CN107189687A - A kind of modulator approach of plant paint tree milk liquid composite coating - Google Patents
A kind of modulator approach of plant paint tree milk liquid composite coating Download PDFInfo
- Publication number
- CN107189687A CN107189687A CN201710444820.3A CN201710444820A CN107189687A CN 107189687 A CN107189687 A CN 107189687A CN 201710444820 A CN201710444820 A CN 201710444820A CN 107189687 A CN107189687 A CN 107189687A
- Authority
- CN
- China
- Prior art keywords
- pretreatment
- lacquer
- emulsion
- tree
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of blacking preparation method based on natural raw lacquer.There is provided a kind of plant paint tree milk liquid compound modulator approach.The pretreatment of lacquer tree emulsion：Raw lacquer is filtered into impurity elimination, is 14 20 revs/min of lower stirring at normal temperature in rotating speed in input oxidation polymerization machine, until lacquer tree emulsion moisture is 5 6%, as can be untill the ㎝ newton bodies of wire drawing 6 10；The pretreatment of vegetable oil：The linseed oil of the double drifts of 40 parts of processes is mixed into input with 60 points of tung oil to polymerize in pot, 245 DEG C are heated to, 4 parts of rosin powder of input, which are together stirred, to be boiled, and is discharged fume simultaneously.When rosin melts completely, be warming up to 275 DEG C, kept for 18 25 minutes, detect viscosity, when vegetable oil turn into can the ㎝ newton body of wire drawing 6 10 can take the dish out of the pot, and stir exhausting smoke evacuation and be cooled to normal temperature.Lacquer tree emulsion and vegetable oil by pretreatment is pressed 50:50 weight in input kneader than mediating 23 hours.
Description
Technical field
The present invention relates to a kind of modulator approach of plant paint tree milk liquid composite coating.
Background technology
Raw lacquer (Raw laequer) refers to the bast scarfing outflow from lacquer tree (Rhus verniciflua Stokes)
Milky white emulsion body.Main component include laccol (60-70%), colloid (5-7%), water-insoluble glycoprotein (- 1%),
Rhus Laccase (- 0.24%) and moisture content (20-25%) etc..When connect melt air after, its color and luster because of oxidation from the superficial to the deep, in proper order
Dark brown is faded to, a kind of hard paint film is eventually become.Raw lacquer paint film is hard bright, wear-resisting, heat-resisting, corrosion-resistant.It is a kind of
Natural paint, in China using existing more than 7000 years usage history, there is the appellation of coating " first ancestor ", politics, warp to China
Help, culture life once produced material impact, was the great discovery after four inventions.Use for convenience, improve its decoration
Performance and other physics and chemistry combination properties, people take all multi-methods to be modified, compound that many raw lacquer coatings have been made.
A kind of natural emulsion of get off is tapped from lacquer tree to be needed to be modified modulation according to technological requirement and could use.
Due to the influence of the factors such as seeds, the place of production, the mode of production, storage time, the poor quality opposite sex is fairly obvious.In lacquer tree emulsion
Main film forming substance laccol is the mixture that catechol base is constituted with aliphatic chain, includes saturation laccol, monoene laccol, two
Alkene laccol, triolefin laccol etc., also, the ratio that these laccols can be shared in laccol total amount due to the difference in seeds and the place of production
Example and chemical constitution are also differed, and complicated composition brings certain difficulty to the modulation modification of lacquer tree emulsion..
The content of the invention
The technical problem to be solved in the present invention is to provide a kind of modulator approach of plant paint tree milk liquid composite coating.
The technical scheme is that：A kind of modulator approach of plant paint tree milk liquid composite coating, it is characterised in that plus
Work method comprises the following steps：
(a) pretreatment of lacquer tree emulsion：
Lacquer tree emulsion is filtered in impurity elimination, input oxidation polymerization machine, is 13-20 revs/min of lower stirring at normal temperature in rotating speed, directly
It is 5-6% to raw lacquer moisture, as can be untill wire drawing 6-10 ㎝ newton bodies；
(b) pretreatment of vegetable oil：
The 40-50 portions of linseed oil by double drifts are polymerize in pot with 60 parts of tung oil inputs, 245 DEG C is heated to, puts into 3-4
Part rosin powder, which is together stirred, to be boiled, and opens air exhauster smoke evacuation；When rosin melts completely, 275 DEG C are warming up to, is kept for 18-25 points
Clock, detect viscosity, when linseed oil turn into can wire drawing 6-10 ㎝ newton bodies can take the dish out of the pot, and stir exhausting smoke evacuation be cooled to normal temperature；
(c) mediate：
Lacquer tree emulsion and vegetable oil by pretreatment is pressed 50:50 weight in input kneader than mediating 2-3 hours
As plant paint tree milk liquid composite coating.
