CN107177401A - A kind of tire banbury sealing ring special environment protection lubricating oil - Google Patents
A kind of tire banbury sealing ring special environment protection lubricating oil Download PDFInfo
- Publication number
- CN107177401A CN107177401A CN201710348572.2A CN201710348572A CN107177401A CN 107177401 A CN107177401 A CN 107177401A CN 201710348572 A CN201710348572 A CN 201710348572A CN 107177401 A CN107177401 A CN 107177401A
- Authority
- CN
- China
- Prior art keywords
- parts
- sealing ring
- oil
- lubricating oil
- banbury
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of tire banbury sealing ring special environment protection lubricating oil.Its technical scheme is made of to include the component of following parts by weight：Environmentally friendly 85 92 parts of naphthenic oil, 6 12 parts of DOTP, 17 parts of molybdenum dialkyl-dithiophosphate, 0.05 0.15 parts of silicone emulsion, 0.8 2.8 parts of SULFURIZED CALCIUM ALKYL PHENATE WITH HIGH BASE NUMBER, 1.0 1.9 parts of zinc dialkyl dithiophosphate.Beneficial effect is：1st, the lubrication oil special to tire banbury sealing ring has higher economic value, greatly reduces the cost of conventional naphthenic oil, while having broken conventional naphthenic oil only does rubber filling oil, the convention of lubricating oil is not done；2nd, simultaneously because with the addition of the additive of lubricating oil, banbury sealing ring oil can be made, with antiwear and reducing friction, sealing ring is protected, extends the sealing ring life-span, make sealing ring gap permanent, keep tight state, compared with conventional naphthenic oil, more fuel-efficient energy-conservation；Aniline point can at any time be adjusted according to rubber tyre ratio requirement, and the use scope of naphthenic oil is increased significantly.
Description
Technical field
The present invention relates to a kind of tire banbury sealing ring lubricating oil, more particularly to a kind of tire banbury sealing ring is special
Use environment-protective lubricant oil.
Background technology
Banbury is indispensable equipment in modern rubber industry, is mainly used in plasticating and kneading for rubber.Its rotor
Sealing device is generally two kinds of forms of mechanical seal and hydraulic packing, using the principle of contact end face seal, sets a pair of phases
To the sealing ring of rotation --- the flat frictional pair that rotating ring is constituted with stationary ring.Sealing ring uses metal material processing, in order to improve
Often built-up welding hard, wear-resistant alloy, and in the course of the work on the wearability of sealing ring, rubbing surface, can be by oil filler point toward two rings
Rubbing surface on inject extreme pressure lubricant, to increase the wearability of friction pair, and prevent material from leaking.Existing tire banbury
The not only excessive fuel consumption of the lubricating oil of sealing ring, and environmental requirement can not be met, so, the tire not only cost increase of production, and
And European Union's REACH environmental regulations can not be reached, this has resulted in the bigger loss of tyre industry, has made tyre industry by larger
Strike.
In addition, naphthenic oil is extract from naphthene base crude, it is the petroleum distillate using cycloalkane as main component,
Naphthenic oil has saturated cyclic carbon-chain structure, with low pour point, high density, high viscosity, the features such as have no toxic side effect, and at it
Ring on generally can also be connected to saturation side chain.Because this structure, make naphthenic oil that both there are some properties of arene, again
Some properties with straight-chain hydrocarbons, and because naphthenic oil comes from natural oil, there is cheap, from the horse's mouth, decision
Naphthenic oil can have a special purposes in many fields.Naphthenic oil is the reasonable selection of following several properties：1.
High dissolving power, 2 excellent cryogenic properties, 3 with some resins and the excellent compatibility of polymer, 4 with the good plasticising of rubber and
Intersolubility.And refer to can be by the naphthenic oils of European Union's REACH environmental regulations for environmentally friendly naphthenic oil, it is desirable to 18 kinds of polycyclic aromatic hydrocarbon contents
Summation<10mg/g , Ben Bing pyrenes<1ppm, effectively utilizes environmentally friendly naphthenic oil in tire banbury sealing ring：The tire of production can
To meet the requirement of European Union's REACH environmental regulations.
The content of the invention
There is provided a kind of tire banbury sealing ring is special aiming at the drawbacks described above that prior art is present for the purpose of the present invention
With environment-protective lubricant oil, not only fuel-economizing, and environmental protection can meet the requirement of European Union's REACH environmental regulations, in addition, can make aniline
Point reduction, and then adapt to various tire formulation requirements.
