CN107217374A - A kind of fabric elastic chiffon face fabric two sides printing technology - Google Patents
A kind of fabric elastic chiffon face fabric two sides printing technology Download PDFInfo
- Publication number
- CN107217374A CN107217374A CN201710657526.0A CN201710657526A CN107217374A CN 107217374 A CN107217374 A CN 107217374A CN 201710657526 A CN201710657526 A CN 201710657526A CN 107217374 A CN107217374 A CN 107217374A
- Authority
- CN
- China
- Prior art keywords
- fabric
- chiffon
- decalcomania
- printing technology
- polyester fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of fabric elastic chiffon face fabric two sides printing technology, comprise the following steps：Warp is done into polyester fiber twisting, by polyester fiber coating spandex fiber, parallel is done in twisting；The orthogonal consolidation of warp and weft is formed into chiffon fabric；Chiffon fabric feeding forming machine is subjected to heat treatment, progress open width looped weft processing in open width looped weft machine is then fed into；Decalcomania is designed as needed, chiffon fabric and the decalcomania paper simultaneous transmission for being printed on thickening agent entered in Pneumatic double-station pressing printing machine, the decalcomania on decalcomania paper is transferred into chiffon fabric produces.The present invention has technological operation simple, stamp efficiency high, the advantages of product qualified rate is high, and gained elastic fabric is bright in colour, good color fastness, level enriches, and flower pattern is naturally, soft, good permeability, can be widely applied to the production and processing of fashionable dress and easy dress, and product specification is high, is worthy to be popularized.
Description
Technical field
The present invention relates to chiffon fabric technical field, more particularly to a kind of fabric elastic chiffon face fabric two sides printing technology.
Background technology
The pronunciation and meaning of " chiffon " title from English Chiffon, means frivolous transparent fabric, is the spinning class production in a product
Product, fabric is frivolous, transparent, soft, elegant.Chiffon classification has silk chiffon and the class of Silk chiffon two, the composition of silk chiffon
Be 100% mulberry silk, and the general composition of Silk chiffon be 100% terylene.With the continuous improvement of people's living standards, people
Increasingly focus on the health care of itself, outdoor activities also become to become more and more popular.Therefore the elastic force of the chiffon fabric of people is proposed
Higher requirement.Fabric elastic chiffon face fabric is to refer to add the good spandex fibre of elasticity in polyester fiber raw materials, but spandex sheet
Non-coloring group in the molecular structure of body, has that dyeing is difficult, color fastness is low, and dyeing easily causes the defects such as spandex hydraulic performance decline,
So as to causing the dyeing of existing fabric elastic chiffon face fabric, it is low to there is dye uptake after complex technical process, dyeing, dyes difficulty
Greatly, staining efficiency is low, the defect such as destructible chiffon fabric performance.Based on above statement, the present invention proposes a kind of elastic chiffon face
Fabric two sides printing technology.
The content of the invention
The invention aims to solve shortcoming present in prior art, and a kind of fabric elastic chiffon face fabric two proposed
Face printing technology.
A kind of fabric elastic chiffon face fabric two sides printing technology, comprises the following steps：
S1, by after polyester fiber shredding through carding machine cards it is neat after, twisting 1800~2200T/M do warp, by terylene
After fiber and spandex fibre shredding, respectively through carding machine cards it is neat after, polyester fiber is coated on around spandex fibre, plus
Twist with the fingers 800~1200T/M and do parallel；
S2, the warp and weft obtained by step S1 are drawn by the fiber axis of weaving loom respectively, set the work of weaving loom
Skill parameter, makes the orthogonal consolidation of warp and weft form chiffon fabric；
S3, will in step S2 gained chiffon fabric feeding forming machine in, setting sizing parameter, carry out heat treatment, then
Chiffon fabric is sent into open width looped weft processing is carried out in open width looped weft machine；
S4, decalcomania is designed as needed, by the chiffon fabric after being handled in step S3 and is printed on stamp dye
The decalcomania paper simultaneous transmission of material enters in Pneumatic double-station pressing printing machine, in the condition of normal pressure that temperature is 168~185 DEG C
Under, superheated steam evaporates 15~25s, and the decalcomania on decalcomania paper is transferred into chiffon fabric produces.
It is preferred that, polyester fiber washs silk for 150D/48F FDY in the warp in the step S1；Terylene in parallel is fine
The FDY tieed up as 75D/48F washs silk, and spandex fibre is 70D spandexs.
It is preferred that, the amount ratio of polyester fiber and spandex fibre is 6.7~8.2 in the parallel in the step S1:1~
1.2。
It is preferred that, the technological parameter of the weaving loom in the step S2 is 3~5mm of leaf gauge, the twist 840~980, twist direction
For Z, it is 7~12m/min to be twisted together speed.
It is preferred that, the sizing parameter in the step S3 is that temperature is 170~185 DEG C, rotation speed of fan be 1000~
1500r/min, door width is 145~165cm, and speed is 50~70m/min.
