CN107265923A - A kind of high impact toughness artificial quartz stone plate - Google Patents

A kind of high impact toughness artificial quartz stone plate Download PDF

Info

Publication number
CN107265923A
CN107265923A CN201710634356.4A CN201710634356A CN107265923A CN 107265923 A CN107265923 A CN 107265923A CN 201710634356 A CN201710634356 A CN 201710634356A CN 107265923 A CN107265923 A CN 107265923A
Authority
CN
China
Prior art keywords
parts
artificial quartz
high impact
stone plate
quartz stone
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710634356.4A
Other languages
Chinese (zh)
Inventor
沈建美
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nantong Goya Stone Industry Co Ltd
Original Assignee
Nantong Goya Stone Industry Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nantong Goya Stone Industry Co Ltd filed Critical Nantong Goya Stone Industry Co Ltd
Priority to CN201710634356.4A priority Critical patent/CN107265923A/en
Publication of CN107265923A publication Critical patent/CN107265923A/en
Pending legal-status Critical Current

Abstract

The present invention relates to a kind of high impact toughness artificial quartz stone plate, fraction proportioning by weight is made up of following components:62 84 parts of particulate material;Broken 28 42 parts of aggregate;41 56 parts of compound;71 82 parts of water reducer;12 parts of coupling agent;3 16 parts of unsaturated-resin;12 15 parts of adhesive;0.3 6 parts of pigment;43 60 parts of plastic flakes;0.8 2 parts of curing agent;20 38 parts of silica flour;0.35 0.5 parts of auxiliary agent.The advantage of the invention is that:The artificial quartz stone plate of the present invention has high impact-resistant toughness, the problems such as solving artificial quartz in lump cracking, deform, product of the invention, in testing, the sheet material center for being 250mm*250mm*15mm from more than 200cm height free-falling impact specification with 1kg solid steel balls, rupture is not produced.

