CN107198824A - 一种远红外抗菌纤维离子贴剂 - Google Patents
一种远红外抗菌纤维离子贴剂 Download PDFInfo
- Publication number
- CN107198824A CN107198824A CN201710420950.3A CN201710420950A CN107198824A CN 107198824 A CN107198824 A CN 107198824A CN 201710420950 A CN201710420950 A CN 201710420950A CN 107198824 A CN107198824 A CN 107198824A
- Authority
- CN
- China
- Prior art keywords
- far
- biotic
- additive
- infrared
- fibrous
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本申请涉及一种远红外抗菌纤维离子贴剂，该贴剂由上至下依次由油光面托纸层、表面覆盖层、离子堆积层、远红外抗菌纤维层、粘贴层构成，并依次紧密粘贴排列；上述所述的远红外抗菌纤维层中，其原料按照重量百分比包括：负离子添加剂3％；远红外添加剂7％；聚酯纤维90％。
Description
技术领域
本申请涉及医疗器械敷料及贴剂技术领域，尤其涉及一种远红外抗菌纤维离子贴剂。
背景技术
由于工作、生活环境的变化，越来越多的人正遭受着由跌打损伤导致的肌肉、关节、骨质增生、肌肉及软组织损伤，引起各类疼痛、肿胀等各类病变，有些患处还容易受到感染，给患者带来极大地痛苦。目前用于消肿止痛、抗菌消炎的治疗，市面上存在形形色色的产品，但主要还是依靠药物的治疗方法，其中相当部分药物的疗效还难以令人满意，而且药物治疗伤痛时间长，存在一定的毒副作用。
电磁场具有镇静、止痛、消炎、化瘀、止泄和改善人体生物电的作用，对治疗骨折、骨质增生、肌肉及软组织损伤具有一定的疗效；远红外线可以改善血液循环、缓解肌肉紧张、减轻疼痛、以及调节自主神经的作用，对于治疗扭伤、骨折、肌腱炎、骨液囊炎、结核组织炎等病症有较好的疗效。但是目前市面上的产品主要还是以单一功能为主，在临床治疗上受到一定的限制。尽管发明专利CN 104147701 A报道了一种驻极体静电远红外贴及其制备方法，该产品在消肿止痛方面具有显著疗效，然而对于某些伴随有微生物感染的伤痛尚缺乏明显的效果，而且驻极体的电荷在使用过程中衰减较快也限制了产品的时效。
发明内容
本发明旨在提供一种远红外抗菌纤维离子贴剂，以解决上述提出问题。
本发明的实施例中提供了一种远红外抗菌纤维离子贴剂，该贴剂由上至下依次由油光面托纸层、表面覆盖层、离子堆积层、远红外抗菌纤维层、粘贴层构成，并依次紧密粘贴排列；上述所述的远红外抗菌纤维层中，其原料按照重量百分比包括：负离子添加剂3％；远红外添加剂7％；聚酯纤维90％。
优选地，所述的负离子添加剂中包括：添加剂载体、电气石负离子粉。
优选地，所述的远红外添加剂中包括：添加剂载体、太极石粉体、纳米二氧化硅、纳米氧化铝、纳米氧化锰、纳米氧化钙。
本发明的实施例提供的技术方案可以包括以下有益效果：
1.本发明公开的远红外抗菌纤维离子贴剂中的离子堆积层具有驻极特性，可以稳定储存电荷，同时产生局部持续的高压静电场，使患处骨骼，肌肉，血管，神经，关节等组织的电解质发生相应的极化，病变部位离子迁移，激活细胞，修复细胞组织，从而改善病变部位的疼痛症状；
2.本发明公开的远红外抗菌纤维层中含有负离子添加剂、远红外添加剂，具有杀菌除臭、改善心肌功能、促进新陈代谢、增强肌体抗病能力，有利于缓解病痛；
