CN107215036A - A kind of aluminium honeycomb diamond plate and its manufacture method - Google Patents
A kind of aluminium honeycomb diamond plate and its manufacture method Download PDFInfo
- Publication number
- CN107215036A CN107215036A CN201710317639.6A CN201710317639A CN107215036A CN 107215036 A CN107215036 A CN 107215036A CN 201710317639 A CN201710317639 A CN 201710317639A CN 107215036 A CN107215036 A CN 107215036A
- Authority
- CN
- China
- Prior art keywords
- plate
- aluminium
- aluminium alloy
- alloy plate
- figured
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to a kind of art work, more particularly, to a kind of aluminium honeycomb diamond plate and its manufacture method.It is mainly the composite plate solved present in prior art and is made up of three layers, five layers of unlike material thin layer, and processing technology is complicated, and decorative pattern is that outer surface is printed or coated and forms, the technical problem easily come off under the adverse circumstances such as expose to the sun and rain etc..The present invention includes being sequentially provided with aluminum honeycomb panel, Figured aluminium plate on aluminium alloy plate, aluminium alloy plate, and aluminium alloy plate, aluminum honeycomb panel, Figured aluminium plate are combined with each other by rubberised layer.The present invention takes aluminium alloy plate, and Figured aluminium plate is cold rolled to through patterned roll, takes aluminium foil and aluminum honeycomb panel is made after gluing, compound rolling, drying；Aluminium alloy plate is made in aluminium alloy plate after cold rolling；Using coating machine on aluminium alloy plate gluing, Figured aluminium plate, aluminium alloy plate are compounded on aluminum honeycomb panel, pressed after heating, are sheared and can go out finished product aluminium honeycomb diamond plate through stamping plate platform.
Description
Technical field
The present invention relates to a kind of art work, more particularly, to a kind of aluminium honeycomb diamond plate and its manufacture method.
Background technology
Current existing aluminum honeycomb panel is generally aluminium-plastic panel or aluminum veneer, there is certain decorative effect, but without fire prevention, it is heat-insulated,
The functions such as sound insulation.Chinese patent discloses a kind of Metal composite honeycomb decorative plate and its manufacture method（Publication number：CN
103129026 A）, it is made up of five layers of unlike material thin layer, including honeycomb metal core plate, macromolecule membranous layer and planar metal
Thin plate, wherein, intermediate layer is honeycomb metal core plate, and honeycomb metal core plate upper and lower surface is macromolecule membranous layer, polymeric membrane
Layer outside is planar metal sheet, and honeycomb decoration plate is by the hot composite molding of above-mentioned five layers of thin layer；Its method is：（1）Take thickness
The sheet metal for being 300-1800mm for 0.1-3mm, width, upper and lower surface covers macromolecule membranous layer, and macromolecule membranous layer thickness is
0.03-1mm；（2）The sheet metal for covering macromolecule membranous layer is transmitted to automatic punching machine equipment automatically, continuous punching is into honeycomb
Shape, stamping forming honeycomb metal plate thickness is between 1-20mm；（3）Covered on the outside of the macromolecule membranous layer of honeycomb metal plate
Lid planar metal sheet, composite honeycomb board is compounded to form by heat, and planar metal sheet thickness is 0.1-2mm；（4）In compound honeybee
The printing of planar metal sheet outer surface or coating of nest plate have different colours, the metal-protective paint of decorative pattern.Chinese patent is also public
A kind of perforated plate with roller-coating pattern is opened（Authorization Notice No.：CN2809077）, it has an at least three-decker, including intermediate layer and
Upper surface layer and undersurface layer positioned at the intermediate layer both sides；Intermediate layer is cellular board, and upper surface layer and undersurface layer are all
Aluminium sheet；The outer surface roller coat of upper surface layer and/or undersurface layer has decorative pattern.But these composite plates are by three layers, five layers of different materials
Matter thin layer is constituted, and processing technology is complicated, and decorative pattern is that outer surface is printed or coated and forms, under the adverse circumstances such as expose to the sun and rain
Easily come off.
