CN107227504A - A kind of preparation method of bamboo fiber towel - Google Patents
A kind of preparation method of bamboo fiber towel Download PDFInfo
- Publication number
- CN107227504A CN107227504A CN201710568426.0A CN201710568426A CN107227504A CN 107227504 A CN107227504 A CN 107227504A CN 201710568426 A CN201710568426 A CN 201710568426A CN 107227504 A CN107227504 A CN 107227504A
- Authority
- CN
- China
- Prior art keywords
- solution
- towel
- bamboo
- spinning
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of preparation method of bamboo fiber towel, it is related to towel and makes field, including preparing bamboo fibre solution, prepare regenerated cellulose solution, prepare spinning solution, spinning, cotton carding, silver lap, drafting, rove, spun yarn, winder, twist thread, reeling, warping, sizing, pass, weave, printing and dyeing, cutting, sewing, it is whole scald, arranging process towel is made.Bamboo fibre has good antibiotic property.Regenerated cellulose has good biocompatibility and skin-friendly, degradable, improves the mechanical performance of material.The preparation technology of the present invention is simple, environmental protection.
Description
Technical field
Field, especially a kind of preparation method of bamboo fiber towel are made the present invention relates to towel.
Background technology
Towel surface looped pile is intensive, soft, and water suction water storage is strong, and wear-resisting, thermal property is good, therefore can directly use
It is one of most important daily necessities of daily life to contact skin.People will continually contact towel daily, due to hair
The easy moisture absorption of towel, after each, is easily bred by various harmful bacterias and corrodes, such as clean not in time, the bacterium on towel cloth
Class, grease, protein etc. can go bad fermentation, and bacterium can make towel body tacky mouldy with geometric progression fast-growth, produce peculiar smell,
Influence the health of people, if the amount reproduction of malignant bacteria, invade after skin, respiratory tract etc., can also harmful to human health
Life.As living standards of the people are stepped into after " fairly well-off " and " rich type ", the consumption idea of resident can be changed than ever
And selection, pursue and this has been human social development with green, environmental protection and healthy household textiles inexorable trend, therefore,
The exploitation of anti-microbial type towel, emerges in large numbers the trend in the epoch that also just coincide, and meets consumer and advocates naturally, being particular about health
Live custom.
The content of the invention
The technical problem to be solved in the present invention is：A kind of environmental protection, bamboo fiber towel with antibacterial effect are provided
Preparation method.
The present invention uses following technical scheme：
A kind of preparation method of bamboo fiber towel, comprises the following steps：
Step one：20g bamboo fibres are weighed, are put into the NaOH aqueous solution that 400g, mass fraction are 17.5%, and place
To temperature in 100 DEG C of thermostat water bath, 60min is boiled in boiling, then bamboo fibre is cleaned to neutrality repeatedly with deionized water；
Step 2：Take 16gLiCl to put into equipped with 40 DEG C, the container of 184g dimethyl acetamides, stirred in constant temperature magnetic force
Mixing makes LiCl fully dissolve in the presence of device, is configured to the solvent that mass fraction is 8%, takes solvent 100g, bamboo fibre 15g, 60
In DEG C thermostat water bath, 8h is mixed, bamboo fibre solution is filtered to obtain；
Step 3：Cotton linter 5g is taken, is dissolved in formic acid, the regenerated cellulose solution of mass concentration 4% is configured to；
Step 4：By bamboo fibre solution and regenerated cellulose solution in mass ratio 4:19 are well mixed, and are shaken using ultrasonic wave
Swing and it is disperseed, magnetic agitation 1h under the conditions of 50 DEG C, then continue to stir 8h at room temperature, obtain spinning solution；
Step 5：Spinning is carried out to spinning solution with wet spinning equipment, enters coagulating bath by spinneret, then through solidifying
Gu obtaining fiber after bath solidification, water-bath stretching, washing, it is positioned over after fiber is dehydrated in 50 DEG C of baking oven and dries 10h；
Step 6：By fiber by cotton carding, silver lap, drafting, rove, spun yarn, winder, twist thread, reeling, warping, sizing, wear
Through, weaving, printing and dyeing, cut, sewing, it is whole scald, arranging process towel is made.
