CN107159249A - The preparation method of ozone Heterogeneous oxidation solid catalyst - Google Patents
The preparation method of ozone Heterogeneous oxidation solid catalyst Download PDFInfo
- Publication number
- CN107159249A CN107159249A CN201710275866.7A CN201710275866A CN107159249A CN 107159249 A CN107159249 A CN 107159249A CN 201710275866 A CN201710275866 A CN 201710275866A CN 107159249 A CN107159249 A CN 107159249A
- Authority
- CN
- China
- Prior art keywords
- weight
- component
- solid catalyst
- dimethyl
- ozone heterogeneous
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to a kind of preparation method of ozone Heterogeneous oxidation solid catalyst, category environmental protection and technical field of chemical engineering catalysts.With perlite, albite, kaolin, red metal and stone, aluminium hydroxide and reddish black masonry carrier are after lithium hypochlorite and double (acetylacetone,2,4-pentanedione) beryllium reamings, surfactant N octadecyldimethyl N ' thmethylpropyl dichloride ammoniums are added after ul-trasonic irradiation progress activation process, carrier in hydrothermal reaction kettle with composite mineralizer borax and potassium sulfate, catalytic activity auxiliary agent predecessor 1, 1, 1 trifluoroacetylacetone (TFA) neodymium, three (2, 2, 6, 6 tetramethyls 3, 5 heptadione acid) gadolinium, three (6, 6, 7, 7, 8, 8, 8 seven fluorine 2, 2 dimethyl 3, 5 octene diketone) dysprosium (III), ten water holmium oxalates, catalytic active center predecessor cobalt edetate, citric acid nickel, zinc lactate and two thiocyanatos silver（I）Sour potassium, hydro-thermal reaction is carried out under the effect of emulsifying agent lauramide propyl-dimethyl dihydroxypropyl ammonium chloride, and drying removes after moisture that calcination obtains ozone Heterogeneous oxidation solid catalyst in Muffle furnace.
Description
Technical field
The present invention relates to a kind of preparation method of ozone Heterogeneous oxidation solid catalyst, category environmental protection and chemical catalyst skill
Art field.
Background technology
Ozonation technology using ozone oxidation ability it is strong the characteristics of, can be by many organic pollution oxidation Decompositions, extensively
For wastewater treatment.Catalytic ozonation technology is divided into ozone homogeneous catalytic oxidation and ozone heterogeneous catalytic oxidation, and ozone is equal
Phase catalysis oxidation has that the more difficult separation and recovery of catalyst is reused, ozone utilization rate is low causes water process operating cost higher,
Organic pollutant removal rate is relatively low simultaneously and easily causing secondary pollution of water is limited to its application；Ozone heterogeneous catalysis oxygen
There is change technology catalyst to be easily isolated and recycled and reusable, ozone utilization rate is high, organic pollutant removal rate is higher, drop
Low water process operating cost and receive significant attention its application the advantages of do not result in secondary pollution.Ozone heterogeneous catalysis
It is to reach local organic matter enrichment by catalyst surface absorption organic matter that oxidation of organic compounds, which is decomposed, while ozone molecule absorption exists
The hydroxyl radical free radical that catalyst surface produces high activity under catalyst action decomposes organic matter.Ozone heterogeneous catalytic oxidation
Handle in waste water technology, core technology is the preparation of ozone Heterogeneous oxidation solid catalyst.
Ozone Heterogeneous oxidation solid catalyst is generally made up of carrier, activated centre and auxiliary agent.Due to being polluted in waste water
Species are various, complex chemical composition feature, can produce harmful effect to performance such as absorption, the mithridatism of catalyst.
Prepare that the carrier structure that ozone Heterogeneous oxidation solid catalyst uses is more single at present, adsorptivity is relatively low；Activated centre is universal
Using normal transition metal salt, mithridatism is poor；Preparation method mainly has infusion process, the precipitation method, mixing method and collosol and gel etc.
Method attachment activity center and adjuvant component are easily liquated out in carrier surface, activated centre and adjuvant component, cause catalyst
Easily lose catalytic activity.For exist in current ozone Heterogeneous oxidation solid catalyst preparation method Catalyst Adsorption compared with
Low, mithridatism is poor and easily loses catalytic activity problem, and exploitation is strengthened using multicomponent porous carrier through reaming, surface active
The adsorptivity of catalyst, catalytic activity auxiliary agent predecessor, normal transition Organometallic are made using Rare-earth chemicals
Compound and precious metal chemical complex are made catalytic active center predecessor and prepared with multicomponent porous carrier through hydro-thermal reaction, high temperature sintering
Ozone Heterogeneous oxidation solid catalyst containing multi-element metal has to improve the preparation method of catalyst mithridatism and catalytic activity
There are larger environmental benefit and higher practical value.
