CN107217196A - A kind of high rigidity sheet metal component - Google Patents
A kind of high rigidity sheet metal component Download PDFInfo
- Publication number
- CN107217196A CN107217196A CN201710389387.8A CN201710389387A CN107217196A CN 107217196 A CN107217196 A CN 107217196A CN 201710389387 A CN201710389387 A CN 201710389387A CN 107217196 A CN107217196 A CN 107217196A
- Authority
- CN
- China
- Prior art keywords
- sheet metal
- metal component
- high rigidity
- mass percent
- rigidity sheet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high rigidity sheet metal component, it is characterised in that：It is made up of the composition of following mass percent：Silicon≤0.2%, tungsten≤0.5%, titanium≤0.8%, aluminium≤2%, potassium≤0.35%, sodium≤0.55%, surplus is iron.The beneficial effects of the invention are as follows：Proportioning is scientific and reasonable, enhances resistance to slip abrasion, abrasive wear and the erosive resistance of part, is adapted to wide popularization and application, improves service life, the titanium and potassium of addition are not easy to break, the good characteristic of security.
Description
Technical field
The present invention relates to a kind of sheet metal component, more particularly to a kind of high rigidity sheet metal component.
Background technology
Metal plate is a kind of for sheet metal（Generally in below 6mm）Synthesis cold machining process, including cut, rush/cutting/and answer
Close, folding, welding, riveting, splicing, shaping（Such as body of a motor car）Deng.Its significant feature is exactly Same Part consistency of thickness.Pass through
The product that metal plate industry is processed is called sheet metal component.The signified sheet metal component of different industries is typically different, title when being used for assembling
Exhale.The manufacture method of sheet metal component is a lot, but sheet metal component generally existing quality prepared by current manufacture method is general, easily rust
Erosion, adaptive capacity to environment is poor, and service life is short；Non- desulfurization process causes fragility big, and easy fracture has potential safety hazard；Coating is not
Uniformly, the problems such as coating is easy to fall off.Further, the sheet metal component generally existing piece surface anti-wear performance of current technique manufacture is poor,
The problem of service life is short.
Therefore, to solve the above problems, special provide a kind of new technical scheme.
The content of the invention
The present invention provides a kind of high rigidity sheet metal component.
The technical solution adopted by the present invention is：
A kind of high rigidity sheet metal component, it is characterised in that：It is made up of the composition of following mass percent：Silicon≤0.2%, tungsten≤0.5%,
Titanium≤0.8%, aluminium≤2%, potassium≤0.35%, sodium≤0.55%, surplus is iron.
Further, the mass percent of the tungsten is 0.1-0.5.
Further, the mass percent of the titanium is 0.3-0.8.
Further, the mass percent of the aluminium is 0.5-2.
Further, the mass percent of the potassium is 0.12-0.35.
Further, the mass percent of the sodium is 0.2-0.55.
Further, the mass percent of the silicon is 0.1-0.2.
The beneficial effects of the invention are as follows：Proportioning is scientific and reasonable, enhances resistance to slip abrasion, abrasive wear and the anti-impact of part
Polishing machine is lost, is adapted to wide popularization and application, improves service life, the titanium and potassium of addition are not easy to break, the good spy of security
Property.
Embodiment
In order to deepen the understanding of the present invention, below in conjunction with embodiment, the invention will be further described, the embodiment
It is only used for explaining the present invention, does not constitute the restriction to protection scope of the present invention.
Embodiment 1
A kind of high rigidity sheet metal component, it is characterised in that：It is made up of the composition of following mass percent：Silicon 0.1%, tungsten 0.1%, titanium
0.3%, aluminium 0.5%, potassium 0.12%, sodium 0.2%, surplus is iron.
The beneficial effects of the invention are as follows：Proportioning is scientific and reasonable, enhances resistance to slip abrasion, abrasive wear and the anti-impact of part
Polishing machine is lost, is adapted to wide popularization and application, improves service life, the titanium and potassium of addition are not easy to break, the good spy of security
Property.
Embodiment 2
A kind of high rigidity sheet metal component, it is characterised in that：It is made up of the composition of following mass percent：Silicon 0.15%, tungsten 0.35%, titanium
0.55%, aluminium 1%, potassium 0.25%, sodium 0.35%, surplus is iron.
The beneficial effects of the invention are as follows：Proportioning is scientific and reasonable, enhances resistance to slip abrasion, abrasive wear and the anti-impact of part
Polishing machine is lost, is adapted to wide popularization and application, improves service life, the titanium and potassium of addition are not easy to break, the good spy of security
Property.
Embodiment 3
A kind of high rigidity sheet metal component, it is characterised in that：It is made up of the composition of following mass percent：Silicon 0.2%, tungsten 0.5%, titanium
0.8%, aluminium 2%, potassium 0.35%, sodium 0.55%, surplus is iron.
The beneficial effects of the invention are as follows：Proportioning is scientific and reasonable, enhances resistance to slip abrasion, abrasive wear and the anti-impact of part
Polishing machine is lost, is adapted to wide popularization and application, improves service life, the titanium and potassium of addition are not easy to break, the good spy of security
Property.
The above described is only a preferred embodiment of the present invention, being not the limit for making any other form to the present invention
System, and any modification made according to technical spirit of the invention or equivalent variations, still fall within model claimed of the invention
Enclose.
Claims (7)
1. a kind of high rigidity sheet metal component, it is characterised in that：It is made up of the composition of following mass percent：Silicon≤0.2%, tungsten≤
0.5%, titanium≤0.8%, aluminium≤2%, potassium≤0.35%, sodium≤0.55%, surplus is iron.
2. a kind of high rigidity sheet metal component according to claim 1, it is characterised in that：The mass percent of the tungsten is 0.1-
0.5。
3. a kind of high rigidity sheet metal component according to claim 1, it is characterised in that：The mass percent of the titanium is 0.3-
0.8。
4. a kind of high rigidity sheet metal component according to claim 1, it is characterised in that：The mass percent of the aluminium is 0.5-
2。
5. a kind of high rigidity sheet metal component according to claim 1, it is characterised in that：The mass percent of the potassium is
0.12-0.35。
6. a kind of high rigidity sheet metal component according to claim 1, it is characterised in that：The mass percent of the sodium is 0.2-
0.55。
7. a kind of high rigidity sheet metal component according to claim 1, it is characterised in that：The mass percent of the silicon is 0.1-
0.2。