CN107245171A - A kind of electricity cables for technical installations sheath CSM material - Google Patents
A kind of electricity cables for technical installations sheath CSM material Download PDFInfo
- Publication number
- CN107245171A CN107245171A CN201710484741.5A CN201710484741A CN107245171A CN 107245171 A CN107245171 A CN 107245171A CN 201710484741 A CN201710484741 A CN 201710484741A CN 107245171 A CN107245171 A CN 107245171A
- Authority
- CN
- China
- Prior art keywords
- parts
- sheath
- attapulgite clay
- csm
- technical installations
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of electricity cables for technical installations sheath CSM material, its raw material includes by weight:40 50 parts of chlorosulfonated polyethylene, 30 40 parts of acrylonitrile butadiene styrene plastic, 60 70 parts of neoprene, 24 parts of dimethyl silicone polymer, 24 parts of calcium stearate, 46 parts of polyethylene glycol, 24 parts of barium stearate, 24 parts of styrene butadiene styrene block copolymer, 25 parts of crosslinking agent, 0.4 1 parts of dioctyl adipate, 0.8 1.6 parts of triphenyl phosphate, 15 25 parts of nanometer calcinated argil, 20 30 parts of diatomite, attapulgite clay compounded 50 60 parts of thing, 2.5 3.5 parts of composite antioxidant.Compactness of the present invention is high, and damping capaicty is strong, and durability can be excellent, and heat endurance is good under the conditions of long term high temperature, the formation in reduction internal flaw and cavity, can effectively alleviate the effect of the external force such as bending, impact, can the resonance of attenuating cable sheath.
Description
Technical field
Chlorosulfonated polyethylene rubber is used the present invention relates to shock absorber part technical field, more particularly to a kind of electricity cables for technical installations sheath
Glue material.
Background technology
Electric wire is widely used in every field, is related to people's lives, industrial production every field, at present, especially in work
The cable used in industry equipment, quality requirement is especially high, and with the fast development of economic technology, people are to industrial equipment quality
It is required that more and more higher, the requirement for the cable performance being particularly used for.During the use of industrial equipment, cable is with work
The vibrations of industry equipment are resonated, and the damping capaicty, impact resistance to cable cover(ing) propose higher requirement, as current
The technical issues that need to address.
The content of the invention
The technical problem existed based on background technology, the present invention is proposed a kind of electricity cables for technical installations sheath chlorosulfonation and gathered
Ethylene rubber material, compactness is high, and damping capaicty is strong, and durability can be excellent, and heat endurance is good under the conditions of long term high temperature, in reduction
Portion's defect and the formation in cavity, can effectively alleviate the effect of the external force such as bending, impact, can the resonance of attenuating cable sheath.
A kind of electricity cables for technical installations sheath CSM material proposed by the present invention, its raw material is by weight
Including:40-50 parts of chlorosulfonated polyethylene, 30-40 parts of acrylonitrile-butadiene-styrene (ABS) plastics, 60-70 parts of neoprene, poly- two
2-4 parts of methylsiloxane, 2-4 parts of calcium stearate, 4-6 parts of polyethylene glycol, 2-4 parts of barium stearate, styrene-butadiene-benzene second
2-4 parts of alkene block copolymer, 2-5 parts of crosslinking agent, 0.4-1 parts of dioctyl adipate, 0.8-1.6 parts of triphenyl phosphate, nanometer is forged
Burn 15-25 parts of clay, 20-30 parts of diatomite, attapulgite clay compounded thing 50-60 parts, 2.5-3.5 parts of composite antioxidant.
Preferably, attapulgite clay compounded thing is prepared using following technique:Attapulgite is heated up, calcined, cooling is placed in hydrogen
Sodium hydroxide solution immersion, is washed, and is dried, and is added aluminium nitride, graphite, sodium tripolyphosphate, soybean oil and is stirred, addition cornstarch,
Sodium sulphate, water stir, and are 8-8.5 with sodium hydroxide regulation system pH value, add the chloro- 2- Hydroxyproyl Trimethyls chlorinations of 3-
Ammonium, dodecenylsuccinic anhydride continue to stir, and with hydrochloric acid regulation system pH value in neutrality, filtering, spray drying obtains bumps
Rod soil compound.