3.本发明公开的负离子添加剂、远红外添加剂中含有添加剂载体，该添加剂载体为一种TiO2空心球颗粒，该TiO2空心球颗粒以花粉为模板制备，然后经过退火过程将花粉去除，得益于花粉表面凹凸的结构，该TiO2空心球颗粒的表面表现为类似花粉的开放的孔网状结构，该开放的孔网状结构能够有效吸附负离子、远红外粉体；同时由于TiO2空心球颗粒粒径较大，其在聚酯纤维中分散均匀，导致其吸附的负离子、远红外粉体也能够均匀分散在聚酯纤维中，有效改善团聚现象的发生。
本申请附加的方面和优点将在下面的描述中部分给出，部分将从下面的描述中变得明显，或通过本申请的实践了解到。应当理解的是，以上的一般描述和后文的细节描述仅是示例性和解释性的，并不能限制本申请。
附图说明
利用附图对本发明作进一步说明，但附图中的实施例不构成对本发明的任何限制，对于本领域的普通技术人员，在不付出创造性劳动的前提下，还可以根据以下附图获得其它的附图。
图1是本发明一种远红外抗菌纤维离子贴剂的截面结构示意图；
其中，1-油光面托纸层，2-表面覆盖层，3-离子堆积层，4-远红外抗菌纤维层，5-粘贴层。
具体实施方式
下面结合具体实施例，进一步阐述本发明。应当理解，这些实施例仅用于说明本发明而不用于限制本发明的范围。此外应理解，在阅读了本发明讲授的内容之后，本领域技术人员可以对本发明作各种改动或修改，这些等价形式同样落于本申请所附权利要求书所限定的范围。
本申请的实施例涉及一种远红外抗菌纤维离子贴剂，结合图1，该贴剂由上至下依次由油光面托纸层1、表面覆盖层2、离子堆积层3、远红外抗菌纤维层4、粘贴层5构成，并依次紧密粘贴排列；所述的油光面托纸层1为格拉辛硅油纸，表面覆盖层2为铝箔或铜箔，离子堆积层3由PTFE膜经离子堆积工艺加工制得，粘贴层5为低致敏性的医用压敏胶无纺布，该远红外抗菌纤维层4是以聚酯纤维为基底，以远红外添加剂、负离子添加剂为填料，通过熔融混纺，制备得到的一种具有负离子、远红外功能的聚酯功能纤维。
该远红外抗菌纤维层4的尺寸小于粘贴层5的尺寸，该离子堆积层3为圆形结构，尺寸小于远红外抗菌纤维层4的尺寸；该表面覆盖层2的尺寸大于远红外抗菌纤维层4的尺寸；该剥离层1的形状和尺寸与粘贴层5相同。
在一种优选地实施方式中，上述所述的远红外抗菌纤维层4中，其原料按照重量百分比包括：负离子添加剂3％；远红外添加剂7％；聚酯纤维90％。
上述所述的负离子添加剂包括：添加剂载体、电气石负离子粉；其中，各物质按照质量份数为：添加剂载体17份、电气石负离子粉5份；各物质的粒径为：添加剂载体50μm、电气石负离子粉500nm。
上述所述的远红外添加剂包括：添加剂载体、太极石粉体、纳米二氧化硅、纳米氧化铝、纳米氧化锰、纳米氧化钙；其中，各物质按照质量份数为：添加剂载体20份、太极石粉体8份、纳米二氧化硅5份、纳米氧化铝3份、纳米氧化锰2份、纳米氧化钙3份；各物质的粒径为：添加剂载体50μm、太极石粉体2μm、纳米二氧化硅300nm、纳米氧化铝100nm、纳米氧化锰50nm、纳米氧化钙100nm。
本申请的技术方案中，对于远红外效应，远红外添加剂中包含有太极石，太极石是一种天然矿石，其主要成分为二氧化硅，不具有任何放射性物质，对人体具有多种有益功能；比如，太极石具有辐射远红外线的功能，从而促进血液循环，使人体升温保暖，加快新陈代谢；太极石还具有抗紫外线、抗菌的功能。如今，将太极石应用于功能材料，特别是将太极石与聚酯纤维相结合，进行功能化改进的方案不多。