The content of the invention
For existing in current ozone Heterogeneous oxidation solid catalyst preparation method, Catalyst Adsorption is relatively low, mithridatism
Poor to lose catalytic activity problem with easy, exploitation strengthens catalyst using multicomponent porous carrier through reaming, surface active
Adsorptivity, catalytic activity auxiliary agent predecessor, normal transition metallo-organic compound and expensive are made using Rare-earth chemicals
Metallic compound is made catalytic active center predecessor and prepared with multicomponent porous carrier through hydro-thermal reaction, high temperature sintering containing polynary gold
The ozone Heterogeneous oxidation solid catalyst of category to improve the preparation method of catalyst mithridatism and catalytic activity, it is characterized in that
Component A can be added in closed reactor and deionized water stirring prepares the aqueous solution, the weight concentration for control component A is 2%~6%,
After the completion of prepared by solution, B component is added under agitation, 35 DEG C~50 DEG C are warming up to, continues stirring reaction 3h~6h, is filtered, instead
Product is answered to obtain reaming modified support after 102 DEG C~106 DEG C dry constant weights；Reaming modified support puts into ultrasound reactor,
The aqueous solution prepared by component C and deionized water is added, the weight concentration of component C is 3%~8%, is uniformly mixed, and control is super
Sound power density is 0.3~0.8W/m3, frequency 20kHz~30kHz, 40 DEG C~55 DEG C, sonic oscillation 2h~5h obtains ultrasound
Surface active carrier mixed liquor；Ultrasonic surface activated carrier mixed liquor is transferred in hydrothermal reaction kettle, add D components and go from
The aqueous solution that sub- water is prepared, the weight concentration of D components is 40%~55%, by weight, D component deionized water solutions:Ultrasonic table
Weight ratio=1 of face activated carrier mixed liquor:（1.5~2）, control 120 DEG C~180 DEG C of temperature, the hydro-thermal reaction time be 8h~
16h, then dries to obtain fine particle；Fine particle is in Muffle furnace, 600 DEG C~950 DEG C, and calcination 3h~8h obtains ozone non-
Homogeneous oxidizing solid catalyst.The component A is made up of lithium hypochlorite, double (acetylacetone,2,4-pentanedione) berylliums, by weight, lithium hypochlorite:
Weight ratio=1 of double (acetylacetone,2,4-pentanedione) berylliums:（1~1.6）, B component is by perlite, albite, kaolin, red metal and stone, hydroxide
Aluminium, celestine composition, by weight, perlite:Albite:Kaolin:Red metal and stone:Aluminium hydroxide:The weight ratio of celestine=
（5~15）:（7~17）:（9~19）:（11~21）:（13~23）:（15~25）, by weight, component A:The weight of B component
The ratio between=1:（10~20）, component C is N- octadecyldimethyls-N '-trimethyl-propyl dichloride ammonium, by weight, C groups
Point:Weight ratio=1 of reaming modified support:（5~10）, D components are by composite mineralizer borax, potassium sulfate, catalytic activity auxiliary agent
Predecessor 1,1,1- trifluoroacetylacetone (TFA)s neodymium, three (DPM dpm,dipivalomethane acid) gadoliniums, three (6,6,7,7,8,8,
Fluoro- 2,2- dimethyl -3, the 5- octene diketone of 8- seven) dysprosium (III), ten water holmium oxalate Rare-earth chemicals, catalytic activity
Center predecessor normal transition metallo-organic compound cobalt edetate, citric acid nickel, zinc lactate and the sulphur of precious metal chemical complex two
Cyanate radical closes silver（I）Sour potassium, emulsifying agent lauramide propyl-dimethyl dihydroxypropyl ammonium chloride composition, by weight, borax:Sulphur
Sour potassium:1,1,1- trifluoroacetylacetone (TFA) neodymiums:Three (DPM dpm,dipivalomethane acid) gadoliniums:Three (6,6,7,7,8,8,8-
Seven fluoro- 2,2- dimethyl -3,5- octenes diketone) dysprosium (III):Ten water holmium oxalates:Cobalt edetate:Citric acid nickel:Zinc lactate:
Two thiocyanatos silver（I）Sour potassium:The weight ratio of lauramide propyl-dimethyl dihydroxypropyl ammonium chloride=（4~8）:（6~
10）:（3~6）:（4~7）:（5~8）:（6~9）:（10~15）:（12~18）:（4~7）:（6~9）:（6~20）.The B
Perlite, albite, kaolin, red metal and stone, aluminium hydroxide, the celestine of component are crushed respectively, and deionized water washing is dry
After dry removing moisture, -200 mesh ,+400 mesh sieves point are carried out through standard screen, it is the mm of 0.0370mm~0.0750 control particle diameter.
