CN107267090A - A kind of cellulose acetate cigarette tipping paper is with connecing mouth glue - Google Patents
A kind of cellulose acetate cigarette tipping paper is with connecing mouth glue Download PDFInfo
- Publication number
- CN107267090A CN107267090A CN201710554017.5A CN201710554017A CN107267090A CN 107267090 A CN107267090 A CN 107267090A CN 201710554017 A CN201710554017 A CN 201710554017A CN 107267090 A CN107267090 A CN 107267090A
- Authority
- CN
- China
- Prior art keywords
- tipping paper
- cellulose acetate
- mouth glue
- cigarette tipping
- glue
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of cellulose acetate cigarette tipping paper with connecing mouth glue, it is characterised in that be made up of the raw material of following percentage by weight：VAE emulsions 70 90% and additive 10% 30%, the additive includes：Polyvinyl alcohol 3.6 3.7%, 2, 2, 4 trimethyls 1, 3 pentanediol diisobutyrates 1 1.2%, glyceryl triacetate 0.8 1%, epoxidized soybean oil 1 1.1%, triethyl citrate 0.7 0.8%, ester gum 3 3.8%, polyalcohol hydrogenated wood rosin glycerol ester 2.5 3.1%, guar gum 0.5 0.7%, dimethyl silicone polymer 0.1 0.2%, White Mineral Oil 0.1 0.2%, 1, 2 benzisothia oxazolyl 3 (2H) ketone 0.002 0.003%, 2 methyl 3 (2H) OITs 0.001 0.002%, the ketone 0.001 0.002% of 5 chlorine, 2 methyl 2H isothiazolines 3 and water 4 4.3%；This kind of cellulose acetate cigarette tipping paper has environmental protection, the characteristic without boric acid with mouth glue is connect, while having excellent wet sticky, upper machine stability and can make the characteristics of machines clean is run.
Description
Technical field
Mouth glue technical field is connect the present invention relates to a kind of cigarette tipping paper, more particularly to a kind of cellulose acetate cigarette tipping
Paper is with connecing mouth glue.
Background technology
Tipping paper is a kind of volume smoking material, for the outer wrapping of cigarette filter tip, connects mouth glue and plays bonding filter tip, cigarette
The effect of branch and tipping paper.
The development of domestic tobacco business has driven the development of related raw and auxiliary material, new material, new technology answering on cigarette
With higher requirement is proposed to cigarette glue, wherein cellulose acetate cigarette tipping paper is exactly one, and cellulose acetate cigarette is with connecing
Fill paper is with the difference of original cigarette tipping paper：The tipping paper is made up of cellulose acetate, and common tipping paper is natural plants
Fiber process is formed；The tipping paper surface is smooth, transparent or semitransparent shape is presented, such as plastic sheeting shape, and fiber is fine and close, and this connects
Fill paper and now big with the contact angle of common water base adhesive, and water base adhesive is difficult to infiltrate through in paper, thus adhesive is proposed
Very high requirement.
The problem of now being run into water base adhesive when being bonded cellulose acetate cigarette tipping paper：Machine operating speed it is very low or
It can not be bonded, when machine operating speed is slightly higher, the phenomenons such as bad rubbing, bubble wrinkle and gas leakage can be produced；Secondly, glue is waited after bonding
After being completely dried, tipping paper is also easy to produce buckling phenomena, and this is due to permeate uneven and paper after such a technique tipping paper gluing
Hardness it is big, cause what tipping paper deformation was caused during glue dries.
The content of the invention
There is environmental protection, the characteristic without boric acid the technical problem to be solved in the present invention is to provide a kind of, while having excellent
Wet sticky, upper machine stability and the cellulose acetate cigarette tipping paper that machines clean is run can be made with connecing mouth glue.
