CN107189677A - A kind of environment-friendlyfireproof fireproof paint of container - Google Patents
A kind of environment-friendlyfireproof fireproof paint of container Download PDFInfo
- Publication number
- CN107189677A CN107189677A CN201710365871.7A CN201710365871A CN107189677A CN 107189677 A CN107189677 A CN 107189677A CN 201710365871 A CN201710365871 A CN 201710365871A CN 107189677 A CN107189677 A CN 107189677A
- Authority
- CN
- China
- Prior art keywords
- parts
- environment
- polyurethane
- carborundum
- alchlor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of environment-friendlyfireproof fireproof paint of container, the raw material of the Environment-friendlyfire-retardant fire-retardant paint, including, by weight, 80~120 parts of organic siliconresin, 60~100 parts of epoxy resin, 50~80 parts of asbestos fibre, 30~50 parts of expanded graphite, 20~40 parts of silica, 20~40 parts of carborundum, 30~50 parts of alchlor, 10~20 parts of attapulgite powder, 30~50 parts of polyurethane asphalt, 10~20 parts of laccol silicon, 50~80 parts of melamine, 40~60 parts of organophosphorus ester, 10~30 parts of borate, ethyl silicate 40~60 part, 20~40 parts of highly-chlorinated polyethylene, 10~30 parts of polyurethane, 5~20 parts of chlorinated paraffin.The present invention can effectively improve the fire protecting performance of container, extend the useful life of container.
Description
Technical field
The invention belongs to container technology field, more particularly to a kind of environment-friendlyfireproof fireproof paint of container.
Background technology
Container refers to specialize in the large-scale goods container being used in turn with some strength, rigidity and specification.Container energy
The huge monster of tens tons of a load-carrying is enough allowed to realize standardization, and the ship being done step-by-step based on this in global range
The logistics system that oceangoing ship, harbour, course line, highway, terminal, bridge, tunnel, multimodal transport match.Container is in transportation
Middle to be corroded by adverse circumstances, such as high temperature or flame barbecue cause the service life of container to be restricted.
The content of the invention
It is an object of the invention to provide a kind of environment-friendlyfireproof fireproof paint of container, the fire line of container can be effectively improved
Can, extend the useful life of container.
The technical scheme that the present invention is provided：
A kind of environment-friendlyfireproof fireproof paint of container, the raw material of the Environment-friendlyfire-retardant fire-retardant paint, including, by weight, organic siliconresin
80~120 parts, 60~100 parts of epoxy resin, 50~80 parts of asbestos fibre, 30~50 parts of expanded graphite, silica 20~40
Part, 20~40 parts of carborundum, 30~50 parts of alchlor, 10~20 parts of attapulgite powder, 30~50 parts of polyurethane asphalt, laccol
10~20 parts of silicon, 50~80 parts of melamine, 40~60 parts of organophosphorus ester, 10~30 parts of borate, ethyl silicate 40~60
Part, 20~40 parts of highly-chlorinated polyethylene, 10~30 parts of polyurethane, 5~20 parts of chlorinated paraffin.
Further, the raw material of the Environment-friendlyfire-retardant fire-retardant paint, including, by weight, 90~110 parts of organic siliconresin, epoxy
70~90 parts of resin, 60~70 parts of asbestos fibre, 35~45 parts of expanded graphite, 25~35 parts of silica, carborundum 25~30
Part, 35~45 parts of alchlor, 12~15 parts of attapulgite powder, 35~40 parts of polyurethane asphalt, 12~15 parts of laccol silicon, trimerization
60~70 parts of cyanamide, 45~55 parts of organophosphorus ester, 15~25 parts of borate, 45~55 parts of silester, highly-chlorinated polyethylene
25~30 parts, 13~27 parts of polyurethane, 7~18 parts of chlorinated paraffin.
Further, the raw material of the Environment-friendlyfire-retardant fire-retardant paint, including, by weight, 95~105 parts of organic siliconresin, epoxy
75~85 parts of resin, 62~68 parts of asbestos fibre, 40~42 parts of expanded graphite, 27~30 parts of silica, carborundum 28~32
Part, 37~43 parts of alchlor, 13~14 parts of attapulgite powder, 36~38 parts of polyurethane asphalt, 13~14 parts of laccol silicon, trimerization
62~67 parts of cyanamide, 46~50 parts of organophosphorus ester, 17~22 parts of borate, 48~51 parts of silester, highly-chlorinated polyethylene
27~32 parts, 14~25 parts of polyurethane, 8~11 parts of chlorinated paraffin.