What the technical method of the present invention was realized in：Lithium hypochlorite LiClO, double (second can be being added in closed reactor
Acyl acetone) beryllium C10H14BeO4The aqueous solution is prepared with deionized water stirring, it is 0.0370mm~0.0750mm to add particle diameter after screening
Perlite, albite, kaolin, red metal and stone, aluminium hydroxide and celestine porous material carrier, in certain temperature and stirring bar
Under part, the small Be of aqueous solution Ionic Radius2+（0.31Å）、Li+（0.60Å）Displace part ion radius in porous material big
Ca2+（0.99Å）、K+（1.33Å）、Ba2+（1.35Å）Plasma, the aperture of porous material carrier becomes big, surface roughness increasing
Plus, filtering dries the reaming modified support input ultrasound reactor after constant weight, adds N- octadecyldimethyls-N '-three
MethyI-oropvD dichloride ammonium C18H37N+(CH3)2CH2CH2CH2N+(CH3)3Cl2 - The aqueous solution, control ultrasonic power density, ultrasound
Wave frequency rate, temperature and sonic oscillation time, under ultrasonic cavitation effect, N- octadecyldimethyls-N '-trimethyl-propyl
Dichloride ammonium C18H37N+(CH3)2CH2CH2CH2N+(CH3)3Cl2 - Be easy to from the aqueous solution escape into reaming modified support duct or
Reaming modified support surface is attached to, is beneficial to being interconnected and carrier surface activation for carrier duct, enhances adsorptivity；It is super
After the completion of sound activation, ultrasonic surface activated carrier mixed liquor is transferred in hydrothermal reaction kettle, with borax Na2B4O7·10H2O, sulphur
Sour potassium K2SO4Composite mineralizer, the trifluoroacetylacetone (TFA) neodymium C of catalytic activity auxiliary agent predecessor 1,1,1-15H12F9NdO6, three (2,2,6,
6- tetramethyl -3,5- heptadione acid) gadolinium C33H57GdO6, three (the fluoro- 2,2- dimethyl -3,5- octenes two of 6,6,7,7,8,8,8- seven
Ketone) dysprosium (III) C30H30DyF21O6, ten water holmium oxalate C6Ho2O12Before Rare-earth chemicals, catalytic active center component
Drive thing normal transition metallo-organic compound cobalt edetate C12H22 O14Co, citric acid nickel C12H10 O14Ni3, zinc lactate
C6H10O6Zn and two thiocyanatos silver（I）Sour potassium K [Ag (SCN)2] precious metal chemical complex, in emulsifying agent lauramide propyl group two
Methyl dihydroxypropyl ammonium chloride [C11H23CONHCH2CH2N(CH3)2CH2CH(OH)CH2OH]+ Cl- The lower progress hydro-thermal of effect is anti-
Should, mineralizer accelerates diffusion, activates reactant lattice, promotes the progress of solid phase reaction, ultrasonic surface activated carrier
With Rare-earth chemicals, normal transition metallo-organic compound, precious metal chemical complex Uniform Doped, emulsifying agent lauroyl
Amine propyl-dimethyl dihydroxypropyl ammonium chloride make reaction solution formed quasi-stationary emulsion prevent separation of solid and liquid, sedimentation, while right
The further surface active of porous carrier, by the way that in certain temperature, the hydro-thermal reaction of time, drying obtains the fine silt of Uniform Doped
Thing；The fine silt thing of Uniform Doped is in Muffle furnace, through high temperature sintering, and organic matter carbonization therein further enhances many
The microcellular structure of hole carrier, obtains porous carrier supported rare earth metal oxide, transition metal oxide and noble metal formation
The ozone Heterogeneous oxidation solid catalyst of catalytic active center, improves the mithridatism and catalytic activity of catalyst.