Its technical scheme is made of to include the component of following parts by weight：
Environmentally friendly naphthenic oil 85-92 parts, 6-12 parts of DOTP, 1-7 parts of molybdenum dialkyl-dithiophosphate, silicone emulsion
0.05-0.15 parts, 0.8-2.8 parts of SULFURIZED CALCIUM ALKYL PHENATE WITH HIGH BASE NUMBER, 1.0-1.9 parts of zinc dialkyl dithiophosphate.
It is preferred that, component of the present invention including following parts by weight is made：
Environmentally friendly 92 parts of naphthenic oil, 12 parts of DOTP, 7 parts of molybdenum dialkyl-dithiophosphate, 0.12 part of silicone emulsion,
2.8 parts of SULFURIZED CALCIUM ALKYL PHENATE WITH HIGH BASE NUMBER, 1.8 parts of zinc dialkyl dithiophosphate.
The beneficial effects of the invention are as follows：1st, not only with lubricating oil it is anti-oxidant, wear-resistant, antiseptic and rustproof, while having rubber
Glue plasticizer, required heat-resisting, cold-resistant, difficult volatilization and good electrical insulating property, it is especially special to tire banbury sealing ring
Lubrication oil has higher economic value, the cost of conventional naphthenic oil is greatly reduced, while having broken conventional cycloalkanes
Oil only does rubber filling oil, and the convention of lubricating oil is not done；
2nd, simultaneously because with the addition of the additive of lubricating oil, banbury sealing ring oil can be made, with antiwear and reducing friction, protection sealing
Ring, extends the sealing ring life-span, makes sealing ring gap permanent, keeps tight state, compared with conventional naphthenic oil, more fuel-efficient energy-conservation；
3rd, due to addition DOTP（DOTP）, make the present invention aniline point can according to rubber tyre ratio requirement,
Adjust at any time, the use scope of naphthenic oil is increased significantly, is minimized the naphthenic oil of some high aniline points, saturated hydrocarbon content subtracts
Few, aromatic hydrocarbon content increases, and further increases the intermiscibility with rubber, strengthens tire anti-slippery, plays good society's effect
Good guarantee is played in benefit, the production to tire.
Embodiment
Illustrated the following is to the preferred embodiments of the present invention, it will be appreciated that preferred embodiment described herein is only
For instruction and explanation of the present invention, it is not intended to limit the present invention.
A kind of tire banbury sealing ring special environment protection lubricating oil that embodiment 1, the present invention are mentioned, it is as follows that it makes formula
（By weight）：
Environmentally friendly 85 parts of naphthenic oil, 8.3 parts of DOTP, 3 parts of molybdenum dialkyl-dithiophosphate, silicone emulsion 0.10
Part, 2 parts of SULFURIZED CALCIUM ALKYL PHENATE WITH HIGH BASE NUMBER, 1.6 parts of zinc dialkyl dithiophosphate.
Existing reference examples 1：A kind of tire banbury sealing ring special environment protection lubricating oil that the present invention is mentioned, it makes formula
It is as follows（By weight）：
85 parts of the common naphthenic oil of non-environmental protection, 8.3 parts of DOTP, 3 parts of molybdenum dialkyl-dithiophosphate, silicone emulsion
0.10 part, 2 parts of SULFURIZED CALCIUM ALKYL PHENATE WITH HIGH BASE NUMBER, 1.6 parts of zinc dialkyl dithiophosphate.
Wherein, the environmentally friendly naphthenic oil that the present invention is used, is the naphthenic oil that index reaches European Union's REACH environmental regulations, and it is marked
It is accurate as follows：
The dioctyl phthalate that the present invention is used（DOTP）It is also environment-friendly type, reaches European Union's REACH environmental regulations, is polychlorostyrene second
Alkene（PVC）Plastics and rubber plastizing agent, precision instrument lubricant, lubricant additive, it has heat-resisting, cold-resistant, difficult volatilization, electricity
Good insulating, it is desirable to which index is as follows：
In addition, molybdenum dialkyl-dithiophosphate is a kind of new effective anti-attrition antiwear additive；SULFURIZED CALCIUM ALKYL PHENATE WITH HIGH BASE NUMBER is at this
Serve in invention acid neutralization, it is oxidation resistant；Silicone emulsion is used as anti-foaming agent；Zinc dialkyl dithiophosphate is a kind of accelerator
（Referred to as：ZDDP）, it is a kind of with antioxygen, the multipurpose additive of anti-rotten and wear-resistant effect, suppresses abrasion, moreover it is possible to prevent lubricating oil
Corrosion, oxidation.