A kind of modulator approach of plant paint tree milk liquid composite coating of the present invention, it is characterised in that processing method is included such as
Lower step：
(a) pretreatment of lacquer tree emulsion：
Lacquer tree emulsion is filtered in impurity elimination, input oxidation polymerization machine, is 13-15 revs/min of lower stirring at normal temperature in rotating speed, directly
It is 5-6% to moisture, as can be untill wire drawing 6-10 ㎝ newton bodies；
(b) pretreatment of vegetable oil：
The linseed oil of the double drifts of 40 parts of processes is polymerize in pot with 60 parts of tung oil inputs, 245 DEG C is heated to, puts into 4 parts of rosin
Powder is together stirred and boiled, and opens air exhauster smoke evacuation；When rosin melts completely, 275 DEG C are warming up to, is kept for 18-25 minutes, inspection
Viscosimetric, when linseed oil turn into can wire drawing 6-10 ㎝ newton bodies can take the dish out of the pot, and stir exhausting smoke evacuation be cooled to normal temperature；
(c) mediate：
Lacquer tree emulsion and vegetable oil by pretreatment is pressed 50:50 weight in input vacuum kneader than mediating 2-3
Hour is plant paint tree milk liquid composite coating.
It is as follows that a kind of modulator approach of plant paint tree milk liquid composite coating of the present invention is characterized in that processing method includes
Step：
(a) pretreatment of lacquer tree emulsion：
Lacquer tree emulsion is filtered in impurity elimination, input oxidation polymerization machine, is 14-20 revs/min of lower stirring at normal temperature in rotating speed, directly
It is 5-6% to raw lacquer moisture, raw lacquer liquid turns into can be untill wire drawing 6-10 ㎝ newton bodies；
(b) pretreatment of vegetable oil：
The linseed oil of the double drifts of 40 parts of processes is mixed into input with 60 parts of tung oil to polymerize in pot, 245 DEG C is heated to, puts into 4 parts
Rosin powder, which is together stirred, to be boiled, and opens air exhauster smoke evacuation.When rosin melts completely, 275 DEG C are warming up to, is kept for 18-25 minutes,
Detect viscosity, when vegetable oil turn into can wire drawing 6-10 ㎝ newton bodies can take the dish out of the pot, and stir exhausting smoke evacuation be cooled to normal temperature.
(c) mediate
Vegetable oil by pretreatment is pressed 50 with lacquer tree emulsion:50 weight in input kneader than mediating 2-3 hours
As transparent raw lacquer coating.
A kind of modulator approach of plant paint tree milk liquid composite coating of the present invention, signified natural raw lacquer refers to from lacquer tree
The emulsion got off is tapped on (Rhus verniciflur stokes), it includes raw lacquer, Vietnam's raw lacquer, Laos's life
Paint, Thailand's raw lacquer, Japanese raw lacquer etc..
A kind of beneficial effect of the modulator approach of plant paint tree milk liquid composite coating of the present invention is due to using new work
Skill, wherein without the metal ion drier such as organic solvent and manganese, lead, mercury, zirconium, so that it is high-quality to provide a kind of environmental protection
Plant paint tree milk liquid composite coating modulator approach.
