CN107245880A - A kind of processing method of feather dress fabric anti-chiseling down - Google Patents
A kind of processing method of feather dress fabric anti-chiseling down Download PDFInfo
- Publication number
- CN107245880A CN107245880A CN201710180178.2A CN201710180178A CN107245880A CN 107245880 A CN107245880 A CN 107245880A CN 201710180178 A CN201710180178 A CN 201710180178A CN 107245880 A CN107245880 A CN 107245880A
- Authority
- CN
- China
- Prior art keywords
- fabric
- processing method
- chiseling down
- feather dress
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of processing method of feather dress fabric anti-chiseling down, this method have selected the fabric that soft mercerized cotton crease-resistant, that frivolous intensity is high is made, the water repellent finishing agent compounded using silica and zinc octoate carries out water repellent processing to it, the softness and glossiness of fabric are kept by high pressure friction glazing again, pass through the coating of modified coating glue, the feather dress fabric fabric improves the anti-chiseling down effect of down jackets with relatively low weightening, and cold resistance, softness are improved.
Description
Technical field
The present invention relates to weaving face fabric processing technique field, and in particular to a kind of processing side of feather dress fabric anti-chiseling down
Method.
Background technology
Today's society, filling class textile has turned into popular, down products (including down jackets, eiderdown quilt etc.) it is even more to turn into
Indispensable daily necessities in people's daily life, due to its soft comfortable, warmth retention property it is good, it is light the features such as it is deep by big
Many likes, but at present, asking for suede is bored because many reasons cause such textile to occur in the production and use process
Topic, not only have impact on overall outward appearance, and the staple got out disorderly flies to give people uncomfortable sensation.And have fabric and stand out from one's fellows
Anti-chiseling down performance, common method has two kinds：One is as far as possible to improve the density of fabric, becomes highly dense woven face
Material, although however, highly dense weaving face fabric is with the foregoing anti-chiseling down performance stood out from one's fellows, gas permeability effect extreme difference；Two are
First fabric press polish is handled during the Final finishing expected over there, sizing material then is applied to trowel finish by glue spreader, sizing material is oozed
Arrive thoroughly in web surface formation glued membrane after the hole of fabric, last drying, to prevent eider down from scurrying out.
Authorization Notice No. CN102433743B patent discloses a kind of processing method of down-proof fabric, and this method includes
Final finishing step, Final finishing step includes water-sprinkling step, calendaring step and baking step, and water-sprinkling step is to contain fabric tying-in
The water-sprinkling groove of functional compounding agent solution, and when going out water-sprinkling groove to fabric mangle, calendaring step be will go out water-sprinkling groove and
Fabric face press polish after mangle, baking step is, by the fabric drying after press polish, to obtain down-proof fabric.The fabric
Anti-chiseling down effect is good, also improves cold-resistant and tear-resistant effect, reference is provided for the technique of anti-chiseling down.
The content of the invention
It is an object of the invention to overcome above-mentioned the deficiencies in the prior art, there is provided a kind of processing of feather dress fabric anti-chiseling down
Method, this method is coated using coating adhesive to the fabric after water resistant, calendering, reaches combining closely for fabric and coating adhesive,
The anti-chiseling down effect of down jackets is improved with relatively low weightening, and cold resistance, softness are improved.
The present invention solves technical problem and adopted the following technical scheme that：
The invention provides a kind of processing method of feather dress fabric anti-chiseling down, comprise the following steps：
（1）Fabric is selected：Select the woven fabric of mercerized cotton, yarn count 15D-25D, fineness 300-420tex；
（2）Water repellent finish：Fabric is put into the tank for fill water repellent finishing agent and impregnated 15-30 minutes, is dried after taking-up to water
Divide content 5-8%；
（3）Calendering：Fabric after water repellent finish, which is passed through in calender, carries out friction glazing, wherein, pressure 10-12Mpa, calender
The ratio between the surface linear speed of friction roller and the translational speed of fabric are 4:1-6:1, the temperature of friction roller is 115-125 DEG C, then will
Fabric drying is to moisture 2-3%；
（4）The preparation of coating adhesive：Polyimide coating glue is mixed with ethyl propionate, is sufficiently stirred for making polyimide coating glue complete
In fully dissolved, solution feeding autoclave, crosslinking agent, crosslinking accelerator, diallyl dimethyl ammoniumchloride, Tween-80 are added,
Nitrogen is filled with to pressure 1-2Mpa, temperature is increased to 40-50 DEG C, stirring reaction is cooled to room temperature after 1-1.5 hours, adds first
Benzene adjusts the viscosity of reactant to 6000-8000mPa/s, obtains coating adhesive；
（5）Coating：The coating adhesive prepared is coated on the fabric after calendering using floating blade coating machine, in 150-160 DEG C
Dry 3-5 minutes.