此外，在实现聚酯纤维功能化的过程中，通过添加具有远红外发射功能、负离子发射功能的无机粉料是一种常用的技术，但是直接将无机粉体加入到聚酯纤维中，由于粉体表面比表面积较大，粉体之间作用力相互吸引，极易形成团聚体，阻碍了粉体的分散，导致聚酯纤维中无机粉体的作用发挥不明显，改性效果不显著；由于电气石负离子粉能够产生负离子效应，而纳米二氧化硅、纳米氧化铝等是一种常用的远红外粒子，其能够产生远红外辐射，从而产生发热的效果；但是通常情况下是将上述两种物质直接添加到聚酯纤维中来对其进行功能化改进，正如以上所述，由于粒径的纳米团聚效应，直接添加的方法会导致纳米粒子的团聚，影响负离子、远红外发射的效果。
因此，在本申请的负离子添加剂、远红外添加剂中均含有一种添加剂载体，该添加剂载体为一种TiO2空心球颗粒。
在形貌方面：该TiO2空心球颗粒以花粉为模板制备，然后经过退火过程将花粉去除，得益于花粉表面凹凸的结构，该TiO2空心球颗粒的表面表现为类似花粉的开放的孔网状结构，该开放的孔网状结构能够有效吸附负离子、远红外粉体；而且，由于TiO2空心球颗粒粒径较大，其在聚酯纤维中分散均匀，导致其吸附的负离子、远红外粉体也能够均匀分散在聚酯纤维中，有效改善团聚现象的发生。
在性质方面，传统上，二氧化钛是一种化学性质稳定的半导体材料，一般表现为光催化性能，用于光催化自清洁材料，或者用于造纸、橡胶等制品中，作为填充剂、着色剂使用，而本申请中，将TiO2空心球颗粒创造性的作为添加剂载体，由于其特殊的结构，对于负离子粉体、远红外粒子等的吸附作用强，并且在聚酯纤维中分散均匀，在本申请的远红外抗菌纤维层中起到关键作用。
在一种优选地实施方式中，涉及该远红外抗菌纤维离子贴剂的制备方法，其制备工艺包括如下步骤：
步骤1，该添加剂载体的制备过程为：首先，筛选出直径50μm的油菜花花粉，取20g用酒精漂洗、干燥；然后，向300ml的去例子水中加入9g的Ti(SO4)2，搅拌20min，再向上述去离子水中加入1.2g的氟化铵和3.8g的尿素，搅拌60min，再向上述去离子水中加入20g油菜花花粉，搅拌20min，将上述去离子水转移到水热釜中，将其在180℃水热反应20h，反应结束后，收集水热釜中白色沉淀，并将其清洗干净，在干燥箱中60℃下干燥15h，然后将其放入马弗炉中460℃退火2h，490℃退火1h，升温速率为2℃/min，退火过程中会将花粉颗粒去除，退火结束后，得到TiO2空心球颗粒，即为添加剂载体；
步骤2，该负离子添加剂和远红外添加剂的制备过程为：
将添加剂载体、电气石负离子粉、钛酸酯偶联剂加入到去例子水中，充分搅拌均匀，得到负离子添加剂浆料，然后将其烘干，研磨成粉，即得负离子添加剂；
将添加剂载体、太极石粉体、纳米二氧化硅、纳米氧化铝、纳米氧化锰、纳米氧化钙、钛酸酯偶联剂加入到去例子水中，充分搅拌均匀，得到远红外添加剂浆料，然后将其烘干，研磨成粉，即得远红外添加剂；
步骤3，该远红外抗菌纤维层4的制备过程为：将远红外添加剂、负离子添加剂和乙二醇混合，搅拌后在室温下超声5h，得到混合液；然后将混合液与精对苯二甲酸、催化助剂进行酯化，聚合，得到聚酯母粒，其中，酯化温度为250℃，压力300KPa，酯化率达到大于94.1％时进行缩聚反应，缩聚温度为280℃，抽真空至40Mpa，缩聚至特性粘度为0.68时，出料，切料，得到聚酯母粒；将聚酯母粒进行干燥，通过熔融挤压纺丝，经后处理加工，得到复合纤维；取防风置于热水中浸泡5h后过滤，取滤液，将复合纤维放入滤液中进行浸泡，浸泡12h后过滤烘干复合纤维，在复合纤维表面喷入苍耳子提取物，冷冻干燥，得到远红外抗菌纤维层4；
步骤4，该远红外抗菌纤维离子贴剂的制备过程为：依次取油光面托纸层1、表面覆盖层2、离子堆积层3、远红外抗菌纤维层4和粘贴层5，并按从上至下的顺序依次层叠，紧密粘结，得到远红外抗菌纤维离子贴剂。
实施例1
