CN107160802A - A kind of automobile glass - Google Patents
A kind of automobile glass Download PDFInfo
- Publication number
- CN107160802A CN107160802A CN201710497884.XA CN201710497884A CN107160802A CN 107160802 A CN107160802 A CN 107160802A CN 201710497884 A CN201710497884 A CN 201710497884A CN 107160802 A CN107160802 A CN 107160802A
- Authority
- CN
- China
- Prior art keywords
- semi
- tempered glass
- glass
- plate
- polymeric membrane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of automobile glass, including pet layer, infrared absorption layer, first semi-tempered glass, second semi-tempered glass, first PC plate, second PC plate and polymeric membrane, first semi-tempered glass outer wall the first PC plate of high-pressure bond, polymeric membrane is provided between first semi-tempered glass and the second semi-tempered glass, second safety glass outer wall high-pressure bond acid polyethylene butyral sheet, acid polyethylene butyral sheet outside high pressure bonds the second PC plate, novel in structural design of the present invention, with superior shock resistance and penetration-resistant energy, it ensure that personal safety and the property safety of in-car.
Description
Technical field
The present invention relates to vehicle glass technical field, specially a kind of automobile glass.
Background technology
Automobile has become a kind of common walking-replacing tool, and sales volume is also more and more, and the thing followed is increasing
Traffic accident, therefore, requirement of the people to the security performance of automobile are also increasingly increased.Vehicle glass is frangible as one kind collision
Product, should more pay attention to its security performance, and the quality of glass can cause certain threat, current vehicle glass safely to life
All it is safety glass or local toughened glass, it is mainly by butyl mercaptan, azo-compound, glycerine dimethacrylate etc.
Composition, its anti-impact force is poor, and anti-fog haze is poor, printing opacity, easily caused by criminal's destruction, threatens the personal safety of in-car
And property safety.
The content of the invention
It is an object of the invention to provide a kind of automobile glass, to solve the problems mentioned in the above background technology.
To achieve the above object, the present invention provides following technical scheme:A kind of automobile glass, including it is pet layer, infrared
Absorbed layer, the first semi-tempered glass, the second semi-tempered glass, the first PC plate, the second PC plate and polymeric membrane, it is characterised in that:
Pet layer bonding infrared absorption layer, infrared absorption layer internal layer are adhered by the first semi-tempered glass;
The PC plate of another side high-pressure bond first of first semi-tempered glass, first semi-tempered glass and the second half
Safety glass is superimposed and polymeric membrane is provided between first semi-tempered glass and the second semi-tempered glass, and polymeric membrane is set
In inner side of first semi-tempered glass away from the first PC plate;Outer wall high pressure viscosity of second semi-tempered glass away from polymeric membrane
Close on the outside of acid polyethylene butyral sheet, the acid polyethylene butyral sheet the further PC plate of high-pressure bond second.
It is preferred that, the polymeric membrane includes being coated with high molecular polymer, the polyphosphazene polymer on basement membrane, the basement membrane
Compound is made up of polyethyl acrylate, polymethyl methacrylate, polystyrene;The thickness of the polymeric membrane is 0.5mm-
1mm。
It is preferred that, the thickness of first semi-tempered glass is 2mm-3mm;The thickness of second semi-tempered glass is
3mm-4mm。
It is preferred that, the thickness of first PC plate and the second PC plate is 1mm-2mm.
It is preferred that, the thickness of the acid polyethylene butyral sheet is 0.8mm-1.8mm.
Compared with prior art, the beneficial effects of the invention are as follows:
(1) novel in structural design of the present invention, with superior shock resistance and penetration-resistant energy, it is ensured that in-car person peace
Complete and property safety.
(2) polymeric membrane that the present invention is used includes being coated with high molecular polymer, the polyphosphazene polymer on basement membrane, basement membrane
Compound is made up of polyethyl acrylate, polymethyl methacrylate, polystyrene, and the polymeric membrane of use can improve glass
Toughness, further increases the anti-impact force of glass.
(3) present invention can prevent that fragment splashing causes secondary damage after toughened glass crushing using two pieces of PC plates.
(4) have pet layer, improve rub resistance and anti-fog properties.
(5) infrared ray can effectively be absorbed.
Brief description of the drawings
Fig. 1 is structure sectional view of the present invention;
In figure:1st, the first semi-tempered glass;2nd, the second semi-tempered glass;3rd, the first PC plate;4th, the second PC plate;5th, macromolecule
Film;6th, acid polyethylene butyral sheet;7th, pet layer;8th, infrared absorption layer.
