CN107141578A - Improve low-smoke halogen-free inflaming-retarding cable - Google Patents
Improve low-smoke halogen-free inflaming-retarding cable Download PDFInfo
- Publication number
- CN107141578A CN107141578A CN201710445572.4A CN201710445572A CN107141578A CN 107141578 A CN107141578 A CN 107141578A CN 201710445572 A CN201710445572 A CN 201710445572A CN 107141578 A CN107141578 A CN 107141578A
- Authority
- CN
- China
- Prior art keywords
- parts
- smoke halogen
- low
- free inflaming
- retarding cable
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Low-smoke halogen-free inflaming-retarding cable, including insulating barrier are improved the invention discloses one kind, the insulating barrier is made up of the component comprising following parts by weight:Resin binder:100 parts, compatilizer:3~8 parts, inorganic combustion inhibitor:60~70 parts, coupling agent:0.5~3 part, antioxidant:0.1~1.5 part, lubricant:5~10 parts.The improvement low-smoke halogen-free inflaming-retarding cable that the present invention is provided, by preparing the improvement of formula, reduces the addition of inorganic metal fire retardant, while cable low-smoke non-halogen flame-retardant performance is ensured, improves the tensile strength and resistance to tearing energy of cable.
Description
Technical field
The present invention relates to a kind of halogen-free cable, and in particular to improves low-smoke halogen-free inflaming-retarding cable.
Background technology
In recent years, it has been found that dense smoke that personnel's cause of death more than 80% in fire incident is produced with material and poisonous
Gas is relevant.With developing rapidly for China's modern industry, Safety countermeasure also should be more and more perfect, many large-scale public
Place, for the secondary disaster (substantial amounts of smog and sour gas are produced during cable fire) for avoiding ignition of cable from causing, to specializing in
Transmission electric energy and the electric wire that uses of communication signal, are not required nothing more than with when cable and surrounding environment catch fire, with can hinder
The only fire resistance such as propagation of flame, and cable can be maintained to continue to transmit electric energy and communication signal, and should also have in burning
Low-smoke, produce gas attack it is low, beneficial to worker safety withdraw scene performance, i.e., should make cable have Halogen,
The performance such as low cigarette, fire-retardant.
Cable insulation refers to the clad that one layer is played insulating effect outside cable core in the construction of cable, the insulation of current cable
Layer is mainly made up of polymer.Low-smoke halogen-free combustion-preventing cable insulation layer is general to use polyolefin as base-material, because polyolefin is pure
Hydrocarbon, resolves into water and carbon dioxide during burning, obvious smog and pernicious gas are not produced.It is simultaneously full in order to reach
Sufficient Halogen, low cigarette, fire-retardant target, current topmost method are a large amount of addition aluminium hydroxides or hydrogen-oxygen in cable insulation
Change the inorganic combustion inhibitors such as magnesium, its loading generally requires the amount more than base-material, and this is greatly lowered the mechanical-physical of material
Can, the performance indications such as its tensile strength, elongation at break is declined to a great extent, the ability for then bearing mechanical external force declines.Largely
The filling of inorganic matter, can also cause the resistance to tearing of CABLE MATERIALS to be deteriorated, once cable locally produces small gap after small gap, stress
Can progressively it expand, and stress is bigger, and the speed that breach expands is faster, ultimately results in cable insulation sleeve and integrally ruptures.
The content of the invention
The technical problems to be solved by the invention are to add a large amount of inorganic metals in the insulating barrier of existing halogen-free flame-retardant cable
Fire retardant, greatly reduces the tensile strength and resistance to tearing energy of cable, causes the quality reduction that cable is overall, it is therefore intended that carry
For improving low-smoke halogen-free inflaming-retarding cable, by preparing the improvement of formula, the addition of inorganic metal fire retardant is reduced, is being ensured
While cable low-smoke non-halogen flame-retardant performance, the tensile strength and resistance to tearing energy of cable are improved.
The present invention is achieved through the following technical solutions:
Low-smoke halogen-free inflaming-retarding cable, including insulating barrier are improved, the insulating barrier is made up of the component comprising following parts by weight:
Resin binder:100 parts,
Compatilizer:3~8 parts,
Inorganic combustion inhibitor:60~70 parts,
Coupling agent:0.5~3 part,
Antioxidant:0.1~1.5 part,
Lubricant:5~10 parts.
Preferably, the insulating barrier is made up of the component comprising following parts by weight:
Resin binder:100 parts,
Compatilizer:5 parts,
Inorganic combustion inhibitor:65 parts,
Coupling agent:2 parts,
Antioxidant:0.9 part,
Lubricant:8 parts.
Preferably, the resin binder is the mixture of LLDPE and ethylene-ethyl acrylate copolymer
Material.
Preferably, the component proportion of the ethylene-ethyl acrylate copolymer and LLDPE is 1:6~1:
10。
Preferably, the compatilizer is the vinyl-acrylate copolymer that copolymer-maleic anhydride is modified.