To solve the above problems, the present invention is adopted the following technical scheme that：
A kind of cellulose acetate cigarette tipping paper is made up with mouth glue is connect of the raw material of following percentage by weight：VAE emulsions 70-
90% and additive 10%-30%, the additive includes polyvinyl alcohol 3.6-3.7%, 2,2,4- trimethyls -1,3- penta 2
Alcohol diisobutyrate 1-1.2%, glyceryl triacetate 0.8-1%, epoxidized soybean oil 1-1.1%, triethyl citrate 0.7-
0.8%th, ester gum 3-3.8%, polyalcohol hydrogenated wood rosin glycerol ester 2.5-3.1%, guar gum 0.5-0.7%, poly dimethyl silicon
Oxygen alkane 0.1-0.2%, (2H) -one 0.002-0.003%, the 2- methyl -3 of White Mineral Oil 0.1-0.2%, 1,2- benzisothia oxazolyl -3
(2H)-OIT 0.001-0.002%, 5- chloro-2-methyl -2H- isothiazolines -3- ketone 0.001-0.002% and water 4-
4.3%.
Further, the glass transition temperature of the VAE emulsions is 0 DEG C -20 DEG C, and solid content is 50%-60%.
Further, the polyvinyl alcohol alcoholysis degree is 80-90%, degree of polymerization 500-2000.
Further, the cellulose acetate cigarette tipping paper is applied to connecing for cellulose acetate cigarette tipping paper with mouth glue is connect
Be filled with and roller coating gluing cigarette machine.
Further, the cellulose acetate cigarette tipping paper is with connecing mouth glue, with the use of cellulose acetate cigarette tipping paper,
Filter stick, plume, that is, make and obtain a complete cigarette.
The invention solves the problems that another technical problem to provide a kind of preparation of cellulose acetate cigarette tipping paper with mouth glue is connect
Method, comprises the following steps：
1) water intaking 4-4.3% is put into stirred tank, is started stirring, is then taken polyvinyl alcohol 3.6-3.7% to be slowly added to
In stirred tank, 5-10min is stirred with 80-120r/min speed, is well mixed polyethylene alcohol and water, then be heated to
85-90 DEG C, and this temperature 2h is kept, normal temperature is finally naturally cooled to, is discharged, polyvinyl alcohol water solution is made, it is standby；
2) take VAE emulsions 70-90% to be put into stirred tank, start stirring, poly- diformazan is then slowly added into stirred tank
Radical siloxane 0.1-0.2% and White Mineral Oil 0.1-0.2%, stirs 13-15min with 80-120r/min speed, adds step
1) polyvinyl alcohol water solution made from, continues to stir 25-30min with 80-120r/min speed, the first mixed material is made,
It is standby；
3) 2,2,4- trimethyl -1,3- pentanediol diisobutyrates 1-1.2%, glyceryl triacetate 0.8-1%, epoxy are taken
Soybean oil 1-1.1% and triethyl citrate 0.7-0.8% are added to step 2) made from the first mixed material, with 80-
120r/min speed stirring 0.8-1h, then adds ester gum 3-3.8%, polyalcohol hydrogenated wood rosin glycerol ester 2.5-
3.1% and guar gum 0.5-0.7%, continues to stir 0.8-1h with 80-120r/min speed, the second mixed material is made, standby
With；
4) (the 2H)-OIT of -3 (2H) -one 0.002-0.003%, 2- methyl of 1,2- benzisothias oxazolyl -3 is taken
0.001-0.002% and 5- chloro-2-methyl -2H- isothiazoline -3- ketone 0.001-0.002% is added to step 3) made from
In two mixed materials, 25-30min is stirred with 80-120r/min speed, the 3rd mixed material is made, it is standby；
5) by step 4) made from the 3rd mixed material viscosity regulation to setting scope discharging, produce the present invention vinegar
Acid cellulose cigarette tipping paper is with connecing mouth glue.