Further, the preparation method of the Environment-friendlyfire-retardant fire-retardant paint comprises the following steps：
A, expanded graphite, silica, carborundum, alchlor, attapulgite powder crushed and mixed, mixed
Close powder；
B, addition organic siliconresin, epoxy resin, asbestos fibre, melamine, organophosphorus ester, boric acid into reactor
Salt, silester, highly-chlorinated polyethylene, polyurethane, 15 minutes~30 points are stirred with 800 revs/min~1000 revs/min of speed
Clock；
C, into reactor add expanded graphite, silica, carborundum, alchlor, attapulgite powder, with 700 turns/
~1000 revs/min of speed is divided to stir 10 minutes~20 minutes；
D, addition chlorinated paraffin, polyurethane asphalt, laccol silicon into reactor, with 800 revs/min~1000 revs/min of speed
Degree stirring 10 minutes~16 minutes.
Further, the expanded graphite, silica, carborundum, alchlor, attapulgite powder are crushed to 100-
200 mesh.
The present invention has the advantages that at least one of following：
The one, present invention, which can be improved effectively, can effectively improve the fire protecting performance of container, extend the use of container
Time limit.
Two, Environmental Safety of the present invention, the bad air such as release formaldehyde, is not conducive to loading food and the peace of other goods
Entirely.
Three, coating produced by the present invention is uniform, fine and smooth, and smooth, adhesion is strong.
Embodiment
Embodiment 1
A kind of environment-friendlyfireproof fireproof paint of container, the raw material of the Environment-friendlyfire-retardant fire-retardant paint, including, by weight, organic siliconresin
80 parts, 60 parts of epoxy resin, 50 parts of asbestos fibre, 30 parts of expanded graphite, 20 parts of silica, 20 parts of carborundum, alchlor
30 parts, 10 parts of attapulgite powder, 30 parts of polyurethane asphalt, 10 parts of laccol silicon, 50 parts of melamine, 40 parts of organophosphorus ester, boron
10 parts of hydrochlorate, ethyl silicate 40 part, 20 parts of highly-chlorinated polyethylene, 10 parts of polyurethane, 5 parts of chlorinated paraffin.
Embodiment 2
A kind of environment-friendlyfireproof fireproof paint of container, the raw material of the Environment-friendlyfire-retardant fire-retardant paint, including, by weight, organic siliconresin
120 parts, 100 parts of epoxy resin, 80 parts of asbestos fibre, 50 parts of expanded graphite, 40 parts of silica, 40 parts of carborundum, three oxidation
50 parts of aluminium, 20 parts of attapulgite powder, 50 parts of polyurethane asphalt, 20 parts of laccol silicon, 80 parts of melamine, 60 parts of organophosphorus ester,
30 parts of borate, 60 parts of silester, 40 parts of highly-chlorinated polyethylene, 30 parts of polyurethane, 20 parts of chlorinated paraffin.
Embodiment 3
A kind of environment-friendlyfireproof fireproof paint of container, the raw material of the Environment-friendlyfire-retardant fire-retardant paint, including, by weight, organic siliconresin
90 parts, 70 parts of epoxy resin, 60 parts of asbestos fibre, 35 parts of expanded graphite, 25 parts of silica, 25 parts of carborundum, alchlor
35 parts, 12 parts of attapulgite powder, 35 parts of polyurethane asphalt, 12 parts of laccol silicon, 60 parts of melamine, 45 parts of organophosphorus ester, boron
15 parts of hydrochlorate, 45 parts of silester, 25 parts of highly-chlorinated polyethylene, 13 parts of polyurethane, 7 parts of chlorinated paraffin.
Embodiment 4
A kind of environment-friendlyfireproof fireproof paint of container, the raw material of the Environment-friendlyfire-retardant fire-retardant paint, including, by weight, organic siliconresin
110 parts, 90 parts of epoxy resin, 70 parts of asbestos fibre, 45 parts of expanded graphite, 35 parts of silica, 30 parts of carborundum, alchlor
45 parts, 15 parts of attapulgite powder, 40 parts of polyurethane asphalt, 15 parts of laccol silicon, 70 parts of melamine, 55 parts of organophosphorus ester, boron
25 parts of hydrochlorate, 55 parts of silester, 30 parts of highly-chlorinated polyethylene, 27 parts of polyurethane, 18 parts of chlorinated paraffin.
