CN107138552A - A kind of production technology of the directly upper joint drawbench of continuous casting spillikin disk circle take-up - Google Patents
A kind of production technology of the directly upper joint drawbench of continuous casting spillikin disk circle take-up Download PDFInfo
- Publication number
- CN107138552A CN107138552A CN201710353438.1A CN201710353438A CN107138552A CN 107138552 A CN107138552 A CN 107138552A CN 201710353438 A CN201710353438 A CN 201710353438A CN 107138552 A CN107138552 A CN 107138552A
- Authority
- CN
- China
- Prior art keywords
- copper
- sedan
- chair
- disk circle
- straight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention proposes a kind of production technology of the directly upper joint drawbench of continuous casting spillikin disk circle take-up, and technological process is:Copper scrap (raw material) → line frequency furnace fusing → composition adjustment → horizontal continuous-casting → traction copper cash → copper cash disk circle winding;Big volume copper cash unwrapping wire → joint drawing (pre- sedan-chair is straight → drawing → essence sedan-chair directly → cut-out → polishing → chamfering) → product inspection → packaging and storage, present invention process changes the mode of piece production finished product of tradition for φ 12mm and following specification, take-up is justified using continuous casting billet deep bid, the technique that directly upper joint drawbench produces finished product, continuous production is accomplished, substantially increase production efficiency, also product head jaw vestige is not present, every sawing is not needed to turn around portion's defect, product lumber recovery is improved, combine drawbench simultaneously and possess that sedan-chair is straight and polishing action, product is directly spent, surface accuracy is greatly improved, expensive goods requirement can be reached, improve value of the product.
Description
Technical field
The present invention relates to the technical field of copper rod production technology, particularly a kind of continuous casting spillikin disk circle take-up is directly upper to combine
The production technology of drawbench.
Background technology
Traditional φ 6.0mm above ledrite continuous casting copper rod is used after continuous casting rod scale sawing, and upper vertical pulling machine produces finished product,
Vertical pulling machine production copper rod is all the production model of a stretching or plane skin, for φ 12mm and following specification, production efficiency
Lowly, and every must sawing turn around portion's jaw trace, reduce lumber recovery, therefore propose that a kind of continuous casting spillikin disk circle take-up is direct
The production technology of upper joint drawbench.
The content of the invention
The purpose of the present invention is exactly to solve the problems of the prior art, proposes a kind of continuous casting spillikin disk circle direct first line of a couplet of take-up
The production technology of drawbench is closed, take-up is justified using continuous casting billet deep bid, directly upper joint drawbench produces the technique of finished product, accomplished
Continuous production, substantially increases production efficiency, also in the absence of product head jaw vestige, it is not necessary to which the every sawing portion of turning around lacks
Fall into, product lumber recovery is improved.
To achieve the above object, the present invention proposes a kind of production of the directly upper joint drawbench of continuous casting spillikin disk circle take-up
Technique, comprises the following steps:
A by copper scrap raw material melted in line frequency furnace and carry out composition adjustment copper material composition for needed for copper it is molten
Liquid;
B copper solutions are copper wires blank by horizontal continuous-casting, are pulled out from thermal insulation furnace body;
C copper rods wire blank completes disk circle winding through supercooling, bending device;
Entered directly into after the heavy-weight coil copper wires unwrapping wire of d disks circle winding and continuously elongated deformation carried out in joint drawbench,
The polished machine polishing of bar after customized cut-off, sedan-chair are straight, then are discharged after automatic chamfering machine chamfering, tack by blanking rack;
E carries out finished product detection, certified products packaging and storage to the fixed length copper rod after drawing.
Preferably, the step c is further comprising the steps of:Cooling device, bending device, pass through cooling and bending device
Cooperation, avoid material fragility and reach purpose that copper rod line bends, the copper rod after bending carries out disk circle winding.
Preferably, copper bar disk justifies the specification no more than 12mm of the copper pole stock diameter wound in the step c.
Preferably, the step d is further comprising the steps of:Pre- sedan-chair is straight, continuous drawing, straight smart sedan-chair, polishing and chamfering, institute
Entered after stating big volume copper wires unwrapping wire in Yu Jiaozhi mechanisms, the copper cash after pre- sedan-chair is straight is deformed by continuous drawing, enters essence
Smart sedan-chair is carried out in Jiao Zhi mechanisms straight, be polished after customized cut-off and chamfering.
Beneficial effects of the present invention:The present invention technological process be:Copper scrap (raw material) → line frequency furnace fusing →
Composition adjustment → horizontal continuous-casting → traction copper cash → copper cash disk circle winding;Big volume copper cash unwrapping wire → (pre- sedan-chair is straight for joint drawing
→ drawing → essence sedan-chair is straight → cut-out → polishing → chamfering) → product inspection → packaging and storage, present invention process for φ 12mm and
Following specification changes the mode of piece production finished product of tradition, and take-up is justified using continuous casting billet deep bid, directly upper joint drawbench
The technique for producing finished product, has accomplished continuous production, has substantially increased production efficiency, also in the absence of product head jaw vestige, no
Every sawing is needed to turn around portion's defect, product lumber recovery is improved, while combining drawbench possesses that sedan-chair is straight and polishing action, production
Product are directly spent, surface accuracy is greatly improved, and can be reached expensive goods requirement, be improved value of the product.