The present invention has advantages below：
1st, not only with lubricating oil it is anti-oxidant, wear-resistant, antiseptic and rustproof, while there is rubber plastizing agent, it is required heat-resisting, resistance to
Cold, difficult volatilization and good electrical insulating property, the especially lubrication oil special to tire banbury sealing ring have higher warp
Ji value, greatly reduces the cost of conventional naphthenic oil, while having broken conventional naphthenic oil only does rubber filling oil, does not do and lubricate
The convention of oil；
2nd, simultaneously because with the addition of the additive of lubricating oil, banbury sealing ring oil can be made, with antiwear and reducing friction, protection sealing
Ring, extends the sealing ring life-span, makes sealing ring gap permanent, keeps tight state, compared with conventional naphthenic oil, more fuel-efficient energy-conservation.
3rd, due to addition DOTP（DOTP）, making the aniline point of the present invention can want according to rubber tyre proportioning
Ask, adjust at any time, the use scope of naphthenic oil is increased significantly, is minimized the naphthenic oil of some high aniline points, saturated hydrocarbons contains
Amount is reduced, and aromatic hydrocarbon content increases, and further increases the intermiscibility with rubber, is strengthened tire anti-slippery, is played good society
Good guarantee is played in meeting benefit, the production to tire.
A kind of tire banbury sealing ring special environment protection lubricating oil that embodiment 2, the present invention are mentioned, it is as follows that it makes formula
（By weight）：
Environmentally friendly 86 parts of naphthenic oil, 6.3 parts of DOTP, 5 parts of molybdenum dialkyl-dithiophosphate, silicone emulsion 0.12
Part, 2.5 parts of SULFURIZED CALCIUM ALKYL PHENATE WITH HIGH BASE NUMBER, 1.3 parts of zinc dialkyl dithiophosphate.
Existing reference examples 2：A kind of tire banbury sealing ring special environment protection lubricating oil that the present invention is mentioned, it makes formula
It is as follows（By weight）：
Environmentally friendly 86 parts of naphthenic oil, 0 part of DOTP, 5 parts of molybdenum dialkyl-dithiophosphate, 0.12 part of silicone emulsion,
2.5 parts of SULFURIZED CALCIUM ALKYL PHENATE WITH HIGH BASE NUMBER, 1.3 parts of zinc dialkyl dithiophosphate.
A kind of tire banbury sealing ring special environment protection lubricating oil that embodiment 3, the present invention are mentioned, it is as follows that it makes formula
（By weight）：
Environmentally friendly 85 parts of naphthenic oil, 7.27 parts of DOTP, 3 parts of molybdenum dialkyl-dithiophosphate, silicone emulsion 0.13
Part, 0.8 part of SULFURIZED CALCIUM ALKYL PHENATE WITH HIGH BASE NUMBER, 1 part of zinc dialkyl dithiophosphate.
Existing reference examples 3：A kind of tire banbury sealing ring special environment protection lubricating oil that the present invention is mentioned, it makes formula
It is as follows（By weight）：
Environmentally friendly 85 parts of naphthenic oil, 7.27 parts of non-environmental protection DOTP, 3 parts of molybdenum dialkyl-dithiophosphate, emulsification silicon
0.13 part of oil, 0.8 part of SULFURIZED CALCIUM ALKYL PHENATE WITH HIGH BASE NUMBER, 1 part of zinc dialkyl dithiophosphate.
A kind of tire banbury sealing ring special environment protection lubricating oil that embodiment 4, the present invention are mentioned, it is as follows that it makes formula
（By weight）：
Environmentally friendly 89 parts of naphthenic oil, 6.27 parts of DOTP, 2 parts of molybdenum dialkyl-dithiophosphate, silicone emulsion 0.13
Part, 1.8 parts of SULFURIZED CALCIUM ALKYL PHENATE WITH HIGH BASE NUMBER, 1.8 parts of zinc dialkyl dithiophosphate.
