CN107216781A - A kind of breakage-proof coating of coloured glaze and its manufacture craft - Google Patents
A kind of breakage-proof coating of coloured glaze and its manufacture craft Download PDFInfo
- Publication number
- CN107216781A CN107216781A CN201710590762.5A CN201710590762A CN107216781A CN 107216781 A CN107216781 A CN 107216781A CN 201710590762 A CN201710590762 A CN 201710590762A CN 107216781 A CN107216781 A CN 107216781A
- Authority
- CN
- China
- Prior art keywords
- parts
- coloured glaze
- breakage
- coating
- proof coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of breakage-proof coating of coloured glaze, its raw material composition is：Ethylenic unsaturation propyl group polyester resin：70 80 parts, styrene：20 25 parts, polymerization inhibitor：12 parts, levelling agent：0.3 1 parts, smooth agent：0.5 1.5 parts, cobalt octoate：0.1 3 parts, ethyl acetate：0.5 1 parts, methyl ethyl ketone peroxide：0.5 1.5 parts, lead dibatyl phithalate：0.5 1.5 parts, above-mentioned number is mass fraction.A kind of manufacture craft of the breakage-proof coating of coloured glaze, comprises the following steps；Ethylenic unsaturation propyl group polyester resin, styrene, polymerization inhibitor, levelling agent and smooth agent are placed in melting pot and carry out miscible filtering to obtain coating；Cobalt octoate and ethyl acetate are placed in normal temperature melting pot and carry out miscible filtering to obtain accelerator；Methyl ethyl ketone peroxide and neck dibatyl phithalate are placed in normal temperature melting pot and carry out miscible filtering to obtain curing agent；Then coating, accelerator and curing agent are sprayed to the surface of coloured glaze in sequence successively.Coating obtained by the present invention can allow the hard light in coloured glaze surface after being sprayed on coloured glaze.
Description
Technical field
The present invention relates to a kind of coating, especially a kind of breakage-proof coating of coloured glaze and its manufacture craft.
Background technology
Coloured glaze has a long history, and its quality is glittering and translucent, bright and glittering, changes irregularly magnificent, fully demonstrates Asians
It is exquisite, fine and smooth and implicit, be a kind of important decoration element, common coloured glaze is typically all that comparison is crisp in the market, very
It is fragile, it is difficult to reduce the fragility of coloured glaze for conventional art and technique, thus can be collided bad casual when.
The content of the invention
The technical problems to be solved by the invention be overcome the defect of prior art there is provided a kind of breakage-proof coating of coloured glaze and its
Manufacture craft, the fragility of coloured glaze outer surface is reduced by external protection,.
In order to solve the above technical problems, the present invention provides a kind of breakage-proof coating of coloured glaze, it is characterised in that its raw material is constituted
For：
Ethylenic unsaturation propyl group polyester resin：70-80 parts；
Styrene：20-25 parts；
Polymerization inhibitor：1-2 parts；
Levelling agent：0.3-1 parts；
Smooth agent：0.5-1.5 parts；
Cobalt octoate：0.1-3 parts；
Ethyl acetate：0.5-1 parts；
Methyl ethyl ketone peroxide：0.5-1.5 parts；
Lead dibatyl phithalate：0.5-1.5 parts；
Above-mentioned number is mass fraction.
A kind of foregoing breakage-proof coating of coloured glaze, it is characterised in that the solids content of the ethylenic unsaturation propyl group polyester resin
For 80%.
A kind of foregoing breakage-proof coating of coloured glaze, it is characterised in that the mass fraction of the ethylenic unsaturation propyl group polyester resin
For 75 parts.
The foregoing breakage-proof coating of a kind of coloured glaze, it is characterised in that the solids content of the cobalt octoate is 12%.
The foregoing breakage-proof coating of a kind of coloured glaze, it is characterised in that the mass fraction of the styrene is 22 parts.
The manufacture craft of the foregoing breakage-proof coating of a kind of coloured glaze, it is characterised in that comprise the following steps；
Step one：By 70-80 parts of ethylenic unsaturation propyl group polyester resin, 20-25 parts of styrene, 1-2 parts of polymerization inhibitor, levelling agent 0.3-
1 part, 0.5-1.5 parts of smooth agent is placed in normal temperature melting pot and carries out miscible, obtained coating after filtering；
Step 2：By 0.5-1 parts of 0.1-3 parts of cobalt octoate and ethyl acetate, it is placed in normal temperature melting pot and carries out miscible, system after filtering
Obtain accelerator；
Step 3：By 0.5-1.5 parts of methyl ethyl ketone peroxide and 0.5-1.5 parts of dibatyl phithalate of neck, normal temperature melting pot is placed in
It is interior to carry out miscible, obtained curing agent after filtering；
Step 4：Then coating, accelerator and curing agent are sprayed to the surface of coloured glaze in sequence successively.