Preferably, the step（2）Water repellent finishing agent by 20-30 parts by weight silica and 0.5-0.8 parts by weight
Zinc octoate is mixed 20-30 minutes at normal temperatures, and 150-160 DEG C of baking is obtained.
Preferably, the step（2）Dry condition is 50-60 DEG C and dried 10-30 minutes.
Preferably, the step（3）The translational speed of fabric is controlled in 15-18 m/min.
Preferably, the step（4）Middle polyimide coating glue, crosslinking agent, crosslinking accelerator, diallyl dimethyl
Ammonium chloride, the weight ratio of Tween-80 are 1: 0.2-0.4: 0.06-0.3: 0.05-0.12: 0.15-0.25.
Preferably, the step（4）Crosslinking agent is selected from di-isopropylbenzene hydroperoxide, hexahydrophthalic anhydride, many isocyanides
One kind or any two or more combination in acid esters, hydroxyethyl methacrylate, DAAM.
Preferably, the step（4）Crosslinking accelerator is selected from AH100, W-T501, XH-H0221Z, XH-H2202Z, 550
In one kind or any two or more combination.
Preferably, the step（5）The dry weightening of fabric is 3-5g/m after coating2。
Compared with prior art, the present invention has following beneficial effect：
（1）The feather dress fabric anti-chiseling down processing method of the present invention, have selected the soft crease-resistant, mercerized cotton that frivolous intensity is high first
The fabric being made, the water repellent finishing agent compounded using silica and zinc octoate carries out water repellent processing to it, then is rubbed by high pressure
Softness and glossiness that calendering keeps fabric are wiped, passes through the coating of modified coating glue so that the feather dress fabric fabric is with relatively low
Weightening improve the anti-chiseling down effects of down jackets, and cold resistance, softness are improved.
（2）The coating adhesive that the present invention is used coating adhesive based on polyimide coating glue, adds excellent anti acid alkali performance
Cationic polymer diallyl dimethyl ammoniumchloride, intermolecular bridging action of line style crosslinking agent, crosslinking promote
Agent, the nonionic surface active agent of moist type, modified coating adhesive have good caking property, resistance to acids and bases, resistance to thermal resistance
Combustion property, is adapted to a variety of coating bondings for spinning cloth or fabric.
Embodiment
Invention is described in further detail below in conjunction with specific embodiment.
Embodiment 1.
A kind of processing method of feather dress fabric anti-chiseling down, comprises the following steps：
（1）Fabric is selected：Select the woven fabric of mercerized cotton, yarn count 15D-25D, fineness 300-420tex；
（2）Water repellent finish：Fabric is put into the tank for fill water repellent finishing agent and impregnated 15-30 minutes, is dried after taking-up to water
Divide content 5-8%, wherein, water repellent finishing agent is by the silica of 20-30 parts by weight and the zinc octoate of 0.5-0.8 parts by weight normal
Temperature is lower to be mixed 20-30 minutes, and 150-160 DEG C of baking is obtained, and dry condition is dried 10-30 minutes for 50-60 DEG C.
（3）Calendering：Fabric after water repellent finish, which is passed through in calender, carries out friction glazing, wherein, pressure 10-12Mpa rolls
The ratio between the surface linear speed of ray machine friction roller and the translational speed of fabric are 4:1-6:1, the temperature of friction roller is 115-125 DEG C, so
Afterwards by fabric drying to moisture 2-3%, wherein, the translational speed of fabric is controlled in 15-18 m/min.
