CN107164998A - 一种石墨烯除醛隔热壁纸、墙布以及制备方法 - Google Patents

一种石墨烯除醛隔热壁纸、墙布以及制备方法 Download PDF

Info

Publication number
CN107164998A
CN107164998A CN201710351876.4A CN201710351876A CN107164998A CN 107164998 A CN107164998 A CN 107164998A CN 201710351876 A CN201710351876 A CN 201710351876A CN 107164998 A CN107164998 A CN 107164998A
Authority
CN
China
Prior art keywords
heat
aldehyde
graphene
wallpaper
wall paper
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710351876.4A
Other languages
English (en)
Inventor
李智璐
耿光强
刘贝贝
车云霞
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Special Novel Material Science And Technology Ltd Of Qingdao Rayleigh
Original Assignee
Special Novel Material Science And Technology Ltd Of Qingdao Rayleigh
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Special Novel Material Science And Technology Ltd Of Qingdao Rayleigh filed Critical Special Novel Material Science And Technology Ltd Of Qingdao Rayleigh
Priority to CN201710351876.4A priority Critical patent/CN107164998A/zh
Publication of CN107164998A publication Critical patent/CN107164998A/zh
Pending legal-status Critical Current

Abstract

本发明属于装饰材料技术领域，涉及一种石墨烯除醛隔热壁纸、墙布以及制备方法，该方法包括：(1)制备除醛涂料或水性环保油墨隔热壁纸涂层；(2)将基材进行预热处理；(3)将隔热壁纸涂层涂覆于经预热处理后的基材上，并加热、压花制成石墨烯除醛隔热壁纸、墙布。在此过程中，壁纸涂层中添加的抗甲醛助剂以及隔热浆料，本发明与普通壁纸相比，不含有甲醛、苯等有机污染物，而且可以从根本上清除甲醛，同时添加有隔热材料，可以有效的阻止热量传递，起到室内保温的功能，并且石墨烯的加入还可以在很大程度上提高壁纸涂层的耐磨性能。

