CN107254213A - A kind of water nano orange pigment - Google Patents
A kind of water nano orange pigment Download PDFInfo
- Publication number
- CN107254213A CN107254213A CN201710614538.5A CN201710614538A CN107254213A CN 107254213 A CN107254213 A CN 107254213A CN 201710614538 A CN201710614538 A CN 201710614538A CN 107254213 A CN107254213 A CN 107254213A
- Authority
- CN
- China
- Prior art keywords
- water
- mill base
- nano
- glycerine
- glue
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of water nano orange pigment, it is made up of the raw material below according to mass percent：Yellow nanometer mill base 15 20%, red nano mill base 10 15%, diethylene glycol (DEG) 3 7%, glycerine 3 7%, antioxidant 5 10%, quick dry agent 8 12%, glue 10 15%, crosslinking agent 3 7%, adhesion promoter 2 4%, surplus is pure water.The present invention is reacted by the chemical combination of all of above raw material, a kind of orange color can be showed, its bright-coloured degree and fine and smooth precision exceed known any printing effect, and the surfaces such as PET, PVC, acrylic can be attached to easily without any coating, water paint of the present invention is thick after having printed only common can need to easily to dissolve the pattern on its surface once drop water, and the present invention also has feature soluble in water.
Description
Technical field
The present invention relates to pigment technology field, specifically a kind of water nano orange pigment.
Background technology
Pigment (Pigment) is used for the powdered substance coloured.It is insoluble in the media such as water, grease, resin, organic solvent
Solution, but can equably disperse in these media and medium can be coloured, and with certain covering power.Pigment is that manufacture is applied
The indispensable raw materials such as material, ink, oil painting color, make-up paint, colored paper.It is also used for plastics, rubber and conjunction
Into the filling and coloring of fiber stoste etc..At present on the market, the pigment and printing being commonly used are used PVC, PET and Asia gram
The equipment pigment such as power, is all that comparison is inferior, and the thing printed is all easy decolouring and chromatograph is more, stigma easily occurs
Point and color be not bright-coloured, and pigment on the market is essentially all water insoluble pigment, can only individually reconcile and can be only achieved
Desired part effect.
The content of the invention
It is an object of the invention to provide a kind of water nano orange pigment, with solve pigment occur in use coating,
The problems such as coarse and not bright-coloured color.
To achieve the above object, the present invention provides following technical scheme：
A kind of water nano orange pigment, is made up of the raw material below according to mass percent：Yellow nanometer mill base 15-
20%th, red nano mill base 10-15%, diethylene glycol (DEG) 3-7%, glycerine 3-7%, antioxidant 5-10%, quick dry agent 8-12%,
Glue 10-15%, crosslinking agent 3-7%, adhesion promoter 2-4%, surplus is pure water.
It is used as further scheme of the invention：The water nano orange pigment, by below according to the original of mass percent
Material composition：It is Yellow nanometer mill base 17-19%, red nano mill base 11-13%, diethylene glycol (DEG) 4-6%, glycerine 4-6%, anti-oxidant
Agent 7-9%, quick dry agent 9-11%, glue 11-13%, crosslinking agent 4-6%, adhesion promoter 2-4%, surplus is pure water.
It is used as further scheme of the invention：The water nano orange pigment, by below according to the original of mass percent
Material composition：Yellow nanometer mill base 18%, red nano mill base 12%, diethylene glycol (DEG) 5%, glycerine 5%, antioxidant 8%, quick-drying
Agent 10%, glue 12%, crosslinking agent 5%, adhesion promoter 3%, pure water 22%.
It is used as further scheme of the invention：The water nano orange pigment, by Yellow nanometer mill base, red nano color
Slurry, diethylene glycol (DEG), glycerine, antioxidant, quick dry agent, glue, crosslinking agent, adhesion promoter, pure water are well mixed after weighing
Produce.
Compared with prior art, the beneficial effects of the invention are as follows：
The present invention is mainly by Yellow nanometer mill base, red nano mill base, diethylene glycol (DEG), glycerine, antioxidant, quick-drying
Agent, glue, crosslinking agent, adhesion promoter, pure water composition, relative ratio are modulated by the effect of needs desired to reach
Effect.Reacted by above all of chemical combination, a kind of orange color can be showed by special printing device, its
Bright-coloured degree and fine and smooth precision exceed known any printing effect, and without any coating can be attached to easily PET,
The surfaces such as PVC, acrylic, PET, PVC and the uncoated printing effect of acryl surface are currently global problem, for now
The scrappage of accurate silk-screen reaches more than four one-tenth, and water paint of the present invention after having printed it is thick only need it is common can be easily once drop water
The pattern on its surface is dissolved, so the present invention also has feature soluble in water, therefore water nano orange pigment is named as.