Embodiment 5
A kind of environment-friendlyfireproof fireproof paint of container, the raw material of the Environment-friendlyfire-retardant fire-retardant paint, including, by weight, organic siliconresin
95 parts, 75 parts of epoxy resin, 62 parts of asbestos fibre, 40 parts of expanded graphite, 27 parts of silica, 28 parts of carborundum, alchlor
37 parts, 13 parts of attapulgite powder, 36 parts of polyurethane asphalt, 13 parts of laccol silicon, 62 parts of melamine, 46 parts of organophosphorus ester, boron
17 parts of hydrochlorate, 48 parts of silester, 27 parts of highly-chlorinated polyethylene, 14 parts of polyurethane, 8 parts of chlorinated paraffin.
The preparation method of the Environment-friendlyfire-retardant fire-retardant paint comprises the following steps：
A, expanded graphite, silica, carborundum, alchlor, attapulgite powder crushed and mixed, mixed
Close powder；Wherein, the expanded graphite, silica, carborundum, alchlor, attapulgite powder are crushed to 100 mesh；
B, addition organic siliconresin, epoxy resin, asbestos fibre, melamine, organophosphorus ester, boric acid into reactor
Salt, silester, highly-chlorinated polyethylene, polyurethane, are stirred 15 minutes with 800 revs/min of speed；
C, into reactor add expanded graphite, silica, carborundum, alchlor, attapulgite powder, with 700 turns/
The speed divided is stirred 10 minutes；
D, addition chlorinated paraffin, polyurethane asphalt, laccol silicon into reactor, 10 points are stirred with 800 revs/min of speed
Clock.
Embodiment 6
A kind of environment-friendlyfireproof fireproof paint of container, the raw material of the Environment-friendlyfire-retardant fire-retardant paint, including, by weight, organic siliconresin
105 parts, 85 parts of epoxy resin, 68 parts of asbestos fibre, 42 parts of expanded graphite, 30 parts of silica, 32 parts of carborundum, alchlor
43 parts, 14 parts of attapulgite powder, 38 parts of polyurethane asphalt, 14 parts of laccol silicon, 67 parts of melamine, 50 parts of organophosphorus ester, boron
22 parts of hydrochlorate, 51 parts of silester, 32 parts of highly-chlorinated polyethylene, 25 parts of polyurethane, 11 parts of chlorinated paraffin.
The preparation method of the Environment-friendlyfire-retardant fire-retardant paint comprises the following steps：
A, expanded graphite, silica, carborundum, alchlor, attapulgite powder crushed and mixed, mixed
Close powder；Wherein, the expanded graphite, silica, carborundum, alchlor, attapulgite powder are crushed to 200 mesh；
B, addition organic siliconresin, epoxy resin, asbestos fibre, melamine, organophosphorus ester, boric acid into reactor
Salt, silester, highly-chlorinated polyethylene, polyurethane, are stirred 30 minutes with 1000 revs/min of speed；
C, addition expanded graphite, silica, carborundum, alchlor, attapulgite powder into reactor, with 1000
Rev/min speed stir 20 minutes；
D, addition chlorinated paraffin, polyurethane asphalt, laccol silicon into reactor, 16 points are stirred with 1000 revs/min of speed
Clock.
The environment-friendlyfireproof fireproof paint of embodiment 1~6 is subjected to performance test, its result is as shown in table 1.Make according to the method described above
Standby environment-friendlyfireproof fireproof paint, physical properties index all meets or exceeds coating container professional standard, and middle semihard is dried
Time is shorter, and volume solids content is higher, and paint film flexibility is more preferable.
The coating property table of 1 embodiment of table 1~6
The environment-friendlyfireproof fireproof paint of embodiment 1~6 is subjected to fire protecting performance test, its result is as shown in table 2.According to above-mentioned side
Environment-friendlyfireproof fireproof paint prepared by method, with excellent fire prevention and water resistance.
The coating fire protecting performance table of 2 embodiment of table 1~6
Technological project is introduced：
The resistance to combustion time：Under defined base material and specific burning condition, test plate (panel) unexposed surface temperature reaches 220 DEG C or test plate (panel) goes out
The time required to now penetrating (min).
