CN107163334A - A kind of foam-in-mould moulding material - Google Patents
A kind of foam-in-mould moulding material Download PDFInfo
- Publication number
- CN107163334A CN107163334A CN201710408010.2A CN201710408010A CN107163334A CN 107163334 A CN107163334 A CN 107163334A CN 201710408010 A CN201710408010 A CN 201710408010A CN 107163334 A CN107163334 A CN 107163334A
- Authority
- CN
- China
- Prior art keywords
- foam
- 4phr
- 1phr
- mould moulding
- moulding material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of foam-in-mould moulding material, it includes the material of following parts by weight, specifically:Synthetic rubber 40phr 50phr, polyolefin elastomer 30phr 40phr, polyethylene 10phr 20phr, calcium carbonate 5phr 10phr, foaming agent 3phr 4phr, zinc oxide 4phr, blowing promotor 3phr 4phr, BIBP vulcanizing agent 0.6phr 1phr, zinc stearate 1phr, stearic acid 1phr.By above-mentioned material proportion, expanded material of the invention has high resilience, the characteristic of little compressible, i.e., completed suitable for being foamed in one set of die, being molded one, and the puzzlement without dimensional contraction.
Description
Technical field
The present invention relates to footwear material technical field, more particularly to a kind of shoe-pad expanded material.
Background technology
It is well-known to have following three kinds of technique in current rubber-plastic foamed industry:
1st, cutting processing is molded into product after the big foaming of rubber and plastic flat board.
2nd, the three-dimensional small foaming post-processing molding finished product of rubber and plastic.
3rd, rubber and plastic shooting foaming finished product.
Wherein, for being molded into product mode after the foaming of rubber and plastic size, it needs two molds to complete;For projecting rubber
For modeling foaming, it is only necessary to which one set of die is completed, but has the shortcomings that stability is poor.
The content of the invention
The purpose of the present invention is to solve the shortcomings of the prior art and a kind of foam-in-mould moulding material is provided, the foaming material
Material has high resilience, the characteristic of little compressible, i.e., completed suitable for being foamed in one set of die, being molded one, and without chi
The puzzlement of very little contraction.
To reach above-mentioned purpose, the present invention is achieved through the following technical solutions.
A kind of foam-in-mould moulding material, includes the material of following parts by weight, specifically:
Further, a kind of foam-in-mould moulding material, includes the material of following parts by weight, specifically:
Further, a kind of foam-in-mould moulding material, includes the material of following parts by weight, specifically:
Beneficial effects of the present invention are:A kind of foam-in-mould moulding material of the present invention, it includes following weight
The material of part, specifically:Synthetic rubber 40phr-50phr, polyolefin elastomer 30phr-40phr, polyethylene 10phr-
20phr, calcium carbonate 5phr-10phr, foaming agent 3phr-4phr, zinc oxide 4phr, blowing promotor 3phr-4phr, BIBP vulcanization
Agent 0.6phr-1phr, zinc stearate 1phr, stearic acid 1phr.Pass through above-mentioned material proportion, foam-in-mould forming material of the invention
Material has high resilience, the characteristic of little compressible, i.e., completed suitable for being foamed in one set of die, being molded one, and without chi
The puzzlement of very little contraction.
Embodiment
With reference to specific embodiment, the present invention will be described.
A kind of embodiment one, foam-in-mould moulding material, includes the material of following parts by weight, specifically:
By above-mentioned material proportion, the foam-in-mould moulding material of the present embodiment one has high resilience, little compressible
Characteristic, i.e., complete suitable for being foamed in one set of die, being molded one, and the puzzlement without dimensional contraction.
A kind of embodiment two, foam-in-mould moulding material, includes the material of following parts by weight, specifically:
By above-mentioned material proportion, the foam-in-mould moulding material of the present embodiment two has high resilience, little compressible
Characteristic, i.e., complete suitable for being foamed in one set of die, being molded one, and the puzzlement without dimensional contraction.
A kind of embodiment three, foam-in-mould moulding material, includes the material of following parts by weight, specifically:
By above-mentioned material proportion, the foam-in-mould moulding material of the present embodiment three has high resilience, little compressible
Characteristic, i.e., complete suitable for being foamed in one set of die, being molded one, and the puzzlement without dimensional contraction.
Above content is only presently preferred embodiments of the present invention, for one of ordinary skill in the art, according to the present invention's
Thought, will change in specific embodiments and applications, and this specification content should not be construed as to the present invention
Limitation.
Claims (3)
1. a kind of foam-in-mould moulding material, it is characterised in that include the material of following parts by weight, specifically:
2. a kind of foam-in-mould moulding material according to right wants 1, it is characterised in that include the thing of following parts by weight
Material, specifically:
3. a kind of foam-in-mould moulding material according to right wants 2, it is characterised in that include the thing of following parts by weight
Material, specifically: