CN107141638A - A kind of PVC foam floor glue middle level - Google Patents
A kind of PVC foam floor glue middle level Download PDFInfo
- Publication number
- CN107141638A CN107141638A CN201710343261.7A CN201710343261A CN107141638A CN 107141638 A CN107141638 A CN 107141638A CN 201710343261 A CN201710343261 A CN 201710343261A CN 107141638 A CN107141638 A CN 107141638A
- Authority
- CN
- China
- Prior art keywords
- parts
- mixing
- mass ratio
- middle level
- pvc foam
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of PVC foam floor glue middle level, according to the mass fraction, specifically it is made by following component：50 60 parts of the positive 7 type resin-oatmeal of Inner Mongol monarch, 20 30 parts of the positive 5 type resin-oatmeal of Inner Mongol monarch, 10 20 parts of plasticiser, 30 40 parts of calcium powder, 0.3 0.6 parts of stabilizer, 59 parts of brightening agent, 0.04 0.08 parts of colorant, 39 parts of impact modifier, 1.5 3.8 parts of lubricant.A kind of PVC foam floor glue middle level provided by experiment, the present invention, passes through the formula of feed change, compared to existing PVC foam plate, its tensile strength is greatly promoted, and reaches the ability of more preferable resistance to deformation, when as floor glue middle level, the depression of floor glue during use can be effectively prevented.
Description
Technical field
The invention belongs to high-molecular compound technical field, and in particular to a kind of PVC foam floor glue middle level.
Background technology
PVC foam plate, also referred to as foamed polyvinyl chloride plate.Be widely used in car, railway carriage ceiling, casing sandwich layer,
Interior decoration plate, skin plate, interior trim plate, office, house, public place building compartment, commercialization decoration
Frame, used in dustless room plate, ceiling board, screen printing, computer lettering, advertisement sign, panel, mark industry and the changes such as plate photograph album plate
Work antiseptic project, thermoforming part, freezer plate, special prepressing reserving works, environmentally friendly template die, sports equipment, cultivation material, beach are prevented
Damp facility, water-resistant material, art designing's material and various light dividing plates replace glass ceiling etc..
When as floor glue middle level, PVC foam plate need to have the ability of good resistance to deformation, due to being used as floor glue
The thickness of PVC foam plate is most thick during middle level, accordingly, it would be desirable to adjust the composition proportion of raw material, reaches that preferably resistance becomes with this
The ability of shape, prevents the depression of floor glue during use.
The content of the invention
In order to solve the above problems, the invention provides a kind of PVC foam floor glue middle level.
The present invention is achieved through the following technical solutions：
A kind of PVC foam floor glue middle level, according to the mass fraction, is specifically made by following component：The positive 7 type tree of Inner Mongol monarch
50-60 parts of cosmetics, 20-30 parts of Inner Mongol monarch positive 5 type resin-oatmeal, 10-20 parts of plasticiser, 30-40 parts of calcium powder, stabilizer 0.3-
0.6 part, 5-9 parts of brightening agent, 0.04-0.08 parts of colorant, 3-9 parts of impact modifier, 1.5-3.8 parts of lubricant；
Further, the plasticiser, by DOP, ESO, DEHP 5-7 in mass ratio:15-25:It is made after 1-4 mixing；
Further, the calcium powder, by coarse whiting, calcium activated 45-60 in mass ratio:It is made after 9-13 mixing；
Further, the stabilizer, by BP-234,665A, 338A 9-15 in mass ratio:4-7:It is made after 1-4 mixing；
Further, the brightening agent, by titanium dioxide, fluorescent whitening agent 800-1000 in mass ratio:Made after 1-2 mixing
；
Further, the colorant, by VB7381, VB7387 4-6 in mass ratio:It is made after 1-2 mixing；
Further, the impact modifier, by P551A, P710 1-5 in mass ratio:It is made after 4-7 mixing.
Compared with prior art, the beneficial effects of the invention are as follows：
By experiment, a kind of PVC foam floor glue middle level for providing of the present invention, by the formula of feed change, compared to
Existing PVC foam plate, its tensile strength is greatly promoted, and reaches the ability of more preferable resistance to deformation, is being used as floor glue middle level
When, it can effectively prevent the depression of floor glue during use.
Embodiment
The preferred embodiments of the present invention are illustrated below, it will be appreciated that preferred embodiment described herein is only used
In the description and interpretation present invention, it is not intended to limit the present invention.