It is preferred that, thickening agent in the step S4 by 18~25wt% of sodium alginate, 30~45wt% of disperse dyes,
3~8wt% of thickener and the water of surplus are compounded and obtained.
A kind of fabric elastic chiffon face fabric two sides printing technology proposed by the present invention, is done warp after being twisted using polyester fiber, adopted
Parallel is done after being twisted with polyester fiber coating spandex fiber, the orthogonal consolidation of warp and weft is formed into fabric elastic chiffon face fabric, and it is right
Fabric carries out sizing and the processing of open width looped weft, then designs decalcomania, prepares thickening agent, is printed using Pneumatic double-station pressing
Flower machine completes the printing technology of fabric elastic chiffon face fabric, and the present invention effectively solves prior art fabric elastic chiffon face fabric dyeing
Process is complicated, and dye uptake is low after dyeing, and dyeing difficulty is big, and staining efficiency is low, the defect such as destructible chiffon fabric performance, with work
Skill is simple to operate, stamp efficiency high, the advantages of product qualified rate is high, and gained elastic fabric is bright in colour, and good color fastness, level is rich
Richness, flower pattern are naturally, soft, good permeability, can be widely applied to the production and processing of fashionable dress and easy dress, and product specification is high,
It is worthy to be popularized.
Embodiment
The present invention is made with reference to specific embodiment further to explain.
Embodiment one
A kind of fabric elastic chiffon face fabric two sides printing technology proposed by the present invention, comprises the following steps：
S1, by 150D/48F FDY wash after a shredding through carding machine cards it is neat after, twisting 2000T/M do warp, will
75D/48F FDY is washed after silk and 70D spandex shreddings, respectively through carding machine cards it is neat after, by amount ratio be 7.5:1.1, will
75D/48F FDY washs silk and is coated on around 70D spandexs, and twisting 1000T/M does parallel；
S2, the warp and weft obtained by step S1 are drawn by the fiber axis of weaving loom respectively, set the work of weaving loom
Skill parameter is leaf gauge 4mm, and the twist 910, twist direction is Z, and it is 10m/min to be twisted together speed, forms the orthogonal consolidation of warp and weft
Chiffon fabric；
S3, will in step S2 gained chiffon fabric feeding forming machine in, set shape parameter as temperature be 178 DEG C, blower fan
Rotating speed is 1250r/min, and door width is 155cm, and speed is 60m/min, carries out heat treatment, chiffon fabric then is sent into open width
Open width looped weft processing is carried out in looped weft machine；
S4, decalcomania is designed as needed, by the chiffon fabric after being handled in step S3 and be printed on by marine alga
Sour sodium 22wt%, disperse dyes 38wt%, thickening agent obtained by the water compounding of thickener 5wt% and surplus decalcomania paper
Simultaneous transmission enters in Pneumatic double-station pressing printing machine, in temperature under 175 DEG C of condition of normal pressure, superheated steam evaporates 20s, will
Decalcomania on decalcomania paper is transferred to chiffon fabric and produced.
Embodiment two
A kind of fabric elastic chiffon face fabric two sides printing technology proposed by the present invention, comprises the following steps：
S1, by 150D/48F FDY wash after a shredding through carding machine cards it is neat after, twisting 2200T/M do warp, will
75D/48F FDY is washed after silk and 70D spandex shreddings, respectively through carding machine cards it is neat after, by amount ratio be 8.2:1.2, will
75D/48F FDY washs silk and is coated on around 70D spandexs, and twisting 1200T/M does parallel；
S2, the warp and weft obtained by step S1 are drawn by the fiber axis of weaving loom respectively, set the work of weaving loom
Skill parameter is leaf gauge 5mm, and the twist 980, twist direction is Z, and it is 12m/min to be twisted together speed, forms the orthogonal consolidation of warp and weft
Chiffon fabric；
S3, will in step S2 gained chiffon fabric feeding forming machine in, set shape parameter as temperature be 185 DEG C, blower fan
Rotating speed is 1500r/min, and door width is 165cm, and speed is 70m/min, carries out heat treatment, chiffon fabric then is sent into open width
Open width looped weft processing is carried out in looped weft machine；
S4, decalcomania is designed as needed, by the chiffon fabric after being handled in step S3 and be printed on by marine alga
Sour sodium 25wt%, disperse dyes 45wt%, thickening agent obtained by the water compounding of thickener 8wt% and surplus decalcomania paper
Simultaneous transmission enters in Pneumatic double-station pressing printing machine, in temperature under 185 DEG C of condition of normal pressure, superheated steam evaporates 25s, will
Decalcomania on decalcomania paper is transferred to chiffon fabric and produced.
