CN107151519A - A kind of protective paint of environmental protection machinery equipment and preparation method thereof - Google Patents
A kind of protective paint of environmental protection machinery equipment and preparation method thereof Download PDFInfo
- Publication number
- CN107151519A CN107151519A CN201710566389.XA CN201710566389A CN107151519A CN 107151519 A CN107151519 A CN 107151519A CN 201710566389 A CN201710566389 A CN 201710566389A CN 107151519 A CN107151519 A CN 107151519A
- Authority
- CN
- China
- Prior art keywords
- parts
- environmental protection
- protective paint
- machinery equipment
- stearic acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of protective paint of environmental protection machinery equipment, include following raw material according to parts by weight：10 ~ 20 parts of stearic acid first APEO, 2 ~ 10 parts of rosin, 2 ~ 6 parts of tung oil, 1 ~ 6 part of cannabis oil, 6 ~ 10 parts of triethanolamine, 5 ~ 10 parts of color stuffing, 3 ~ 9 parts of epoxy organosilicon, 10 ~ 60 parts of solvent, 5 ~ 15 parts of coalescents, 2 ~ 10 parts of methyl polyester resin, 7 ~ 13 parts of bentonite, 10 ~ 15 parts of thickener, 5 ~ 8 parts of corrosion inhibiter, 5 ~ 10 parts of surfactant.The present invention provides a kind of protective paint of environmental protection equipment and preparation method thereof; preparation method; simple and easy to apply, contamination-free, the protective paint prepared is applied in environmental protection machinery equipment; plant equipment can be protected to be contaminated thing gas attack; the rich texture of the paint film of protective paint, friction will not produce electrostatic, there is excellent water resistance, elasticity; smear smooth, drying time is short.
Description
Technical field
The invention belongs to environmental protection machinery protection field, and in particular to a kind of protective paint of environmental protection machinery equipment and its preparation
Method.
Background technology
Environmental protection machinery equipment refer to be used for control environmental pollution, environment-friendly active charcoal improve environmental quality and have production unit or
Construction and installation unit manufactures and built engineering goods, structures and the system come.Also it is believed that, environmental protection equipment refer to administer
The machining product of environmental pollution, such as deduster, weldering fume purifier, monomer water treatment facilities, noise controller.Environmental protection is set
It is standby also to include the power-equipment of conveying flowing material containing pollutant, such as water pump, blower fan, conveyer；Also include ensureing simultaneously
The monitoring and controlling instrument that Pollution treatment installation is normally run, such as detecting instrument, pressure gauge, flow monitoring device.Environment
Improvement has been very urgent thing.Environmental protection equipment should include complete set of equipments：Such as air cleaner, sewage disposal is set
It is standby, ozone generator, industrial oxygenerating machine etc..The equipment that environment can be administered in industry or family.
Because the environment that environmental protection machinery equipment is contacted is extremely severe, such as dust, weldering cigarette, dusty gas or liquid, machinery
Equipment surface is subject to corrode, it is therefore necessary to propose a kind of protective paint of environmental protection machinery equipment.
The content of the invention
In view of the above-mentioned problems, the technical problem to be solved in the present invention is to provide a kind of protective paint of environmental protection machinery equipment and
Its preparation method.
To achieve the above object, the technical scheme is that：A kind of protective paint of environmental protection machinery equipment, according to weight
Part includes following raw material：10 ~ 20 parts of stearic acid first APEO, 2 ~ 10 parts of rosin, 2 ~ 6 parts of tung oil, 1 ~ 6 part of cannabis oil, three
6 ~ 10 parts of monoethanolamine, 5 ~ 10 parts of color stuffing, 3 ~ 9 parts of epoxy organosilicon, 10 ~ 60 parts of solvent, 5 ~ 15 parts of coalescents, methyl polyester
2 ~ 10 parts of resin, 7 ~ 13 parts of bentonite, 10 ~ 15 parts of thickener, 5 ~ 8 parts of corrosion inhibiter, 5 ~ 10 parts of surfactant.
Further, following raw material is included according to parts by weight：10 parts of stearic acid first APEO, 2 parts of rosin, tung oil 2
Part, 1 part of cannabis oil, 6 parts of triethanolamine, 5 parts of color stuffing, 3 parts of epoxy organosilicon, 10 parts of solvent, 5 parts of coalescents, methyl gather
2 parts of ester resin, 7 parts of bentonite, 10 parts of thickener, 5 parts of corrosion inhibiter, 5 parts of surfactant.