（4）The preparation of coating adhesive：50 parts of polyimide coating glues are mixed with ethyl propionate, are sufficiently stirred for making polyimides
Coating adhesive is completely dissolved, in solution feeding autoclave, add 15 parts of di-isopropylbenzene hydroperoxides, 5 parts of crosslinking accelerator W-T501,
3 parts of diallyl dimethyl ammoniumchlorides, 8 parts of Tween-80s, are filled with nitrogen to pressure 1-2Mpa, temperature is increased to 40-50 DEG C,
After stirring reaction 1-1.5 hours, room temperature is cooled to, toluene is added and adjusts the viscosity of reactant to 6000-8000mPa/s, obtain
To coating adhesive；
（5）Coating：The coating adhesive prepared is coated on the fabric after calendering using floating blade coating machine, in 150-160 DEG C
Dry 3-5 minutes, the dry weightening of fabric is 3-5g/m after coating2。
Embodiment 2.
A kind of processing method of feather dress fabric anti-chiseling down, comprises the following steps：
（1）Fabric is selected：Select the woven fabric of mercerized cotton, yarn count 15D-25D, fineness 300-420tex；
（2）Water repellent finish：Fabric is put into the tank for fill water repellent finishing agent and impregnated 15-30 minutes, is dried after taking-up to water
Divide content 5-8%, wherein, water repellent finishing agent is by the silica of 20-30 parts by weight and the zinc octoate of 0.5-0.8 parts by weight normal
Temperature is lower to be mixed 20-30 minutes, and 150-160 DEG C of baking is obtained, and dry condition is dried 10-30 minutes for 50-60 DEG C.
（3）Calendering：Fabric after water repellent finish, which is passed through in calender, carries out friction glazing, wherein, pressure 10-12Mpa rolls
The ratio between the surface linear speed of ray machine friction roller and the translational speed of fabric are 4:1-6:1, the temperature of friction roller is 115-125 DEG C, so
Afterwards by fabric drying to moisture 2-3%, wherein, the translational speed of fabric is controlled in 15-18 m/min.
（4）The preparation of coating adhesive：60 parts of polyimide coating glues are mixed with ethyl propionate, are sufficiently stirred for making polyimides
Coating adhesive is completely dissolved, and in solution feeding autoclave, adds 18 parts of hexahydrophthalic anhydrides, 6 parts of crosslinking accelerator XH-
H0221Z, 5 parts of diallyl dimethyl ammoniumchlorides, 12 parts of Tween-80s, are filled with nitrogen to pressure 1-2Mpa, temperature is increased to
40-50 DEG C, stirring reaction is cooled to room temperature after 1-1.5 hours, adds toluene and adjusts the viscosity of reactant to 6000-
8000mPa/s, obtains coating adhesive；
（5）Coating：The coating adhesive prepared is coated on the fabric after calendering using floating blade coating machine, in 150-160 DEG C
Dry 3-5 minutes, the dry weightening of fabric is 3-5g/m after coating2。
Embodiment 3.
A kind of processing method of feather dress fabric anti-chiseling down, comprises the following steps：
（1）Fabric is selected：Select the woven fabric of mercerized cotton, yarn count 15D-25D, fineness 300-420tex；
（2）Water repellent finish：Fabric is put into the tank for fill water repellent finishing agent and impregnated 15-30 minutes, is dried after taking-up to water
Divide content 5-8%, wherein, water repellent finishing agent is by the silica of 20-30 parts by weight and the zinc octoate of 0.5-0.8 parts by weight normal
Temperature is lower to be mixed 20-30 minutes, and 150-160 DEG C of baking is obtained, and dry condition is dried 10-30 minutes for 50-60 DEG C.
（3）Calendering：Fabric after water repellent finish, which is passed through in calender, carries out friction glazing, wherein, pressure 10-12Mpa rolls
The ratio between the surface linear speed of ray machine friction roller and the translational speed of fabric are 4:1-6:1, the temperature of friction roller is 115-125 DEG C, so
Afterwards by fabric drying to moisture 2-3%, wherein, the translational speed of fabric is controlled in 15-18 m/min.