The content of the invention
The present invention is to provide a kind of aluminium honeycomb diamond plate and its manufacture method, and it is mainly present in solution prior art
Composite plate is made up of three layers, five layers of unlike material thin layer, and processing technology is complicated, and decorative pattern is outer surface printing or coating
Into the technical problem easily come off under the adverse circumstances such as expose to the sun and rain etc..
The above-mentioned technical problem of the present invention is mainly what is be addressed by following technical proposals：
A kind of aluminium honeycomb diamond plate of the present invention, including aluminium alloy plate, the upper surface of described aluminium alloy plate is sequentially provided with aluminium honeybee
Nest plate, Figured aluminium plate, aluminium alloy plate, aluminum honeycomb panel, Figured aluminium plate are combined with each other by rubberised layer.
Aluminium honeycomb diamond plate is by upper strata Figured aluminium plate, middle level aluminum honeycomb panel and lower floor's aluminium alloy plate by gluing, compound, baking
It is composited after dry, static pressure.
The difficult point of the present invention is Figured aluminium plate unlike flat board aluminium sheet, it is impossible to is cleaned, rolled using traditional cleaning way
In Figured aluminium plate processed, decorative pattern plate surface band oil is more, and washing or alkali cleaning can not be extracted with rubber roll, and remained on surface is water stain；And use
The cleaning of low-flash solvent naphtha can then avoid it is water stain, but can oil residues, moistened surface tension force is extremely difficult to 32N, and common
Flat aluminium sheet can be easily reached 76N using washing or alkali cleaning moistened surface tension force.And general glue and oil are immiscible, therefore very
Easy degumming, Figured aluminium plate of the invention is pre-processed before gluing, and using Wire brush roller by the wire drawing texturing of the aluminium sheet back side, oil is cleaned
And sided corona treatment, so that the aluminium sheet after compound is difficult degumming.And the decorative pattern of roller coat is easily protected from environmental and falls paint, decorative pattern
The decorative pattern of aluminium sheet will not change, durable in use, and with good skidproof effect.The present invention have also been devised one automation
Recombination line, so as to realize batch production, reduces production cost.
Preferably, described Figured aluminium plate is formed by aluminium alloy plate rolling, aluminium alloy plate is rolled aluminium alloy plate.
A kind of manufacture method of aluminium honeycomb diamond plate, described method includes：
A. take thickness for 3-5mm aluminium alloy plates, 0.1-3.0mm Figured aluminium plate be cold rolled to through patterned roll, carry out oil cleaning and
Sided corona treatment；Take 0.01-0.1mm aluminium foils and aluminum honeycomb panel is made after gluing, compound rolling, drying；Thickness is taken for 3-8mm
Aluminium alloy plate, is made the aluminium alloy plate that thickness is 0.1-1.0mm after cold rolling；
B. using coating machine in the upper surface of aluminium alloy plate, the lower surface gluing of Figured aluminium plate, then by recombination line by decorative pattern
Aluminium sheet is compounded in the upper surface of aluminum honeycomb panel, and aluminium alloy plate is compounded in the lower surface of aluminum honeycomb panel, the sheet material feeding after being combined
Heated in baking oven；
C. the sheet material after drying enters pressing line and pressed, then by cutter by sheet shearing to required length, most
It can go out finished product aluminium honeycomb diamond plate by plate platform is stamped.
Pretreatment and compound two procedures of the innovative point of the present invention in Figured aluminium plate, difficult point is that diamond plate is uneven,
Operation of rolling band oil, and difficulty of deoiling, oil are not allowed with glue, easy degumming, so those skilled in the art can not make.The present invention is adopted
The attachment of Figured aluminium plate and glue is improved with the method for unique Figured aluminium plate pretreatment mode-wire drawing, oil cleaning, corona；It is multiple
The compound ability of glue is improved using the combined temp control of Discrete control during conjunction, and infrared heating can be by the metallic aluminium short time
Inside it is heated to the temperature of technological requirement.