Embodiment
Below in conjunction with the embodiment of the present invention, the technical scheme in the embodiment of the present invention is clearly and completely described,
Obviously, described embodiment is only a part of embodiment of the invention, rather than whole embodiments.Based in the present invention
Embodiment, the every other embodiment that those of ordinary skill in the art are obtained under the premise of creative work is not made, all
Belong to the scope of protection of the invention.
Embodiment 1
In the embodiment of the present invention, a kind of water nano orange pigment is made up of the raw material below according to mass percent：It is yellow
Color nano color paste 15%, red nano mill base 10%, diethylene glycol (DEG) 3%, glycerine 3%, antioxidant 5%, quick dry agent 8%, glue
Water 10%, crosslinking agent 3%, adhesion promoter 2%, surplus is pure water.
By Yellow nanometer mill base, red nano mill base, diethylene glycol (DEG), glycerine, antioxidant, quick dry agent, glue, crosslinking
Agent, adhesion promoter, pure water are well mixed after weighing and produced.
Embodiment 2
In the embodiment of the present invention, a kind of water nano orange pigment is made up of the raw material below according to mass percent：It is yellow
Color nano color paste 20%, red nano mill base 15%, diethylene glycol (DEG) 7%, glycerine 7%, antioxidant 10%, quick dry agent 12%,
Glue 15%, crosslinking agent 7%, adhesion promoter 4%, surplus is pure water.
By Yellow nanometer mill base, red nano mill base, diethylene glycol (DEG), glycerine, antioxidant, quick dry agent, glue, crosslinking
Agent, adhesion promoter, pure water are well mixed after weighing and produced.
Embodiment 3
In the embodiment of the present invention, a kind of water nano orange pigment is made up of the raw material below according to mass percent：It is yellow
Color nano color paste 17%, red nano mill base 11%, diethylene glycol (DEG) 4%, glycerine 4%, antioxidant 7%, quick dry agent 9%, glue
Water 11%, crosslinking agent 4%, adhesion promoter 2%, surplus is pure water.
By Yellow nanometer mill base, red nano mill base, diethylene glycol (DEG), glycerine, antioxidant, quick dry agent, glue, crosslinking
Agent, adhesion promoter, pure water are well mixed after weighing and produced.
Embodiment 4
In the embodiment of the present invention, a kind of water nano orange pigment is made up of the raw material below according to mass percent：It is yellow
Color nano color paste 19%, red nano mill base 13%, diethylene glycol (DEG) 6%, glycerine 6%, antioxidant 9%, quick dry agent 11%, glue
Water 13%, crosslinking agent 6%, adhesion promoter 4%, surplus is pure water.
By Yellow nanometer mill base, red nano mill base, diethylene glycol (DEG), glycerine, antioxidant, quick dry agent, glue, crosslinking
Agent, adhesion promoter, pure water are well mixed after weighing and produced.
Embodiment 5
In the embodiment of the present invention, a kind of water nano orange pigment is made up of the raw material below according to mass percent：It is yellow
Color nano color paste 18%, red nano mill base 12%, diethylene glycol (DEG) 5%, glycerine 5%, antioxidant 8%, quick dry agent 10%, glue
Water 12%, crosslinking agent 5%, adhesion promoter 3%, pure water 22%.
By Yellow nanometer mill base, red nano mill base, diethylene glycol (DEG), glycerine, antioxidant, quick dry agent, glue, crosslinking
Agent, adhesion promoter, pure water are well mixed after weighing and produced.
Embodiment 6
In the embodiment of the present invention, a kind of water nano orange pigment is made up of the raw material below according to mass percent：It is yellow
Color nano color paste 16%, red nano mill base 14%, diethylene glycol (DEG) 6%, glycerine 4%, antioxidant 9%, quick dry agent 9%, glue
Water 14%, crosslinking agent 4%, adhesion promoter 2%, surplus is pure water.
By Yellow nanometer mill base, red nano mill base, diethylene glycol (DEG), glycerine, antioxidant, quick dry agent, glue, crosslinking
Agent, adhesion promoter, pure water are well mixed after weighing and produced.