The modulator approach for the plant paint tree milk liquid composite coating that the present invention is provided is the special oil for lacquer tree emulsion
What bag water-bound was carried out.Main film forming substance laccol in lacquer tree emulsion is that catechol base is constituted from different aliphatic chain bases
Mixture, includes saturation laccol, monoene laccol, diene laccol, triolefin laccol etc., also, these laccols can due to seeds and
The difference in the place of production and ratio and chemical constitution shared in laccol total amount is also differed.In addition, in lacquer tree emulsion also
Containing laccase, moisture, gumminess, oil content etc., these compositions also due to seeds, the place of production, storage, the difference of the mode of production,
Their relative scales in system can also change.This technology by control laccol polymerize molecular weight and moisture,
The Abietyl modified linseed oil of addition, tung oil, are aided with kneading, obtain plant paint tree milk liquid composite coating and modulator approach.
The plant paint tree milk liquid composite coating provided using the present invention is detected according to national standard；
1st, the reset condition of plant paint tree milk liquid composite coating；
Table 1
2nd, plant paint tree milk liquid composite coating paint film property；
Table 2
Embodiment
Below in conjunction with the embodiment of the present invention, the technical scheme in the embodiment of the present invention is clearly and completely retouched
State, it is clear that described embodiment is only a part of embodiment of the invention, rather than whole embodiments.Based on the present invention
In embodiment, the every other implementation that those of ordinary skill in the art are obtained under the premise of creative work is not made
Example, belongs to the scope of protection of the invention.
Embodiment 1：A kind of modulator approach of plant paint tree milk liquid composite coating, in the following manner：1st, lacquer tree emulsion
Pretreatment：By the manly big wooden lacquer tree emulsion filtering impurity elimination of water content 25%, put into oxidation polymerization machine, be 14- in rotating speed
20 revs/min of lower stirring at normal temperature, until raw lacquer moisture is 5-6%, raw lacquer liquid turns into can be untill wire drawing 6-10 ㎝ newton bodies；
2nd, the pretreatment of vegetable oil：The linseed oil of the double drifts of 40 parts of processes is polymerize in pot with 60 parts of tung oil inputs, 245 DEG C, throwing are heated to
Enter 4 parts of rosin powder and together stir to boil, open air exhauster smoke evacuation.When rosin melts completely, 275 DEG C are warming up to, 18- is kept
25 minutes, detect viscosity, when linseed oil turn into can wire drawing 6-10 ㎝ newton bodies can take the dish out of the pot, and stir exhausting smoke evacuation be cooled to
Normal temperature.3rd, the raw lacquer and linseed oil by pretreatment are pressed 50:Mediated in 50 weight ratio input kneader and 2-3 hours be
Can.
Embodiment 2：A kind of modulator approach of plant paint tree milk liquid composite coating, 1, the pretreatment of lacquer tree emulsion：It will contain
The Shaanxi clovershrub lacquer tree emulsion of manly big wooden the lacquer tree emulsion and water content 30% of water 25% presses 1:1 weight is than mixing
(average moisture content 27.5%) is filtered in impurity elimination, input oxidation polymerization machine, is 14-20 revs/min of lower stirring at normal temperature in rotating speed, directly
It is 5-6% to raw lacquer moisture, as can be untill wire drawing 6-10 ㎝ newton bodies；2nd, the pretreatment of vegetable oil：By 40 parts of processes
The linseed oil of double drifts polymerize in pot with 60 parts of tung oil inputs, is heated to 245 DEG C, and 4 parts of rosin powder of input, which are together stirred, to be boiled,
Open air exhauster smoke evacuation.When rosin melts completely, 275 DEG C are warming up to, is kept for 18-25 minute, detection viscosity, as can wire drawing
6-10 ㎝ newton bodies can take the dish out of the pot, and stir exhausting smoke evacuation be cooled to normal temperature.3rd, by the lacquer tree emulsion by pretreatment and plant
Oil presses 50:50 weight in input kneader than mediating 2-3 hours.
