CN105420581A - Ceramic metal material - Google Patents
Ceramic metal material Download PDFInfo
- Publication number
- CN105420581A CN105420581A CN201510759341.1A CN201510759341A CN105420581A CN 105420581 A CN105420581 A CN 105420581A CN 201510759341 A CN201510759341 A CN 201510759341A CN 105420581 A CN105420581 A CN 105420581A
- Authority
- CN
- China
- Prior art keywords
- parts
- oxide
- ceramic
- metal material
- ceramic metal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a ceramic metal material. The ceramic metal material is composed of, by weight, 15-30 parts of iron oxide, 5-15 parts of zirconium oxide, 10-20 parts of aluminum oxide, 15-35 parts of silicon nitride, 5-15 parts of silicon dioxide, 3-8 parts of calcium borate, 2-5 parts of lithium oxide, 5-10 parts of paraffin, 2-5 parts of zinc stearate, 1-10 parts of copper powder, 1-6 parts of zinc oxide and 3-8 parts of polyvinyl alcohol. Compared with the prior art, the ceramic metal material has good abrasion resistance, corrosion resistance and impact resistance; meanwhile, the defect that ceramic is poor in flexibility is overcome, and good characteristics of alloy metal are kept; besides, heat resistance is high, ductility is high, and the service life of a product is prolonged.
Description
Technical field
The present invention relates to technical field of metal, be specifically related to a kind of ceramic metallic material.
Background technology
The matrix material that ceramic-metal composite is made up of with metallographic phase or alloy one or more ceramic phases.Pottery in sintering metal has high-melting-point, the oxide compound of high rigidity or compound hard to tolerate, and metallographic phase is transition element and alloy thereof mainly.Different according to each composition phase percentage, sintering metal is divided into pottery for matrix and is matrix two kinds with metal.
Along with the development of new technology revolution, require the development improving constantly machining productivity and reduce production cost, particularly numerically-controlled machine, require the new-type cutter that exploitation is higher than inserted tool cutting speed, more wear-resisting.Current various high strength, high rigidity, corrosion-resistant, wear-resisting and resistant to elevated temperatures be difficult to cut novel material increasing.At present, Vertical Mill is a kind of desirable large-scale milling equipment, is widely used in the industries such as cement, electric power, metallurgy, chemical industry, nonmetalliferous ore, and collection fragmentation, drying, grinding, classification are transported in one, production efficiency is high, bulk, particulate state and powder raw material can be worn into required pulverulent material.But which type of alloy metal material no matter the grinding roller on Vertical Mill use, because environment for use is severe, serious wear, therefore work-ing life is all very short, probably 5000 hours (half a year is more), affects Vertical Mill output greatly like this.
Therefore for the problems referred to above, of the present inventionly a kind of new technical scheme is proposed.
Summary of the invention
The object of this invention is to provide a kind of ceramic metallic material with excellent abrasive resistance, corrosion-resistant, anti-impact pressure.
The present invention is achieved through the following technical solutions:
A kind of ceramic metallic material, comprises the raw material composition of following parts by weight: ferric oxide 15 ~ 30 parts, zirconium white 5 ~ 15 parts, 10 ~ 20 parts, aluminum oxide, silicon nitride 15 ~ 35 parts, silicon-dioxide 5 ~ 15 parts, lime borate 3 ~ 8 parts, Lithium Oxide 98min 2 ~ 5 parts, 5 ~ 10 parts, paraffin, Zinic stearas 2 ~ 5 parts, copper powder 1 ~ 10 part, 1 ~ 6 part, zinc oxide, polyvinyl alcohol 3 ~ 8 parts.
Preferably, a kind of ceramic metallic material, comprises the raw material composition of following parts by weight: ferric oxide 15 ~ 25 parts, zirconium white 8 ~ 15 parts, 12 ~ 20 parts, aluminum oxide, silicon nitride 15 ~ 30 parts, silicon-dioxide 5 ~ 10 parts, lime borate 3 ~ 8 parts, Lithium Oxide 98min 2 ~ 5 parts, 5 ~ 10 parts, paraffin, Zinic stearas 2 ~ 5 parts, copper powder 2 ~ 8 parts, 1 ~ 4 part, zinc oxide, polyvinyl alcohol 3 ~ 8 parts.