Embodiment
Below in conjunction with the accompanying drawing in the embodiment of the present invention, the technical scheme in the embodiment of the present invention is carried out clear, complete
Site preparation is described, it is clear that described embodiment is only a part of embodiment of the invention, rather than whole embodiments.It is based on
Embodiment in the present invention, it is every other that those of ordinary skill in the art are obtained under the premise of creative work is not made
Embodiment, belongs to the scope of protection of the invention.
Referring to Fig. 1, the present invention provides a kind of technical scheme:A kind of automobile glass, including pet layer 7, infrared absorption
The 8, first semi-tempered glass 1 of layer, the second semi-tempered glass 2, the first PC plate 3, the second PC plate 4 and polymeric membrane 5, its feature exist
In:The bonding of pet layer 7 infrared absorption layer 8, the internal layer of infrared absorption layer 8 are adhered by the first semi-tempered glass 1;
The first PC plate of another side high-pressure bond 3 of first semi-tempered glass 1, first semi-tempered glass 1 and
Two semi-tempered glass 2 are superimposed and polymeric membrane 5, high score are provided between the semi-tempered glass 2 of first semi-tempered glass 1 and second
Sub- film 5 is arranged on inner side of first semi-tempered glass 1 away from the first PC plate 3;Second semi-tempered glass 2 is away from polymeric membrane
5 outer wall high-pressure bond acid polyethylene butyral sheet 6, the outside of the acid polyethylene butyral sheet 6 further high pressure viscosity
Close the second PC plate 4.
In the present embodiment, polymeric membrane 5 includes basement membrane, is coated with high molecular polymer on basement membrane, high molecular polymer by
Polyethyl acrylate, polymethyl methacrylate, polystyrene composition;The thickness of the polymeric membrane is 0.5mm-1mm.This hair
The polymeric membrane of bright use can improve the toughness of glass, further increase the anti-impact force of glass.
In the present embodiment, the thickness of the first semi-tempered glass 1 is 2mm-3mm;The thickness of second semi-tempered glass 2 is 3mm-
4mm;The thickness of first PC plate 3 and the second PC plate 4 is 1mm-2mm;The thickness of acid polyethylene butyral sheet 6 is 0.8mm-
1.8mm。
Novel in structural design of the present invention, with superior shock resistance and penetration-resistant energy, it is ensured that in-car personal safety
And property safety;The present invention can prevent that fragment splashing causes secondary damage after toughened glass crushing using two pieces of PC plates.
Although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of changes, modification can be carried out to these embodiments, replace without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (5)
1. a kind of automobile glass, including pet layer (7), infrared absorption layer (8), the first semi-tempered glass (1), the second half steel
Change glass (2), the first PC plate (3), the second PC plate (4) and polymeric membrane (5), it is characterised in that:Pet layer (7) bonds infrared suction
Receive layer (8), infrared absorption layer (8) internal layer and be adhered by the first semi-tempered glass (1);
The PC plate of another side high-pressure bond first (3) of first semi-tempered glass (1), first semi-tempered glass (1) with
Second semi-tempered glass (2) is superimposed and macromolecule is provided between first semi-tempered glass (1) and the second semi-tempered glass (2)
Film (5), polymeric membrane (5) is arranged on inner side of the first semi-tempered glass (1) away from the first PC plate (3);Second half tempered
Outer wall high-pressure bond acid polyethylene butyral sheet (6) of the glass (2) away from polymeric membrane (5), the acid polyethylene butyral
The further PC plate of high-pressure bond second (4) on the outside of sheet material (6).
2. a kind of automobile glass according to claim 1, it is characterised in that:The polymeric membrane (5) includes basement membrane,
Be coated with high molecular polymer on the basement membrane, the high molecular polymer by polyethyl acrylate, polymethyl methacrylate,
Polystyrene is constituted;The thickness of the polymeric membrane is 0.5mm-1mm.
3. a kind of automobile glass according to claim 1, it is characterised in that:First semi-tempered glass (1)
Thickness is 2mm-3mm;The thickness of second semi-tempered glass (2) is 3mm-4mm.
4. a kind of automobile glass according to claim 1, it is characterised in that:First PC plate (3) and the 2nd PC
The thickness of plate (4) is 1mm-2mm.
5. a kind of automobile glass according to claim 1, it is characterised in that:The acid polyethylene butyral sheet
(6) thickness is 0.8mm-1.8mm.