Embodiment 1
A kind of PVC foam floor glue middle level, according to the mass fraction, is specifically made by following component：The positive 7 type tree of Inner Mongol monarch
50 parts of cosmetics, 20 parts of the positive 5 type resin-oatmeal of Inner Mongol monarch, 10 parts of plasticiser, 30 parts of calcium powder, 0.3 part of stabilizer, 5 parts of brightening agent, color
0.04 part of material, 3 parts of impact modifier, 1.5 parts of lubricant；
Further, the plasticiser, by DOP, ESO, DEHP in mass ratio 5:15:It is made after 1 mixing；
Further, the calcium powder, by coarse whiting, calcium activated in mass ratio 45:It is made after 9 mixing；
Further, the stabilizer, by BP-234,665A, 338A in mass ratio 9:4:It is made after 1 mixing；
Further, the brightening agent, by titanium dioxide, fluorescent whitening agent in mass ratio 800:It is made after 1 mixing；
Further, the colorant, by VB7381, VB7387 in mass ratio 4:It is made after 1 mixing；
Further, the impact modifier, by P551A, P710 in mass ratio 1:It is made after 4 mixing.
Embodiment 2
A kind of PVC foam floor glue middle level, according to the mass fraction, is specifically made by following component：The positive 7 type tree of Inner Mongol monarch
60 parts of cosmetics, 30 parts of the positive 5 type resin-oatmeal of Inner Mongol monarch, 20 parts of plasticiser, 40 parts of calcium powder, 0.6 part of stabilizer, 9 parts of brightening agent, color
0.08 part of material, 9 parts of impact modifier, 3.8 parts of lubricant；
Further, the plasticiser, by DOP, ESO, DEHP in mass ratio 7:25:It is made after 4 mixing；
Further, the calcium powder, by coarse whiting, calcium activated in mass ratio 60:It is made after 13 mixing；
Further, the stabilizer, by BP-234,665A, 338A in mass ratio 15:7:It is made after 4 mixing；
Further, the brightening agent, by titanium dioxide, fluorescent whitening agent in mass ratio 1000:It is made after 1 mixing；
Further, the colorant, by VB7381, VB7387 in mass ratio 6:It is made after 1 mixing；
Further, the impact modifier, by P551A, P710 in mass ratio 5:It is made after 4 mixing.
Embodiment 3
A kind of PVC foam floor glue middle level, according to the mass fraction, is specifically made by following component：The positive 7 type tree of Inner Mongol monarch
55 parts of cosmetics, 25 parts of the positive 5 type resin-oatmeal of Inner Mongol monarch, 15 parts of plasticiser, 35 parts of calcium powder, 0.4 part of stabilizer, 7 parts of brightening agent, color
0.06 part of material, 6 parts of impact modifier, 2.2 parts of lubricant；
Further, the plasticiser, by DOP, ESO, DEHP in mass ratio 6:10:It is made after 3 mixing；
Further, the calcium powder, by coarse whiting, calcium activated in mass ratio 55:It is made after 12 mixing；
Further, the stabilizer, by BP-234,665A, 338A in mass ratio 12:5:It is made after 3 mixing；
Further, the brightening agent, by titanium dioxide, fluorescent whitening agent in mass ratio 900:It is made after 1 mixing；
Further, the colorant, by VB7381, VB7387 in mass ratio 5:It is made after 1.5 mixing；
Further, the impact modifier, by P551A, P710 in mass ratio 4:It is made after 7 mixing.
Embodiment 4
A kind of PVC foam floor glue middle level, according to the mass fraction, is specifically made by following component：The positive 7 type tree of Inner Mongol monarch
53 parts of cosmetics, 22 parts of the positive 5 type resin-oatmeal of Inner Mongol monarch, 11 parts of plasticiser, 31 parts of calcium powder, 0.4 part of stabilizer, 6 parts of brightening agent, color
0.05 part of material, 4 parts of impact modifier, 2.1 parts of lubricant；
Further, the plasticiser, by DOP, ESO, DEHP in mass ratio 6:17:It is made after 3 mixing；
Further, the calcium powder, by coarse whiting, calcium activated in mass ratio 50:It is made after 11 mixing；
Further, the stabilizer, by BP-234,665A, 338A in mass ratio 13:5:It is made after 3 mixing；
Further, the brightening agent, by titanium dioxide, fluorescent whitening agent in mass ratio 860:It is made after 2 mixing；
Further, the colorant, by VB7381, VB7387 in mass ratio 5:It is made after 2 mixing；
Further, the impact modifier, by P551A, P710 in mass ratio 3:It is made after 4 mixing.
Embodiment 5
A kind of PVC foam floor glue middle level, according to the mass fraction, is specifically made by following component：The positive 7 type tree of Inner Mongol monarch
58 parts of cosmetics, 29 parts of the positive 5 type resin-oatmeal of Inner Mongol monarch, 17 parts of plasticiser, 37 parts of calcium powder, 0.5 part of stabilizer, 8 parts of brightening agent, color
0.08 part of material, 7 parts of impact modifier, 3.5 parts of lubricant；
Further, the plasticiser, by DOP, ESO, DEHP in mass ratio 6:20:It is made after 3 mixing；
Further, the calcium powder, by coarse whiting, calcium activated in mass ratio 58:It is made after 10 mixing；
Further, the stabilizer, by BP-234,665A, 338A in mass ratio 12:6:It is made after 1 mixing；
Further, the brightening agent, by titanium dioxide, fluorescent whitening agent in mass ratio 900:It is made after 2 mixing；
Further, the colorant, by VB7381, VB7387 in mass ratio 5:It is made after 2 mixing；
Further, the impact modifier, by P551A, P710 in mass ratio 1:It is made after 5 mixing.