Embodiment three
A kind of fabric elastic chiffon face fabric two sides printing technology proposed by the present invention, comprises the following steps：
S1, by 150D/48F FDY wash after a shredding through carding machine cards it is neat after, twisting 1800T/M do warp, will
75D/48F FDY is washed after silk and 70D spandex shreddings, respectively through carding machine cards it is neat after, by amount ratio be 6.7:1, by 75D/
48F FDY washs silk and is coated on around 70D spandexs, and twisting 800T/M does parallel；
S2, the warp and weft obtained by step S1 are drawn by the fiber axis of weaving loom respectively, set the work of weaving loom
Skill parameter is leaf gauge 3mm, and the twist 840, twist direction is Z, and it is 7m/min to be twisted together speed, the orthogonal consolidation of warp and weft is formed snow
Textile fabric；
S3, will in step S2 gained chiffon fabric feeding forming machine in, set shape parameter as temperature be 170 DEG C, blower fan
Rotating speed is 1000r/min, and door width is 145cm, and speed is 50m/min, carries out heat treatment, chiffon fabric then is sent into open width
Open width looped weft processing is carried out in looped weft machine；
S4, decalcomania is designed as needed, by the chiffon fabric after being handled in step S3 and be printed on by marine alga
Sour sodium 18wt%, disperse dyes 30wt%, thickening agent obtained by the water compounding of thickener 3wt% and surplus decalcomania paper
Simultaneous transmission enters in Pneumatic double-station pressing printing machine, in temperature under 168 DEG C of condition of normal pressure, superheated steam evaporates 15s, will
Decalcomania on decalcomania paper is transferred to chiffon fabric and produced.
The combination property of elastic chiffon face printed fabric prepared respectively in the test embodiment of the present invention one~tri-, and with it is commercially available
The combination property of elastic chiffon face printed fabric (make to ratio) be compared, draw following result：
| Embodiment | One | Two | Three | Comparative example |
| Fracture strength (N) | 562 | 575 | 558 | 380 |
| Rebound degree (%) | 93.3 | 95.8 | 94.2 | 87.6 |
| Dye-uptake (%) | 95.1 | 97.4 | 94.9 | 86.5 |
| Color fastness | 5 | 5 | 5 | 3 |
The foregoing is only a preferred embodiment of the present invention, but protection scope of the present invention be not limited thereto,
Any one skilled in the art the invention discloses technical scope in, technique according to the invention scheme and its
Inventive concept is subject to equivalent substitution or change, should all be included within the scope of the present invention.
Claims (6)
1. a kind of fabric elastic chiffon face fabric two sides printing technology, it is characterised in that comprise the following steps：
S1, by after polyester fiber shredding through carding machine cards it is neat after, twisting 1800~2200T/M do warp, by polyester fiber
After spandex fibre shredding, respectively through carding machine cards it is neat after, polyester fiber is coated on around spandex fibre, twist
800~1200T/M does parallel；
S2, the warp and weft obtained by step S1 are drawn by the fiber axis of weaving loom respectively, the technique ginseng of setting weaving loom
Number, makes the orthogonal consolidation of warp and weft form chiffon fabric；
S3, will in step S2 gained chiffon fabric feeding forming machine in, setting sizing parameter, carry out heat treatment, then will snow
Open width looped weft processing is carried out in textile fabric feeding open width looped weft machine；
S4, decalcomania is designed as needed, by the chiffon fabric after being handled in step S3 and is printed on thickening agent
Decalcomania paper simultaneous transmission enters in Pneumatic double-station pressing printing machine, in the case where temperature is 168~185 DEG C of condition of normal pressure, mistake
Vapours evaporates 15~25s, and the decalcomania on decalcomania paper is transferred into chiffon fabric produces.
2. a kind of fabric elastic chiffon face fabric two sides printing technology according to claim 1, it is characterised in that in the step S1
Warp in polyester fiber wash silk for 150D/48F FDY；Polyester fiber in parallel washs silk for 75D/48F FDY, and spandex is fine
Tie up as 70D spandexs.
3. a kind of fabric elastic chiffon face fabric two sides printing technology according to claim 1, it is characterised in that in the step S1
Parallel in polyester fiber and spandex fibre amount ratio be 6.7~8.2:1~1.2.
4. a kind of fabric elastic chiffon face fabric two sides printing technology according to claim 1, it is characterised in that in the step S2
Weaving loom technological parameter be 3~5mm of leaf gauge, the twist 840~980, twist direction is Z, be twisted together speed be 7~12m/min.
5. a kind of fabric elastic chiffon face fabric two sides printing technology according to claim 1, it is characterised in that in the step S3
Sizing parameter be that temperature is 170~185 DEG C, rotation speed of fan be 1000~1500r/min, door width be 145~165cm, speed
For 50~70m/min.
6. a kind of fabric elastic chiffon face fabric two sides printing technology according to claim 1, it is characterised in that in the step S4
Thickening agent by 18~25wt% of sodium alginate, 30~45wt% of disperse dyes, 3~8wt% of thickener and surplus water compounding and
.