Embodiment 7
In the embodiment of the present invention, a kind of water nano orange pigment is made up of the raw material below according to mass percent：It is yellow
Color nano color paste 19%, red nano mill base 11%, diethylene glycol (DEG) 4%, glycerine 6%, antioxidant 6%, quick dry agent 11%, glue
Water 11%, crosslinking agent 6%, adhesion promoter 4%, surplus is pure water.
By Yellow nanometer mill base, red nano mill base, diethylene glycol (DEG), glycerine, antioxidant, quick dry agent, glue, crosslinking
Agent, adhesion promoter, pure water are well mixed after weighing and produced.
Embodiment 8
In the embodiment of the present invention, a kind of water nano orange pigment is made up of the raw material below according to mass percent：It is yellow
Color nano color paste 19%, red nano mill base 12%, diethylene glycol (DEG) 4%, glycerine 5%, antioxidant 7%, quick dry agent 10%, glue
Water 11%, crosslinking agent 5%, adhesion promoter 3%, surplus is pure water.
By Yellow nanometer mill base, red nano mill base, diethylene glycol (DEG), glycerine, antioxidant, quick dry agent, glue, crosslinking
Agent, adhesion promoter, pure water are well mixed after weighing and produced.
Embodiment 9
In the embodiment of the present invention, a kind of water nano orange pigment is made up of the raw material below according to mass percent：It is yellow
Color nano color paste 18%, red nano mill base 11%, diethylene glycol (DEG) 5%, glycerine 6%, antioxidant 8%, quick dry agent 11%, glue
Water 12%, crosslinking agent 6%, adhesion promoter 3%, surplus is pure water.
By Yellow nanometer mill base, red nano mill base, diethylene glycol (DEG), glycerine, antioxidant, quick dry agent, glue, crosslinking
Agent, adhesion promoter, pure water are well mixed after weighing and produced.
The present invention not only solves the demand to high-end product dyestuff, the color come is dyed for product not only and its fresh
Gorgeous, and can debug concentration according to desired color demand, conventional dyestuff applies on electronic correlation product not only color
Color dim but also relatively rough, the present invention solves this problem with regard to straightforward, dyes the high-end product come not only color
It is bright-coloured and uncoated on coloured silk, it is most important that coating of the present invention is also soluble in water.
It is obvious to a person skilled in the art that the invention is not restricted to the details of above-mentioned one exemplary embodiment, Er Qie
In the case of without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter
From the point of view of which point, embodiment all should be regarded as exemplary, and be nonrestrictive, the scope of the present invention is by appended power
Profit is required rather than described above is limited, it is intended that all in the implication and scope of the equivalency of claim by falling
Change is included in the present invention.
Moreover, it will be appreciated that although the present specification is described in terms of embodiments, not each embodiment is only wrapped
Containing an independent technical scheme, this narrating mode of specification is only that for clarity, those skilled in the art should
Using specification as an entirety, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
It may be appreciated other embodiment.
Claims (4)
1. a kind of water nano orange pigment, it is characterised in that be made up of the raw material below according to mass percent：Yellow nanometer
Mill base 15-20%, red nano mill base 10-15%, diethylene glycol (DEG) 3-7%, glycerine 3-7%, antioxidant 5-10%, quick dry agent
8-12%, glue 10-15%, crosslinking agent 3-7%, adhesion promoter 2-4%, surplus is pure water.
2. water nano orange pigment according to claim 1, it is characterised in that by below according to the original of mass percent
Material composition：It is Yellow nanometer mill base 17-19%, red nano mill base 11-13%, diethylene glycol (DEG) 4-6%, glycerine 4-6%, anti-oxidant
Agent 7-9%, quick dry agent 9-11%, glue 11-13%, crosslinking agent 4-6%, adhesion promoter 2-4%, surplus is pure water.
3. water nano orange pigment according to claim 1, it is characterised in that by below according to the original of mass percent
Material composition：Yellow nanometer mill base 18%, red nano mill base 12%, diethylene glycol (DEG) 5%, glycerine 5%, antioxidant 8%, quick-drying
Agent 10%, glue 12%, crosslinking agent 5%, adhesion promoter 3%, pure water 22%.
4. according to any described water nano orange pigments of claim 1-3, it is characterised in that by Yellow nanometer mill base, red
After color nano color paste, diethylene glycol (DEG), glycerine, antioxidant, quick dry agent, glue, crosslinking agent, adhesion promoter, pure water are weighed
It is well mixed to produce.