Control group
Existing PVC foam plate.
Tensile strength during above-mentioned 6 kinds of PVC foams plate same thickness is measured, as a result such as table 1：
Table 1
| Tensile strength (MPa) | |
| Embodiment 1 | 82.5 |
| Embodiment 2 | 85.7 |
| Embodiment 3 | 84.2 |
| Embodiment 4 | 81.0 |
| Embodiment 5 | 83.6 |
| Control group | 60.8 |
As shown in Table 1, a kind of PVC foam floor glue middle level for providing of the present invention, by the formula of feed change, compared to
Existing PVC foam plate, its tensile strength is greatly promoted, and reaches the ability of more preferable resistance to deformation, is being used as floor glue middle level
When, it can effectively prevent the depression of floor glue during use.
Finally it should be noted that：The preferred embodiments of the present invention are these are only, are not intended to limit the invention, although
The present invention is described in detail with reference to embodiment, for those skilled in the art, it still can be to foregoing
Technical scheme described in each embodiment is modified, or to which part technical characteristic carry out equivalent substitution, but it is all
Within the spirit and principles in the present invention, any modification, equivalent substitution and improvements made etc. should be included in the protection of the present invention
Within the scope of.
Claims (9)
1. a kind of PVC foam floor glue middle level, it is characterised in that according to the mass fraction, is specifically made by following component：The Inner Mongol
It is 50-60 parts of monarch's positive 7 type resin-oatmeal, 20-30 parts of Inner Mongol monarch positive 5 type resin-oatmeal, 10-20 parts of plasticiser, 30-40 parts of calcium powder, steady
Determine 0.3-0.6 parts of agent, 5-9 parts of brightening agent, 0.04-0.08 parts of colorant, 3-9 parts of impact modifier, 1.5-3.8 parts of lubricant；
The plasticiser, by DOP, ESO, DEHP 5-7 in mass ratio:15-25:It is made after 1-4 mixing；
The calcium powder, by coarse whiting, calcium activated 45-60 in mass ratio:It is made after 9-13 mixing；
The stabilizer, by BP-234,665A, 338A 9-15 in mass ratio:4-7:It is made after 1-4 mixing；
The brightening agent, by titanium dioxide, fluorescent whitening agent 800-1000 in mass ratio:It is made after 1-2 mixing；
The colorant, by VB7381, VB7387 4-6 in mass ratio:It is made after 1-2 mixing；
The impact modifier, by P551A, P710 1-5 in mass ratio:It is made after 4-7 mixing.
2. a kind of PVC foam floor glue middle level according to claim 1, it is characterised in that according to the mass fraction, specifically by
Following component is made：53-58 parts of Inner Mongol monarch positive 7 type resin-oatmeal, 23-26 parts of Inner Mongol monarch positive 5 type resin-oatmeal, plasticiser 13-
16 parts, 32-38 parts of calcium powder, 0.4-0.5 parts of stabilizer, 6-8 parts of brightening agent, 0.05-0.07 parts of colorant, 5-7 parts of impact modifier, profit
1.9-2.5 parts of lubrication prescription.
3. a kind of PVC foam floor glue middle level according to claim 1, it is characterised in that according to the mass fraction, specifically by
Following component is made：55 parts of the positive 7 type resin-oatmeal of Inner Mongol monarch, 25 parts of the positive 5 type resin-oatmeal of Inner Mongol monarch, 15 parts of plasticiser, calcium powder
35 parts, 0.4 part of stabilizer, 7 parts of brightening agent, 0.06 part of colorant, 6 parts of impact modifier, 2.2 parts of lubricant.
4. a kind of PVC foam floor glue middle level according to claim 1, it is characterised in that:The plasticiser, by DOP,
ESO, DEHP in mass ratio 6:10:It is made after 3 mixing.
5. a kind of PVC foam floor glue middle level according to claim 1, it is characterised in that:The calcium powder, by coarse whiting, work
Property calcium in mass ratio 55:It is made after 12 mixing.
6. a kind of PVC foam floor glue middle level according to claim 1, it is characterised in that:The stabilizer, by BP-
234th, 665A, 338A in mass ratio 12:5:It is made after 3 mixing.
7. a kind of PVC foam floor glue middle level according to claim 1, it is characterised in that:The brightening agent, by titanium white
Powder, fluorescent whitening agent in mass ratio 900:It is made after 1 mixing.
8. a kind of PVC foam floor glue middle level according to claim 1, it is characterised in that:The colorant, by VB7381,
VB7387 in mass ratio 5:It is made after 1.5 mixing.
9. a kind of PVC foam floor glue middle level according to claim 1, it is characterised in that:The impact modifier, by
P551A, P710 in mass ratio 3:It is made after 4 mixing.