步骤1，该添加剂载体的制备过程为：首先，筛选出直径50μm的油菜花花粉，取20g用酒精漂洗、干燥；然后，向300ml的去例子水中加入9g的Ti(SO4)2，搅拌20min，再向上述去离子水中加入1.2g的氟化铵和3.8g的尿素，搅拌60min，再向上述去离子水中加入20g油菜花花粉，搅拌20min，将上述去离子水转移到水热釜中，将其在180℃水热反应20h，反应结束后，收集水热釜中白色沉淀，并将其清洗干净，在干燥箱中60℃下干燥15h，然后将其放入马弗炉中460℃退火2h，490℃退火1h，升温速率为2℃/min，退火过程中会将花粉颗粒去除，退火结束后，得到TiO2空心球颗粒，即为添加剂载体；
步骤2，该负离子添加剂和远红外添加剂的制备过程为：
将添加剂载体、电气石负离子粉、钛酸酯偶联剂加入到去例子水中，充分搅拌均匀，得到负离子添加剂浆料，然后将其烘干，研磨成粉，即得负离子添加剂；
将添加剂载体、纳米氧化铝、纳米氧化锰、纳米氧化钙、钛酸酯偶联剂加入到去例子水中，充分搅拌均匀，得到远红外添加剂浆料，然后将其烘干，研磨成粉，即得远红外添加剂；
步骤3，该远红外抗菌纤维层4的制备过程为：将远红外添加剂、负离子添加剂和乙二醇混合，搅拌后在室温下超声5h，得到混合液；然后将混合液与精对苯二甲酸、催化助剂进行酯化，聚合，得到聚酯母粒，其中，酯化温度为250℃，压力300KPa，酯化率达到大于94.1％时进行缩聚反应，缩聚温度为280℃，抽真空至40Mpa，缩聚至特性粘度为0.68时，出料，切料，得到聚酯母粒；将聚酯母粒进行干燥，通过熔融挤压纺丝，经后处理加工，得到复合纤维；取防风置于热水中浸泡5h后过滤，取滤液，将复合纤维放入滤液中进行浸泡，浸泡12h后过滤烘干复合纤维，在复合纤维表面喷入苍耳子提取物，冷冻干燥，得到远红外抗菌纤维层4；
步骤4，该远红外抗菌纤维离子贴剂的制备过程为：依次取油光面托纸层1、表面覆盖层2、离子堆积层3、远红外抗菌纤维层4和粘贴层5，并按从上至下的顺序依次层叠，紧密粘结，得到远红外抗菌纤维离子贴剂。
实施例2
步骤1，该添加剂载体的制备过程为：首先，筛选出直径50μm的油菜花花粉，取20g用酒精漂洗、干燥；然后，向300ml的去例子水中加入9g的Ti(SO4)2，搅拌20min，再向上述去离子水中加入1.2g的氟化铵和3.8g的尿素，搅拌60min，再向上述去离子水中加入20g油菜花花粉，搅拌20min，将上述去离子水转移到水热釜中，将其在180℃水热反应20h，反应结束后，收集水热釜中白色沉淀，并将其清洗干净，在干燥箱中60℃下干燥15h，然后将其放入马弗炉中460℃退火2h，490℃退火1h，升温速率为2℃/min，退火过程中会将花粉颗粒去除，退火结束后，得到TiO2空心球颗粒，即为添加剂载体；
步骤2，该负离子添加剂和远红外添加剂的制备过程为：
将添加剂载体、电气石负离子粉、钛酸酯偶联剂加入到去例子水中，充分搅拌均匀，得到负离子添加剂浆料，然后将其烘干，研磨成粉，即得负离子添加剂；
将添加剂载体、纳米二氧化硅、纳米氧化铝、纳米氧化锰、纳米氧化钙、钛酸酯偶联剂加入到去例子水中，充分搅拌均匀，得到远红外添加剂浆料，然后将其烘干，研磨成粉，即得远红外添加剂；
步骤3，该远红外抗菌纤维层4的制备过程为：将远红外添加剂、负离子添加剂和乙二醇混合，搅拌后在室温下超声5h，得到混合液；然后将混合液与精对苯二甲酸、催化助剂进行酯化，聚合，得到聚酯母粒，其中，酯化温度为250℃，压力300KPa，酯化率达到大于94.1％时进行缩聚反应，缩聚温度为280℃，抽真空至40Mpa，缩聚至特性粘度为0.68时，出料，切料，得到聚酯母粒；将聚酯母粒进行干燥，通过熔融挤压纺丝，经后处理加工，得到复合纤维；取防风置于热水中浸泡5h后过滤，取滤液，将复合纤维放入滤液中进行浸泡，浸泡12h后过滤烘干复合纤维，在复合纤维表面喷入苍耳子提取物，冷冻干燥，得到远红外抗菌纤维层4；