Preferably, attapulgite clay compounded thing is prepared using following technique:25-30 parts of attapulgites are heated up by weight,
Calcining, cooling is placed in concentration and soaked for 2-2.4mol/L sodium hydroxide solutions, washed, dried, adds 4-8 parts of aluminium nitride, 4-8
Part graphite, 1-2 parts of sodium tripolyphosphates, 30-50 parts of soybean oils stirrings, add 8-12 parts of cornstarch, 4-8 parts of sodium sulphate, 140-
180 parts of water stir, and are 8-8.5 with sodium hydroxide regulation system pH value, add the chloro- 2- Hydroxyproyl Trimethyls chlorine of 4-8 parts of 3-
Change ammonium, 2-4 parts of dodecenylsuccinic anhydrides to continue to stir, with hydrochloric acid regulation system pH value in neutrality, filtering is spray-dried
To attapulgite clay compounded thing.
Preferably, attapulgite clay compounded thing is prepared using following technique:25-30 parts of attapulgites are warming up to by weight
700-740 DEG C, 4-8h is calcined, cooling is placed in concentration and soaked 1-2 days for 2-2.4mol/L sodium hydroxide solutions, washed, dried,
4-8 portions of aluminium nitride, 4-8 portions of graphite, 1-2 portions of sodium tripolyphosphates, 30-50 portions of soybean oils are added with 2000-2400r/min rotating speed
80-120min is stirred, 8-12 parts of cornstarch, 4-8 parts of sodium sulphate, 140-180 parts of water is added and stirs, adjusted with sodium hydroxide
Section system pH be 8-8.5, add 4-8 parts of 3- chloro-2-hydroxypropyl-trimethyl ammonium chlorides, 2-4 parts of dodecenylsuccinic anhydrides after
Continuous stirring 4-8h, with hydrochloric acid regulation system pH value in neutrality, filtering, spray drying obtains attapulgite clay compounded thing.
Preferably, crosslinking agent includes by weight:1-2 parts of benzoyl peroxide, 0.8-1.2 parts of diethylenetriamines, three
Paracyanogen 2-4 parts of triallyl of acid.
Preferably, composite antioxidant includes by weight:0.8-1.6 parts of styrenyl-N- phenylanilines, 3,5- bis- uncles
0.6-1.2 parts of butyl -4- hydroxycinnamic acids, phosphorous acid three (2,4- bis- 2-methyl-2-phenylpropane base) 1-2 parts of ester.
The present invention is using neoprene, acrylonitrile-butadiene-styrene (ABS) plastics, chlorosulfonated polyethylene synergy conduct
Base material, benzoyl peroxide, diethylenetriamines, TAC collaboration make densification of the invention as vulcanizing system
Property it is high, damping capaicty is strong, and durability can be excellent;In attapulgite clay compounded thing, attapulgite through calcining, alkalization after, with aluminium nitride,
Graphite, sodium tripolyphosphate compounding, then after soybean oil high-speed stirred, mutual good dispersion, after being well mixed with cornstarch,
Acted on through sodium peroxydisulfate, the reactive groups of 3- chloro-2-hydroxypropyl-trimethyl ammonium chlorides can with hydroxy combining in above-mentioned material, then
It is esterified, is obtained containing quaternary ammonium cation group, hydroxy-acid group and alkenyl long chain group product, flowing using alkenyl succinic anhydride
Property is good, and filling capacity is excellent;Attapulgite clay compounded thing and diatomite, nanometer calcinated argil as filler reinforcement material, and
Compounded with dimethyl silicone polymer, SBS, make the present invention under the conditions of long term high temperature
Heat endurance is good, and filling capacity is good, not only can effectively alleviate the effect of the external force such as bending, impact, and can be effectively in the present invention
Portion's structure is safeguarded;Triphenyl phosphate, dioctyl adipate can increase the interior lubricity of material, reduce internal flaw of the present invention
With the formation in cavity, further compounded with attapulgite clay compounded thing, not only fillibility is good, and storeroom is uniformly dispersed, and it is fine and close
Performance is high, and damping capaicty is further enhanced, can the resonance of attenuating cable sheath, and cost is low, and effect is obvious;Styryl
Change-N- phenylanilines, 3,5- di-t-butyl -4- hydroxycinnamic acids and (the 2-methyl-2-phenylpropane bases of the 2,4- bis-) ester of phosphorous acid three are as compound anti-
Oxygen agent, not only can effectively slow down aging speed of the present invention, and elongation at break conservation rate is high, and mechanical property is good, service life
It is long.
