CN107216506A - A kind of oil resistant synthetic rubber - Google Patents
A kind of oil resistant synthetic rubber Download PDFInfo
- Publication number
- CN107216506A CN107216506A CN201710401882.6A CN201710401882A CN107216506A CN 107216506 A CN107216506 A CN 107216506A CN 201710401882 A CN201710401882 A CN 201710401882A CN 107216506 A CN107216506 A CN 107216506A
- Authority
- CN
- China
- Prior art keywords
- parts
- synthetic rubber
- oil resistant
- resistant synthetic
- rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of oil resistant synthetic rubber, in parts by mass, including following material:32 40 parts of haloflex, 52 60 parts of nitrile rubber, 8 parts of brombutyl, 8 parts of magnesia, 10 parts of white carbon, 23 parts of 01 reinforcing agents of XJ, 60 parts of N550 carbon blacks, 40 parts of N660 carbon blacks, 25 parts of fine particle calcium carbonate, 40 parts of dioctyl ester, 6 parts of zinc oxide, 1,801 3 parts of stearic acid, 1 part of paraffin, 3.2 parts of barium stearate, 2.3 parts of age resistor, 0.4 part of cTp antiscorching agent, modified 7.5 parts of coumarone resin, 1.9 parts of accelerator, 3.1 parts of sulphur.The oil resistant synthetic rubber of the present invention is made by conventional mixing, the characteristics of with high temperature resistant, oil resistivity, resistance to ozone, good air-tightness, and its compatibility, pliability, flexible resistance energy and oil resistance reach professional standard, and meeting production needs and user's needs.
Description
Technical field
The present invention relates to a kind of synthetic rubber, more particularly to a kind of oil resistant synthetic rubber.
Background technology
Rubber is divided into two kinds of natural rubber and synthetic rubber, for the characteristic of cost-effective raising rubber, in 20 generation
Record just starts produce synthetic rubber, developed rapidly after the forties, because its have high resiliency, insulating properties, air-tightness, oil resistant,
The performance such as high temperature resistant or low temperature, is widely used in industrial or agricultural, national defence, traffic and daily life.
The content of the invention
The present invention provides a kind of oil resistant synthetic rubber, and synthetic rubber has compatibility, pliability, flexible resistance energy, oil resistant
Professional standard can be reached with ageing-resistant performance.
To reach above-mentioned purpose, realized by following scheme:A kind of oil resistant synthetic rubber, it is characterised in that:Oil resistant is synthesized
Rubber is by mass parts:32-40 parts of haloflex, 52-60 parts of nitrile rubber, 8 parts of brombutyl, 8 parts of magnesia, in vain
10 parts of carbon black, 23 parts of XJ-01 reinforcing agents, 60 parts of N550 carbon blacks, 40 parts of N660 carbon blacks, 25 parts of fine particle calcium carbonate, 40 parts of dioctyl ester, oxidation
6 parts of zinc, 1,801 3 parts of stearic acid, 1 part of paraffin, 3.2 parts of barium stearate, 2.3 parts of age resistor, 0.4 part of cTp antiscorching agent is modified ancient
7.5 parts of the grand resin of horse, 1.9 parts of accelerator, 3.1 parts of sulphur.
It is preferred that, it is by mass parts:32 parts of haloflex, 60 parts of nitrile rubber, 8 parts of brombutyl, magnesia 8
Part, 10 parts of white carbon, 23 parts of XJ-01 reinforcing agents, 60 parts of N550 carbon blacks, 40 parts of N660 carbon blacks, 25 parts of fine particle calcium carbonate, 40 parts of dioctyl ester,
6 parts of zinc oxide, 1,801 3 parts of stearic acid, 1 part of paraffin, 3.2 parts of barium stearate, 2.3 parts of age resistor, 0.4 part of cTp antiscorching agent changes
7.5 parts of property coumarone resin, 1.9 parts of accelerator, 3.1 parts of sulphur.
It is preferred that, it is by mass parts:40 parts of haloflex, 52 parts of nitrile rubber, 8 parts of brombutyl, magnesia 8
Part, 10 parts of white carbon, 23 parts of XJ-01 reinforcing agents, 60 parts of N550 carbon blacks, 40 parts of N660 carbon blacks, 25 parts of fine particle calcium carbonate, 40 parts of dioctyl ester,
6 parts of zinc oxide, 1,801 3 parts of stearic acid, 1 part of paraffin, 3.2 parts of barium stearate, 2.3 parts of age resistor, 0.4 part of cTp antiscorching agent is modified
7.5 parts of coumarone resin, 1.9 parts of accelerator, 3.1 parts of sulphur.
The haloflex is haloflex 135A.
The nitrile rubber is nitrile rubber 3305.
The brombutyl is brombutyl 2039.
The age resistor is anti-aging agent RD, either antioxidant 4010NA or the combination of the two;Wherein:What the two was combined
Match as 1.1 parts of RD age resistor, 1.2 parts of 4010NA age resistor.
The accelerator is the combination of altax, either accelerant CZ or NA-22 vulcanization accelerators, or three;
Wherein:The proportioning of triplicity is 0.7 part of DM accelerator, 0.5 part of CZ accelerator, 0.7 part of NA-22 vulcanization accelerators.