Embodiment 3：A kind of modulator approach of plant paint tree milk liquid composite coating, in the following manner：1st, raw lacquer is pre-
Processing：The early lacquer tree emulsion in Guizhou the west of Guizhou Province of manly big wooden the lacquer tree emulsion and water content 32% of water content 25% is pressed 1:1 weight
Amount is put into oxidation polymerization machine than mixing (average moisture content 28.5%) filtering impurity elimination, is 14-20 revs/min of lower normal temperature in rotating speed
Stirring, until moisture is 5-6%, as can be untill wire drawing 6-10 ㎝ newton bodies；2nd, the pretreatment of vegetable oil：By 40 parts
Linseed oil by double drifts polymerize in pot with 60 parts of tung oil inputs, is heated to 245 DEG C, and 4 parts of rosin powder of input, which are together stirred, to be endured
System, opens air exhauster smoke evacuation.When rosin melts completely, 275 DEG C are warming up to, is kept for 18-25 minutes, viscosity is detected, works as linseed oil
As can wire drawing 6-10 ㎝ newton bodies can take the dish out of the pot, and stir exhausting smoke evacuation be cooled to normal temperature.3rd, by the paint by pretreatment
Tree milk liquid and vegetable oil press 50:50 weight in input kneader than mediating 2-3 hours.
Embodiment 4：A kind of modulator approach of plant paint tree milk liquid composite coating, in the following manner：1st, lacquer tree emulsion
Pretreatment：By the early lacquer tree emulsion filtering impurity elimination in Guizhou the west of Guizhou Province of water content 32%, put into oxidation polymerization machine, be in rotating speed
13-15 revs/min of lower stirring at normal temperature, until moisture is 5-6%, raw lacquer liquid turns into can be untill wire drawing 6-10 ㎝ newton bodies；2、
The pretreatment of vegetable oil：The linseed oil of the double drifts of 40 parts of processes is polymerize in pot with 60 parts of tung oil inputs, 245 DEG C, input are heated to
4 parts of rosin powder are together stirred and boiled, and open air exhauster smoke evacuation.When rosin melts completely, 275 DEG C are warming up to, 18-25 is kept
Minute, detect viscosity, when vegetable oil turn into can wire drawing 6-10 ㎝ newton bodies can take the dish out of the pot, and stir exhausting smoke evacuation be cooled to often
Temperature.3rd, the lacquer tree emulsion and vegetable oil by pretreatment are pressed 50:Mediated in 50 weight ratio input kneader and 2-3 hours be
Can.
Embodiment 5：A kind of modulator approach of plant paint tree milk liquid composite coating, in the following manner：1st, lacquer tree emulsion
Pretreatment：By the Shaanxi clovershrub lacquer tree emulsion filtering impurity elimination of water content 30%, put into oxidation polymerization machine, be in rotating speed
14-20 revs/min of lower stirring at normal temperature, until moisture is 5-6%, as can be untill wire drawing 6-10 ㎝ newton bodies；2nd, vegetable oil
Pretreatment：The linseed oil of the double drifts of 40 parts of processes is polymerize in pot with 60 parts of tung oil inputs, 245 DEG C is heated to, puts into 4 portions of pines
Together stirring is boiled at face powder end, opens air exhauster smoke evacuation.When rosin melts completely, 275 DEG C are warming up to, is kept for 18-25 minutes,
Detect viscosity, when vegetable oil turn into can wire drawing 6-10 ㎝ newton bodies can take the dish out of the pot, and stir exhausting smoke evacuation be cooled to normal temperature.3、
Lacquer tree emulsion and vegetable oil by pretreatment is pressed 50:50 weight in input kneader than mediating 2-3 hours.
Embodiment 6：A kind of modulator approach of plant paint tree milk liquid composite coating, in the following manner：1st, lacquer tree emulsion
Pretreatment：By the manly big wooden lacquer tree emulsion of water content 25%, 30%, 32%, 22%, Shaanxi clovershrub lacquer tree emulsion, expensive
State the west of Guizhou Province morning lacquer tree emulsion, Vietnam's lacquer tree emulsion press 1:1:1:1 weight filters impurity elimination than mixing (average moisture content 27.3%),
Put into oxidation polymerization machine, be 14-20 revs/min of lower stirring at normal temperature in rotating speed, until moisture is 5-6%, as can wire drawing
Untill 6-10 ㎝ newton bodies；2nd, the pretreatment of vegetable oil：The linseed oil of the double drifts of 40 parts of processes is polymerize pot with 60 parts of tung oil inputs
It is interior, 245 DEG C are heated to, 4 parts of rosin powder of input, which are together stirred, to be boiled, and opens air exhauster smoke evacuation.When rosin melts completely, rise
Temperature to 275 DEG C, keep 18-25 minute, detect viscosity, when vegetable oil as can wire drawing 6-10 ㎝ newton bodies can take the dish out of the pot, and
Stirring exhausting smoke evacuation is cooled to normal temperature.3rd, the lacquer tree emulsion and vegetable oil by pretreatment are pressed 50:50 weight is pinched than input
Mediated 2-3 hours in conjunction machine.