（4）The preparation of coating adhesive：55 parts of polyimide coating glues are mixed with ethyl propionate, are sufficiently stirred for making polyimides
Coating adhesive is completely dissolved, and in solution feeding autoclave, adds 22 parts of polyisocyanates, 10 parts of crosslinking accelerator XH-H2202Z, 8
Part diallyl dimethyl ammoniumchloride, 15 parts of Tween-80s, are filled with nitrogen to pressure 1-2Mpa, temperature is increased to 40-50 DEG C,
After stirring reaction 1-1.5 hours, room temperature is cooled to, toluene is added and adjusts the viscosity of reactant to 6000-8000mPa/s, obtain
To coating adhesive；
（5）Coating：The coating adhesive prepared is coated on the fabric after calendering using floating blade coating machine, in 150-160 DEG C
Dry 3-5 minutes, the dry weightening of fabric is 3-5g/m after coating2。
Embodiment 4.
A kind of processing method of feather dress fabric anti-chiseling down, comprises the following steps：
（1）Fabric is selected：Select the woven fabric of mercerized cotton, yarn count 15D-25D, fineness 300-420tex；
（2）Water repellent finish：Fabric is put into the tank for fill water repellent finishing agent and impregnated 15-30 minutes, is dried after taking-up to water
Divide content 5-8%, wherein, water repellent finishing agent is by the silica of 20-30 parts by weight and the zinc octoate of 0.5-0.8 parts by weight normal
Temperature is lower to be mixed 20-30 minutes, and 150-160 DEG C of baking is obtained, and dry condition is dried 10-30 minutes for 50-60 DEG C.
（3）Calendering：Fabric after water repellent finish, which is passed through in calender, carries out friction glazing, wherein, pressure 10-12Mpa rolls
The ratio between the surface linear speed of ray machine friction roller and the translational speed of fabric are 4:1-6:1, the temperature of friction roller is 115-125 DEG C, so
Afterwards by fabric drying to moisture 2-3%, wherein, the translational speed of fabric is controlled in 15-18 m/min.
（4）The preparation of coating adhesive：48 parts of polyimide coating glues are mixed with ethyl propionate, are sufficiently stirred for making polyimides
Coating adhesive is completely dissolved, in solution feeding autoclave, add 15 parts of DAAMs, 6 parts of crosslinking accelerators 550,10 parts
Diallyl dimethyl ammoniumchloride, 12 parts of Tween-80s, are filled with nitrogen to pressure 1-2Mpa, temperature is increased to 40-50 DEG C, stirs
After mixing reaction 1-1.5 hours, room temperature is cooled to, toluene is added and adjusts the viscosity of reactant to 6000-8000mPa/s, obtain
Coating adhesive；
（5）Coating：The coating adhesive prepared is coated on the fabric after calendering using floating blade coating machine, in 150-160 DEG C
Dry 3-5 minutes, the dry weightening of fabric is 3-5g/m after coating2。
Embodiment 5.
A kind of processing method of feather dress fabric anti-chiseling down, comprises the following steps：
（1）Fabric is selected：Select the woven fabric of mercerized cotton, yarn count 15D-25D, fineness 300-420tex；
（2）Water repellent finish：Fabric is put into the tank for fill water repellent finishing agent and impregnated 15-30 minutes, is dried after taking-up to water
Divide content 5-8%, wherein, water repellent finishing agent is by the silica of 20-30 parts by weight and the zinc octoate of 0.5-0.8 parts by weight normal
Temperature is lower to be mixed 20-30 minutes, and 150-160 DEG C of baking is obtained, and dry condition is dried 10-30 minutes for 50-60 DEG C.
（3）Calendering：Fabric after water repellent finish, which is passed through in calender, carries out friction glazing, wherein, pressure 10-12Mpa rolls
The ratio between the surface linear speed of ray machine friction roller and the translational speed of fabric are 4:1-6:1, the temperature of friction roller is 115-125 DEG C, so
Afterwards by fabric drying to moisture 2-3%, wherein, the translational speed of fabric is controlled in 15-18 m/min.
（4）The preparation of coating adhesive：52 parts of polyimide coating glues are mixed with ethyl propionate, are sufficiently stirred for making polyimides
Coating adhesive is completely dissolved, and in solution feeding autoclave, adds 9 parts of hydroxyethyl methacrylates, 8 parts of crosslinking accelerator AH100,8
Part diallyl dimethyl ammoniumchloride, 6 parts of Tween-80s, are filled with nitrogen to pressure 1-2Mpa, temperature is increased to 40-50 DEG C, stirs
After mixing reaction 1-1.5 hours, room temperature is cooled to, toluene is added and adjusts the viscosity of reactant to 6000-8000mPa/s, obtain
Coating adhesive；
（5）Coating：The coating adhesive prepared is coated on the fabric after calendering using floating blade coating machine, in 150-160 DEG C
Dry 3-5 minutes, the dry weightening of fabric is 3-5g/m after coating2。
Described above is only the preferred embodiment of the present invention, and protection scope of the present invention is not limited merely to above-mentioned implementation
Example, all technical schemes belonged under thinking of the present invention belong to protection scope of the present invention.It should be pointed out that for the art
Those of ordinary skill for, some improvements and modifications without departing from the principles of the present invention, these improvements and modifications
It should be regarded as protection scope of the present invention.
Claims (8)
1. a kind of processing method of feather dress fabric anti-chiseling down, it is characterised in that comprise the following steps：
（1）Fabric is selected：Select the woven fabric of mercerized cotton, yarn count 15D-25D, fineness 300-420tex；
（2）Water repellent finish：Fabric is put into the tank for fill water repellent finishing agent and impregnated 15-30 minutes, is dried after taking-up to water
Divide content 5-8%；
（3）Calendering：Fabric after water repellent finish, which is passed through in calender, carries out friction glazing, wherein, pressure 10-12Mpa, calender
The ratio between the surface linear speed of friction roller and the translational speed of fabric are 4:1-6:1, the temperature of friction roller is 115-125 DEG C, then will
Fabric drying is to moisture 2-3%；
（4）The preparation of coating adhesive：Polyimide coating glue is mixed with ethyl propionate, is sufficiently stirred for making polyimide coating glue complete
In fully dissolved, solution feeding autoclave, crosslinking agent, crosslinking accelerator, diallyl dimethyl ammoniumchloride, Tween-80 are added,
Nitrogen is filled with to pressure 1-2Mpa, temperature is increased to 40-50 DEG C, stirring reaction is cooled to room temperature after 1-1.5 hours, adds first
Benzene adjusts the viscosity of reactant to 6000-8000mPa/s, obtains coating adhesive；
（5）Coating：The coating adhesive prepared is coated on the fabric after calendering using floating blade coating machine, in 150-160 DEG C
Dry 3-5 minutes.
2. the processing method of feather dress fabric anti-chiseling down according to claim 1, it is characterised in that the step（2）Refuse
Water finishing agent mixes 20-30 points at normal temperatures by the silica of 20-30 parts by weight and the zinc octoate of 0.5-0.8 parts by weight
Clock, 150-160 DEG C of baking is obtained.
3. the processing method of feather dress fabric anti-chiseling down according to claim 1, it is characterised in that the step（2）It is dry
Dry condition is 50-60 DEG C and dried 10-30 minutes.
4. the processing method of feather dress fabric anti-chiseling down according to claim 1, it is characterised in that the step（3）Knit
The translational speed of thing is controlled in 15-18 m/min.
5. the processing method of feather dress fabric anti-chiseling down according to claim 1, it is characterised in that the step（4）In
Polyimide coating glue, crosslinking agent, crosslinking accelerator, diallyl dimethyl ammoniumchloride, the weight of Tween-80 ratio are 1:
0.2-0.4: 0.06-0.3: 0.05-0.12: 0.15-0.25。
6. the processing method of feather dress fabric anti-chiseling down according to claim 1, it is characterised in that the step（4）Hand over
Join agent and be selected from di-isopropylbenzene hydroperoxide, hexahydrophthalic anhydride, polyisocyanates, hydroxyethyl methacrylate, diacetone
One kind or any two or more combination in acrylamide.
7. the processing method of feather dress fabric anti-chiseling down according to claim 1, it is characterised in that the step（4）Hand over
Join the one kind or any two or more combination of accelerator in AH100, W-T501, XH-H0221Z, XH-H2202Z, 550.
8. the processing method of feather dress fabric anti-chiseling down according to claim 1, it is characterised in that the step（5）Apply
The dry weightening of fabric is 3-5g/m after layer2。