Further, one kind in methyl acetate, ethyl acetate, propyl acetate, methanol and ethanol of the solvent or
Their mixture of person.
Further, the thickener is starch derivatives, specially in starch phosphate sodium, the starch phosphate of phosphorylation two
One or two；The corrosion inhibiter is polycarboxylic acids, organophosphor carboxylic acid and the mixture containing co-polymer of sulfonate, and its mass ratio is
2:2:1。
Further, the methyl polyester resin is band active methyl polyester resin.
Further, the surfactant is sodium sulfate of polyethenoxy ether of fatty alcohol, sldium lauryl sulfate, lauroyl
It is a kind of or many in glutamic acid, glycerol stearate monoesters, lignosulfonates, heavy alkylbenzene sulfonate and alkylsulfonate
Kind.
A kind of preparation method of the protective paint of environmental protection machinery equipment, is mainly included the following steps that：
Step 1：The component of following parts by weight is weighed respectively：10 ~ 20 parts of stearic acid first APEO, 2 ~ 10 parts of rosin, paulownia
Oil 2 ~ 6 parts, 1 ~ 6 part of cannabis oil, 6 ~ 10 parts of triethanolamine, 5 ~ 10 parts of color stuffing, 3 ~ 9 parts of epoxy organosilicon, 10 ~ 60 parts of solvent,
5 ~ 15 parts of coalescents, 2 ~ 10 parts of methyl polyester resin, 7 ~ 13 parts of bentonite, 10 ~ 15 parts of thickener, 5 ~ 8 parts of corrosion inhibiter, surface
5 ~ 10 parts of activating agent；
Step 2：The stearic acid first APEO that step 1 is weighed is added in the reactor for filling solvent, starts stirring, is stirred
Speed is 100 ~ 150/min, is gradually heated up, when temperature is risen into 70 ~ 80 DEG C, 20 ~ 40min of insulation is carried out, until stearic acid first
Untill APEO is completely dissolved, stearic acid first polyoxyethylene ethereal solution is formed；
Step 3：Stearic acid first polyoxyethylene ethereal solution is cooled to after room temperature, while stirring be added dropwise rosin, tung oil, cannabis oil,
Continue to stir 20 ~ 40min after triethanolamine, color stuffing, epoxy organosilicon, completion of dropping；
Step 4：Continue to add coalescents, methyl polyester resin, bentonite, thickener, corrosion inhibiter, surface work into reactor
Property agent, stir in addition, and it is 50 ~ 70 DEG C to keep temperature in reactor, after 20 ~ 40min of stirring, 1 ~ 3h of standing is produced
Protective paint finished product.
Further, it is cooled to the natural type of cooling in the step 3.
The beneficial effects of the present invention are：The present invention provides a kind of protective paint of environmental protection equipment and preparation method thereof, system
Preparation Method, simple and easy to apply, contamination-free, the protective paint prepared is applied in environmental protection machinery equipment, can protect plant equipment
Thing gas attack is contaminated, the rich texture of the paint film of protective paint, friction will not produce electrostatic, there is excellent water resistance, bullet
Property, smear smooth, drying time is short.Due to adding bentonite in protective paint as inserts, paint film can be enriched, increase hides
Gai Li, assigns paint and is difficult precipitation and good brushability, it also has stronger hygroscopicity and cementability, not only natural environmental-protective
And improve the hygroscopicity and cementability of paint；
Color stuffing is added in the present invention and provides color and covering power for paint film, the protective value and decorative effect of paint is improved, it is resistance to
The good pigment of time property can improve the service life of paint.
Solvent used in the present invention is selected from the esters alcohol organic solvents such as methyl acetate, ethyl acetate, ethanol, dissolving effect
It is really good, and these solvents are harmless, and the protective paint prepared is also harmless to human body.
Embodiment
In order to make the purpose , technical scheme and advantage of the present invention be clearer, with reference to embodiments, to the present invention
It is described in further detail.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, do not limit
The fixed present invention.
Embodiment 1
A kind of protective paint of environmental protection machinery equipment, includes following raw material according to parts by weight：10 parts of stearic acid first APEO,
2 parts of rosin, 2 parts of tung oil, 1 part of cannabis oil, 6 parts of triethanolamine, 5 parts of color stuffing, 3 parts of epoxy organosilicon, 10 parts of solvent, film forming are helped
5 parts of agent, 2 parts of methyl polyester resin, 7 parts of bentonite, 10 parts of thickener, 5 parts of corrosion inhibiter, 5 parts of surfactant.