Embodiment 7：A kind of modulator approach of plant paint tree milk liquid composite coating, by foregoing six with institute in example
The plant paint tree milk liquid composite coating of acquisition is detected according to national standard to its reset condition respectively, then again will
It is coated on woodenware and pottery object according to coating application operational procedure, and its testing result is as follows：
Plant paint tree milk liquid composite coating reset condition testing result：Table 3
Plant paint tree milk liquid composite coating paint film property testing result：Table 4
Show that indices are substantially close from above-mentioned 6 with the Indexs measure result of example, this technology has fine
Repeatability.
Embodiment 8：A kind of modulator approach of plant paint tree milk liquid composite coating, processing method comprises the following steps：
(a) pretreatment of lacquer tree emulsion：
Lacquer tree emulsion is filtered in impurity elimination, input oxidation polymerization machine, is 13 revs/min of lower stirring at normal temperature in rotating speed, until raw
It is 5% to paint moisture, as can be untill the ㎝ newton bodies of wire drawing 6；
(b) pretreatment of vegetable oil：
The linseed oil of the double drifts of 40 parts of processes is polymerize in pot with 60 parts of tung oil inputs, 245 DEG C is heated to, puts into 3 parts of rosin
Powder is together stirred and boiled, and opens air exhauster smoke evacuation；When rosin melts completely, 275 DEG C are warming up to, is kept for 18 minutes, detection is viscous
Degree, when linseed oil turn into can the ㎝ newton body of wire drawing 6 can take the dish out of the pot, and stir exhausting smoke evacuation be cooled to normal temperature；
(c) mediate：
Lacquer tree emulsion and vegetable oil by pretreatment is pressed 50:50 weight in input kneader than mediating 2 hours i.e.
For plant paint tree milk liquid composite coating.
Embodiment 9：A kind of modulator approach of plant paint tree milk liquid composite coating, processing method comprises the following steps：
(a) pretreatment of lacquer tree emulsion：
Lacquer tree emulsion is filtered in impurity elimination, input oxidation polymerization machine, is 20 revs/min of lower stirring at normal temperature in rotating speed, until raw
It is 6% to paint moisture, as can be untill the ㎝ newton bodies of wire drawing 10；
(b) pretreatment of vegetable oil：
The linseed oil of the double drifts of 50 parts of processes is polymerize in pot with 60 parts of tung oil inputs, 245 DEG C is heated to, puts into 4 parts of rosin
Powder is together stirred and boiled, and opens air exhauster smoke evacuation；When rosin melts completely, 275 DEG C are warming up to, is kept for 25 minutes, detection is viscous
Degree, when linseed oil turn into can the ㎝ newton body of wire drawing 10 can take the dish out of the pot, and stir exhausting smoke evacuation be cooled to normal temperature；
(c) mediate：
Lacquer tree emulsion and vegetable oil by pretreatment is pressed 50:50 weight in input kneader than mediating 3 hours i.e.
For plant paint tree milk liquid composite coating.
Embodiment 10：A kind of modulator approach of plant paint tree milk liquid composite coating, processing method comprises the following steps：
(a) pretreatment of lacquer tree emulsion：
Lacquer tree emulsion is filtered in impurity elimination, input oxidation polymerization machine, is 17 revs/min of lower stirring at normal temperature in rotating speed, until raw
It is 5.5% to paint moisture, as can be untill the ㎝ newton bodies of wire drawing 8；
(b) pretreatment of vegetable oil：
The linseed oil of the double drifts of 45 parts of processes is polymerize in pot with 60 parts of tung oil inputs, 245 DEG C is heated to, puts into 3.5 portions of pines
Together stirring is boiled at face powder end, opens air exhauster smoke evacuation；When rosin melts completely, 275 DEG C are warming up to, is kept for 22 minutes, detection
Viscosity, when linseed oil turn into can the ㎝ newton body of wire drawing 8 can take the dish out of the pot, and stir exhausting smoke evacuation be cooled to normal temperature；
(c) mediate：
Lacquer tree emulsion and vegetable oil by pretreatment is pressed 50:50 weight in input kneader than mediating 2.5 hours
As plant paint tree milk liquid composite coating.