Embodiment
Below, technical scheme is described in detail by specific embodiment.
Embodiment 1
A kind of electricity cables for technical installations sheath CSM material proposed by the present invention, its raw material is by weight
Including:40 parts of chlorosulfonated polyethylene, 40 parts of acrylonitrile-butadiene-styrene (ABS) plastics, 60 parts of neoprene, polydimethylsiloxanes
4 parts of alkane, 2 parts of calcium stearate, 6 parts of polyethylene glycol, 2 parts of barium stearate, 4 parts of SBS,
2 parts of crosslinking agent, 1 part of dioctyl adipate, 0.8 part of triphenyl phosphate, 25 parts of nanometer calcinated argil, 20 parts of diatomite, concave convex rod
Native 60 parts of compound, 2.5 parts of composite antioxidant.
Embodiment 2
A kind of electricity cables for technical installations sheath CSM material proposed by the present invention, its raw material is by weight
Including:50 parts of chlorosulfonated polyethylene, 30 parts of acrylonitrile-butadiene-styrene (ABS) plastics, 70 parts of neoprene, polydimethylsiloxanes
2 parts of alkane, 4 parts of calcium stearate, 4 parts of polyethylene glycol, 4 parts of barium stearate, 2 parts of SBS,
5 parts of crosslinking agent, 0.4 part of dioctyl adipate, 1.6 parts of triphenyl phosphate, 15 parts of nanometer calcinated argil, 30 parts of diatomite is concavo-convex
Rod 50 parts of compound of soil, 3.5 parts of composite antioxidant.
Attapulgite clay compounded thing is prepared using following technique:Attapulgite is heated up, calcined, cooling is placed in sodium hydroxide
Solution soak, wash, dry, add aluminium nitride, graphite, sodium tripolyphosphate, soybean oil stirring, add cornstarch, sodium sulphate,
Water stirs, and is 8-8.5 with sodium hydroxide regulation system pH value, adds 3- chloro-2-hydroxypropyl-trimethyl ammonium chlorides, laurylene
Base succinic anhydride continues to stir, and with hydrochloric acid regulation system pH value in neutrality, filtering, spray drying obtains attapulgite clay compounded
Thing.
Embodiment 3
A kind of electricity cables for technical installations sheath CSM material proposed by the present invention, its raw material is by weight
Including:42 parts of chlorosulfonated polyethylene, 38 parts of acrylonitrile-butadiene-styrene (ABS) plastics, 66 parts of neoprene, polydimethylsiloxanes
3.5 parts of alkane, 2.5 parts of calcium stearate, 5.5 parts of polyethylene glycol, 2.5 parts of barium stearate, s-B-S block is total to
3.5 parts of polymers, 3 parts of crosslinking agent, 0.8 part of dioctyl adipate, 1 part of triphenyl phosphate, 22 parts of nanometer calcinated argil, diatomite 22
Part, attapulgite clay compounded 57 parts of thing, 2.8 parts of composite antioxidant.
Attapulgite clay compounded thing is prepared using following technique:28 parts of attapulgites are heated up by weight, calcined, cooling,
It is placed in concentration to soak for 2.2mol/L sodium hydroxide solutions, washs, dry, adds 6 parts of aluminium nitride, 6 parts of graphite, 1.5 parts of trimerizations
Sodium phosphate, 40 parts of soybean oil stirrings, add 10 parts of cornstarch, 6 parts of sodium sulphate, 160 parts of water and stir, adjusted with sodium hydroxide
Section system pH is 8-8.5, adds 6 parts of 3- chloro-2-hydroxypropyl-trimethyl ammonium chlorides, 3 parts of dodecenylsuccinic anhydrides and continues to stir
Mix, with hydrochloric acid regulation system pH value in neutrality, filtering, spray drying obtains attapulgite clay compounded thing.
Crosslinking agent includes by weight:1 part of benzoyl peroxide, 1.2 parts of diethylenetriamines, TAC
2 parts.Composite antioxidant includes by weight:1.6 parts of styrenyl-N- phenylanilines, 3,5- di-t-butyl -4- hydroxy cinnamates
0.6 part of acid, phosphorous acid three (2,4- bis- 2-methyl-2-phenylpropane base) 2 parts of ester.
