CN107236420A - Winding-type CNG gas cylinders coating and its application - Google Patents
Winding-type CNG gas cylinders coating and its application Download PDFInfo
- Publication number
- CN107236420A CN107236420A CN201710588632.8A CN201710588632A CN107236420A CN 107236420 A CN107236420 A CN 107236420A CN 201710588632 A CN201710588632 A CN 201710588632A CN 107236420 A CN107236420 A CN 107236420A
- Authority
- CN
- China
- Prior art keywords
- component
- winding
- gas cylinder
- cng gas
- type cng
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a kind of winding-type CNG gas cylinder coating, including priming paint and finish paint, the priming paint includes component A and component B, and component A is by epoxy resin, modified flexible-epoxy, color stuffing A, dispersant, defoamer, levelling agent, cyclohexanone, dimethylbenzene, butanol composition;Component B is polyamide;The finish paint includes component a and component b, and component a is by Hydroxylated acrylic resin, modified flexible polyester resin, color stuffing a, dispersant, defoamer, levelling agent, cyclohexanone, dimethylbenzene, butyl acetate composition;Component b is polyisocyanate resin.Winding-type CNG gas cylinders coating of the present invention be mainly optimized in terms of resin, color stuffing, auxiliary agent, curing agent it is supporting, design can air drying, good adhesive force, the coating of impact property can be kept after 150 DEG C of dry 8h of high temperature again.
Description
Technical field
The present invention relates to technical field of coatings, and in particular to a kind of winding-type CNG gas cylinder coating, meanwhile, the present invention is also related to
And the application of the coating.
Background technology
Composites gas cylinder is in steel inner container outer surface, with the carbon fiber winding of impregnating resin and cured and be made
Gas cylinder.But composites gas cylinder, electrochemical corrosion is easily caused because carbon fiber is directly contacted with metal bottle in the prior art,
Cause the interfacial adhesion of winding layer and steel inner container low, composites gas cylinder is poor to the tolerance degree of severe storage requirement.
Because epoxy resin has very strong cohesive force, molecular structure is fine and close, and mechanical property is good, and adhesive force is strong, stability
Good, the advantages of heat resistance is strong is widely used in fields such as machinery, electronics, space flight and aviation, coating, bondings.But ring
The cured product of oxygen tree fat is the three-dimensional network structure body with compared with high crosslink density, and main sub-chain motion is extremely difficult, is typical case
Fragile material.
The content of the invention
It is an object of the invention to provide a kind of winding-type CNG gas cylinder coating.
A kind of winding-type CNG gas cylinder coating, including priming paint and finish paint, the priming paint include component A and component B, described group
A is divided to be made up of following raw material:Epoxy resin, modified flexible-epoxy, color stuffing A, dispersant, defoamer, levelling agent, hexamethylene
Ketone, dimethylbenzene, butanol;The component B is polyamide;
The finish paint includes component a and component b, and the component a is made up of following raw material:Hydroxylated acrylic resin, modification
Flexible polyester resin, color stuffing a, dispersant, defoamer, levelling agent, cyclohexanone, dimethylbenzene, butyl acetate;The component b is
Polyisocyanate resin.
Further, the color stuffing A includes titanium dioxide, iron oxide red, trbasic zinc phosphate, aluminium triphosphate, barium sulfate, mica
Powder, talcum powder, strontium chromate.
Further, the color stuffing a includes titanium dioxide, barium sulfate.
Further, the priming paint is made up of the raw material of following parts by weight:
Further, the finish paint is made up of the raw material of following parts by weight:
Further, described modification flexible-epoxy is polyurethane modified epoxy resin.
Further, described modification flexible polyester resin is Niu Peisi Setel 168ss-80.
Further, described polyurethane modified epoxy resin is prepared from the following raw materials in parts by weight:
Further, described polyurethane modified epoxy resin is prepared from by following methods:
Step a:Add PEPA in the reactor, dewater treatment, after be passed through nitrogen, add the isocyanide of isophorone two
Acid esters, 300-500r/min stirrings reach theoretical value in 80-85 DEG C of reaction to NCO- content;
Step b:N-N dimethylformamides, bisphenolA-epichlorohydrin type epoxy resin, two bays are added in the reactor
Sour dibutyl tin, is warming up to 80-85 DEG C and reacts 3 hours, that is, obtain polyurethane modified epoxy resin.
Winding-type CNG gas cylinder coating of the present invention has the advantages that:
(1) priming paint of winding-type CNG gas cylinder coating of the present invention is main fills out from epoxy resin, modified flexible-epoxy, face
Be optimized in terms of material, auxiliary agent, curing agent it is supporting, design can air drying, again can be after 150 DEG C of dry 8h of high temperature
The good adhesive force of holding, the coating of impact property.The finish paint of winding-type CNG gas cylinder coating of the present invention is from hydroxy acrylic acid tree
Be optimized in terms of fat, modified flexible polyester resin, color stuffing, auxiliary agent, curing agent it is supporting, design can normal temperature do
It is dry, good adhesive force, the coating of impact property can be kept after 150 DEG C of dry 8h of high temperature again.Priming paint that the present invention is designed with
Finish paint is supported the use, and paint film adhesion is strong, and impact resistance, ageing resistace are excellent.
(2) priming paint of winding-type CNG gas cylinder coating of the present invention selects epoxy resin, there is very strong adhesive force to metal, and
It with good decay resistance, can effectively extend the service life of coated article, be modified while the present invention is introduced in formula
Flexible-epoxy, being greatly improved after the toughness of paint film, and paint film high-temperature baking resistant has more preferable mechanical performance.
(3) finish paint of the present invention selects Hydroxylated acrylic resin, and with being modified flexible polyester resin compatibility, it is ensured that paint film is good
UV resistant performance, improve the shock resistance of Bulk coat, low-temperature bending performance.