Preferably, the inorganic combustion inhibitor is one or both of aluminium hydroxide and magnesium hydroxide mixture.
Preferably, the coupling agent coordination build titanate coupling agent.
Preferably, (β-(3, the 5- three-level butyl -4- hydroxy phenyls) propionic acid) pentaerythritol ester of antioxidant four and double ten
The mixed material of two carbon alcohol esters, and the proportioning of the mixed material is followed successively by 10:1.
Preferably, the lubricant is magnesium stearate and the mixture of silicone powder.
The present invention compared with prior art, has the following advantages and advantages:
Low-smoke halogen-free inflaming-retarding cable is improved the invention provides one kind, by preparing the improvement of formula, inorganic gold is reduced
Belong to the addition of fire retardant, while cable low-smoke non-halogen flame-retardant performance is ensured, improve the tensile strength of cable and tear-resistant
Performance.
Embodiment
For the object, technical solutions and advantages of the present invention are more clearly understood, with reference to embodiment, to present invention work
Further to describe in detail, exemplary embodiment and its explanation of the invention is only used for explaining the present invention, is not intended as to this
The restriction of invention.
Embodiment 1
Low-smoke halogen-free inflaming-retarding cable, including insulating barrier are improved the invention provides one kind, the insulating barrier is by comprising following
The component of parts by weight is made:
Resin binder:100 parts,
The vinyl-acrylate copolymer that copolymer-maleic anhydride is modified:3 parts,
Aluminium hydroxide:60 parts,
It is coordinated build titanate coupling agent:0.5 part,
Antioxidant:0.1 part,
Lubricant:5 parts;
The resin binder is the mixed material of LLDPE and ethylene-ethyl acrylate copolymer, and second
The component proportion of alkene-ethyl acrylate copolymer and LLDPE is 1:8.
(β-(3, the 5- three-level butyl -4- hydroxy phenyls) propionic acid) pentaerythritol ester of antioxidant four and double Lauryl Alcohol esters
Mixed material, and the proportioning of the mixed material is followed successively by 10:1.
The lubricant is the mixture of magnesium stearate and silicone powder, and the proportioning of magnesium stearate and silicone powder is 1:12.
Embodiment 2
Low-smoke halogen-free inflaming-retarding cable, including insulating barrier are improved the invention provides one kind, the insulating barrier is by comprising following
The component of parts by weight is made:
Resin binder:100 parts,
The vinyl-acrylate copolymer that copolymer-maleic anhydride is modified:8 parts,
Aluminium hydroxide:70 parts,
It is coordinated build titanate coupling agent:3 parts,
Antioxidant:1.5 parts,
Lubricant:10 parts;
The resin binder is the mixed material of LLDPE and ethylene-ethyl acrylate copolymer, and second
The component proportion of alkene-ethyl acrylate copolymer and LLDPE is 1:8.
(β-(3, the 5- three-level butyl -4- hydroxy phenyls) propionic acid) pentaerythritol ester of antioxidant four and double Lauryl Alcohol esters
Mixed material, and the proportioning of the mixed material is followed successively by 10:1.
The lubricant is the mixture of magnesium stearate and silicone powder, and the proportioning of magnesium stearate and silicone powder is 1:12.
Embodiment 3
Low-smoke halogen-free inflaming-retarding cable, including insulating barrier are improved the invention provides one kind, the insulating barrier is by comprising following
The component of parts by weight is made:
Resin binder:100 parts,
The vinyl-acrylate copolymer that copolymer-maleic anhydride is modified:5 parts,
Aluminium hydroxide:65 parts,
It is coordinated build titanate coupling agent:2 parts,
Antioxidant:0.9 part,
Lubricant:8 parts;
The resin binder is the mixed material of LLDPE and ethylene-ethyl acrylate copolymer, and second
The component proportion of alkene-ethyl acrylate copolymer and LLDPE is 1:8.
(β-(3, the 5- three-level butyl -4- hydroxy phenyls) propionic acid) pentaerythritol ester of antioxidant four and double Lauryl Alcohol esters
Mixed material, and the proportioning of the mixed material is followed successively by 10:1.
The lubricant is the mixture of magnesium stearate and silicone powder, and the proportioning of magnesium stearate and silicone powder is 1:12.
Embodiment 4
Low-smoke halogen-free inflaming-retarding cable, including insulating barrier are improved the invention provides one kind, the insulating barrier is by comprising following
The component of parts by weight is made:
Resin binder:100 parts,
The vinyl-acrylate copolymer that copolymer-maleic anhydride is modified:5 parts,
Aluminium hydroxide:65 parts,
It is coordinated build titanate coupling agent:2 parts,
Antioxidant:0.9 part,
Lubricant:8 parts;
The resin binder is the mixed material of LLDPE and ethylene-ethyl acrylate copolymer, and second
The component proportion of alkene-ethyl acrylate copolymer and LLDPE is 1:6.