Embodiment 4
A kind of electricity cables for technical installations sheath CSM material proposed by the present invention, its raw material is by weight
Including:48 parts of chlorosulfonated polyethylene, 32 parts of acrylonitrile-butadiene-styrene (ABS) plastics, 68 parts of neoprene, polydimethylsiloxanes
2.5 parts of alkane, 3.5 parts of calcium stearate, 4.5 parts of polyethylene glycol, 3.5 parts of barium stearate, s-B-S block is total to
2.5 parts of polymers, 4 parts of crosslinking agent, 0.6 part of dioctyl adipate, 1.4 parts of triphenyl phosphate, 18 parts of nanometer calcinated argil, diatomite
28 parts, attapulgite clay compounded 53 parts of thing, 3.2 parts of composite antioxidant.
Attapulgite clay compounded thing is prepared using following technique:25 parts of attapulgites are warming up to 740 DEG C, calcining by weight
4h, cooling is placed in concentration and soaked 1 day for 2.4mol/L sodium hydroxide solutions, washed, dried, adds 8 parts of aluminium nitride, 4 parts of stones
Ink, 2 parts of sodium tripolyphosphates, 30 portions of soybean oils stir 80min with 2400r/min rotating speed, add 12 parts of cornstarch, 4 parts of sulphur
Sour sodium, 180 parts of water stir, and are 8-8.5 with sodium hydroxide regulation system pH value, add the chloro- 2- Hydroxyproyl Trimethyls of 4 parts of 3-
Ammonium chloride, 4 parts of dodecenylsuccinic anhydrides continue to stir 4h, with hydrochloric acid regulation system pH value in neutrality, filter, spray drying
Obtain attapulgite clay compounded thing.
Crosslinking agent includes by weight:1.5 parts of benzoyl peroxide, 1 part of diethylenetriamines, TAC
3 parts.Composite antioxidant includes by weight:1.2 parts of styrenyl-N- phenylanilines, 3,5- di-t-butyl -4- hydroxy cinnamates
0.9 part of acid, phosphorous acid three (2,4- bis- 2-methyl-2-phenylpropane base) 1.5 parts of ester.
Embodiment 5
A kind of electricity cables for technical installations sheath CSM material proposed by the present invention, its raw material is by weight
Including:45 parts of chlorosulfonated polyethylene, 35 parts of acrylonitrile-butadiene-styrene (ABS) plastics, 67 parts of neoprene, polydimethylsiloxanes
3 parts of alkane, 3 parts of calcium stearate, 5 parts of polyethylene glycol, 3 parts of barium stearate, 3 parts of SBS,
3.5 parts of crosslinking agent, 0.7 part of dioctyl adipate, 1.2 parts of triphenyl phosphate, 20 parts of nanometer calcinated argil, 25 parts of diatomite is recessed
Native 55 parts of the compound of convex rod, 3 parts of composite antioxidant.
Attapulgite clay compounded thing is prepared using following technique:30 parts of attapulgites are warming up to 700 DEG C, calcining by weight
8h, cooling is placed in concentration and soaked 2 days for 2mol/L sodium hydroxide solutions, washed, dried, adds 4 parts of aluminium nitride, 8 parts of graphite, 1
Part sodium tripolyphosphate, 50 portions of soybean oils stir 120min with 2000r/min rotating speed, add 8 parts of cornstarch, 8 parts of sodium sulphate,
140 parts of water stir, and are 8-8.5 with sodium hydroxide regulation system pH value, add the chloro- 2- Hydroxyproyl Trimethyls chlorinations of 8 parts of 3-
Ammonium, 2 parts of dodecenylsuccinic anhydrides continue to stir 8h, and with hydrochloric acid regulation system pH value in neutrality, filtering, spray drying is obtained
Attapulgite clay compounded thing.
Crosslinking agent includes by weight:2 parts of benzoyl peroxide, 0.8 part of diethylenetriamines, TAC
4 parts.Composite antioxidant includes by weight:0.8 part of styrenyl-N- phenylanilines, 3,5- di-t-butyl -4- hydroxy cinnamates
1.2 parts of acid, phosphorous acid three (2,4- bis- 2-methyl-2-phenylpropane base) 1 part of ester.
The foregoing is only a preferred embodiment of the present invention, but protection scope of the present invention be not limited thereto,
Any one skilled in the art the invention discloses technical scope in, technique according to the invention scheme and its
Inventive concept is subject to equivalent substitution or change, should all be included within the scope of the present invention.