A kind of in methyl acetate, ethyl acetate, propyl acetate, methanol and ethanol of the solvent or theirs is mixed
Compound.
The thickener be starch derivatives, specially starch phosphate sodium, one kind in the starch phosphate of phosphorylation two or
Two kinds；The corrosion inhibiter is polycarboxylic acids, organophosphor carboxylic acid and the mixture containing co-polymer of sulfonate, and its mass ratio is 2:2:1.
The methyl polyester resin is band active methyl polyester resin.
The surfactant is sodium sulfate of polyethenoxy ether of fatty alcohol, sldium lauryl sulfate, lauroyl glutamate, hard
One or more in resin acid monoglyceride, lignosulfonates, heavy alkylbenzene sulfonate and alkylsulfonate.
A kind of preparation method of the protective paint of environmental protection machinery equipment, is mainly included the following steps that：
Step 1：The component of following parts by weight is weighed respectively：10 parts of stearic acid first APEO, 2 parts of rosin, 2 parts of tung oil,
1 part of cannabis oil, 6 parts of triethanolamine, 5 parts of color stuffing, 3 parts of epoxy organosilicon, 10 parts of solvent, 5 parts of coalescents, methyl polyester tree
2 parts of fat, 7 parts of bentonite, 10 parts of thickener, 5 parts of corrosion inhibiter, 5 parts of surfactant；
Step 2：The stearic acid first APEO that step 1 is weighed is added in the reactor for filling solvent, starts stirring, is stirred
Speed is 100r/min, is gradually heated up, when temperature is risen into 70 DEG C, carries out insulation 20min, until stearic acid first APEO
Untill being completely dissolved, stearic acid first polyoxyethylene ethereal solution is formed；
Step 3：Stearic acid first polyoxyethylene ethereal solution is cooled to after room temperature, while stirring be added dropwise rosin, tung oil, cannabis oil,
Continue to stir 20min after triethanolamine, color stuffing, epoxy organosilicon, completion of dropping；
Step 4：Continue to add coalescents, methyl polyester resin, bentonite, thickener, corrosion inhibiter, surface work into reactor
Property agent, stir in addition, and it is 50 DEG C to keep temperature in reactor, after stirring 20min, standing 1h produces protection and painted
Product.
The natural type of cooling is cooled in the step 3.
Embodiment 2
A kind of protective paint of environmental protection machinery equipment, includes following raw material according to parts by weight：15 parts of stearic acid first APEO,
6 parts of rosin, 5 parts of tung oil, 3 parts of cannabis oil, 8 parts of triethanolamine, 7 parts of color stuffing, 6 parts of epoxy organosilicon, 50 parts of solvent, film forming are helped
10 parts of agent, 6 parts of methyl polyester resin, 10 parts of bentonite, 13 parts of thickener, 9 parts of corrosion inhibiter, 7 parts of surfactant.
A kind of in methyl acetate, ethyl acetate, propyl acetate, methanol and ethanol of the solvent or theirs is mixed
Compound.
The thickener be starch derivatives, specially starch phosphate sodium, one kind in the starch phosphate of phosphorylation two or
Two kinds；The corrosion inhibiter is polycarboxylic acids, organophosphor carboxylic acid and the mixture containing co-polymer of sulfonate, and its mass ratio is 2:2:1.
The methyl polyester resin is band active methyl polyester resin.
The surfactant is sodium sulfate of polyethenoxy ether of fatty alcohol, sldium lauryl sulfate, lauroyl glutamate, hard
One or more in resin acid monoglyceride, lignosulfonates, heavy alkylbenzene sulfonate and alkylsulfonate.
A kind of preparation method of the protective paint of environmental protection machinery equipment, is mainly included the following steps that：
Step 1：The component of following parts by weight is weighed respectively：15 parts of stearic acid first APEO, 6 parts of rosin, 5 parts of tung oil,
3 parts of cannabis oil, 8 parts of triethanolamine, 7 parts of color stuffing, 6 parts of epoxy organosilicon, 50 parts of solvent, 10 parts of coalescents, methyl polyester
6 parts of resin, 10 parts of bentonite, 13 parts of thickener, 9 parts of corrosion inhibiter, 7 parts of surfactant；
Step 2：The stearic acid first APEO that step 1 is weighed is added in the reactor for filling solvent, starts stirring, is stirred
Speed is 120/min, is gradually heated up, when temperature is risen into 75 DEG C, carries out insulation 30min, until stearic acid first APEO
Untill being completely dissolved, stearic acid first polyoxyethylene ethereal solution is formed；
Step 3：Stearic acid first polyoxyethylene ethereal solution is cooled to after room temperature, while stirring be added dropwise rosin, tung oil, cannabis oil,
Continue to stir 30min after triethanolamine, color stuffing, epoxy organosilicon, completion of dropping；
Step 4：Continue to add coalescents, methyl polyester resin, bentonite, thickener, corrosion inhibiter, surface work into reactor
Property agent, stir in addition, and it is 60 DEG C to keep temperature in reactor, after stirring 30min, standing 2h produces protection and painted
Product.