Description

A kind of high impact toughness artificial quartz stone plate
Technical field
The present invention relates to stone material field, more particularly to a kind of high impact toughness artificial quartz stone plate.
Background technology
Artificial quartz in lump belongs to fragility polymer composite, and it has extremely strong acidproof, corrosion-resistant, wear-resistant, resistance to height The characteristics such as temperature.The formula of prior art manufacture artificial quartz in lump is mainly quartz, silica flour and the hardened shaping of resin collocation After formed.Because artificial quartz in lump also has the characteristic expanded with heat and contract with cold simultaneously, it there is certain shrinkage stress, impact flexibility, break The mechanical properties such as elongation are split, the artificial quartz in lump manufactured by the formula and technology of production synthetic quartz is also existed at present Defect, particularly impact flexibility be not good, when material bears the internal stress brought because expanding with heat and contract with cold, or the external impact power being subject to When, material is easily cracking, deformation.Therefore, it is necessary to provide it is a kind of have high impact toughness, be difficult the artificial of craze and transfiguration Quartzite slate.
The content of the invention
The technical problem to be solved in the present invention is to provide a kind of high impact toughness synthetic quartz for being less prone to cracking, deforming Stone slab.
In order to solve the above technical problems, the technical scheme is that:A kind of high impact toughness artificial quartz stone plate, its Innovative point is:Fraction proportioning by weight is made up of following components:
62-84 parts of particulate material;
Broken aggregate 28-42 parts;
41-56 parts of compound;
71-82 parts of water reducer;
1-2 parts of coupling agent;
3-16 parts of unsaturated-resin;
12-15 parts of adhesive;
0.3-6 part of pigment;
43-60 parts of plastic flakes;
0.8-2 parts of curing agent;
20-38 parts of silica flour;
0.35-0.5 part of auxiliary agent.
Further, the unsaturated-resin is unsaturated polyester resin.
Further, described auxiliary agent is the mixture of silane coupler and peroxide -2-ethyl hexanoic acid tert-butyl, described The part by weight of silane coupler and peroxide -2-ethyl hexanoic acid tert-butyl is 4: 1.
The advantage of the invention is that:The stone material formula of the present invention, artificial quartz stone plate of the invention has high impact-resistant Toughness, solve artificial quartz in lump cracking, deformation the problems such as, product of the invention, in testing, with 1kg solid steel balls from More than 200cm height free-falling impact specification is 250mm*250mm*15mm sheet material center, and rupture is not produced.
Cost is low, makes simple, weight matters, adds water reducer, can also effectively draining, addition grinding aid modification if raining Material, has obstructed the self deterioration and the osmotic absorption to unsaturated-resin of raw material so that absorption of the raw material to unsaturated-resin The consumption of main influence sheet deformation and the unsaturated-resin of aging in formula is substantially reduced, greatly reduces, so as to improve The intensity of sheet material, greatly reduces production cost, is unlikely to deform the sheet material produced, non-aging.
Embodiment
The following examples can make professional and technical personnel that the present invention is more fully understood, but therefore not send out this It is bright to be limited among described scope of embodiments.
Embodiment 1
The high impact toughness artificial quartz stone plate of present invention fraction proportioning by weight is made up of following components:
62 parts of particulate material;
Broken 28 parts of aggregate;
41 parts of compound;
71 parts of water reducer;
1 part of coupling agent;
3 parts of unsaturated-resin;
12 parts of adhesive;
0.3 part of pigment;
43 parts of plastic flakes;
0.8 part of curing agent;
20 parts of silica flour;
0.35 part of auxiliary agent.
Auxiliary agent is the mixture of silane coupler and peroxide -2-ethyl hexanoic acid tert-butyl, silane coupler and peroxidating- The part by weight of the 2 ethyl hexanoic acid tert-butyl ester is 4: 1.
Embodiment 2
The high impact toughness artificial quartz stone plate of present invention fraction proportioning by weight is made up of following components:
84 parts of particulate material;
Broken 42 parts of aggregate;
56 parts of compound;
82 parts of water reducer;
2 parts of coupling agent;
16 parts of unsaturated-resin;
15 parts of adhesive;
6 parts of pigment;
60 parts of plastic flakes;
2 parts of curing agent;
38 parts of silica flour;
0.5 part of auxiliary agent.
Auxiliary agent is the mixture of silane coupler and peroxide -2-ethyl hexanoic acid tert-butyl, silane coupler and peroxidating- The part by weight of the 2 ethyl hexanoic acid tert-butyl ester is 4: 1.
Embodiment 3
The high impact toughness artificial quartz stone plate of present invention fraction proportioning by weight is made up of following components:
73 parts of particulate material;
Broken 34 parts of aggregate;
48 parts of compound;
77 parts of water reducer;
1 part of coupling agent;
8 parts of unsaturated-resin;
13 parts of adhesive;
3 parts of pigment;
52 parts of plastic flakes;
1.2 parts of curing agent;
29 parts of silica flour;
0.43 part of auxiliary agent.
Auxiliary agent is the mixture of silane coupler and peroxide -2-ethyl hexanoic acid tert-butyl, silane coupler and peroxidating- The part by weight of the 2 ethyl hexanoic acid tert-butyl ester is 4: 1.
The artificial quartz stone plate of the present invention has high impact-resistant toughness, solves artificial quartz in lump cracking, deformation etc. and asks Topic, product of the invention, in testing, impacting specification from more than 200cm height free-falling with 1kg solid steel balls is 250mm*250mm*15mm sheet material center, rupture is not produced.
Cost is low, makes simple, weight matters, adds water reducer, can also effectively draining, addition grinding aid modification if raining Material, has obstructed the self deterioration and the osmotic absorption to unsaturated-resin of raw material so that absorption of the raw material to unsaturated-resin The consumption of main influence sheet deformation and the unsaturated-resin of aging in formula is substantially reduced, greatly reduces, so as to improve The intensity of sheet material, greatly reduces production cost, is unlikely to deform the sheet material produced, non-aging.
It should be understood by those skilled in the art that, the present invention is not limited to the above embodiments, above-described embodiment and explanation Merely illustrating the principles of the invention described in book, without departing from the spirit and scope of the present invention, the present invention also have Various changes and modifications, these changes and improvements all fall within the protetion scope of the claimed invention.The claimed scope of the invention By appended claims and its equivalent thereof.

Claims (3)

1. a kind of high impact toughness artificial quartz stone plate, it is characterised in that:Fraction proportioning by weight is made up of following components:
62-84 parts of particulate material;
Broken aggregate 28-42 parts;
41-56 parts of compound;
71-82 parts of water reducer;
1-2 parts of coupling agent;
3-16 parts of unsaturated-resin;
12-15 parts of adhesive;
0.3-6 part of pigment;
43-60 parts of plastic flakes;
0.8-2 parts of curing agent;
20-38 parts of silica flour;
0.35-0.5 part of auxiliary agent.
2. high impact toughness artificial quartz stone plate according to claim 1, it is characterised in that:The unsaturated-resin is Unsaturated polyester resin.
3. high impact toughness artificial quartz stone plate according to claim 1, it is characterised in that:Described auxiliary agent is silane The mixture of coupling agent and peroxide -2-ethyl hexanoic acid tert-butyl, the silane coupler and the tertiary fourth of peroxidating -2 ethyl hexanoic acid The part by weight of ester is 4: 1.
CN201710634356.4A 2017-07-29 2017-07-29 A kind of high impact toughness artificial quartz stone plate Pending CN107265923A (en)