Existing reference examples 4：A kind of tire banbury sealing ring special environment protection lubricating oil that the present invention is mentioned, it makes formula
It is as follows（By weight）：
Environmentally friendly 89 parts of naphthenic oil, 6.27 parts of DOTP, 0 part of molybdenum dialkyl-dithiophosphate, silicone emulsion 0.13
Part, 1.8 parts of SULFURIZED CALCIUM ALKYL PHENATE WITH HIGH BASE NUMBER, 1.8 parts of zinc dialkyl dithiophosphate.
A kind of tire banbury sealing ring special environment protection lubricating oil that embodiment 5, the present invention are mentioned, it is as follows that it makes formula
（By weight）：
Environmentally friendly 92 parts of naphthenic oil, 6 parts of DOTP, 1 part of molybdenum dialkyl-dithiophosphate, 0.05 part of silicone emulsion,
2.8 parts of SULFURIZED CALCIUM ALKYL PHENATE WITH HIGH BASE NUMBER, 1.9 parts of zinc dialkyl dithiophosphate.
Existing reference examples 5：A kind of tire banbury sealing ring special environment protection lubricating oil that the present invention is mentioned, it makes formula
It is as follows（By weight）：
Environmentally friendly 92 parts of naphthenic oil, 6 parts of DOTP, 1 part of molybdenum dialkyl-dithiophosphate, 0.05 part of silicone emulsion,
0 part of SULFURIZED CALCIUM ALKYL PHENATE WITH HIGH BASE NUMBER, 0 part of zinc dialkyl dithiophosphate.
Embodiment 1-5 and reference examples 1-5 are processed into the special naphthenic oil of finished tire banbury sealing ring to carry out respectively
Performance test obtains result such as following table：
This experiment is tested with aniline point in 100 or so environmentally friendly naphthenic oil：
With colourity<3 non-environmental protection naphthenic oil is compared, aniline point 90 or so, is counted by table one it has been found that the benzene of EXPERIMENTAL EXAMPLE 1
Amine point declines, and is dropped to more than 80, is more suitable for and rubber compounding by 100 or so, and all by EU REACH Legislation certification,
Antioxidant and antiwear property is good, no acidic corrosivity, colourity<0.5, it is relatively purer.
And reference examples 1, the naphthenic oil of non-environmental protection is added, oil product acidic corrosive is higher, it is impossible to pass through European Union's REACH methods
Rule；Reference examples 2, DOTP are not added, then aniline point is constant, but aniline point height can have an impact to tire anti-slippery；Reference examples
3, DOTP not environmentally is added, then whole product can not pass through REACH regulation certifications；Reference examples 4, dialkyl disulfides are not added
For molybdenum phosphate, wear resistence declines；Reference examples 5, no SULFURIZED CALCIUM ALKYL PHENATE WITH HIGH BASE NUMBER and zinc dialkyl dithiophosphate, antioxidant,
Wear resistence and corrosion resistance decline.Thus illustrate, the tire banbury sealing ring produced according to the formula of the present invention is special
With oil, its performance is optimal.
It is described above, only it is the part preferred embodiment of the present invention, any those skilled in the art may profit
Equivalent technical scheme is changed or is revised as with the technical scheme of above-mentioned elaboration.Therefore, the technology according to the present invention
Any simple modification or substitute equivalents that scheme is carried out, belong to the greatest extent the scope of protection of present invention.
Claims (2)
1. a kind of tire banbury sealing ring special environment protection lubricating oil, it is characterized in that：Component including following parts by weight is made：
Environmentally friendly naphthenic oil 85-92 parts, 6-12 parts of DOTP, 1-7 parts of molybdenum dialkyl-dithiophosphate, silicone emulsion
0.05-0.15 parts, 0.8-2.8 parts of SULFURIZED CALCIUM ALKYL PHENATE WITH HIGH BASE NUMBER, 1.0-1.9 parts of zinc dialkyl dithiophosphate.
2. tire banbury sealing ring special environment protection lubricating oil according to claim 1, it is characterized in that：Including following weight
The component of part is made：
Environmentally friendly 92 parts of naphthenic oil, 12 parts of DOTP, 7 parts of molybdenum dialkyl-dithiophosphate, 0.12 part of silicone emulsion,
2.8 parts of SULFURIZED CALCIUM ALKYL PHENATE WITH HIGH BASE NUMBER, 1.8 parts of zinc dialkyl dithiophosphate.