Description

一种石墨烯除醛隔热壁纸、墙布以及制备方法
技术领域
本发明属于装饰材料技术领域，涉及一种石墨烯除醛隔热壁纸、墙布以及制备方法。
背景技术
壁纸，也称为墙纸、墙布，它是一种应用相当广泛的室内装饰材料。因为壁纸具有色彩多样、图案丰富、豪华气派、安全环保、施工方便、价格适宜等多种其它室内装饰材料所无法比拟的特点，故在欧美、东南亚、日本等发达国家和地区得到相当程度的普及。近年来，我国室内装饰装修持续升温，一度遭冷落的壁纸以其绚丽的新姿态重新走进了客厅、卧室、酒店、会议室等。目前设置于卧室背景墙或客厅背景墙的壁纸，人们对房屋进行装修时所用的木材、石材、涂料、油漆等材料都不同程度地含有对人体有害的化学物质，特别是装饰材料中释放出来的甲醛、苯等有机物对人体危害极大，通常采用通风或喷洒有害物清除剂的方法，或在室内放置植物来吸收有害气体，这种处理方法收效甚微，并且壁纸只是作为了单方面的装饰作用，没有发挥其进一步的居家舒适性。
如何制作一种除醛壁纸、墙布，使其本身不含甲醛，并且具有分解甲醛的功能，且同时可以实现室内墙壁的隔热保温，满足居家安全、环保、舒适的性能具有重要意义。
发明内容
本发明针对上述的精装家居装修中甲醛污染以及冬夏室内外温差较大等问题，提供了一种石墨烯除醛隔热壁纸、墙布以及制备方法。
为了达到上述目的，本发明采用的技术方案为，
一种石墨烯除醛隔热壁纸和墙布，其特征在于，所述隔热壁纸和墙布均由石墨烯除醛涂料或水性环保油墨所制备的隔热涂层制备而成；
所述石墨烯除醛涂料按重量份数具体包括以下份数：
所述抗甲醛助剂为石墨烯和纳米二氧化钛的混合物，其质量比为1:10-10:1；
所述水性环保油墨按重量份数具体包括以下份数：
作为优选，所述多功能助剂为多功能胺类助剂；所述分散剂为六偏磷酸钠和十二烷基硫酸钠按照质量比1:2组成的混合物；所述防水剂为有机硅疏水防水剂；所述消泡剂为矿物碳氢化合物类消泡剂、非离子型烷基共聚物消泡剂的一种或两种；所述增稠剂为缔合型碱溶胀增稠剂或聚氨酯增稠剂中的至少一种；所述水性树脂为丙烯酸共聚物、纯丙聚合物、苯丙、聚氨酯、有机硅、聚四氟乙烯树脂中的任意一种或几种；所述颜填料浆为钛白粉、重质碳酸钙浆、高岭土、滑石粉、超细方解石粉、硅藻土、硫酸钡、云母粉中的至少一种物质加入润湿分散助剂中并与去离子水分散搅拌而成的浆状物质；所述隔热浆料为膨胀珍珠岩、海泡石、蛭石、空心玻璃微珠、空心陶瓷微珠、发泡聚苯乙烯颗粒、气凝胶、膨胀石墨中的至少一种物质加入润湿分散助剂与去离子水分散搅拌而成的浆状物质。
作为优选，所述水溶性树脂为丙烯酸共聚物、纯丙聚合物、苯丙、聚氨酯、有机硅、聚四氟乙烯树脂中的一种或几种；所述颜料浆为黄、红、蓝、三种颜色中的一种或几种，并将其加入润湿分散助剂与去离子水分散搅拌而成的浆状物质，所述黄色颜料浆选用的颜料为联苯胺黄，红色颜料浆选用的颜料为洋红，蓝色颜料浆选用的颜料为酞青蓝；所述助剂为增稠剂、表面活性剂、消泡剂、抗甲醛助剂按重量比为1:2:1:1混合组成，所述抗甲醛助剂为石墨烯和纳米二氧化钛的混合物，其质量比为1:10-10:1；所述隔热浆料为膨胀珍珠岩、海泡石、蛭石、空心玻璃微珠、空心陶瓷微珠、发泡聚苯乙烯颗粒、气凝胶、膨胀石墨中的至少一种物质加入润湿分散助剂与去离子水分散搅拌而成的浆状物质。
一种制备石墨烯除醛隔热壁纸和墙布的方法，具体包括以下步骤：
(1)制备除醛涂料或水性环保油墨的隔热壁纸涂层；
(2)将基材进行预热处理；
(3)将隔热壁纸涂层涂覆于经预热处理后的基材上，并加热、压花制成石墨烯除醛隔热壁纸或墙布。
作为优选，所述基材包括纸基、PVC、无纺布、织物、布基、金箔中的任意一种。
作为优选，所述预热处理依次包括第一预热处理和第二预热处理。
作为优选，所述第一预热处理满足以下条件：起始温度为20-25℃，升温速率为1-5℃/min，升温时间为1-3min；所述第二预热处理的升温速率为6-10℃/min，升温时间为1-5min。
作为优选，所述加热温度为110-130℃，加热时间为30-50min。
与现有技术相比，本发明的优点和积极效果在于，