The feature and advantage of the present invention will be described in detail by embodiment combination accompanying drawing.
Brief description of the drawings
Fig. 1 is that a kind of technological process of the production technology of directly upper joint drawbench of continuous casting spillikin disk circle take-up of the invention is shown
It is intended to;
Fig. 2 is a kind of founding traction knot of the production technology of directly upper joint drawbench of continuous casting spillikin disk circle take-up of the invention
Structure schematic diagram;
Fig. 3 is a kind of joint drawbench of the production technology of directly upper joint drawbench of continuous casting spillikin disk circle take-up of the invention
The schematic diagram of production.
Embodiment
Refering to a kind of production technology of the directly upper joint drawbench of continuous casting spillikin disk circle take-up of Fig. 1 to Fig. 3 present invention, including
Following steps:
A by copper scrap raw material melted in line frequency furnace and carry out composition adjustment copper material composition for needed for copper it is molten
Liquid;
B copper solutions are copper wires blank by horizontal continuous-casting, are pulled out from thermal insulation furnace body;
C copper rods wire blank completes disk circle winding through supercooling, bending device;
Entered directly into after the heavy-weight coil copper wires unwrapping wire of d disks circle winding and continuously elongated deformation carried out in joint drawbench,
The polished machine polishing of bar after customized cut-off, sedan-chair are straight, then are discharged after automatic chamfering machine chamfering, tack by blanking rack;
E carries out finished product detection, certified products packaging and storage to the fixed length copper rod after drawing.
The step c is further comprising the steps of:Cooling device, bending device, by cooling down the cooperation with bending device, keep away
Open material fragility and reach purpose that copper rod line bends, the copper rod after bending carries out disk circle winding.Copper bar disk in the step c
The specification no more than 12mm for the copper pole stock diameter that circle is wound.The step d is further comprising the steps of:Pre- sedan-chair is straight, continuous drawing
Pull out, smart sedan-chair is straight, polish and chamfering, entered after the big volume copper wires unwrapping wire in Yu Jiaozhi mechanisms, the copper cash warp after pre- sedan-chair is straight
Continuous drawing deformation is crossed, enters in Jing Jiaozhi mechanisms and carries out smart sedan-chair directly, be polished after customized cut-off and chamfering.
Present invention process changes the mode of piece production finished product of tradition for φ 12mm and following specification, using continuous casting
Base deep bid justifies take-up, and directly upper joint drawbench produces the technique of finished product, accomplished continuous production, substantially increases production effect
Rate, also in the absence of product head jaw vestige, it is not necessary to which every sawing is turned around portion's defect, product lumber recovery is improved, simultaneously
Joint drawbench possesses that sedan-chair is straight and polishing action, and product is directly spent, surface accuracy is greatly improved, and can reach expensive goods requirement,
Improve value of the product.
Above-described embodiment is the description of the invention, is not limitation of the invention, it is any to simple transformation of the present invention after
Scheme belong to protection scope of the present invention.
Claims (4)
1. a kind of production technology of the directly upper joint drawbench of continuous casting spillikin disk circle take-up, it is characterised in that:Comprise the following steps:
Copper scrap raw material are melted and carry out the copper solution of composition adjustment copper material composition for needed for by a in line frequency furnace;
B copper solutions are copper wires blank by horizontal continuous-casting, are pulled out from thermal insulation furnace body;
C copper rods wire blank completes disk circle winding through supercooling, bending device;
Entered directly into after the heavy-weight coil copper wires unwrapping wire of d disks circle winding and continuously elongated deformation, fixed length are carried out in joint drawbench
The polished machine polishing of bar after cut-out, sedan-chair are straight, then are discharged after automatic chamfering machine chamfering, tack by blanking rack;
E carries out finished product detection, certified products packaging and storage to the fixed length copper rod after drawing.
2. a kind of production technology of directly upper joint drawbench of continuous casting spillikin disk circle take-up as claimed in claim 1, its feature
It is:The step c is further comprising the steps of:Cooling device, bending device, by cooling down the cooperation with bending device, are avoided
Material fragility and reach the purpose that copper rod line bends, copper rod after bending carries out disk circle winding.
3. a kind of production technology of directly upper joint drawbench of continuous casting spillikin disk circle take-up as claimed in claim 1, its feature
It is:The step d is further comprising the steps of:Pre- sedan-chair is straight, continuous drawing, straight smart sedan-chair, polishing and chamfering, the big volume copper wires
Entered after unwrapping wire in Yu Jiaozhi mechanisms, the copper cash after pre- sedan-chair is straight is deformed by continuous drawing, is entered and is entered in Jing Jiaozhi mechanisms
Row essence sedan-chair is straight, is polished after customized cut-off and chamfering.
4. a kind of production technology of directly upper joint drawbench of continuous casting spillikin disk circle take-up as claimed in claim 1, its feature
It is:The specification no more than 12mm for the copper rod gauge or diameter of wire that copper bar disk circle is wound in the step c.