Relative to art methods, outstanding feature of the present invention is that perlite, albite, kaolinite are used in technology of preparing
Native, red metal and stone, aluminium hydroxide, celestine porous material make carrier, due to lithium hypochlorite LiClO and double (acetylacetone,2,4-pentanedione) berylliums
C10H14BeO4Reaming effect, N- octadecyldimethyls-N '-trimethyl-propyl dichloride ammonium C18H37N+(CH3)2CH2CH2CH2N+(CH3)3Cl2 -, lauramide propyl-dimethyl dihydroxypropyl ammonium chloride [C11H23CONHCH2CH2N(CH3)2CH2CH(OH)CH2OH]+ Cl- To being interconnected and surface activation for duct；Make rare earth metal organic by hydro-thermal reaction
Compound, normal transition metallo-organic compound and precious metal chemical complex reach Uniform Doped and are attached to carrier surface and duct
Interior, high temperature sintering makes organic matter carbonization strengthen and form multi-level microcellular structure, porous carrier supported rare earth metal
The multi-element metal catalytic active center of oxide, transition metal oxide and noble metal formation is combined more firm with porous carrier
Gu, the ozone Heterogeneous oxidation solid catalyst of preparation has a stronger adsorptivity, the cooperative effect of multi-element metal, particularly mixes
Miscellaneous noble metal has stability and high activity, can suppress liquating out for metal catalytic activity component, improve catalyst
Mithridatism and catalytic activity, with good environmental benefit and economic benefit.
Embodiment
Embodiment 1:1.35g lithium hypochlorites, double (acetylacetone,2,4-pentanedione) berylliums of 1.65g, 140ml deionized waters are added to volume for 500ml
Can be uniformly mixed in closed reactor, the weight concentration of the aqueous solution is 2.1%, lithium hypochlorite:Double (acetylacetone,2,4-pentanedione) berylliums
Weight ratio=1:1.2；Add deionized water wash to it is neutral, 103 DEG C dry and remove the mesh of -200 mesh of sieving after moisture~+400
The 2.75g perlites of standard screen, 3.75g albites, 4.75g kaolin, the red metals and stones of 5.75g, 6.75g aluminium hydroxides, 7.75g days
The weight of green stone, lithium hypochlorite and double (acetylacetone,2,4-pentanedione) berylliums（3g）:The weight of porous material（31.5g）=1:10.5, it is warming up to 36
DEG C, obtain reaming modified support 31g after continuing stirring reaction 3.2h, filtering, 103 DEG C of dry constant weights；In 500ml ultrasonic responses
In device, reaming modified support 31g is put into, 3.25gN- octadecyldimethyls-N '-trimethyl-propyl dichloride ammonium is added molten
In the aqueous solution of 100ml deionized waters, the weight concentration of the aqueous solution is 3.1%, is uniformly mixed, N- hexadecyldimethylamines
Base-N '-trimethyl-propyl dichloride ammonium（3.25g）:Reaming modified support（31g ）=1:9.5；The ultrasonic power density is controlled to be
0.4 W/m3, ultrasonic frequency 21kHz, 41 DEG C of temperature, sonic oscillation 2.2h；After the completion of ultrasonic activation, ultrasound reactor
In ultrasonic surface activated carrier mixed liquor be transferred in 500ml hydrothermal reaction kettles, add by 2.1g boraxs, 3.05g sulfuric acid
Potassium, 1.6g1,1,1- trifluoroacetylacetone (TFA)s neodymium, 2.05g tri- (DPM dpm,dipivalomethane acid) gadolinium, 2.6g tri- (6,
The fluoro- 2,2- dimethyl -3,5- octenes diketone of 6,7,7,8,8,8- seven) dysprosium (III), the water holmium oxalates of 3.05g ten, 5.05g grapes
Saccharic acid cobalt, 6.1g citric acids nickel, 2.05g zinc lactates, the thiocyanatos of 3.1g bis- silver（I）Sour potassium, 3.05g lauramide propyl group
The aqueous solution that dimethyl dihydroxypropyl ammonium chloride and 50ml deionized waters are prepared, the weight concentration of the aqueous solution is 40.3%, should
The weight of the aqueous solution:Weight=83.8g of ultrasonic surface activated carrier mixed liquor:134.25g =1:1.6,125 DEG C of temperature is controlled,
The hydro-thermal reaction time is 8.3h, then dries to obtain fine silt thing for 105 DEG C；Fine silt thing is in Muffle furnace, 620 DEG C, calcination 3.2h,
After cooling down, the ozone Heterogeneous oxidation solid catalyst of fine particle shape can obtain.