The natural type of cooling is cooled in the step 3.
Embodiment 3
A kind of protective paint of environmental protection machinery equipment, includes following raw material according to parts by weight：20 parts of stearic acid first APEO,
10 parts of rosin, 6 parts of tung oil, 6 parts of cannabis oil, 10 parts of triethanolamine, 10 parts of color stuffing, 9 parts of epoxy organosilicon, 60 parts of solvent, into
15 parts of film auxiliary agent, 10 parts of methyl polyester resin, 13 parts of bentonite, 15 parts of thickener, 8 parts of corrosion inhibiter, 10 parts of surfactant.
A kind of in methyl acetate, ethyl acetate, propyl acetate, methanol and ethanol of the solvent or theirs is mixed
Compound.
The thickener be starch derivatives, specially starch phosphate sodium, one kind in the starch phosphate of phosphorylation two or
Two kinds；The corrosion inhibiter is polycarboxylic acids, organophosphor carboxylic acid and the mixture containing co-polymer of sulfonate, and its mass ratio is 2:2:1.
The methyl polyester resin is band active methyl polyester resin.
The surfactant is sodium sulfate of polyethenoxy ether of fatty alcohol, sldium lauryl sulfate, lauroyl glutamate, hard
One or more in resin acid monoglyceride, lignosulfonates, heavy alkylbenzene sulfonate and alkylsulfonate.
A kind of preparation method of the protective paint of environmental protection machinery equipment, is mainly included the following steps that：
Step 1：The component of following parts by weight is weighed respectively：20 parts of stearic acid first APEO, 10 parts of rosin, 6 parts of tung oil,
6 parts of cannabis oil, 10 parts of triethanolamine, 10 parts of color stuffing, 9 parts of epoxy organosilicon, 60 parts of solvent, 15 parts of coalescents, methyl gather
10 parts of ester resin, 13 parts of bentonite, 15 parts of thickener, 8 parts of corrosion inhibiter, 10 parts of surfactant；
Step 2：The stearic acid first APEO that step 1 is weighed is added in the reactor for filling solvent, starts stirring, is stirred
Speed is 150/min, is gradually heated up, when temperature is risen into 80 DEG C, carries out insulation 40min, until stearic acid first APEO
Untill being completely dissolved, stearic acid first polyoxyethylene ethereal solution is formed；
Step 3：Stearic acid first polyoxyethylene ethereal solution is cooled to after room temperature, while stirring be added dropwise rosin, tung oil, cannabis oil,
Continue to stir 40min after triethanolamine, color stuffing, epoxy organosilicon, completion of dropping；
Step 4：Continue to add coalescents, methyl polyester resin, bentonite, thickener, corrosion inhibiter, surface work into reactor
Property agent, stir in addition, and it is 70 DEG C to keep temperature in reactor, after stirring 40min, standing 3h produces protection and painted
Product.
The natural type of cooling is cooled in the step 3.
Performance test
According to GB/T1724-79, coating appearance, drying time, adhesive force are carried out to the present embodiment 1, embodiment 2, embodiment 3
It can test, and be compared as a control group with prior art, the following form of test result：
| Embodiment 1 | Embodiment 2 | Embodiment 3 | Control group | |
| Coating appearance | Smooth coating | Smooth coating | Smooth coating | There is scratch |
| Drying time（h） | 1 | 1.2 | 0.8 | 1.5 |
| Adhesive force（Level） | ≤2 | ≤2 | ≤3 | ≤3 |
The preferred embodiments of the present invention are the foregoing is only, are not intended to limit the invention, although with reference to the foregoing embodiments
The present invention is described in detail, for those skilled in the art, it still can be to foregoing embodiments institute
The technical scheme of record is modified, or carries out equivalent substitution to which part technical characteristic.It is all the present invention spirit and
Within principle, any modification, equivalent substitution and improvements made etc. should be included in the scope of the protection.