本发明通过先制备除醛涂料以及水性环保油墨隔热壁纸涂层，并对基材进行二次预热处理，然后将隔热壁纸涂层涂覆于经预热处理后的基材上，并加热、压花制成石墨烯除醛隔热壁纸、墙布。在此过程中，壁纸涂层中添加的抗甲醛助剂以及隔热浆料，与传统的壁纸涂层配方相比，利用了石墨烯的光催化性能和超高导热性能，增加了分子以及载体之间的相互作用，提高了材料对空气中游离甲醛的分解效率和净化能力，并且隔热浆料的加入，使得壁纸、墙布具有了优异的保温隔热性能。此外，对基材进行的预热处理能够减小或避免基材在涂覆壁纸涂层后加热过程中发生的应变，从而能够提高所制得石墨烯除醛隔热壁纸、墙布的力学性能和除醛效果，且在加热条件下物料间的相互作用能够有效提高所制得石墨烯除醛隔热壁纸、墙布的韧性和抗拉强度。该方法制得的石墨烯除醛隔热壁纸、墙布具有除醛隔热、保温、净化空气的作用，且环保无污染。
具体实施方式
为了能够更清楚地理解本发明的上述目的、特征和优点，下面结合实施例对本发明做进一步说明。需要说明的是，在不冲突的情况下，本申请的实施例及实施例中的特征可以相互组合。
在下面的描述中阐述了很多具体细节以便于充分理解本发明，但是，本发明还可以采用不同于在此描述的其他方式来实施，因此，本发明并不限于下面公开说明书的具体实施例的限制。
实施例1
(1)将去离子水5份，多功能胺助剂(AMP-95)0.3份，水性丙烯酸树脂42.5份，颜填料浆30份，分散剂(六偏磷酸钠和十二烷基硫酸钠质量比为1:2)0.5份，防水剂0.5份，非离子型烷基共聚物消泡剂(CHE COAT DF9000)0.3份，缔合型碱溶胀增稠剂(CHE COATVT-183)0.1份，聚氨酯增稠剂(CHE COAT VT-903)0.1份，杀菌剂(科莱恩HF-1)0.5份，抗甲醛助剂(纳米TiO2和石墨烯比例为2:8)0.2份，隔热浆料20份混合制得除醛隔热涂料壁纸涂层；
(2)将纸在20℃的起始温度下以2℃/min的升温速率升温3min以进行第一预热处理；接着以7℃/min的升温速率升温2min以进行第二预热处理；
(3)将除醛隔热涂料壁纸涂层涂覆于经预热处理后的纸上，并在110℃的温度下加热35min、压花制成石墨烯除醛隔热壁纸1。
实施例2
(1)将去离子水3份，多功能胺助剂(AMP-95)0.2份，水性丙烯酸树脂49.5份，颜填料浆5份，分散剂(六偏磷酸钠和十二烷基硫酸钠质量比为1:2)0.3份，防水剂0.8份，非离子型烷基共聚物消泡剂(CHE COAT DF9000)0.2份，缔合型碱溶胀增稠剂(CHE COATVT-183)0.1份，聚氨酯增稠剂(CHE COAT VT-903)0.2份，杀菌剂(科莱恩HF-1)0.5份，抗甲醛助剂(纳米TiO2和石墨烯比例为5:5)0.2份，隔热浆料40份混合制得除醛隔热涂料壁纸涂层；
(2)将无纺布在25℃的起始温度下以3℃/min的升温速率升温2min以进行第一预热处理；接着以10℃/min的升温速率升温3min以进行第二预热处理；
(3)将除醛隔热涂料壁纸涂层涂覆于经预热处理后的无纺布上，并在120℃的温度下加热30min、压花制成石墨烯除醛隔热墙布2。
实施例3
(1)将去离子水5.5份，水性丙烯酸树脂30份，酞青蓝颜料浆32份，消泡剂(CHECOAT DF9000)0.5份，聚氨酯增稠剂(CHE COATVT-903)0.5份，水溶性阴离子氟碳1份，抗甲醛助剂(纳米TiO2和石墨烯比例为8:2)0.5份，隔热浆料30份混合制得水性环保油墨隔热壁纸涂层；
(2)将织物在25℃的起始温度下以1℃/min的升温速率升温3min以进行第一预热处理；接着以8℃/min的升温速率升温5min以进行第二预热处理；
(3)将水性环保油墨隔热壁纸涂层涂覆于经预热处理后的织物上，并在125℃的温度下加热40min、压花制成石墨烯除醛隔热墙布3。
对实施例1-3提供的石墨烯除醛隔热壁纸、墙布的效果进检测，其中净化甲醛率测试方法执行JC/T1074-2008《室内空气净化功能涂覆材料净化功能》规定的Ι类要求进行测试。
表1：实施例1-3提供的石墨烯除醛隔热壁纸、墙布的检测结果：
以上所述，仅是本发明的较佳实施例而已，并非是对本发明作其它形式的限制，任何熟悉本专业的技术人员可能利用上述揭示的技术内容加以变更或改型为等同变化的等效实施例应用于其它领域，但是凡是未脱离本发明技术方案内容，依据本发明的技术实质对以上实施例所作的任何简单修改、等同变化与改型，仍属于本发明技术方案的保护范围。