Embodiment 2:0.24g lithium hypochlorites, double (acetylacetone,2,4-pentanedione) berylliums of 0.36g, 10ml deionized waters, being added to volume is
100ml's can be uniformly mixed in closed reactor, and the weight concentration of the aqueous solution is 5.7%, lithium hypochlorite:Double (levulinics
Ketone) beryllium weight ratio=1:1.5；Add deionized water wash to it is neutral, 103 DEG C dry remove -200 mesh of sieving after moisture~+
The 1.45g perlites of 400 mesh standard sieves, 1.65g albites, 1.85g kaolin, the red metals and stones of 2.05g, 2.25g aluminium hydroxides,
The weight of 2.45g celestines, lithium hypochlorite and double (acetylacetone,2,4-pentanedione) berylliums（0.6g）:The weight of porous material（11.7g）=1:
19.5,48 DEG C are warming up to, reaming modified support 11.5g is obtained after continuing stirring reaction 5.8h, filtering, 105 DEG C of dry constant weights；
In 100ml ultrasound reactors, reaming modified support 11.5g is put into, 2.2gN- octadecyldimethyls-N '-front three is added
Base-propyl group dichloride ammonium is dissolved in the aqueous solution of 26ml deionized waters, and the weight concentration of the aqueous solution is 7.8%, and stirring mixing is equal
It is even, N- octadecyldimethyls-N '-trimethyl-propyl dichloride ammonium（2.2g）:Reaming modified support（11.5g ）=1:5.2；
It is 0.7 W/m to control ultrasonic power density3, ultrasonic frequency 29kHz, 54 DEG C of temperature, sonic oscillation 4.7h；Ultrasonic activation is completed
Afterwards, the ultrasonic surface activated carrier mixed liquor in ultrasound reactor is transferred in 100ml hydrothermal reaction kettles, add by
0.78g boraxs, 0.97g potassium sulfates, 0.58g1,1,1- trifluoroacetylacetone (TFA)s neodymium, 0.67g tri- (2,2,6,6- tetramethyls -3,5- heptan
Two ketone acids) gadolinium, 0.78g tri- (the fluoro- 2,2- dimethyl -3,5- octenes diketone of 6,6,7,7,8,8,8- seven) dysprosium (III), 0.87g ten
Water holmium oxalate, 1.48g cobalt edetates, 1.77g citric acids nickel, 0.68g zinc lactates, the thiocyanatos of 0.87g bis- silver（I）Acid
The aqueous solution that potassium, 1.98g lauramides propyl-dimethyl dihydroxypropyl ammonium chloride and 10ml deionized waters are prepared, the aqueous solution
Weight concentration is 53.3%, the weight of the aqueous solution:Weight=21.43g of ultrasonic surface activated carrier mixed liquor:39.7g =1:
1.9,175 DEG C of temperature is controlled, the hydro-thermal reaction time is 15.5h, then dries to obtain fine silt thing for 105 DEG C；Fine silt thing is in Muffle
In stove, 930 DEG C, calcination 7.5h after cooling down, can obtain the ozone Heterogeneous oxidation solid catalyst of fine particle shape.
Comparative example 1:Preparation process is not added with lithium hypochlorite, double (acetylacetone,2,4-pentanedione) berylliums, N- octadecyldimethyls-N '-front three
Outside base-propyl group dichloride ammonium, lauramide propyl-dimethyl dihydroxypropyl ammonium chloride, borax and potassium sulfate, whole preparation process,
Preparation condition is identical with embodiment 1.
The parameter of ozone Heterogeneous oxidation solid catalyst prepared by embodiment 1, embodiment 2 and comparative example 1 is included in table 1.