(4) the modified flexible-epoxy of the present invention is polyurethane modified epoxy resin, using polyurethane modified epoxy resin,
And content of raw material in resins synthesis is rationally designed, make the polyurethane modified epoxy resin being made both have epoxy resin excellent
Adhesive force, decay resistance, while the toughness of reinforced epoxy again, every excellent combination property.
The application of above-mentioned winding-type CNG gas cylinder coating, comprises the following steps:
Shot Blasting is carried out to gas cylinder;The component A of priming paint, component B are well mixed, to all spray-applied primers of gas cylinder;Will
Component a, the component b of finish paint are well mixed, to gas cylinder two ends spray paint;Composite is carried out to bottle in the middle of gas cylinder to twine
Around 150 DEG C of baking 8h.
Embodiment
Based on the design philosophy of the present invention, below, in conjunction with specific embodiments to a kind of winding-type CNG gas cylinders of the present invention
Coating is described in further detail:
Embodiment 1-3
The preparation of modified flexible-epoxy:
Using the formulation weight composition shown in following table, prepare modified flexible-epoxy a, modified flexible-epoxy b, change
Property flexible-epoxy c.
The preparation method of modified flexible-epoxy is as follows:
Step a:Add PEPA in the reactor, dewater treatment, after be passed through nitrogen, add the isocyanide of isophorone two
Acid esters, 300-500r/min stirrings reach theoretical value in 80-85 DEG C of reaction to NCO- content;
Step b:N-N dimethylformamides, bisphenolA-epichlorohydrin type epoxy resin, two bays are added in the reactor
Sour dibutyl tin, is warming up to 80-85 DEG C and reacts 3 hours, that is, obtain being modified flexible-epoxy.
The modification flexible-epoxy a that is prepared according to above-mentioned preparation method, modified flexible-epoxy b, modification are soft
Property epoxy resin c is added in winding-type CNG gas cylinder base coats.
Embodiment 1-3 winding-type CNG gas cylinder base coat component A raw material weights composition is as shown in the table:
Embodiment 1-3 winding-type CNG gas cylinder base coat component B raw material weights composition is as shown in the table:
Embodiment 1-3 winding-type CNG gas cylinder top coat component a raw material weights composition is as shown in the table:
Embodiment 1-3 winding-type CNG gas cylinder base coat component b raw material weights composition is as shown in the table:
The winding-type CNG gas cylinders coating prepared to embodiment 1-3 carries out performance test, testing result such as following table institute
Show:
Primer performance test result is as follows:
Finish paint the performance test results are as follows:
Bottom surface composite coating test result is as follows:
Claims (10)
1. a kind of winding-type CNG gas cylinder coating, it is characterised in that the coating includes priming paint and finish paint, the priming paint includes group
Point A and component B, the component A are made up of following raw material:
Epoxy resin, modified flexible-epoxy, color stuffing A, dispersant, defoamer, levelling agent, cyclohexanone, dimethylbenzene, fourth
Alcohol;
The component B is polyamide;
The finish paint includes component a and component b, and the component a is made up of following raw material:
Hydroxylated acrylic resin, modified flexible polyester resin, color stuffing a, dispersant, defoamer, levelling agent, cyclohexanone, diformazan
Benzene, butyl acetate;
The component b is polyisocyanate resin.
2. a kind of winding-type CNG gas cylinder coating according to claim 1, it is characterised in that the color stuffing A includes titanium white
Powder, iron oxide red, trbasic zinc phosphate, aluminium triphosphate, barium sulfate, mica powder, talcum powder, strontium chromate.
3. a kind of winding-type CNG gas cylinder coating according to claim 1, it is characterised in that the color stuffing a includes titanium white
Powder, barium sulfate.
4. a kind of winding-type CNG gas cylinder coating according to claim 2, it is characterised in that the priming paint is by following weight
The raw material composition of number:
5. a kind of winding-type CNG gas cylinder coating according to claim 3, it is characterised in that the finish paint is by following weight
The raw material composition of number:
6. a kind of winding-type CNG gas cylinder coating according to claim 1, it is characterised in that described modification flexible epoxy
Resin is polyurethane modified epoxy resin.
7. a kind of winding-type CNG gas cylinder coating according to claim 1, it is characterised in that described modification flexible polyester
Resin is the Niu Peisi ss-80 of Setel 168.
8. a kind of winding-type CNG gas cylinder coating according to claim 6, it is characterised in that described polyurethane-modified ring
Oxygen tree fat is prepared from the following raw materials in parts by weight:
9. a kind of winding-type CNG gas cylinder coating according to claim 8, it is characterised in that described polyurethane-modified ring
Oxygen tree fat is prepared from by following methods:
Step a:Add PEPA in the reactor, dewater treatment, after be passed through nitrogen, add the isocyanic acid of isophorone two
Ester, 300-500r/min stirrings reach theoretical value in 80-85 DEG C of reaction to NCO- content;
Step b:N-N dimethylformamides, bisphenolA-epichlorohydrin type epoxy resin, tin dilaurate two are added in the reactor
Butyl tin, is warming up to 80-85 DEG C and reacts 3 hours, that is, obtain polyurethane modified epoxy resin.
10. a kind of application of winding-type CNG gas cylinder coating as claimed in any one of claims 1-9 wherein, it is characterised in that described
The application of coating comprises the following steps:
Shot Blasting is carried out to gas cylinder;The component A of priming paint, component B are well mixed, to all spray-applied primers of gas cylinder;By finish paint
Component a, component b be well mixed, to gas cylinder two ends spray paint;The winding of composite, 150 are carried out to bottle in the middle of gas cylinder
DEG C baking 8h.