar design layer
Change the fireproof wear-resisting layer of two silicon, alundum (Al2O3).
The compound decorative wall panels of the present invention, moulding layer is compound for planar design layer 3 and three-dimensional contouring layer 2, can both design
Go out the strong space pattern of various shapes third dimension, can show anti-marble grain in planar design layer 3 again or set the plane of line
Modelling pattern；Three-dimensional contouring layer 2 is synthesis type PVC lines, specially calcium silicates modified PVC or calcium carbonate modified PVC, makes conjunction
It is molded PVC lines toughness to strengthen, moulding is more three-dimensional plentiful；Also abnormity UV is coated with containing disilicon trioxide, three on moulding layer
The fireproof wear-resisting layer of Al 2 O, this coating is free of penetrating odor and harmless, is sprayed with the special-shaped UV modes sprayed
Apply uniform, the fireproof wear-resisting layer 4 of formation can prevent from being scratched damage when composite decorative wall plate from using and with certain fire prevention
Fire resistance；Backplane level is using the glass magnesium fiberboard or calcium silicate board that thickness is 1.5-2.5cm, and this board quality is light, intensity
Height, and more common marble decorative boards price also bottom；Backplane level 1, three-dimensional contouring layer 2, the compound of planar design layer 3 all make
Covered and completed on machine in suction with resins synthesis glue, synthesis mode is simple and easy to apply, and each layer of resins synthesis glue bond used makes respectively
It is tightly combined between layer, is difficult degumming deformation.
General principle, principal character and the advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and that described in above-described embodiment and specification is the present invention
Principle, various changes and modifications of the present invention are possible without departing from the spirit and scope of the present invention, these change and
Improvement is both fallen within the range of claimed invention.The protection domain of application claims by appended claims and its
Equivalent is defined.
Claims (9)
1. a kind of compound profile wall board, including backplane level (1) and moulding layer, it is characterised in that：Also covered on described moulding layer
It is stamped fireproof wear-resisting layer (4).
2. a kind of compound profile wall board according to claim 1, it is characterised in that：Described moulding layer is made including solid
Type layer (2) and planar design layer (3), the planar design layer (3) are covered in the top (2) of three-dimensional contouring layer.
3. a kind of compound profile wall board according to claim 1, it is characterised in that：The planar design layer (3) can be complete
It is complete envelope above backplane level (1) with gusset.
4. a kind of a kind of any one of claims 1-3 preparation methods of compound profile wall board, it is characterised in that including
Following steps：
Step one：Mould is produced according to the moulding of product；
Step 2：By 45-90% modified PVC, 2-9% accelerator triethanolamines, 2-10% curing agent vinyl triamines,
10%-50% stone flour, is coated under die surface, normal temperature and pressure after stirring and solidifies 5-8 minutes；
Step 3：The above-mentioned modified PVC lines three-dimensional contouring layer (2) being cured is covered on machine with backplane level (1) in suction, temperature is set
Put at 30 °, handled 2-5 minutes using adhesive bonding；
Step 4：The above-mentioned PVC lines three-dimensional contouring layer (2) being combined with backplane level (1) is covered into machine with planar design layer (3) in suction
On, temperature setting is handled 2-5 minutes at 180 ° by adhesive bonding；
Step 5：Sheet material after above-mentioned backplane level (1) and moulding layer are compound, in the side abnormity UV sprays of planar design layer (3)
The fireproof wear-resisting layer (4) containing disilicon trioxide, alundum (Al2O3) is scribbled, total coating weight is more than or equal to 80g/m2。
5. described in planar design layer (3) be polyvinyl chloride resin film or heat transfer film.
6. a kind of preparation method of compound profile wall board according to claim 4, it is characterised in that：Described backplane level
(1) it is glass magnesium fiberboard or calcium silicate board plate, its thickness is 1.5-2.5cm.
7. a kind of preparation method of compound profile wall board according to claim 4, it is characterised in that：Described modified PVC
For calcium silicates or calcium carbonate modified PVC.
8. a kind of preparation method of compound profile wall board according to claim 4, it is characterised in that：Described adhesive is
Resins synthesis glue.
9. a kind of preparation method of compound profile wall board according to claim 4, it is characterised in that：In step 2：Will
90% modified PVC, 3% accelerator, 3% curing agent, 4% stone flour is coated in die surface, normal temperature and pressure after stirring
Lower solidification 6 minutes.