The oil resistant synthetic rubber, is made by conventional compounding process.
Beneficial effect:
The oil resistant synthetic rubber of the present invention is kneaded by conventional method and is made, with high temperature resistant, oil resistivity, resistance to ozone, air-tightness
Good the characteristics of, compared with prior art oil resistant rubber, primary raw material is changed, by haloflex CPE, nitrile rubber
NBR, tri- kinds of primary raw materials of brombutyl BIIR composition, the synthetic rubber compatibility being made, pliability, flexible resistance energy,
Oil resistant and ageing-resistant performance can reach professional standard, and meeting production needs and user's needs, therefore, makees under oiliness environment
Oil-resisting rubber hose is used.
Embodiment
Embodiment 1:
A kind of oil resistant synthetic rubber, in parts by mass, including following components:32 parts of haloflex, 60 parts of nitrile rubber, bromination
8 parts of butyl rubber, 8 parts of magnesia, 10 parts of white carbon, 23 parts of XJ-01 reinforcing agents, 60 parts of N550 carbon blacks, 40 parts of N660 carbon blacks,
25 parts of fine particle calcium carbonate, 40 parts of dioctyl ester, 6 parts of zinc oxide, 1,801 3 parts of stearic acid, 1 part of paraffin, 3.2 parts of barium stearate, age resistor 2.3
Part, 0.4 part of cTp antiscorching agent, modified 7.5 parts of coumarone resin, 1.9 parts of accelerator, 3.1 parts of sulphur.
This kind of oil resistant synthetic rubber, routinely mixing is produced.
This kind of oil resistant synthetic rubber, oil resistance is good.
This kind of oil resistant synthetic rubber performance such as following table:
。
Embodiment 2:
A kind of oil resistant synthetic rubber, in parts by mass, including following components:40 parts of haloflex, 52 parts of nitrile rubber, bromination
8 parts of butyl rubber, 8 parts of magnesia, 10 parts of white carbon, 23 parts of XJ-01 reinforcing agents, 60 parts of N550 carbon blacks, 40 parts of N660 carbon blacks,
25 parts of fine particle calcium carbonate, 40 parts of dioctyl ester, 6 parts of zinc oxide, 1,801 3 parts of stearic acid, 1 part of paraffin, 3.2 parts of barium stearate, age resistor 2.3
Part, 0.4 part of cTp antiscorching agent, modified 7.5 parts of coumarone resin, 1.9 parts of accelerator, 3.1 parts of sulphur.
This kind of oil resistant synthetic rubber, routinely mixing is produced.
This kind of oil resistant synthetic rubber, oil resistance is good.
This kind of oil resistant synthetic rubber performance such as following table:
。
Invention can be further appreciated that by the embodiment of the present invention given above, above example is only the several of the present invention
Specific embodiment, but the present invention design be not limited thereto, it is all using this design to the present invention progress unsubstantiality change,
The behavior for invading the scope of the present invention all should be belonged to.
Claims (8)
1. a kind of oil resistant synthetic rubber, it is characterised in that in parts by mass, including following components:32-40 parts of haloflex,
52-60 parts of nitrile rubber, 8 parts of brombutyl, 8 parts of magnesia, 10 parts of white carbon, 23 parts of XJ-01 reinforcing agents, N550 charcoals
Black 60 parts, 40 parts of N660 carbon blacks, 25 parts of fine particle calcium carbonate, 40 parts of dioctyl ester, 6 parts of zinc oxide, 1,801 3 parts of stearic acid, 1 part of paraffin is stearic
Sour 3.2 parts of barium, 2.3 parts of age resistor, 0.4 part of cTp antiscorching agent, modified 7.5 parts of coumarone resin, 1.9 parts of accelerator, sulphur 3.1
Part;Oil resistant synthetic rubber is made by conventional mixing in above-mentioned formula.
2. oil resistant synthetic rubber according to claim 1, it is characterised in that in parts by mass, including following components:Chlorination
32 parts of polyethylene, 60 parts of nitrile rubber.
3. oil resistant synthetic rubber according to claim 1, it is characterised in that in parts by mass, including following components:Chlorination
40 parts of polyethylene, 52 parts of nitrile rubber.
4. according to any described oil resistant synthetic rubber of claims 1 to 3, it is characterised in that the haloflex is chlorination
Polyethylene 135A.
5. according to any described oil resistant synthetic rubber of claims 1 to 3, it is characterised in that the nitrile rubber is butyronitrile rubber
Glue 3305.
6. oil resistant synthetic rubber according to claim 1, it is characterised in that the brombutyl is butyl rubber bromide
Glue 2039.
7. oil resistant synthetic rubber according to claim 1, it is characterised in that the age resistor is anti-aging agent RD or anti-
Old agent 4010NA or the combination of the two;Wherein the two proportioning combined is 1.1 parts of RD age resistor, 1.2 parts of 4010NA age resistor.
8. oil resistant synthetic rubber according to claim 1, it is characterised in that the accelerator is altax, or is promoted
Enter agent CZ, either the combination of NA-22 vulcanization accelerators or three;Wherein the proportioning of triplicity is 0.7 part of DM accelerator,
0.5 part of CZ accelerator, 0.7 part of NA-22 vulcanization accelerators.