Embodiment 11：A kind of modulator approach of plant paint tree milk liquid composite coating, processing method comprises the following steps：
(a) pretreatment of lacquer tree emulsion：
Lacquer tree emulsion is filtered in impurity elimination, input oxidation polymerization machine, is 13-15 revs/min of lower stirring at normal temperature in rotating speed, directly
It is 5.5% to moisture, as can be untill the ㎝ newton bodies of wire drawing 7；
(b) pretreatment of vegetable oil：
The linseed oil of the double drifts of 40 parts of processes is polymerize in pot with 60 parts of tung oil inputs, 245 DEG C is heated to, puts into 4 parts of rosin
Powder is together stirred and boiled, and opens air exhauster smoke evacuation；When rosin melts completely, 275 DEG C are warming up to, is kept for 21 minutes, detection is viscous
Degree, when linseed oil turn into can the ㎝ newton body of wire drawing 7 can take the dish out of the pot, and stir exhausting smoke evacuation be cooled to normal temperature；
(c) mediate：
Lacquer tree emulsion and vegetable oil by pretreatment is pressed 50:50 weight is smaller than mediating 3 in input vacuum kneader
When be plant paint tree milk liquid composite coating.
Although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of changes, modification can be carried out to these embodiments, replace without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (2)
1. a kind of modulator approach of plant paint tree milk liquid composite coating, it is characterised in that processing method comprises the following steps：
(a) pretreatment of lacquer tree emulsion：
Lacquer tree emulsion is filtered in impurity elimination, input oxidation polymerization machine, is 13-20 revs/min of lower stirring at normal temperature in rotating speed, until raw lacquer
Moisture is 5-6%, as can be untill wire drawing 6-10 ㎝ newton bodies；
(b) pretreatment of vegetable oil：
The 40-50 portions of linseed oil by double drifts are polymerize in pot with 60 parts of tung oil inputs, 245 DEG C is heated to, puts into 3-4 parts of rosin
Powder is together stirred and boiled, and opens air exhauster smoke evacuation；When rosin melts completely, 275 DEG C are warming up to, is kept for 18-25 minutes, detection
Viscosity, when linseed oil turn into can wire drawing 6-10 ㎝ newton bodies can take the dish out of the pot, and stir exhausting smoke evacuation be cooled to normal temperature；
(c) mediate：
Lacquer tree emulsion and vegetable oil by pretreatment is pressed 50:Mediated in 50 weight ratio input kneader and 2-3 hours be
Plant paint tree milk liquid composite coating.
2. according to a kind of modulator approach of plant paint tree milk liquid composite coating of claim 1, it is characterised in that processing method bag
Include following steps：
(a) pretreatment of lacquer tree emulsion：
Lacquer tree emulsion is filtered in impurity elimination, input oxidation polymerization machine, is 13-15 revs/min of lower stirring at normal temperature in rotating speed, until moisture
Content is 5-6%, as can be untill wire drawing 6-10 ㎝ newton bodies；
(b) pretreatment of vegetable oil：
The linseed oil of the double drifts of 40 parts of processes is polymerize in pot with 60 parts of tung oil inputs, 245 DEG C is heated to, puts into 4 parts of rosin powder
Together stirring is boiled, and opens air exhauster smoke evacuation；When rosin melts completely, 275 DEG C are warming up to, is kept for 18-25 minutes, detection is viscous
Degree, when linseed oil turn into can wire drawing 6-10 ㎝ newton bodies can take the dish out of the pot, and stir exhausting smoke evacuation be cooled to normal temperature；
(c) mediate：
Lacquer tree emulsion and vegetable oil by pretreatment is pressed 50:50 weight in input vacuum kneader than mediating 2-3 hours
As plant paint tree milk liquid composite coating.