Preferably, the temperature of described baking oven is 50-200 DEG C, wind speed is 1.0-3.0m/s.Baking oven uses segmented control
The combined temp control program of system, mode of heating is infrared heating, and with hot air circulation combined drying glue, the temperature of baking oven can
Adjust.
Preferably, described sheet material is sent to after baking oven, 50-80 DEG C is first to heat to, 20-30min is incubated, then with 10
DEG C/min speed cools to 10-20 DEG C, is incubated 20-30min；Be heated to 120-150 DEG C, be incubated 20-30min, then with
10 DEG C/min speed cools to 50-70 DEG C, is incubated 20-30min；Finally heated to 180-200 DEG C, 20-30min is incubated, so
After cool to room temperature.
Therefore, the compound number of plies of the present invention is few, and simple production process, production efficiency is high；Aluminium honeycomb diamond plate has attractive in appearance, anti-
Sliding, corrosion-resistant, solderable, lightweight, intensity is high, shock resistance, sound insulation, it is heat-insulated the advantages of；The decorative pattern of diamond plate is permanent flower
Line, is not in roller coated pattern or prints the problem of decorative pattern comes off.Available for architecture indoor external decoration, furniture, tool box bottom plate,
Floor etc..
Brief description of the drawings
Accompanying drawing 1 is a kind of structural representation of the present invention；
Accompanying drawing 2 is a kind of structural representation of process equipment of the present invention；
Accompanying drawing 3 is a kind of structural representation of patterned roll of the present invention.
Parts, position and numbering in figure：Aluminium alloy plate 1, aluminum honeycomb panel 2, Figured aluminium plate 3, coating machine 4, recombination line 5,
Baking oven 6, pressing line 7, cutter 8, stamp plate platform 9, roll body 10, flower-pattern layer 11, wire brush 12.
Embodiment
Below by embodiment, and with reference to accompanying drawing, technical scheme is described in further detail.
Embodiment：A kind of aluminium honeycomb diamond plate of this example, such as Fig. 1, by up of three layers, including upper strata：Figured aluminium plate 3；In
Layer：Aluminum honeycomb panel 2；Lower floor：Aluminium alloy plate 1.Wherein, upper strata Figured aluminium plate is formed by aluminium alloy plate rolling, middle level aluminum honeycomb panel
It is made up of aluminium foil after gluing, compound rolling, drying, lower floor's aluminium alloy plate is rolled aluminium alloy plate.Aluminium honeycomb diamond plate is by upper
Layer Figured aluminium plate, middle level aluminum honeycomb panel and lower floor's aluminium alloy plate are composited after gluing, compound, drying, static pressure.
A kind of manufacture method of aluminium honeycomb diamond plate, its step is：Such as Fig. 2,
A. take thickness for 3-5mm aluminium alloy plates, 0.1-3.0mm Figured aluminium plate 3 be cold rolled to through patterned roll, carry out oil cleaning and
Sided corona treatment；Take 0.01-0.1mm aluminium foils and aluminum honeycomb panel 2 is made after gluing, compound rolling, drying；Thickness is taken for 3-
8mm aluminium alloy plates, are made the aluminium alloy plate 1 that thickness is 0.1-1.0mm after cold rolling；Such as Fig. 3, patterned roll includes roll body 10,
The outer surface of roll body is provided with flower-pattern layer 11, is provided with wire brush 12 in the middle part of flower-pattern layer, opposite direction from wire brush to roll body rotation direction
Tilt；
B. coating machine 4 is utilized in the upper surface of aluminium alloy plate 1, the lower surface gluing of Figured aluminium plate 3, then will by recombination line 5
Figured aluminium plate is compounded in the upper surface of aluminum honeycomb panel 2, and aluminium alloy plate is compounded in the lower surface of aluminum honeycomb panel 2, the plate after being combined
Material, which is sent in baking oven 6, to be heated；Baking oven uses the combined temp control program that segmented is controlled, and mode of heating is red
External heat, with hot air circulation combined drying glue, the temperature of baking oven is adjustable, and temperature range is between 50-200 DEG C, and wind speed is
1.0-3.0m/s。
C. the sheet material after drying enters pressing line 7 and pressed, and is then grown sheet shearing to required by cutter 8
Degree, most can go out finished product aluminium honeycomb diamond plate through stamping plate platform 9 afterwards.