The beneficial effects of the invention are as follows：The present invention is applied to the tipping of cellulose acetate tipping paper, it is adaptable to roller coating gluing
Cigarette equipment, equipment includes：Protos 70, Protos 1-8, Protos 90E, the Protos 2-2 of German Hao Ni companies；
The GD-121 of Italian GD companies；The PASSIM 7000 and 8000 of handkerchief Lyceum company of Britain；Changde Yan Ji Co., Ltds
ZJ17, ZJ112, ZJ116 and ZJ118, the present invention use cooperatively cellulose acetate cigarette tipping paper, filter stick, plume, that is, are made to
To a complete cigarette, of the invention this connects mouth glue and meets relevant regulations of the tobacco business to water base cigarette glue, original to connect mouth
Glue Dichlorodiphenyl Acetate cellulose cigarette tipping paper is difficult wetting, and glue is very big to the contact angle of the tipping paper, and glue is difficult on tipping paper surface
Sprawled；By the adjusting and optimizing to formula, cellulose acetate tipping paper of the invention is connect with mouth glue Dichlorodiphenyl Acetate cellulose is connect
Dress paper can be good at wetting, and contact angle diminishes, makes bonding more firm, connect mouth glue compared to original, the cellulose acetate
Tipping paper is bigger with the wet viscous force for connecing mouth glue so that after tipping paper gluing, before glue is unseasoned, can also make tipping paper and filter tip
There is good bonding force, so as to ensure that the operation of machine；Cellulose acetate tipping paper use connects the anti-shear ability of mouth glue more
By force, under high shear, disk roller band glue is stable, and glue does not occur to splash, whirl coating, and gluing is uniform, and the cellulose acetate tipping paper is with connecing
Faster, after glue is dried, particle is harder, it is easy to brushed by the brush on machine from tipping paper cutter and drum for mouth glue rate of drying
Fall, so as to ensure that the clean run of machine.
Embodiment
Embodiment 1
A kind of cellulose acetate cigarette tipping paper is made up with mouth glue is connect of the raw material of following percentage by weight：VAE emulsions
81.2% and additive 18.8%, the additive includes trimethyl -1, the 3- pentanediol two of polyvinyl alcohol 3.6%, 2,2,4-
Isobutyrate 1.2%, glyceryl triacetate 0.8%, epoxidized soybean oil 1%, triethyl citrate 0.8%, ester gum
3.8%th, polyalcohol hydrogenated wood rosin glycerol ester 2.5%, guar gum 0.5%, dimethyl silicone polymer 0.1%, White Mineral Oil 0.2%, 1,2-
Benzisothia oxazolyl -3 (2H) -one 0.003%, 2- methyl -3 (2H)-OIT 0.001%, 5- chloro-2-methyls -2H- are different
Thiazoline -3- ketone 0.001% and water 4.3%.
A kind of cellulose acetate cigarette tipping paper preparation method for connecing mouth glue, comprises the following steps：
1) water intaking 4.3% is put into stirred tank, is started stirring, is then taken polyvinyl alcohol 3.6% to be slowly added to stirred tank
In, 10min is stirred with 120r/min speed, polyethylene alcohol and water is well mixed, then 90 DEG C are heated to, and keep this
Temperature 2h, is finally naturally cooled to normal temperature, discharging, and polyvinyl alcohol water solution is made, standby；
2) take VAE emulsions 81.2% to be put into stirred tank, start stirring, poly dimethyl is then slowly added into stirred tank
Siloxanes 0.1% and White Mineral Oil 0.2%, stir 15min with 120r/min speed, add step 1) made from polyvinyl alcohol
The aqueous solution, continues to stir 30min with 120r/min speed, the first mixed material is made, standby；
3) 2,2,4- trimethyl -1,3- pentanediol diisobutyrates 1.2%, glyceryl triacetate 0.8%, epoxy soybean are taken
Oil 1% and triethyl citrate 0.8% are added to step 2) made from the first mixed material, stirred with 120r/min speed
1h, then adds ester gum 3.8%, polyalcohol hydrogenated wood rosin glycerol ester 2.5% and guar gum 0.5%, continues with 120r/
Min speed stirring 1h, is made the second mixed material, standby；
4) 1,2- benzisothias oxazolyl -3 (2H) -one 0.003%, 2- methyl -3 (2H)-He of OIT 0.001% are taken
5- chloro-2-methyl -2H- isothiazoline -3- ketone 0.001% is added to step 3) made from the second mixed material, with 120r/
Min speed stirring 30min, is made the 3rd mixed material, standby；
5) by step 4) made from the 3rd mixed material viscosity regulation to 5520, discharging, the acetic acid for producing the present invention is fine
The plain cigarette tipping paper of dimension is with connecing mouth glue.