步骤4，该远红外抗菌纤维离子贴剂的制备过程为：依次取油光面托纸层1、表面覆盖层2、离子堆积层3、远红外抗菌纤维层4和粘贴层5，并按从上至下的顺序依次层叠，紧密粘结，得到远红外抗菌纤维离子贴剂。
实施例3
步骤1，该添加剂载体的制备过程为：首先，筛选出直径50μm的油菜花花粉，取20g用酒精漂洗、干燥；然后，向300ml的去例子水中加入9g的Ti(SO4)2，搅拌20min，再向上述去离子水中加入1.2g的氟化铵和3.8g的尿素，搅拌60min，再向上述去离子水中加入20g油菜花花粉，搅拌20min，将上述去离子水转移到水热釜中，将其在180℃水热反应20h，反应结束后，收集水热釜中白色沉淀，并将其清洗干净，在干燥箱中60℃下干燥15h，然后将其放入马弗炉中460℃退火2h，490℃退火1h，升温速率为2℃/min，退火过程中会将花粉颗粒去除，退火结束后，得到TiO2空心球颗粒，即为添加剂载体；
步骤2，该负离子添加剂和远红外添加剂的制备过程为：
将添加剂载体、电气石负离子粉、钛酸酯偶联剂加入到去例子水中，充分搅拌均匀，得到负离子添加剂浆料，然后将其烘干，研磨成粉，即得负离子添加剂；
将添加剂载体、太极石粉体、纳米二氧化硅、纳米氧化铝、纳米氧化锰、纳米氧化钙、钛酸酯偶联剂加入到去例子水中，充分搅拌均匀，得到远红外添加剂浆料，然后将其烘干，研磨成粉，即得远红外添加剂；
步骤3，该远红外抗菌纤维层4的制备过程为：将远红外添加剂、负离子添加剂和乙二醇混合，搅拌后在室温下超声5h，得到混合液；然后将混合液与精对苯二甲酸、催化助剂进行酯化，聚合，得到聚酯母粒，其中，酯化温度为250℃，压力300KPa，酯化率达到大于94.1％时进行缩聚反应，缩聚温度为280℃，抽真空至40Mpa，缩聚至特性粘度为0.68时，出料，切料，得到聚酯母粒；将聚酯母粒进行干燥，通过熔融挤压纺丝，经后处理加工，得到复合纤维；取防风置于热水中浸泡5h后过滤，取滤液，将复合纤维放入滤液中进行浸泡，浸泡12h后过滤烘干复合纤维，在复合纤维表面喷入苍耳子提取物，冷冻干燥，得到远红外抗菌纤维层4；
步骤4，该远红外抗菌纤维离子贴剂的制备过程为：依次取油光面托纸层1、表面覆盖层2、离子堆积层3、远红外抗菌纤维层4和粘贴层5，并按从上至下的顺序依次层叠，紧密粘结，得到远红外抗菌纤维离子贴剂。
利用远红外线照射下升温的原理，采用远红外温升法测试装置测试本申请的远红外抗菌纤维离子贴剂的远红外性能：在相同条件下，由于本申请实施例1-3中的贴剂采用了远红外抗菌纤维层，与采用纯PET纤维层的贴剂相比，温度升高的多，采用纯PET纤维层的贴剂在1000s内温度升高了11.3℃，而实施例1-3中的贴剂在1000s内温度分别升高了19.1℃、21.8℃、24.6℃，说明本申请中所述的远红外抗菌纤维离子贴剂表现良好的远红外发射功能，具有良好的实用性，能有效发挥蓄热保暖、促进血液循环等作用。
以上所述仅为本发明的较佳方式，并不用以限制本发明，凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (8)
1.一种远红外抗菌纤维离子贴剂，其特征在于，该贴剂由上至下依次由油光面托纸层、表面覆盖层、离子堆积层、远红外抗菌纤维层、粘贴层构成，并依次紧密粘贴排列；上述所述的远红外抗菌纤维层中，其原料按照重量百分比包括：负离子添加剂3％；远红外添加剂7％；聚酯纤维90％。