Claims (6)
1. a kind of electricity cables for technical installations sheath CSM material, it is characterised in that its raw material is wrapped by weight
Include:40-50 parts of chlorosulfonated polyethylene, 30-40 parts of acrylonitrile-butadiene-styrene (ABS) plastics, 60-70 parts of neoprene, poly- diformazan
2-4 parts of radical siloxane, 2-4 parts of calcium stearate, 4-6 parts of polyethylene glycol, 2-4 parts of barium stearate, s-B-S
2-4 parts of block copolymer, 2-5 parts of crosslinking agent, 0.4-1 parts of dioctyl adipate, 0.8-1.6 parts of triphenyl phosphate, nanometer calcining
15-25 parts of clay, 20-30 parts of diatomite, attapulgite clay compounded thing 50-60 parts, 2.5-3.5 parts of composite antioxidant.
2. electricity cables for technical installations sheath CSM material according to claim 1, it is characterised in that concavo-convex
Rod soil compound is prepared using following technique:Attapulgite is heated up, calcined, cooling is placed in sodium hydroxide solution immersion, washed
Wash, dry, add aluminium nitride, graphite, sodium tripolyphosphate, soybean oil stirring, add cornstarch, sodium sulphate, water and stir,
It is 8-8.5 with sodium hydroxide regulation system pH value, adds 3- chloro-2-hydroxypropyl-trimethyl ammonium chlorides, dodecenylsuccinic anhydride
Continue to stir, with hydrochloric acid regulation system pH value in neutrality, filtering, spray drying obtains attapulgite clay compounded thing.
3. electricity cables for technical installations sheath CSM material according to claim 1 or claim 2, it is characterised in that
Attapulgite clay compounded thing is prepared using following technique:25-30 parts of attapulgites are heated up by weight, calcined, cooling is placed in dense
Spend and soaked for 2-2.4mol/L sodium hydroxide solutions, washed, dried, add 4-8 parts of aluminium nitride, 4-8 parts of graphite, 1-2 parts of trimerizations
Sodium phosphate, 30-50 parts of soybean oil stirrings, add 8-12 parts of cornstarch, 4-8 parts of sodium sulphate, 140-180 parts of water and stir,
It is 8-8.5 with sodium hydroxide regulation system pH value, adds 4-8 parts of 3- chloro-2-hydroxypropyl-trimethyl ammonium chlorides, 2-4 parts of laurylenes
Base succinic anhydride continues to stir, and with hydrochloric acid regulation system pH value in neutrality, filtering, spray drying obtains attapulgite clay compounded
Thing.
4. according to any one of the claim 1-3 electricity cables for technical installations sheath CSM materials, its feature
It is, attapulgite clay compounded thing is prepared using following technique:25-30 parts of attapulgites are warming up to 700-740 DEG C by weight,
4-8h is calcined, cooling is placed in concentration and soaked 1-2 days for 2-2.4mol/L sodium hydroxide solutions, washed, dried, adds 4-8 parts of nitrogen
Change aluminium, 4-8 parts of graphite, 1-2 parts of sodium tripolyphosphates, 30-50 portions of soybean oils and 80- is stirred with 2000-2400r/min rotating speed
120min, adds 8-12 parts of cornstarch, 4-8 parts of sodium sulphate, 140-180 parts of water and stirs, use sodium hydroxide regulation system
PH value is 8-8.5, adds 4-8 parts of 3- chloro-2-hydroxypropyl-trimethyl ammonium chlorides, 2-4 parts of dodecenylsuccinic anhydrides and continues to stir
4-8h, with hydrochloric acid regulation system pH value in neutrality, filtering, spray drying obtains attapulgite clay compounded thing.
5. according to any one of the claim 1-4 electricity cables for technical installations sheath CSM materials, its feature
It is, crosslinking agent includes by weight:1-2 parts of benzoyl peroxide, 0.8-1.2 parts of diethylenetriamines, cyanuric acid triolefin
2-4 parts of propyl ester.
6. according to any one of the claim 1-5 electricity cables for technical installations sheath CSM materials, its feature
It is, composite antioxidant includes by weight:0.8-1.6 parts of styrenyl-N- phenylanilines, 3,5- di-t-butyl -4- hydroxyls
0.6-1.2 parts of base cinnamic acid, phosphorous acid three (2,4- bis- 2-methyl-2-phenylpropane base) 1-2 parts of ester.