(β-(3, the 5- three-level butyl -4- hydroxy phenyls) propionic acid) pentaerythritol ester of antioxidant four and double Lauryl Alcohol esters
Mixed material, and the proportioning of the mixed material is followed successively by 10:1.
The lubricant is the mixture of magnesium stearate and silicone powder, and the proportioning of magnesium stearate and silicone powder is 1:12.
Embodiment 5
Low-smoke halogen-free inflaming-retarding cable, including insulating barrier are improved the invention provides one kind, the insulating barrier is by comprising following
The component of parts by weight is made:
Resin binder:100 parts,
The vinyl-acrylate copolymer that copolymer-maleic anhydride is modified:5 parts,
Aluminium hydroxide:65 parts,
It is coordinated build titanate coupling agent:2 parts,
Antioxidant:0.9 part,
Lubricant:8 parts;
The resin binder is the mixed material of LLDPE and ethylene-ethyl acrylate copolymer, and second
The component proportion of alkene-ethyl acrylate copolymer and LLDPE is 1:10.
(β-(3, the 5- three-level butyl -4- hydroxy phenyls) propionic acid) pentaerythritol ester of antioxidant four and double Lauryl Alcohol esters
Mixed material, and the proportioning of the mixed material is followed successively by 10:1.
The lubricant is the mixture of magnesium stearate and silicone powder, and the proportioning of magnesium stearate and silicone powder is 1:12.
Product will be prepared and carry out performance test, test result such as table 1
The performance test results of sample prepared by the embodiment 1~5 of table 1
Sample | Tensile strength (MPa) | Elongation at break (%) | Oxygen index (OI) (%) | Smoke density (Dm) |
Embodiment 1 | 21 | 450 | 30 | 105 |
Embodiment 2 | 23 | 460 | 31 | 102 |
Embodiment 3 | 25 | 480 | 35 | 98 |
Embodiment 4 | 22 | 470 | 33 | 101 |
Embodiment 5 | 24 | 470 | 33 | 99 |
Shown by the experimental data of table 1, the low-smoke halogen-free flame-proof cable material that the present invention is provided not only has good
Flame retardant effect, with excellent mechanical and physical performance is also shown, the performance indications such as its tensile strength, elongation at break are carried significantly
Rise, bear the ability enhancing of mechanical external force, be conducive to the quality for pointing out cable overall.
Above-described embodiment, has been carried out further to the purpose of the present invention, technical scheme and beneficial effect
Describe in detail, should be understood that the embodiment that the foregoing is only the present invention, be not intended to limit the present invention
Protection domain, within the spirit and principles of the invention, any modification, equivalent substitution and improvements done etc. all should be included
Within protection scope of the present invention.
Claims (9)
1. low-smoke halogen-free inflaming-retarding cable is improved, including insulating barrier, it is characterised in that the insulating barrier is by including following parts by weight
Component is made:
Resin binder:100 parts,
Compatilizer:3~8 parts,
Inorganic combustion inhibitor:60~70 parts,
Coupling agent:0.5~3 part,
Antioxidant:0.1~1.5 part,
Lubricant:5~10 parts.
2. improvement low-smoke halogen-free inflaming-retarding cable according to claim 1, it is characterised in that the insulating barrier is by comprising following
The component of parts by weight is made:
Resin binder:100 parts,
Compatilizer:5 parts,
Inorganic combustion inhibitor:65 parts,
Coupling agent:2 parts,
Antioxidant:0.9 part,
Lubricant:8 parts.
3. improvement low-smoke halogen-free inflaming-retarding cable according to claim 1, it is characterised in that the resin binder is linear low
The mixed material of density polyethylene and ethylene-ethyl acrylate copolymer.
4. improvement low-smoke halogen-free inflaming-retarding cable according to claim 3, it is characterised in that the ethylene-ethylacrylate
The component proportion of copolymer and LLDPE is 1:6~1:10.
5. improvement low-smoke halogen-free inflaming-retarding cable according to claim 1, it is characterised in that the compatilizer is maleic anhydride
Copolymer-modified vinyl-acrylate copolymer.
6. improvement low-smoke halogen-free inflaming-retarding cable according to claim 1, it is characterised in that the inorganic combustion inhibitor is hydrogen-oxygen
Change one or both of aluminium and magnesium hydroxide mixture.
7. improvement low-smoke halogen-free inflaming-retarding cable according to claim 1, it is characterised in that the coupling agent is coordinated build titanium
Acid esters coupling agent.
8. improvement the low-smoke halogen-free inflaming-retarding cable according to claim 1, it is characterised in that (β-(3,5- of antioxidant four
Three-level butyl -4- hydroxy phenyls) propionic acid) pentaerythritol ester and double Lauryl Alcohol esters mixed material, and the mixed material
Proportioning is followed successively by 10:1.
9. improvement low-smoke halogen-free inflaming-retarding cable according to claim 1, it is characterised in that the lubricant is magnesium stearate
With the mixture of silicone powder.