Claims (8)
1. a kind of protective paint of environmental protection machinery equipment, it is characterised in that include following raw material according to parts by weight：Stearic acid first is gathered
10 ~ 20 parts of oxygen vinethene, 2 ~ 10 parts of rosin, 2 ~ 6 parts of tung oil, 1 ~ 6 part of cannabis oil, 6 ~ 10 parts of triethanolamine, 5 ~ 10 parts of color stuffing,
3 ~ 9 parts of epoxy organosilicon, 10 ~ 60 parts of solvent, 5 ~ 15 parts of coalescents, 2 ~ 10 parts of methyl polyester resin, 7 ~ 13 parts of bentonite, increasing
Thick dose 10 ~ 15 parts, 5 ~ 8 parts of corrosion inhibiter, 5 ~ 10 parts of surfactant.
2. the protective paint of a kind of environmental protection machinery equipment according to claim 1, it is characterised in that include according to parts by weight
Following raw material：10 parts of stearic acid first APEO, 2 parts of rosin, 2 parts of tung oil, 1 part of cannabis oil, 6 parts of triethanolamine, color stuffing 5
It is part, 3 parts of epoxy organosilicon, 10 parts of solvent, 5 parts of coalescents, 2 parts of methyl polyester resin, 7 parts of bentonite, 10 parts of thickener, slow
Lose 5 parts of agent, 5 parts of surfactant.
3. the protective paint of a kind of environmental protection machinery equipment according to claim 1, it is characterised in that the solvent is selected from vinegar
A kind of or their mixture in sour methyl esters, ethyl acetate, propyl acetate, methanol and ethanol.
4. the protective paint of a kind of environmental protection machinery equipment according to claim 1, it is characterised in that the thickener is shallow lake
One or both of powder derivative, specially starch phosphate sodium, the starch phosphate of phosphorylation two；The corrosion inhibiter is poly- carboxylic
Acid, organophosphor carboxylic acid and the mixture containing co-polymer of sulfonate, its mass ratio are 2:2:1.
5. a kind of protective paint of environmental protection machinery equipment according to claim 1, it is characterised in that the methyl polyester tree
Fat is band active methyl polyester resin.
6. a kind of protective paint of environmental protection machinery equipment according to claim 1, it is characterised in that the surfactant
For sodium sulfate of polyethenoxy ether of fatty alcohol, sldium lauryl sulfate, lauroyl glutamate, glycerol stearate monoesters, sulfomethylated lignin
One or more in hydrochlorate, heavy alkylbenzene sulfonate and alkylsulfonate.
7. a kind of preparation method of the protective paint of environmental protection machinery equipment, it is characterised in that mainly include the following steps that：
Step 1：The component of following parts by weight is weighed respectively：10 ~ 20 parts of stearic acid first APEO, 2 ~ 10 parts of rosin, paulownia
Oil 2 ~ 6 parts, 1 ~ 6 part of cannabis oil, 6 ~ 10 parts of triethanolamine, 5 ~ 10 parts of color stuffing, 3 ~ 9 parts of epoxy organosilicon, 10 ~ 60 parts of solvent,
5 ~ 15 parts of coalescents, 2 ~ 10 parts of methyl polyester resin, 7 ~ 13 parts of bentonite, 10 ~ 15 parts of thickener, 5 ~ 8 parts of corrosion inhibiter, surface
5 ~ 10 parts of activating agent；
Step 2：The stearic acid first APEO that step 1 is weighed is added in the reactor for filling solvent, starts stirring, is stirred
Speed is 100 ~ 150/min, is gradually heated up, when temperature is risen into 70 ~ 80 DEG C, 20 ~ 40min of insulation is carried out, until stearic acid first
Untill APEO is completely dissolved, stearic acid first polyoxyethylene ethereal solution is formed；
Step 3：Stearic acid first polyoxyethylene ethereal solution is cooled to after room temperature, while stirring be added dropwise rosin, tung oil, cannabis oil,
Continue to stir 20 ~ 40min after triethanolamine, color stuffing, epoxy organosilicon, completion of dropping；
Step 4：Continue to add coalescents, methyl polyester resin, bentonite, thickener, corrosion inhibiter, surface work into reactor
Property agent, stir in addition, and it is 50 ~ 70 DEG C to keep temperature in reactor, after 20 ~ 40min of stirring, 1 ~ 3h of standing is produced
Protective paint finished product.
8. the preparation method of the protective paint of a kind of environmental protection machinery equipment according to claim 7, it is characterised in that described
The natural type of cooling is cooled in step 3.