The specific embodiment of the present invention is the foregoing is only, but the architectural feature of the present invention is not limited thereto, Ren Heben
The technical staff in field is in the field of the invention, and the change or modification made all are covered among the scope of the claims of the present invention.
Claims (6)
1. a kind of aluminium honeycomb diamond plate, including aluminium alloy plate（1）, it is characterised in that described aluminium alloy plate（1）Upper surface according to
It is secondary to be provided with aluminum honeycomb panel（2）, Figured aluminium plate（3）, aluminium alloy plate, aluminum honeycomb panel（2）, Figured aluminium plate pass through rubberised layer（4）It is compound
Together.
2. a kind of aluminium honeycomb diamond plate according to claim 1, it is characterised in that described Figured aluminium plate（3）By aluminium alloy
Plate rolling is formed, and aluminium alloy plate is rolled aluminium alloy plate.
3. a kind of manufacture method of aluminium honeycomb diamond plate, it is characterised in that described method includes：
A. thickness is taken for 3-5mm aluminium alloy plates, and 0.1-3.0mm Figured aluminium plate is cold rolled to through patterned roll（3）, carry out oily cleaning
And sided corona treatment；Take 0.01-0.1mm aluminium foils and aluminum honeycomb panel is made after gluing, compound rolling, drying（2）；Taking thickness is
3-8mm aluminium alloy plates, are made the aluminium alloy plate that thickness is 0.1-1.0mm after cold rolling（1）；
B. coating machine is utilized（4）In aluminium alloy plate（1）Upper surface, Figured aluminium plate（3）Lower surface gluing, then by compound
Line（5）Figured aluminium plate is compounded in aluminum honeycomb panel（2）Upper surface, aluminium alloy plate is compounded in aluminum honeycomb panel（2）Lower surface,
Sheet material after compound is sent to baking oven（6）It is interior to be heated；
C. the sheet material after drying enters pressing line（7）Pressed, then pass through cutter（8）By sheet shearing to required length
Degree, most afterwards through stamping plate platform（9）Finished product aluminium honeycomb diamond plate can be gone out.
4. a kind of manufacture method of aluminium honeycomb diamond plate according to claim 3, it is characterised in that the temperature of described baking oven
Spend for 50-200 DEG C, wind speed is 1.0-3.0m/s.
5. a kind of manufacture method of aluminium honeycomb diamond plate according to claim 3, it is characterised in that described patterned roll bag
Roll body is included（10）, the outer surface of roll body is provided with flower-pattern layer（11）, flower-pattern layer middle part is provided with wire brush（12）, wire brush is to roll body
The opposite direction of rotation direction is tilted.
6. a kind of manufacture method of aluminium honeycomb diamond plate according to claim 4, it is characterised in that described sheet material feeding
To after baking oven, 50-80 DEG C is first to heat to, 20-30min is incubated, 10-20 DEG C, insulation are then cooled to 10 DEG C/min speed
20-30min；120-150 DEG C is heated to, 20-30min is incubated, 50-70 DEG C, guarantor are then cooled to 10 DEG C/min speed
Warm 20-30min；Finally heated to 180-200 DEG C, 20-30min is incubated, room temperature is then cooled to.