2.根据权利要求1所述的一种远红外抗菌纤维离子贴剂，其特征在于，所述的负离子添加剂中包括：添加剂载体、电气石负离子粉；各物质的质量份数为：添加剂载体17份、电气石负离子粉5份；各物质的粒径为：添加剂载体50μm、电气石负离子粉500nm。
3.根据权利要求1所述的一种远红外抗菌纤维离子贴剂，其特征在于，所述的远红外添加剂中包括：添加剂载体、太极石粉体、纳米二氧化硅、纳米氧化铝、纳米氧化锰、纳米氧化钙。
4.根据权利要求3所述的一种远红外抗菌纤维离子贴剂，其特征在于，所述的远红外添加剂中，各物质的质量份数为：添加剂载体20份、太极石粉体8份、纳米二氧化硅5份、纳米氧化铝3份、纳米氧化锰2份、纳米氧化钙3份。
5.根据权利要求4所述的一种远红外抗菌纤维离子贴剂，其特征在于，所述的远红外添加剂中，各物质的粒径为：添加剂载体50μm、太极石粉体2μm、纳米二氧化硅300nm、纳米氧化铝100nm、纳米氧化锰50nm、纳米氧化钙100nm。
6.根据权利要求1-5任一项所述的一种远红外抗菌纤维离子贴剂的制备方法，其特征在于，所述的制备工艺具体步骤如下：
步骤1，该添加剂载体的制备过程为：首先，筛选出直径50μm的油菜花花粉，取20g用酒精漂洗、干燥；然后，向300ml的去例子水中加入9g的Ti(SO4)2，搅拌20min，再向上述去离子水中加入1.2g的氟化铵和3.8g的尿素，搅拌60min，再向上述去离子水中加入20g油菜花花粉，搅拌20min，将上述去离子水转移到水热釜中，将其在180℃水热反应20h，反应结束后，收集水热釜中白色沉淀，并将其清洗干净，在干燥箱中60℃下干燥15h，然后将其放入马弗炉中460℃退火2h，490℃退火1h，升温速率为2℃/min，退火过程中会将花粉颗粒去除，退火结束后，得到TiO2空心球颗粒，即为添加剂载体；
步骤2，该负离子添加剂和远红外添加剂的制备过程为：
将添加剂载体、电气石负离子粉、钛酸酯偶联剂加入到去例子水中，充分搅拌均匀，得到负离子添加剂浆料，然后将其烘干，研磨成粉，即得负离子添加剂；
将添加剂载体、太极石粉体、纳米二氧化硅、纳米氧化铝、纳米氧化锰、纳米氧化钙、钛酸酯偶联剂加入到去例子水中，充分搅拌均匀，得到远红外添加剂浆料，然后将其烘干，研磨成粉，即得远红外添加剂；
步骤3，该远红外抗菌纤维层的制备过程为：将远红外添加剂、负离子添加剂和乙二醇混合，搅拌后在室温下超声5h，得到混合液；然后将混合液与精对苯二甲酸、催化助剂进行酯化，聚合，得到聚酯母粒，其中，酯化温度为250℃，压力300KPa，酯化率达到大于94.1％时进行缩聚反应，缩聚温度为280℃，抽真空至40Mpa，缩聚至特性粘度为0.68时，出料，切料，得到聚酯母粒；将聚酯母粒进行干燥，通过熔融挤压纺丝，经后处理加工，得到复合纤维；取防风置于热水中浸泡5h后过滤，取滤液，将复合纤维放入滤液中进行浸泡，浸泡12h后过滤烘干复合纤维，在复合纤维表面喷入苍耳子提取物，冷冻干燥，得到远红外抗菌纤维层；
步骤4，该远红外抗菌纤维离子贴剂的制备过程为：依次取油光面托纸层、表面覆盖层、离子堆积层、远红外抗菌纤维层和粘贴层，并按从上至下的顺序依次层叠，紧密粘结，得到远红外抗菌纤维离子贴剂。
7.根据权利要求6所述的一种远红外抗菌纤维离子贴剂的制备方法，其特征在于，所述的油光面托纸层为格拉辛硅油纸，表面覆盖层为铝箔或铜箔，离子堆积层由PTFE膜经离子堆积工艺加工制得，粘贴层为低致敏性的医用压敏胶无纺布。
8.根据权利要求7所述的一种远红外抗菌纤维离子贴剂的制备方法，其特征在于，该远红外抗菌纤维层的尺寸小于粘贴层的尺寸，该离子堆积层为圆形结构，尺寸小于远红外抗菌纤维层的尺寸；该表面覆盖层的尺寸大于远红外抗菌纤维层的尺寸；该剥离层的形状和尺寸与粘贴层相同。