Preferably, the glass transition temperature of VAE emulsions is 10 DEG C in the present embodiment, solid content is 50%.
Preferably, polyvinyl alcohol alcoholysis degree is 80%, the degree of polymerization 2000 in the present embodiment.
The conventional index that mouth glue is connect in the embodiment of the present invention 1 is as follows：
| Conventional detection project | Testing result |
| Outward appearance | White uniformity emulsion |
| Viscosity (25 DEG C, RVT4#, mpas) | 5520 |
| Evaporate residue (%) | 52.7 |
| PH value | 4.4 |
Embodiment 2
A kind of cellulose acetate cigarette tipping paper is made up with mouth glue is connect of the raw material of following percentage by weight：VAE emulsions
81.4% and additive 18.6%, the additive includes trimethyl -1, the 3- pentanediol two of polyvinyl alcohol 3.7%, 2,2,4-
It is isobutyrate 1%, glyceryl triacetate 1%, epoxidized soybean oil 1%, triethyl citrate 0.8%, ester gum 3%, many
First alcohol hydrogenated wood rosin glycerol ester 3.1%, guar gum 0.7%, dimethyl silicone polymer 0.1%, White Mineral Oil 0.2%, 1,2- benzisothias
Oxazolyl -3 (2H) -one 0.003%, 2- methyl -3 (2H)-OIT 0.001%, 5- chloro-2-methyl -2H- isothiazolines -
3- ketone 0.001% and water 4%.
A kind of cellulose acetate cigarette tipping paper preparation method for connecing mouth glue, comprises the following steps：
1) water intaking 4% is put into stirred tank, is started stirring, is then taken polyvinyl alcohol 3.7% to be slowly added in stirred tank,
10min is stirred with 80r/min speed, polyethylene alcohol and water is well mixed, then is heated to 85 DEG C, and keeps this temperature
2h, is finally naturally cooled to normal temperature, discharging, and polyvinyl alcohol water solution is made, standby；
2) take VAE emulsions 81.4% to be put into stirred tank, start stirring, poly dimethyl is then slowly added into stirred tank
Siloxanes 0.1% and White Mineral Oil 0.2%, stir 15min with 80r/min speed, add step 1) made from polyvinyl alcohol
The aqueous solution, continues to stir 30min with 80r/min speed, the first mixed material is made, standby；
3) 2,2,4- trimethyl -1,3- pentanediol diisobutyrates 1%, glyceryl triacetate 1%, epoxidized soybean oil are taken
1% and triethyl citrate 0.8% be added to step 2) made from the first mixed material, 1h is stirred with 80r/min speed,
Then ester gum 3%, polyalcohol hydrogenated wood rosin glycerol ester 3.1% and guar gum 0.7% are added, is continued with 80r/min speed
Degree stirring 1h, is made the second mixed material, standby；
4) 1,2- benzisothias oxazolyl -3 (2H) -one 0.003%, 2- methyl -3 (2H)-He of OIT 0.001% are taken
5- chloro-2-methyl -2H- isothiazoline -3- ketone 0.001% is added to step 3) made from the second mixed material, with 80r/min
Speed stirring 30min, be made the 3rd mixed material, it is standby；
5) by step 4) made from the 3rd mixed material viscosity regulation to 5340, discharging, the acetic acid for producing the present invention is fine
The plain cigarette tipping paper of dimension is with connecing mouth glue.
Preferably, the glass transition temperature of VAE emulsions is 20 DEG C in the present embodiment, solid content is 60%.
Preferably, polyvinyl alcohol alcoholysis degree is 90%, the degree of polymerization 1000 in the present embodiment.