The embodiment of table 1 and comparative example prepare ozone Heterogeneous oxidation solid catalysis agent parameter
| Project | Average pore size (nm) | Pore volume (cm3/g) | BET is than surface (m2/g) |
| Embodiment 1 | 4.511 | 0.6026 | 797.83 |
| Embodiment 2 | 4.017 | 0.5530 | 696.40 |
| Comparative example 1 | 2.029 | 0.3030 | 496.60 |
Claims (2)
1. a kind of preparation method of ozone Heterogeneous oxidation solid catalyst, it is characterized in that A groups can added in closed reactor
Divide and deionized water stirring prepares the aqueous solution, the weight concentration for controlling component A is 2%~6%, after the completion of prepared by solution, in stirring
Lower addition B component, is warming up to 35 DEG C~50 DEG C, continues stirring reaction 3h~6h, and filtering, reaction product is dry at 102 DEG C~106 DEG C
Reaming modified support is obtained after dry constant weight, reaming modified support input ultrasound reactor, addition is matched somebody with somebody by component C and deionized water
The aqueous solution of system, the weight concentration of component C is 3%~8%, is uniformly mixed, and it is 0.3~0.8W/ to control ultrasonic power density
m3, frequency 20kHz~30kHz, 40 DEG C~55 DEG C, sonic oscillation 2h~5h obtains ultrasonic surface activated carrier mixed liquor, transfer
Into hydrothermal reaction kettle, the aqueous solution that D components and deionized water are prepared is added, the weight concentration of D components is 40%~55%, is pressed
Weight meter, D component deionized water solutions:Weight ratio=1 of ultrasonic surface activated carrier mixed liquor:（1.5~2）, control temperature
120 DEG C~180 DEG C, the hydro-thermal reaction time is 8h~16h, then dries to obtain fine silt thing, fine silt thing is in Muffle furnace, 600
DEG C~950 DEG C, calcination 3h~8h obtains ozone Heterogeneous oxidation solid catalyst；The component A by expanding agent lithium hypochlorite,
Double (acetylacetone,2,4-pentanedione) beryllium compositions, by weight, lithium hypochlorite:Weight ratio=1 of double (acetylacetone,2,4-pentanedione) berylliums:（1~1.6）, B groups
Divide and be made up of perlite, albite, kaolin, red metal and stone, aluminium hydroxide, celestine, by weight, perlite:Albite:It is high
Ridge soil:Red metal and stone:Aluminium hydroxide:The weight ratio of celestine=（5~15）:（7~17）:（9~19）:（11~21）:（13~
23）:（15~25）, by weight, component A:Weight ratio=1 of B component:（10~20）, component C is N- hexadecyldimethylamines
Base-N '-trimethyl-propyl dichloride ammonium, by weight, component C:Weight ratio=1 of reaming modified support:（5~10）, D groups
Divide by composite mineralizer borax, potassium sulfate, the trifluoroacetylacetone (TFA) neodymium of catalytic activity auxiliary agent predecessor 1,1,1-, three (2,2,6,6-
Tetramethyl -3,5- heptadione acid) gadolinium, three (the fluoro- 2,2- dimethyl -3,5- octenes diketone of 6,6,7,7,8,8,8- seven) dysprosiums
(III), ten water holmium oxalate Rare-earth chemicals, catalytic active center predecessor normal transition metallo-organic compound Portugal
Grape saccharic acid cobalt, citric acid nickel, zinc lactate and the thiocyanato of precious metal chemical complex two silver（I）Sour potassium, emulsifying agent lauramide third
Base dimethyl dihydroxypropyl ammonium chloride is constituted, by weight, borax:Potassium sulfate:1,1,1- trifluoroacetylacetone (TFA) neodymiums:Three (2,2,
6,6- tetramethyl -3,5- heptadione acid) gadolinium:Three (the fluoro- 2,2- dimethyl -3,5- octenes diketone of 6,6,7,7,8,8,8- seven) dysprosiums
(III):Ten water holmium oxalates:Cobalt edetate:Citric acid nickel:Zinc lactate:Two thiocyanatos silver（I）Sour potassium:Lauramide third
The weight ratio of base dimethyl dihydroxypropyl ammonium chloride=（4~8）:（6~10）:（3~6）:（4~7）:（5~8）:（6~9）:
（10~15）:（12~18）:（4~7）:（6~9）:（6~20）.
2. B component is by perlite, albite, kaolin, red metal and stone, aluminium hydroxide, celestine group according to claim 1
Into perlite, albite, kaolin, red metal and stone, aluminium hydroxide, celestine are crushed respectively, and deionized water washing drying is removed
Go after moisture, sieved through standard screen, it is 0.0370mm~0.0750mm to control particle diameter.