The beneficial effect that the present invention is reached：Coating obtained by the present invention can allow coloured glaze after being sprayed on coloured glaze
The hard light in surface, rapid draing, and with preferably guarantor's light and colour retention, and this coating is clear coat, Bu Huifang
Hinder the expression that coloured glaze is attractive in appearance.
Embodiment
The present invention is further described below.Following examples are only used for clearly illustrating the technical side of the present invention
Case, and can not be limited the scope of the invention with this.
A kind of breakage-proof coating of coloured glaze, its raw material, which is constituted, is：
Ethylenic unsaturation propyl group polyester resin：70-80 parts；
Styrene：20-25 parts；
Polymerization inhibitor：1-2 parts；
Levelling agent：0.3-1 parts；
Smooth agent：0.5-1.5 parts；
Cobalt octoate：0.1-3 parts；
Ethyl acetate：0.5-1 parts；
Methyl ethyl ketone peroxide：0.5-1.5 parts；
Lead dibatyl phithalate：0.5-1.5 parts；
Above-mentioned number is mass fraction.
It is preferred that, the solids content of the ethylenic unsaturation propyl group polyester resin is 80%.
It is preferred that, the mass fraction of the ethylenic unsaturation propyl group polyester resin is 75 parts.
It is preferred that, the solids content of the cobalt octoate is 12%.
It is preferred that, the mass fraction of the styrene is 22 parts.
A kind of manufacture craft of the breakage-proof coating of coloured glaze, comprises the following steps；
Step one：By 70-80 parts of ethylenic unsaturation propyl group polyester resin, 20-25 parts of styrene, 1-2 parts of polymerization inhibitor, levelling agent 0.3-
1 part, 0.5-1.5 parts of smooth agent is placed in normal temperature melting pot and carries out miscible, obtained coating after filtering；
Step 2：By 0.5-1 parts of 0.1-3 parts of cobalt octoate and ethyl acetate, it is placed in normal temperature melting pot and carries out miscible, system after filtering
Obtain accelerator；
Step 3：By 0.5-1.5 parts of methyl ethyl ketone peroxide and 0.5-1.5 parts of dibatyl phithalate of neck, normal temperature melting pot is placed in
It is interior to carry out miscible, obtained curing agent after filtering；
Step 4：Then coating, accelerator and curing agent are sprayed to the surface of coloured glaze in sequence successively.
The beneficial effect that the present invention is reached：Coating obtained by the present invention can allow coloured glaze after being sprayed on coloured glaze
The hard light in surface, rapid draing, and with preferably guarantor's light and colour retention, and this coating is clear coat, Bu Huifang
Hinder the expression that coloured glaze is attractive in appearance.
Described above is only the preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For member, without departing from the technical principles of the invention, some improvement and deformation can also be made, these improve and deformed
Also it should be regarded as protection scope of the present invention.
Claims (6)
1. a kind of breakage-proof coating of coloured glaze, it is characterised in that its raw material, which is constituted, is：
Ethylenic unsaturation propyl group polyester resin：70-80 parts；
Styrene：20-25 parts；
Polymerization inhibitor：1-2 parts；
Levelling agent：0.3-1 parts；
Smooth agent：0.5-1.5 parts；
Cobalt octoate：0.1-3 parts；
Ethyl acetate：0.5-1 parts；
Methyl ethyl ketone peroxide：0.5-1.5 parts；
Lead dibatyl phithalate：0.5-1.5 parts；
Above-mentioned number is mass fraction.
2. a kind of breakage-proof coating of coloured glaze according to claim 1, it is characterised in that the ethylenic unsaturation propyl group polyester resin
Solids content be 80%.
3. a kind of breakage-proof coating of coloured glaze according to claim 2, it is characterised in that the ethylenic unsaturation propyl group polyester resin
Mass fraction be 75 parts.
4. the breakage-proof coating of a kind of coloured glaze according to claim 1, it is characterised in that the solids content of the cobalt octoate is
12%。
5. the breakage-proof coating of a kind of coloured glaze according to claim 1, it is characterised in that the mass fraction of the styrene is 22
Part.
6. the manufacture craft of the breakage-proof coating of a kind of coloured glaze according to claim 1, it is characterised in that comprise the following steps；
Step one：By 70-80 parts of ethylenic unsaturation propyl group polyester resin, 20-25 parts of styrene, 1-2 parts of polymerization inhibitor, levelling agent 0.3-
1 part, 0.5-1.5 parts of smooth agent is placed in normal temperature melting pot and carries out miscible, obtained coating after filtering；
Step 2：By 0.5-1 parts of 0.1-3 parts of cobalt octoate and ethyl acetate, it is placed in normal temperature melting pot and carries out miscible, system after filtering
Obtain accelerator；
Step 3：By 0.5-1.5 parts of methyl ethyl ketone peroxide and 0.5-1.5 parts of dibatyl phithalate of neck, normal temperature melting pot is placed in
It is interior to carry out miscible, obtained curing agent after filtering；
Step 4：Then coating, accelerator and curing agent are sprayed to the surface of coloured glaze in sequence successively.