The conventional index that mouth glue is connect in the embodiment of the present invention 2 is as follows：
| Conventional detection project | Testing result |
| Outward appearance | White uniformity emulsion |
| 25 DEG C of viscosity, RVT4#, mpas) | 5340 |
| Evaporate residue (%) | 52.9 |
| PH value | 4.3 |
The beneficial effects of the invention are as follows：The present invention is applied to the tipping of cellulose acetate tipping paper, it is adaptable to roller coating gluing
Cigarette equipment, equipment includes：Protos 70, Protos 1-8, Protos 90E, the Protos 2-2 of German Hao Ni companies；
The GD-121 of Italian GD companies；The PASSIM 7000 and 8000 of handkerchief Lyceum company of Britain；Changde Yan Ji Co., Ltds
ZJ17, ZJ112, ZJ116 and ZJ118, the present invention use cooperatively cellulose acetate cigarette tipping paper, filter stick, plume, that is, are made to
To a complete cigarette, the present invention meets relevant regulations of the tobacco business to water base cigarette glue, original to connect mouth glue Dichlorodiphenyl Acetate
Cellulose cigarette tipping paper is difficult wetting, and glue is very big to the contact angle of the tipping paper, and glue is difficult to be sprawled on tipping paper surface；
By the adjusting and optimizing to formula, cellulose acetate tipping paper of the invention with connect mouth glue Dichlorodiphenyl Acetate cellulose tipping paper can be very
Good wetting, contact angle diminishes, makes bonding more firm, mouth glue is connect compared to original, and the cellulose acetate tipping paper is with connecing
The wet viscous force of mouth glue is bigger so that after tipping paper gluing, before glue is unseasoned, tipping paper and filter tip can also had viscous well
Relay, so as to ensure that the operation of machine；The cellulose acetate tipping paper is stronger with the anti-shear ability for connecing mouth glue, in high shear
Under, disk roller band glue is stable, and glue does not occur to splash, whirl coating, and gluing is uniform, and the cellulose acetate tipping paper is with connecing mouth glue rate of drying
Faster, after glue is dried, particle is harder, it is easy to brush from tipping paper cutter and drum by the brush on machine, so as to ensure
The clean run of machine.
The foregoing is only a specific embodiment of the invention, but protection scope of the present invention is not limited thereto, any
The change or replacement expected without creative work, should all cover and be defined in the new protection domain of this practicality.
Claims (4)
1. a kind of cellulose acetate cigarette tipping paper is with connecing mouth glue, it is characterised in that be made up of the raw material of following percentage by weight：
VAE emulsions 70-90% and additive 10%-30%, the additive includes polyvinyl alcohol 3.6-3.7%, 2,2,4- front threes
Base -1,3- pentanediol diisobutyrates 1-1.2%, glyceryl triacetate 0.8-1%, epoxidized soybean oil 1-1.1%, citric acid three
It is ethyl ester 0.7-0.8%, ester gum 3-3.8%, polyalcohol hydrogenated wood rosin glycerol ester 2.5-3.1%, guar gum 0.5-0.7%, poly-
Dimethyl siloxane 0.1-0.2%, (2H) the -one 0.002-0.003% of White Mineral Oil 0.1-0.2%, 1,2- benzisothia oxazolyl -3,
2- methyl -3 (2H)-OIT 0.001-0.002%, 5- chloro-2-methyl -2H- isothiazoline -3- ketone 0.001-
0.002% and water 4-4.3%.
2. a kind of cellulose acetate cigarette tipping paper as claimed in claim 1 is with connecing mouth glue, it is characterised in that：The VAE emulsions
Glass transition temperature be 0 DEG C -20 DEG C, solid content is 50%-60%.
3. a kind of cellulose acetate cigarette tipping paper as claimed in claim 1 is with connecing mouth glue, it is characterised in that：The polyvinyl alcohol
Alcoholysis degree is 80-90%, degree of polymerization 500-2000.
4. a kind of cellulose acetate cigarette tipping paper as claimed in claim 1 is with connecing mouth glue, it is characterised in that：The acetate fiber
The plain cigarette tipping paper cigarette machine for connecing mouth glue suitable for tipping and the roller coating gluing of cellulose acetate cigarette tipping paper.