Claims (8)

1.一种石墨烯除醛隔热壁纸和墙布，其特征在于，所述隔热壁纸和墙布均由石墨烯除醛涂料或水性环保油墨所制备的隔热涂层制备而成；
所述石墨烯除醛涂料按重量份数具体包括以下份数：
所述抗甲醛助剂为石墨烯和纳米二氧化钛的混合物，其质量比为1:10-10:1；
所述水性环保油墨按重量份数具体包括以下份数：
2.根据权利要求1所述的一种石墨烯除醛隔热壁纸和墙布，其特征在于，所述多功能助剂为多功能胺类助剂；所述分散剂为六偏磷酸钠和十二烷基硫酸钠按照质量比1:2组成的混合物；所述防水剂为有机硅疏水防水剂；所述消泡剂为矿物碳氢化合物类消泡剂、非离子型烷基共聚物消泡剂的一种或两种；所述增稠剂为缔合型碱溶胀增稠剂或聚氨酯增稠剂中的至少一种；所述水性树脂为丙烯酸共聚物、纯丙聚合物、苯丙、聚氨酯、有机硅、聚四氟乙烯树脂中的任意一种或几种；所述颜填料浆为钛白粉、重质碳酸钙浆、高岭土、滑石粉、超细方解石粉、硅藻土、硫酸钡、云母粉中的至少一种物质加入润湿分散助剂中并与去离子水分散搅拌而成的浆状物质；所述隔热浆料为膨胀珍珠岩、海泡石、蛭石、空心玻璃微珠、空心陶瓷微珠、发泡聚苯乙烯颗粒、气凝胶、膨胀石墨中的至少一种物质加入润湿分散助剂与去离子水分散搅拌而成的浆状物质。
3.根据权利要求1所述的一种石墨烯除醛隔热壁纸和墙布，其特征在于，所述水溶性树脂为丙烯酸共聚物、纯丙聚合物、苯丙、聚氨酯、有机硅、聚四氟乙烯树脂中的一种或几种；所述颜料浆为黄、红、蓝、三种颜色中的一种或几种，并将其加入润湿分散助剂与去离子水分散搅拌而成的浆状物质，所述黄色颜料浆选用的颜料为联苯胺黄，红色颜料浆选用的颜料为洋红，蓝色颜料浆选用的颜料为酞青蓝；所述助剂为增稠剂、表面活性剂、消泡剂、抗甲醛助剂按重量比为1:2:1:1混合组成，所述抗甲醛助剂为石墨烯和纳米二氧化钛的混合物，其质量比为1:10-10:1；所述隔热浆料为膨胀珍珠岩、海泡石、蛭石、空心玻璃微珠、空心陶瓷微珠、发泡聚苯乙烯颗粒、气凝胶、膨胀石墨中的至少一种物质加入润湿分散助剂与去离子水分散搅拌而成的浆状物质。
4.一种制备权利要求2或3中所述的一种石墨烯除醛隔热壁纸和墙布的方法，其特征在于，具体包括以下步骤：
(1)制备除醛涂料或水性环保油墨的隔热壁纸涂层；
(2)将基材进行预热处理；
(3)将隔热壁纸涂层涂覆于经预热处理后的基材上，并加热、压花制成石墨烯除醛隔热壁纸或墙布。
5.根据权利要求4所述的一种制备利要求2或3中所述的一种石墨烯除醛隔热壁纸和墙布的方法，其特征在于：所述基材包括纸基、PVC、无纺布、织物、布基、金箔中的任意一种。
6.根据权利要求4所述的一种制备利要求2或3中所述的一种石墨烯除醛隔热壁纸和墙布的方法，其特征在于：所述预热处理依次包括第一预热处理和第二预热处理。
7.根据权利要求4所述的一种制备利要求2或3中所述的一种石墨烯除醛隔热壁纸和墙布的方法，其特征在于：所述第一预热处理满足以下条件：起始温度为20-25℃，升温速率为1-5℃/min，升温时间为1-3min；所述第二预热处理的升温速率为6-10℃/min，升温时间为1-5min。
8.根据权利要求4所述的一种制备利要求2或3中所述的一种石墨烯除醛隔热壁纸和墙布的方法，其特征在于：所述加热温度为110-130℃，加热时间为30-50min。
CN201710351876.4A 2017-05-18 2017-05-18 一种石墨烯除醛隔热壁纸、墙布以及制备方法 Pending CN107164998A (zh)