Preferably, the nano-carbon powder of 2 ~ 10 parts is also comprised.
The invention has the beneficial effects as follows: compared with prior art, material proposed by the invention, there is excellent abrasive resistance, corrosion-resistant, anti-impact pressure, also overcome the shortcoming of ceramic poor in flexibility simultaneously, maintain the superperformance of alloyed metal, and thermotolerance is strong, ductility is high, improves the work-ing life of product.
Embodiment
Below in conjunction with embodiment, the present invention is described further.
Embodiment 1
A kind of ceramic metallic material, comprises the raw material composition of following parts by weight: ferric oxide 15 parts, zirconium white 5 parts, 10 parts, aluminum oxide, silicon nitride 15 parts, silicon-dioxide 5 parts, lime borate 3 parts, Lithium Oxide 98min 2 parts, 5 parts, paraffin, Zinic stearas 2 parts, copper powder 1 part, 1 part, zinc oxide, polyvinyl alcohol 3 parts, nano-carbon powder 2 parts.
Embodiment 2
A kind of ceramic metallic material, comprises the raw material composition of following parts by weight: ferric oxide 22 parts, zirconium white 10 parts, 15 parts, aluminum oxide, silicon nitride 22 parts, silica 10 part, lime borate 5 parts, Lithium Oxide 98min 3 parts, 7 parts, paraffin, Zinic stearas 3 parts, copper powder 5 parts, 3 parts, zinc oxide, polyvinyl alcohol 5 parts, nano-carbon powder 7 parts.
Embodiment 3
A kind of ceramic metallic material, comprises the raw material composition of following parts by weight: ferric oxide 30 parts, zirconium white 15 parts, 20 parts, aluminum oxide, silicon nitride 35 parts, silica 15 parts, lime borate 8 parts, Lithium Oxide 98min 5 parts, 10 parts, paraffin, Zinic stearas 5 parts, copper powder 10 parts, 6 parts, zinc oxide, polyvinyl alcohol 8 parts, nano-carbon powder 10 parts.
Compared with prior art, material proposed by the invention, has excellent abrasive resistance, corrosion-resistant, anti-impact pressure, also overcome the shortcoming of ceramic poor in flexibility simultaneously, maintain the superperformance of alloyed metal, and, thermotolerance is strong, and ductility is high, improves the work-ing life of product.
The above is only embodiments of the invention, is not restriction the present invention being made to any other form, and any amendment done according to embodiment proposed by the invention or equivalent variations, still belong to the present invention's scope required for protection.
Claims (3)
1. a ceramic metallic material, is characterized in that: the raw material composition comprising following parts by weight: ferric oxide 15 ~ 30 parts, zirconium white 5 ~ 15 parts, 10 ~ 20 parts, aluminum oxide, silicon nitride 15 ~ 35 parts, silicon-dioxide 5 ~ 15 parts, lime borate 3 ~ 8 parts, Lithium Oxide 98min 2 ~ 5 parts, 5 ~ 10 parts, paraffin, Zinic stearas 2 ~ 5 parts, copper powder 1 ~ 10 part, 1 ~ 6 part, zinc oxide, polyvinyl alcohol 3 ~ 8 parts.
2. a kind of ceramic metallic material according to claim 1, is characterized in that: the raw material composition comprising following parts by weight: ferric oxide 15 ~ 25 parts, zirconium white 8 ~ 15 parts, 12 ~ 20 parts, aluminum oxide, silicon nitride 15 ~ 30 parts, silicon-dioxide 5 ~ 10 parts, lime borate 3 ~ 8 parts, Lithium Oxide 98min 2 ~ 5 parts, 5 ~ 10 parts, paraffin, Zinic stearas 2 ~ 5 parts, copper powder 2 ~ 8 parts, 1 ~ 4 part, zinc oxide, polyvinyl alcohol 3 ~ 8 parts.
3. a kind of ceramic metallic material according to claim 1, is characterized in that: the nano-carbon powder also comprising 2 ~ 10 parts.