Flame propagation ratio：When the flame propagation ratio of asbestos board is " 0 ", the flame propagation ratio of Oak Tree plank is
When " 100 ", the surface characteristics of flame data that subject material has.
Fire resistances：Lost with burning quality, be carbonized volume to represent.
Mass loss：Test specimen is under regulation coating ratio and regulation burning condition, the difference (g) of quality before and after burning.
Char volume：Test specimen is under regulation coating ratio and defined burning condition, maximum length that base material is carbonized, most
Product (the cm of big width and depth capacity3)。
The resistance to combustion time：Tested by GB/T15442.2 regulation.
Flame propagation ratio：Tested by GB/T15442.3 regulation.
Fire retardance：Tested by GB/T15442.4 regulation.
Claims (5)
1. a kind of environment-friendlyfireproof fireproof paint of container, it is characterised in that the raw material of the Environment-friendlyfire-retardant fire-retardant paint, including, by weight, have
80~120 parts of machine silicones, 60~100 parts of epoxy resin, 50~80 parts of asbestos fibre, 30~50 parts of expanded graphite, titanium dioxide
20~40 parts of silicon, 20~40 parts of carborundum, 30~50 parts of alchlor, 10~20 parts of attapulgite powder, polyurethane asphalt 30~
50 parts, 10~20 parts of laccol silicon, 50~80 parts of melamine, 40~60 parts of organophosphorus ester, 10~30 parts of borate, silicic acid second
40~60 parts of ester, 20~40 parts of highly-chlorinated polyethylene, 10~30 parts of polyurethane, 5~20 parts of chlorinated paraffin.
2. the environment-friendlyfireproof fireproof paint of a kind of container according to claim 1, it is characterised in that the Environment-friendlyfire-retardant fire-retardant paint
Raw material, including, by weight, 90~110 parts of organic siliconresin, 70~90 parts of epoxy resin, 60~70 parts of asbestos fibre, expansion
35~45 parts of graphite, 25~35 parts of silica, 25~30 parts of carborundum, 35~45 parts of alchlor, attapulgite powder 12~
15 parts, 35~40 parts of polyurethane asphalt, 12~15 parts of laccol silicon, 60~70 parts of melamine, 45~55 parts of organophosphorus ester, boron
15~25 parts of hydrochlorate, 45~55 parts of silester, 25~30 parts of highly-chlorinated polyethylene, 13~27 parts of polyurethane, chlorinated paraffin 7~
18 parts.
3. the environment-friendlyfireproof fireproof paint of a kind of container according to claim 1, it is characterised in that the Environment-friendlyfire-retardant fire-retardant paint
Raw material, including, by weight, 95~105 parts of organic siliconresin, 75~85 parts of epoxy resin, 62~68 parts of asbestos fibre, expansion
40~42 parts of graphite, 27~30 parts of silica, 28~32 parts of carborundum, 37~43 parts of alchlor, attapulgite powder 13~
14 parts, 36~38 parts of polyurethane asphalt, 13~14 parts of laccol silicon, 62~67 parts of melamine, 46~50 parts of organophosphorus ester, boron
17~22 parts of hydrochlorate, 48~51 parts of silester, 27~32 parts of highly-chlorinated polyethylene, 14~25 parts of polyurethane, chlorinated paraffin 8~
11 parts.
4. the environment-friendlyfireproof fireproof paint of a kind of container according to claim 1, it is characterised in that the Environment-friendlyfire-retardant fire-retardant paint
Preparation method comprises the following steps：
A, expanded graphite, silica, carborundum, alchlor, attapulgite powder crushed and mixed, mixed
Powder；
B, into reactor add organic siliconresin, epoxy resin, asbestos fibre, melamine, organophosphorus ester, borate,
Silester, highly-chlorinated polyethylene, polyurethane, are stirred 15 minutes~30 minutes with 800 revs/min~1000 revs/min of speed；
C, into reactor add expanded graphite, silica, carborundum, alchlor, attapulgite powder, with 700 revs/min~
1000 revs/min of speed is stirred 10 minutes~20 minutes；
D, addition chlorinated paraffin, polyurethane asphalt, laccol silicon into reactor, are stirred with 800 revs/min~1000 revs/min of speed
Mix 10 minutes~16 minutes.
5. the environment-friendlyfireproof fireproof paint of a kind of container according to claim 1, it is characterised in that the expanded graphite, two
Silica, carborundum, alchlor, attapulgite powder are crushed to 100-200 mesh.