It is preferred that, the spinning speed described in step 5 is 100m/min, 10 DEG C of coagulation bath temperature.
The beneficial effects of the present invention are：
1) bamboo fibre has good antibiotic property.
2) regenerated cellulose has good biocompatibility and skin-friendly, degradable, improves the mechanical performance of material.
3) preparation technology is simple, environmental protection.
Embodiment
With reference to embodiment, the present invention will be further described.
Embodiment 1
A kind of preparation method of bamboo fiber towel, comprises the following steps：
Step one：20g bamboo fibres are weighed, are put into the NaOH aqueous solution that 400g, mass fraction are 17.5%, and place
To temperature in 100 DEG C of thermostat water bath, 60min is boiled in boiling, then bamboo fibre is cleaned to neutrality repeatedly with deionized water；
Step 2：Take 16gLiCl to put into equipped with 40 DEG C, the container of 184g dimethyl acetamides, stirred in constant temperature magnetic force
Mixing makes LiCl fully dissolve in the presence of device, is configured to the solvent that mass fraction is 8%, takes solvent 100g, bamboo fibre 15g, 60
In DEG C thermostat water bath, 8h is mixed, bamboo fibre solution is filtered to obtain；
Step 3：Cotton linter 5g is taken, is dissolved in formic acid, the regenerated cellulose solution of mass concentration 4% is configured to；
Step 4：By bamboo fibre solution and regenerated cellulose solution in mass ratio 4:19 are well mixed, and are shaken using ultrasonic wave
Swing and it is disperseed, magnetic agitation 1h under the conditions of 50 DEG C, then continue to stir 8h at room temperature, obtain spinning solution；
Step 5：Spinning is carried out to spinning solution with wet spinning equipment, enters coagulating bath by spinneret, then through solidifying
Gu obtaining fiber after bath solidification, water-bath stretching, washing, it is positioned over after fiber is dehydrated in 50 DEG C of baking oven and dries 10h；
Step 6：By fiber by cotton carding, silver lap, drafting, rove, spun yarn, winder, twist thread, reeling, warping, sizing, wear
Through, weaving, printing and dyeing, cut, sewing, it is whole scald, arranging process towel is made.
Spinning speed described in step 5 is 100m/min, 10 DEG C of coagulation bath temperature.
Claims (2)
1. a kind of preparation method of bamboo fiber towel, it is characterised in that comprise the following steps：
Step one：20g bamboo fibres are weighed, are put into the NaOH aqueous solution that 400g, mass fraction are 17.5%, and be placed into temperature
Spend in the thermostat water bath for 100 DEG C, 60min is boiled in boiling, then bamboo fibre is cleaned to neutrality repeatedly with deionized water；
Step 2：16gLiCl is taken to put into equipped with 40 DEG C, the container of 184g dimethyl acetamides, in constant temperature blender with magnetic force
In the presence of LiCl is fully dissolved, be configured to mass fraction be 8% solvent, take solvent 100g, bamboo fibre 15g, 60 DEG C of perseverances
In warm water bath, 8h is mixed, bamboo fibre solution is filtered to obtain；
Step 3：Cotton linter 5g is taken, is dissolved in formic acid, the regenerated cellulose solution of mass concentration 4% is configured to；
Step 4：By bamboo fibre solution and regenerated cellulose solution in mass ratio 4:19 are well mixed, and use ultrasonic oscillation pair
It is disperseed, magnetic agitation 1h under the conditions of 50 DEG C, then continues to stir 8h at room temperature, obtains spinning solution；
Step 5：Spinning is carried out to spinning solution with wet spinning equipment, enters coagulating bath by spinneret, then through coagulating bath
Fiber is obtained after solidification, water-bath stretching, washing, is positioned over after fiber is dehydrated in 50 DEG C of baking oven and dries 10h；
Step 6：By fiber by cotton carding, silver lap, drafting, rove, spun yarn, winder, twist thread, reeling, warping, sizing, pass,
Towel is made in weaving, printing and dyeing, cutting, sewing, whole boiling hot, arranging process.
2. a kind of preparation method of bamboo fiber towel according to claim 1, it is characterised in that：Spinning described in step 5
Silk speed is 100m/min, 10 DEG C of coagulation bath temperature.